CN108999360A - A kind of metal fluorocarbon heat insulation decoration integrated plate production technology - Google Patents
A kind of metal fluorocarbon heat insulation decoration integrated plate production technology Download PDFInfo
- Publication number
- CN108999360A CN108999360A CN201810794338.7A CN201810794338A CN108999360A CN 108999360 A CN108999360 A CN 108999360A CN 201810794338 A CN201810794338 A CN 201810794338A CN 108999360 A CN108999360 A CN 108999360A
- Authority
- CN
- China
- Prior art keywords
- plate
- paint
- detection
- detect
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of metal fluorocarbon heat insulation decoration integrated plate production technologies, the metal fluorocarbon heat insulation decoration integrated plate production craft step is as follows: step 1: substrate inspection, the detection of length and width: bullet board ends 10 centimetres of left-right positions, midline positions, it is respectively measured at 1 with steel tape, it is accurate to 1 millimeter, takes the average value of this 3 measured values as plate face length (width) value.This process flow can carry out effective coating to fluorine carbon insulation and decoration, guarantee the quality stability of plate coating surface, Vinylidene Chloride diluent is used simultaneously, it can be improved dilution effect and evaporation rate, and isocyanates or polyamide curing agent can be selected according to the actual situation, have good solidification effect.
Description
Technical field
The present invention relates to fluorine carbon heat insulating decorative board production technical field more particularly to a kind of metal fluorocarbon are heat insulation decoration integrated
Board production technology.
Background technique
Metal fluorocarbon coating is a kind of efficient, multipurpose, and the fluorine carbon copolymer of chemosetting is that the bi-component room temperature of raw material is solid
Change coating, metal fluorocarbon coating has the excellent properties such as outstanding durability, protectiveness, dicoration, through outdoor long-time service and people
Work accelerated aging test shows that the fluorine carbon bond energy that fluorocarbon resin molecule connects in metal fluorocarbon coating enough supports anti-ultraviolet degradation and makees
With showing extremely excellent durability, UV resistant and against weather, keep metal fluorocarbon lacquer coat permanent perfect as new, subtract
The requirement repaired less.
In terms of the decorative panel selection of some high-end residentials, plate can also be processed using metal fluorocarbon coating, still
In current technique, the diluent selection for priming paint can generally select lacquer thinner, dilution of this diluent to paint
Speed is not fast enough, while in process flow, controlled in terms of the paint roller of finishing coat and drying it is incomplete so that finished product plate is easy
There is bubbling and dent and other issues.
Summary of the invention
The purpose of the present invention is to solve disadvantages existing in the prior art, and the one kind proposed has mosquito repellent and distributes
The coating of fragrance effect.
To achieve the goals above, present invention employs following technical solutions:
A kind of metal fluorocarbon heat insulation decoration integrated plate production technology, the metal fluorocarbon heat insulation decoration integrated plate production technology
Steps are as follows:
Step 1: substrate inspection, the detection of length and width: bullet board ends 10 centimetres of left-right positions, midline positions are used
Steel tape respectively measures at 1, is accurate to 1 millimeter, takes the average value of this 3 measured values as plate face length (width) value；
The detection of thickness: with bow compass and vernier caliper conjunction measuring, each 10 centimetres away from plate both sides, both ends, plotted point is each
A value (at 4) is surveyed, 10 centimetres away from plate both sides, respectively surveys 1 value (at 2) with cross central line plotted point, totally 6 measured values, essence
Really to 1 millimeter；
The detection of edge nonstraightness: plate is lain against on horizontal platform, is mutually leaned on the side of 2 meters of long guiding rulers with edges of boards, then use
Maximal clearance between the edge and guiding ruler side of the clearance gauge measurement plate that minimum thickness is 0.01 millimeter；
The detection of warped degree: lying against plate is concave upright on horizontal platform, edge-on above plate with 2 meters of long guiding rulers, then
The maximum chinky altitude between guiding ruler and plate is measured with the clearance gauge that minimum thickness is 0.01 millimeter.
Step 2: hair plates sanding, detects hair plates sanding finished plate thickness deviation: extracting 10% measurement therein.If there is
Rejected product continues checking next block of plate, if any continuous two pieces of rejected products, to expand measurement range to 50%；
The selection in abrasive band: the abrasive band of 40 mesh or 80 mesh is selected.
Step 3: UV infiltration priming paint (primary), detect plate gap and wet-film thickness: plate gap is no more than 20 centimetres,
Wet-film thickness is 20 ± 5 microns；
Detect UV priming paint levelability；
It detects the aridity of UV priming paint: being touched by naked hand, whether thoughts and feelings has viscous feel；
Detect the coating surface of plate: the case where having detected whether bubble, shrinkage cavity and being unevenly coated.
Step 4: paint film sanding (primary), whether detection production board base has bright spot: the bright spot of continuous three pieces of plate bases is no more than
10/square metre；
It detects whether sand occur show-through；
Select the suitable sand amount of cutting；
Moment checks plate face effect；
Paint film sanding abrasive band selects: abrasive band is 320 mesh.
Step 5: UV putty (infiltration priming paint is secondary), the gap between detection plate and plate: is no more than 20 centimetres；
Detection wet-film thickness: 50 ± 5 microns be should be.
Detect UV levelability；
Detection UV stationary state: being touched by naked hand, and whether thoughts and feelings has viscous feel；
Sampling Detection after paint film sanding: it chooses therein 1% and checks hardness, i.e., with the 3H pencil polished with 45 degree of angles edge paint
Film edge part is drawn forward, if can scratch paint film will adjust the intensity of illumination of lamp in time, until the paint film of continuous two boards is hard
Degree is qualified；
Detect curing temperature: time interval is 30 minutes；
Detect the painting surface layer of every block of plate: the case where having detected whether bubble, shrinkage cavity and being unevenly coated.
Step 6: paint film sanding (secondary), whether detection production board base has bright spot: the bright spot of continuous three pieces of plate bases is no more than
10/square metre；
It detects whether sand occur show-through；
Select the suitable sand amount of cutting；
Moment checks plate face effect；
Paint film sanding abrasive band selects: abrasive band is 320 mesh.
Step 7: rolling lacquer painting applies, the uniformity of former paint stirring: precipitation status of the former paint of detection in whipping process is detected,
Until being stirred to no precipitating；
The selection of diluent；
The addition of curing agent；
Adjust viscous viscosity: diluent additive amount is 15% or so of former paint.Viscosity is in 40-60 seconds/painting -4,25 DEG C (or 80-
90 seconds/apply -2,25 DEG C).
Select the sieve mesh number of filtering finishing coat；
The allotment of paint amount: finishing coat dosage is deployed according to the principle of " a small amount of multiple "；
Control roller speed: roller speed is 2-3 ms/min.
Adjust air pressure and atomization；
Detect the wet-film thickness of roller coating: wet-film thickness should be 35 ± 5 microns.
Step 8: the drying of finishing coat, setting baking temperature: 50 to 70 DEG C；
Setting baking time: 180 to 210 minutes；
The random sampling of drying process: the plate or while drying in batches for randomly selecting 1% from every batch of randomly select 1 block of plate
Material examines paint film pencil hardness；
It detects the solidification situation of paint film: viscous situation whether occurs；
It detects hardness of paint film: being not less than 2H.
Step 9: the case where examining plate coating surface.
Step 10: overlay film, detects whether the protective film of product；
Detect the compression strength of packing case；
Product quality list is detected whether；
Whether high-visible detect mark, work certificate, operation instructions, the text of product quality list and pattern.
Preferably, the type that diluent is selected in the 7th step is Vinylidene Chloride lacquer diluent.
Preferably, the type that curing agent is selected in the 7th step is polyamide or isocyanate curing agent.
A kind of metal fluorocarbon heat insulation decoration integrated plate production technology provided by the invention, this process flow can be to fluorine carbon
Insulation and decoration carries out effective coating, guarantees the quality stability of plate coating surface, while using Vinylidene Chloride diluent, can
Dilution effect and evaporation rate are improved, and isocyanates or polyamide curing agent can be selected according to the actual situation, tool
There is good solidification effect.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, below in conjunction with specific embodiment, to this
Invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, not
For limiting the present invention.
A kind of metal fluorocarbon heat insulation decoration integrated plate production technology, the metal fluorocarbon heat insulation decoration integrated plate production technology
Steps are as follows:
Step 1: substrate inspection, the detection of length and width: bullet board ends 10 centimetres of left-right positions, midline positions are used
Steel tape respectively measures at 1, is accurate to 1 millimeter, takes the average value of this 3 measured values as plate face length (width) value；
The detection of thickness: with bow compass and vernier caliper conjunction measuring, each 10 centimetres away from plate both sides, both ends, plotted point is each
A value (at 4) is surveyed, 10 centimetres away from plate both sides, respectively surveys 1 value (at 2) with cross central line plotted point, totally 6 measured values, essence
Really to 1 millimeter；
The detection of edge nonstraightness: plate is lain against on horizontal platform, is mutually leaned on the side of 2 meters of long guiding rulers with edges of boards, then use
Maximal clearance between the edge and guiding ruler side of the clearance gauge measurement plate that minimum thickness is 0.01 millimeter；
The detection of warped degree: lying against plate is concave upright on horizontal platform, edge-on above plate with 2 meters of long guiding rulers, then
The maximum chinky altitude between guiding ruler and plate is measured with the clearance gauge that minimum thickness is 0.01 millimeter.
Step 2: hair plates sanding, detects hair plates sanding finished plate thickness deviation: extracting 10% measurement therein.If there is
Rejected product continues checking next block of plate, if any continuous two pieces of rejected products, to expand measurement range to 50%；
The selection in abrasive band: the abrasive band of 40 mesh or 80 mesh is selected.
Step 3: UV infiltration priming paint (primary), detect plate gap and wet-film thickness: plate gap is no more than 20 centimetres,
Wet-film thickness is 20 ± 5 microns；
Detect UV priming paint levelability；
It detects the aridity of UV priming paint: being touched by naked hand, whether thoughts and feelings has viscous feel；
Detect the coating surface of plate: the case where having detected whether bubble, shrinkage cavity and being unevenly coated.
Step 4: paint film sanding (primary), whether detection production board base has bright spot: the bright spot of continuous three pieces of plate bases is no more than
10/square metre；
It detects whether sand occur show-through；
Select the suitable sand amount of cutting；
Moment checks plate face effect；
Paint film sanding abrasive band selects: abrasive band is 320 mesh.
Step 5: UV putty (infiltration priming paint is secondary), the gap between detection plate and plate: is no more than 20 centimetres；
Detection wet-film thickness: 50 ± 5 microns be should be.
Detect UV levelability；
Detection UV stationary state: being touched by naked hand, and whether thoughts and feelings has viscous feel；
Sampling Detection after paint film sanding: it chooses therein 1% and checks hardness, i.e., with the 3H pencil polished with 45 degree of angles edge paint
Film edge part is drawn forward, if can scratch paint film will adjust the intensity of illumination of lamp in time, until the paint film of continuous two boards is hard
Degree is qualified；
Detect curing temperature: time interval is 30 minutes；
Detect the painting surface layer of every block of plate: the case where having detected whether bubble, shrinkage cavity and being unevenly coated.
Step 6: paint film sanding (secondary), whether detection production board base has bright spot: the bright spot of continuous three pieces of plate bases is no more than
10/square metre；
It detects whether sand occur show-through；
Select the suitable sand amount of cutting；
Moment checks plate face effect；
Paint film sanding abrasive band selects: abrasive band is 320 mesh.
Step 7: rolling lacquer painting applies, the uniformity of former paint stirring: precipitation status of the former paint of detection in whipping process is detected,
Until being stirred to no precipitating；
The selection of diluent: the type of diluent is Vinylidene Chloride lacquer diluent；
The addition of curing agent: the type of curing agent is polyamide or isocyanate curing agent；
Adjust viscous viscosity: diluent additive amount is 15% or so of former paint.Viscosity is in 40-60 seconds/painting -4,25 DEG C (or 80-
90 seconds/apply -2,25 DEG C).
Select the sieve mesh number of filtering finishing coat；
The allotment of paint amount: finishing coat dosage is deployed according to the principle of " a small amount of multiple "；
Control roller speed: roller speed is 2-3 ms/min.
Adjust air pressure and atomization；
Detect the wet-film thickness of roller coating: wet-film thickness should be 35 ± 5 microns.
Step 8: the drying of finishing coat, setting baking temperature: 50 to 70 DEG C；
Setting baking time: 180 to 210 minutes；
The random sampling of drying process: the plate or while drying in batches for randomly selecting 1% from every batch of randomly select 1 block of plate
Material examines paint film pencil hardness；
It detects the solidification situation of paint film: viscous situation whether occurs；
It detects hardness of paint film: being not less than 2H.
Step 9: examining, compared according to content in table.
Step 10: overlay film, detects whether the protective film of product；
Detect the compression strength of packing case；
Product quality list is detected whether；
Whether high-visible detect mark, work certificate, operation instructions, the text of product quality list and pattern.
Claims (3)
1. a kind of metal fluorocarbon heat insulation decoration integrated plate production technology, it is characterised in that: the metal fluorocarbon is heat insulation decoration integrated
Steps are as follows for board production technology:
Step 1: substrate inspection, the detection of length and width: bullet board ends 10 centimetres of left-right positions, midline positions use coil of strip
Ruler respectively measures at 1, is accurate to 1 millimeter, takes the average value of this 3 measured values as plate face length (width) value；
The detection of thickness: with bow compass and vernier caliper conjunction measuring, each 10 centimetres away from plate both sides, both ends, plotted point respectively surveys one
A value (at 4), respectively surveys 1 value (at 2) with cross central line plotted point, totally 6 measured values, are accurate to 1 by 10 centimetres away from plate both sides
Millimeter；
The detection of edge nonstraightness: plate is lain against on horizontal platform, is mutually leaned on the side of 2 meters of long guiding rulers with edges of boards, then with minimum
With a thickness of the maximal clearance between the edge and guiding ruler side of 0.01 millimeter of clearance gauge measurement plate；
The detection of warped degree: lying against plate is concave upright on horizontal platform, edge-on above plate with 2 meters of long guiding rulers, then with most
The small clearance gauge with a thickness of 0.01 millimeter measures the maximum chinky altitude between guiding ruler and plate.
Step 2: hair plates sanding, detects hair plates sanding finished plate thickness deviation: extracting 10% measurement therein.If there is not conforming to
Lattice product continue checking next block of plate, if any continuous two pieces of rejected products, to expand measurement range to 50%；
The selection in abrasive band: the abrasive band of 40 mesh or 80 mesh is selected.
Step 3: UV infiltration priming paint (primary), detect plate gap and wet-film thickness: plate gap is no more than 20 centimetres, wet film
With a thickness of 20 ± 5 microns；
Detect UV priming paint levelability；
It detects the aridity of UV priming paint: being touched by naked hand, whether thoughts and feelings has viscous feel；
Detect the coating surface of plate: the case where having detected whether bubble, shrinkage cavity and being unevenly coated.
Step 4: paint film sanding (primary), whether detection production board base has bright spot: the bright spot of continuous three pieces of plate bases is no more than 10
A/square metre；
It detects whether sand occur show-through；
Select the suitable sand amount of cutting；
Moment checks plate face effect；
Paint film sanding abrasive band selects: abrasive band is 320 mesh.
Step 5: UV putty (infiltration priming paint is secondary), the gap between detection plate and plate: is no more than 20 centimetres；
Detection wet-film thickness: 50 ± 5 microns be should be.
Detect UV levelability；
Detection UV stationary state: being touched by naked hand, and whether thoughts and feelings has viscous feel；
Sampling Detection after paint film sanding: it chooses therein 1% and checks hardness, that is, use the 3H pencil polished with 45 degree of angles along paint film side
Edge point is drawn forward, if can scratch paint film will adjust the intensity of illumination of lamp in time, until the hardness of paint film of continuous two boards closes
Lattice；
Detect curing temperature: time interval is 30 minutes；
Detect the painting surface layer of every block of plate: the case where having detected whether bubble, shrinkage cavity and being unevenly coated.
Step 6: paint film sanding (secondary), whether detection production board base has bright spot: the bright spot of continuous three pieces of plate bases is no more than 10
A/square metre；
It detects whether sand occur show-through；
Select the suitable sand amount of cutting；
Moment checks plate face effect；
Paint film sanding abrasive band selects: abrasive band is 320 mesh.
Step 7: rolling lacquer painting applies, the uniformity of former paint stirring: precipitation status of the former paint of detection in whipping process is detected, until
It is stirred to no precipitating；
The selection of diluent；
The addition of curing agent；
Adjust viscous viscosity: diluent additive amount is 15% or so of former paint.Viscosity is in 40-60 seconds/painting -4,25 DEG C (or 80-90
Second/painting -2,25 DEG C).
Select the sieve mesh number of filtering finishing coat；
The allotment of paint amount: finishing coat dosage is deployed according to the principle of " a small amount of multiple "；
Control roller speed: roller speed is 2-3 ms/min.
Adjust air pressure and atomization；
Detect the wet-film thickness of roller coating: wet-film thickness should be 35 ± 5 microns.
Step 8: the drying of finishing coat, setting baking temperature: 50 to 70 DEG C；
Setting baking time: 180 to 210 minutes；
The random sampling of drying process: randomly select 1% plate or randomly select the inspection of 1 block of plate from every batch of when drying in batches
Test paint film pencil hardness；
It detects the solidification situation of paint film: viscous situation whether occurs；
It detects hardness of paint film: being not less than 2H.
Step 9: the case where examining plate coating surface.
Step 10: overlay film, detects whether the protective film of product；
Detect the compression strength of packing case；
Product quality list is detected whether；
Whether high-visible detect mark, work certificate, operation instructions, the text of product quality list and pattern.
2. a kind of metal fluorocarbon heat insulation decoration integrated plate production technology according to claim 1, it is characterised in that: described
The type that diluent is selected in seven steps is Vinylidene Chloride lacquer diluent.
3. a kind of metal fluorocarbon heat insulation decoration integrated plate production technology according to claim 1, it is characterised in that: described
The type that curing agent is selected in seven steps is polyamide or isocyanate curing agent.