CN108840658A - A kind of burning process of dark-red enameled pottery - Google Patents
A kind of burning process of dark-red enameled pottery Download PDFInfo
- Publication number
- CN108840658A CN108840658A CN201810671585.8A CN201810671585A CN108840658A CN 108840658 A CN108840658 A CN 108840658A CN 201810671585 A CN201810671585 A CN 201810671585A CN 108840658 A CN108840658 A CN 108840658A
- Authority
- CN
- China
- Prior art keywords
- dark
- red enameled
- enameled pottery
- burning process
- kiln
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of burning process of dark-red enameled pottery, and kiln discharge, preparation process are further comprising the steps of after naturally cooling to room temperature after traditional first time burning process:(1), the dark-red enameled pottery after kiln discharge entered back into drying room be dried to 50-60 degree, it is spare;(2), on the firing chamber that tradition fires boccaro kiln put carbon block, lighted by air blower air distribution, sand pad or dottle pin placed above the flare lighted, dark-red enameled pottery is placed on above after a certain amount of coal dust is spread on sand pad or dottle pin, then in one sand cage pot of dark-red enameled pottery upper cover;(3), when being fired by small fire to high fire to 900-1300 DEG C when firing, take out product with iron wooden fork;(4), the dark-red enameled pottery of taking-up be placed on hold the smoking in hole of combustibles.The present invention does not add any chemical element in sintering procedure, by improving on the basis of the burning process to traditional dark-red enameled pottery, dodges the bright dark-red enameled pottery with riot of color effect of gold to burn out.
Description
Technical field
The invention belongs to dark-red enameled pottery burning techniques fields, and in particular to a kind of burning process of dark-red enameled pottery.
Background technique
The production of dark-red enameled pottery starts from the Ming Dynasty, and hereafter gradually prosperous, after Ming and Qing, dark-red enameled pottery has become the symbol of tea culture.
It is made tea with dark-red enameled pottery and neither takes tea by force and smell good, and without ripe soup gas, the color of tealeaves can kept the long period, made because it also has
Type it is simple and unsophisticated it is unique, makings is particularly good, the advantages that stroking gently through tea bubble, hand, ancient jade green can be become and favored by people.
Dark-red enameled pottery product currently on the market causes the dark-red enameled pottery color burnt out single, outside since burning process limits
Tarnish is seen, so that the dicoration of dark-red enameled pottery appearance is not strong, without ornamental value.Although present part of the manufacturer adds respectively in pug
The chemical substances colorants such as kind metal oxide can be fabricated to various chromatic colours, pass through the chemistry member changed in purple clay
Element, to achieve the purpose that discoloration.But although chemical element diversification that the color of furnace body can be made to become is added, it is chemical
Mass pigmentation agent has toxicity mostly, and after using it to make tea as dark-red enameled pottery made of colorant, human health is often damaged
Evil.
Summary of the invention
The purpose of the present invention is to provide a kind of burning process of dark-red enameled pottery.The present invention does not add any in sintering procedure
Chemical element, by being improved on the basis of the burning process to traditional dark-red enameled pottery, to burn out golden bright and five variegation of sudden strain of a muscle
The dark-red enameled pottery of bright-coloured effect.
The technical solution adopted by the present invention:A kind of burning process of dark-red enameled pottery passes through after traditional first time burning process
Kiln discharge after room temperature is naturally cooled to, preparation process is further comprising the steps of:(1), the dark-red enameled pottery after kiln discharge entered back into drying
Room is dried to 50-60 degree, spare;(2), tradition fire boccaro kiln firing chamber on put carbon block, by air blower air distribution point
Combustion places sand pad or dottle pin above the flare lighted, dark-red enameled pottery is placed on after a certain amount of coal dust is spread on sand pad or dottle pin
Above, then in one sand cage pot of dark-red enameled pottery upper cover;(3), when being fired by small fire to high fire to 900-1300 DEG C when firing, with iron wooden fork
Take out product;(4), the dark-red enameled pottery of taking-up be placed on hold the smoking in hole of combustibles, it is enterprising in dark-red enameled pottery with sand cage pot cover
Row is smoked to be cooled down after a certain period of time, further takes out product,.
Further, traditional first time burning process is:Grinding, aging, embryo processed, repairs embryo and calcining at mud refining.
Further, it is one of perpendicular cave kiln, electrical kiln or gas kiln that tradition, which fires sand device kiln,.
Further, the combustibles are one or both of sawdust, wood shavings or bark.
Further, it is described smoke the time be 3-5 hours.
The present invention compared with prior art the beneficial effect is that:Burning process of the invention is compared to general dark-red enameled pottery color
It is changeable, it presents and dodges the bright effect with riot of color of gold;The present invention changes the physical property of boccaro, the more tea of a pot, can
With with pot is steeped various tealeaves will not taint of odour.
Specific embodiment
A kind of burning process of dark-red enameled pottery, preparation process include the following steps:Grinding:By boccaro raw material, pulverize,
It is screened to 60 mesh;Mud refining:Mixing pug is stirred in soil kneader, the pug refined vacuumizes again;It is aging:The mud that will have been refined
Expect equal portions, is placed in closed environment and stands;Embryo processed:By aging good pug, by patting slice by hand, hand is moulded into type;It forges
It burns:The mold base is put into kiln and is calcined, then natural cooling;
After above-mentioned first time fires cooling kiln discharge, then the dark-red enameled pottery after kiln discharge is entered back into drying room and is dried to 50-60 degree;
Carbon block is put on the firing chamber of perpendicular cave kiln, is lighted by air blower air distribution, sand pad or dottle pin are placed above the flare lighted,
Dark-red enameled pottery is placed on above after spreading a certain amount of coal dust on sand pad or dottle pin, then in one sand cage pot of dark-red enameled pottery upper cover;It fires
When being fired by small fire to high fire to 900-1300 DEG C, take out product with iron wooden fork;The dark-red enameled pottery of taking-up is placed on and holds sawdust, plane
It is colored or bark to smoke in hole, it is smoked on dark-red enameled pottery with sand cage pot cover and is cooled down after a certain period of time, further take out product, i.e.,
At.The perpendicular cave kiln of firing can be also fired in electrical kiln or gas kiln in the technical program.
Claims (5)
1. a kind of burning process of dark-red enameled pottery, after traditional first time burning process after naturally cooling to room temperature kiln discharge,
It is characterized in that its preparation process is further comprising the steps of:(1), the dark-red enameled pottery after kiln discharge entered back into drying room be dried to 50-60
Degree, it is spare;(2), tradition fire boccaro kiln firing chamber on put carbon block, lighted by air blower air distribution, in the fire lighted
Sand pad or dottle pin are placed above seedling, dark-red enameled pottery are placed on above after a certain amount of coal dust is spread on sand pad or dottle pin, then in boccaro
One sand cage pot of pot upper cover;(3), when being fired by small fire to high fire to 900-1300 DEG C when firing, take out product with iron wooden fork;(4),
The dark-red enameled pottery of taking-up is placed on and holds the smoking in hole of combustibles, carries out smoking certain time on dark-red enameled pottery with sand cage pot cover
After cool down, further take out product,.
2. a kind of burning process of dark-red enameled pottery according to claim 1, which is characterized in that the tradition is fired for the first time
Technique is:Grinding, aging, embryo processed, repairs embryo and calcining at mud refining.
3. a kind of burning process of dark-red enameled pottery according to claim 1, which is characterized in that it is perpendicular cave that tradition, which fires sand device kiln,
One of kiln, electrical kiln or gas kiln.
4. a kind of burning process of dark-red enameled pottery according to claim 1, which is characterized in that the combustibles be sawdust,
One or both of wood shavings or bark.
5. a kind of burning process of dark-red enameled pottery according to claim 1, which is characterized in that it is described smoke the time be 3-5 it is small
When.