CN108841272A - 一种外墙保温防渗漏负离子涂料 - Google Patents

一种外墙保温防渗漏负离子涂料 Download PDF

Info

Publication number
CN108841272A
CN108841272A CN201810466193.8A CN201810466193A CN108841272A CN 108841272 A CN108841272 A CN 108841272A CN 201810466193 A CN201810466193 A CN 201810466193A CN 108841272 A CN108841272 A CN 108841272A
Authority
CN
China
Prior art keywords
parts
exterior
heat insulation
negative ion
wall heat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810466193.8A
Other languages
English (en)
Inventor
朱德官
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Lead Technology Co Ltd
Original Assignee
Shanghai Lead Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Lead Technology Co Ltd filed Critical Shanghai Lead Technology Co Ltd
Priority to CN201810466193.8A priority Critical patent/CN108841272A/zh
Publication of CN108841272A publication Critical patent/CN108841272A/zh
Withdrawn legal-status Critical Current

Abstract

本发明提供一种外墙保温防渗漏负离子涂料,涉及建筑涂料领域，其特征在于由质量份的以下原料组成：包括电气石粉10‑20份、稀土镧元素1‑10份、硅藻土10‑18份、碳酸钙15‑25份、二氧化钛5‑10份、二氧化硅5‑10份、空心玻璃微珠10‑20份、玻璃纤维3‑10份、白水泥25‑35份、硅酸铝粉3‑9份、水玻璃2‑10份、助剂2‑10份、丙烯酸脂乳液90‑120份，其有益效果是：生产工艺简单环保，原料价廉易得，集多种功能于一体保温隔热、防渗漏效果好、有效的释放负离子增加空气中负离子的浓度，净化空气减少空气污染。

Description

一种外墙保温防渗漏负离子涂料
技术领域
本发明涉及建筑涂料领域，具体涉及一种外墙保温防渗漏负离子涂料。
背景技术
保温涂料是近几年发展起来的新型功能涂料。将其用于建筑物的表面。有效隔离室内外温度变化起到隔热保温的作用，而现有的外墙保温涂料保存在着保温效果差、容易渗漏，不友好环境等技术缺陷，针对现有技术的不足，因此发明一种外墙保温防渗漏负离子涂料，其有益效果是：生产工艺简单环保，原料价廉易得，集多种功能于一体保温隔热、防渗漏效果好、有效的释放负离子增加空气中负离子的浓度，净化空气减少空气污染。
发明内容
本发明就是为了解决现有技术中的问题，提供一种外墙保温防渗漏负离子涂料。
本发明所要解决的技术问题，通过以下技术方案实现。
一种外墙保温防渗漏负离子涂料，其特征在于由质量份的以下原料组成：包括电气石粉10-20份、稀土镧元素1-10份、硅藻土10-18份、碳酸钙15-25份、二氧化钛5-10份、二氧化硅5-10份、空心玻璃微珠10-20份、玻璃纤维3-10份、白水泥25-35份、硅酸铝粉3-9份、水玻璃2-10份、助剂2-10份、丙烯酸脂乳液90-120份。
进一步的所述一种外墙保温负离子涂料，其特征在于由质量份的以下原料组成：包括电气石粉12-18份、稀土镧元素2-9份、硅藻土10-16份、碳酸钙20-25份、二氧化钛6-10份、二氧化硅6-10份、空心玻璃微珠12-18份、玻璃纤维3-9份、白水泥25-30份、硅酸铝粉4-9份、水玻璃4-10份、助剂2-10份、丙烯酸脂乳液100-120份。
进一步的所述一种外墙保温负离子涂料， 其特征在于所述助剂为改性剂、成膜剂、分散剂、消泡剂、保水剂、流平剂份量比为1:1:1:1:1:1。
进一步的所述一种外墙保温负离子涂料，制备方法包括以下步骤：先将所述硅酸铝粉、水玻璃、助剂、丙烯酸脂乳液加入到调速搅拌机中中速搅拌30-45分钟；再加入所述电气石粉、稀土镧元素、硅藻土、碳酸钙、二氧化钛、二氧化硅、空心玻璃微珠、玻璃纤维、白水泥高速搅拌45-60分钟即可制得成品。
本发明其有益效果是：生产工艺简单环保，原料价廉易得，集多种功能于一体保温隔热、防渗漏效果好、有效的释放负离子增加空气中负离子的浓度，净化空气减少空气污染。
具体实施方式
实施例1：一种外墙保温防渗漏负离子涂料，其特征在于由质量份的以下原料组成：包括电气石粉10份、稀土镧元素5份、硅藻土10份、碳酸钙25份、二氧化钛10份、二氧化硅8份、空心玻璃微珠15份、玻璃纤维6份、白水泥35份、硅酸铝粉9份、水玻璃10份、助剂5份、丙烯酸脂乳液100份。
本实施例所述一种外墙保温负离子涂料， 其特征在于所述助剂为改性剂、成膜剂、分散剂、消泡剂、保水剂、流平剂份量比为1:1:1:1:1:1。
本实施例所述一种外墙保温负离子涂料，制备方法包括以下步骤：先将所述硅酸铝粉、水玻璃、助剂、丙烯酸脂乳液加入到调速搅拌机中中速搅拌45分钟；再加入所述电气石粉、稀土镧元素、硅藻土、碳酸钙、二氧化钛、二氧化硅、空心玻璃微珠、玻璃纤维、白水泥高速搅拌60分钟即可制得成品。
实施例2：一种外墙保温防渗漏负离子涂料，其特征在于由质量份的以下原料组成：包括电气石粉15份、稀土镧元素7份、硅藻土15份、碳酸钙21份、二氧化钛8份、二氧化硅8份、空心玻璃微珠18份、玻璃纤维6份、白水泥31份、硅酸铝粉7份、水玻璃10份、助剂5份、丙烯酸脂乳液110份。
本实施例所述一种外墙保温负离子涂料， 其特征在于所述助剂为改性剂、成膜剂、分散剂、消泡剂、保水剂、流平剂份量比为1:1:1:1:1:1。
本实施例所述一种外墙保温负离子涂料，制备方法包括以下步骤：先将所述硅酸铝粉、水玻璃、助剂、丙烯酸脂乳液加入到调速搅拌机中中速搅拌45分钟；再加入所述电气石粉、稀土镧元素、硅藻土、碳酸钙、二氧化钛、二氧化硅、空心玻璃微珠、玻璃纤维、白水泥高速搅拌60分钟即可制得成品。
实施例3：一种外墙保温防渗漏负离子涂料，其特征在于由质量份的以下原料组成：包括电气石粉20份、稀土镧元素10份、硅藻土18份、碳酸钙18份、二氧化钛10份、二氧化硅8份、空心玻璃微珠20份、玻璃纤维10份、白水泥35份、硅酸铝粉7份、水玻璃10份、助剂10份、丙烯酸脂乳液120份。
本实施例所述一种外墙保温负离子涂料， 其特征在于所述助剂为改性剂、成膜剂、分散剂、消泡剂、保水剂、流平剂份量比为1:1:1:1:1:1。
本实施例所述一种外墙保温负离子涂料，制备方法包括以下步骤：先将所述硅酸铝粉、水玻璃、助剂、丙烯酸脂乳液加入到调速搅拌机中中速搅拌45分钟；再加入所述电气石粉、稀土镧元素、硅藻土、碳酸钙、二氧化钛、二氧化硅、空心玻璃微珠、玻璃纤维、白水泥高速搅拌60分钟即可制得成品。
上述实施例仅是对本发明的说明并非对本发明做出形式上的限制，在不脱离本发明的技术方案范围之内任何利用上述揭示的技术内容做出简单变化的等同等方案均属于本发明的保护范围。

Claims (4)

1.一种外墙保温防渗漏负离子涂料，其特征在于由质量份的以下原料组成：包括电气石粉10-20份、稀土镧元素1-10份、硅藻土10-18份、碳酸钙15-25份、二氧化钛5-10份、二氧化硅5-10份、空心玻璃微珠10-20份、玻璃纤维3-10份、白水泥25-35份、硅酸铝粉3-9份、水玻璃2-10份、助剂2-10份、丙烯酸脂乳液90-120份。
2.根据权利要求1所述一种外墙保温负离子涂料，其特征在于由质量份的以下原料组成：包括电气石粉12-18份、稀土镧元素2-9份、硅藻土10-16份、碳酸钙20-25份、二氧化钛6-10份、二氧化硅6-10份、空心玻璃微珠12-18份、玻璃纤维3-9份、白水泥25-30份、硅酸铝粉4-9份、水玻璃4-10份、助剂2-10份、丙烯酸脂乳液100-120份。
3.根据权利要求1所述一种外墙保温负离子涂料， 其特征在于所述助剂为改性剂、成膜剂、分散剂、消泡剂、保水剂、流平剂份量比为1:1:1:1:1:1。
4.根据权利要求1所述一种外墙保温负离子涂料，制备方法包括以下步骤：先将所述硅酸铝粉、水玻璃、助剂、丙烯酸脂乳液加入到调速搅拌机中中速搅拌30-45分钟；再加入所述电气石粉、稀土镧元素、硅藻土、碳酸钙、二氧化钛、二氧化硅、空心玻璃微珠、玻璃纤维、白水泥高速搅拌45-60分钟即可制得成品。
CN201810466193.8A 2018-05-16 2018-05-16 一种外墙保温防渗漏负离子涂料 Withdrawn CN108841272A (zh)