CN108840598A - A kind of regular patterns textured man-made stone plate and preparation method thereof - Google Patents
A kind of regular patterns textured man-made stone plate and preparation method thereof Download PDFInfo
- Publication number
- CN108840598A CN108840598A CN201810846063.7A CN201810846063A CN108840598A CN 108840598 A CN108840598 A CN 108840598A CN 201810846063 A CN201810846063 A CN 201810846063A CN 108840598 A CN108840598 A CN 108840598A
- Authority
- CN
- China
- Prior art keywords
- parts
- auxiliary
- preparation
- regular patterns
- tone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of regular patterns textured man-made stone plates and preparation method thereof, comprise the following methods, a, first production crystal transparent particle, are then fed into feeder；B, mass-tone is prepared and auxiliary color is prepared, and the cooperation of prepared crystal transparent particle, mass-tone and auxiliary colorant is adequately mixed；Pipeline and mixer are carried out installation connection by c；The raw material mixed is sufficiently poured into processing mold by d；Raw material in mold is taken out by e, then carries out cutting plate；F carries out sanding to the raw material after cutting through and polishes；G checks appearance, and attaches protective film.Artificial stone prepared by the present invention, the grain effect for solving the existing natural stone of entity plane materiel can be accomplished seamless spliced again, and have antibacterial, the continuity of color, reproducibility is radiationless, and pattern is more natural, more smooth, fine and smooth.
Description
Technical field
The present invention relates to artificial stone processing technique field, especially a kind of regular patterns textured man-made stone plate and its preparation
Method.
Background technique
Artificial stone typically refers to artificial solid material, artificial stone quartz, artificial stone hilllock stone etc..Artificial stone type is not
Together, ingredient is also not quite similar.Ingredient is mainly resin, aluminium powder, pigment and curing agent.Using high molecular functional archiotecture material
Material, manufacturing process is a kind of chemical material reaction process, is generated and goes back with the progress of human society science and technology
It is that a kind of novel environment friendly is compound that the Practical science material artificial stone continuously improved, which is mainly used in architectural decoration it,
Material.Compared to traditional construction materials such as stainless steel, ceramics, artificial stone is not only vdiverse in function, various colors, and application range is also more wide
It is general.Artificial stone nontoxicity, radioactivity, fire-retardant, not viscous oil, not permeable dirt, antibacterial and mouldproof, wear-resisting, impact resistance, easily maintenance, seamless spelling
Connect, moulding it is changeable.
Current decorative pattern plane materiel mainly embodies in natural stone, according to the growth requirement in market, in various decorative applications
Increasingly it is intended to the decorative pattern of natural formula, however traditional artificial slabstone, pattern is not regular enough, and aesthetics is poor, for above
The problem of, herein it is proposed that a kind of regular patterns textured man-made stone plate and preparation method thereof.
Summary of the invention
The present invention is to solve above-mentioned phenomenon, using the technical solution of following modification, a kind of regular patterns Artificial pattern slate
Material and preparation method thereof comprises the following methods,
A, first production crystal transparent particle, are then fed into feeder；
B, mass-tone is prepared and auxiliary color is prepared, and the cooperation of prepared crystal transparent particle, mass-tone and auxiliary colorant is carried out abundant
Mixing；
Pipeline and mixer are carried out installation connection by c；
The raw material mixed is sufficiently poured into processing mold by d；
Raw material in mold is taken out by e, then carries out cutting plate；
F carries out sanding to the raw material after cutting through and polishes；
G checks appearance, and attaches protective film.
As present invention further optimization mode, in step b, major ingredient formula includes 8-12 parts of unsaturated-resin, hydrogen-oxygen
Aluminium powder 12-20 parts of change, yellow 1.2-2.4 parts of slurry, 0.6-1.4 parts of black wash, 1-2.4 parts of red slurry, 0.8-1.6 parts of white slurry, crystal are saturating
Bright particle 5-10 parts and curing agent 1.5-3.5 parts, ratio is weighed as required, and mill base is added and stirs 1 minute, unsaturated-resin is added
Stirring 2 minutes, is added filler aluminium hydroxide and stirs 15 minutes, 80 revs/min of mixing speed by 40 revs/min of mixing speed；Then it detects
6Pa.S/34 DEG C of slurry viscosity, reaction time 15-25 minute, 118 DEG C of reaction temperature.
As present invention further optimization mode, in step b, the auxiliary chromogen material include 4-15 parts of unsaturated-resin,
10-18 parts of aluminium-hydroxide powder, 1.2-2.4 parts of titanium white, charcoal grind 1.6-3.4 parts, 1.8-4.2 parts of iron oxide red, 0.8-2.0 parts of middle Huang and
1.2-2.8 parts of thickener, ratio is weighed as required, and mill base is added and stirs 1 minute, and unsaturated-resin is added and stirs 2 minutes, stirring
40 revs/min of speed, filler aluminium hydroxide is added and stirs 15 minutes, 80 revs/min of mixing speed；Detect slurry viscosity 5.5Pa.S/34
DEG C, it the reaction time 17 seconds, 120 DEG C of reaction temperature, being vacuumized after detection is qualified, vacuum degree is in -0.085MPa, and the time 15 minutes.
As present invention further optimization mode, the pipeline connection includes that major ingredient pipeline pipeline first puts on inner membrance,
5 length of tubing are connected respectively；Inner membrance is put in auxiliary colour tube road, will be connected before mashing pump with 4 stainless steel tubes respectively, mashing pump
Two auxiliary color mixers are installed with 1.5 cun of connections of wired hose below, 1.2 cun of wired hoses are filled in every kind of mixer, major-minor
Access the separator of 6 root canal of band on color, the internal diameters of 6 tubules is 8mm, and secondary auxiliary color accesses the separator of 4 root canals, 4 tubules
Internal diameter is 8mm, and major ingredient pipe 2 are fixed on electric swing platform, after 2 major-minor colors are placed on major ingredient pipe, remaining 4 masters
Time auxiliary colour tubes of auxiliary color and 4, which are placed on before mass-tone pipe, to put in order as compartment, and spacing distance is that 70mm and 100mm is successively followed
Ring.
As present invention further optimization mode, in step d, in casting process, major-minor color flow is 3kg/min, secondary
Auxiliary color flow is 2kg/min, starts to start mass-tone when auxiliary mill base material enters mixing tube, mass-tone flow is 26kg/min, very
For reciprocal of duty cycle in 0.65MPa, crystal transparent particle feeding flow is 1.5kg/min, feeding be distributed as 0mm, 150mm, 280mm,
330mm, 390mm, 490mm, 590mm, 630mm, 750mm, 820mm open two kinds of auxiliary colors and swing, swing interval and the time is
400mm:1min,460mm:30s,520mm:45s,120mm:1min,70mm:1.5min,10mm:50s, every section be repeated 3 times, press
According to casting amount be arranged steel band speed 1.45m/min, check line on the reaction time be 14 points 30 seconds, temperature control at 115 DEG C.
As present invention further optimization mode, in step e, automatic length cutting plate size 3668mm is set, checks plate
Material it is offline having a size of length 3668mm, width 817mm, with a thickness of 14.5-14.7mm.
As present invention further optimization mode, in step f, repair broadside, width 762mm, positive back side sanding,
With a thickness of 12.35mm after sanding.
Compared with prior art, artificial stone prepared by the present invention solves the grain effect of the existing natural stone of entity plane materiel
It can accomplish again seamless spliced, and there is antibacterial, the continuity of color, reproducibility is radiationless, and pattern is more natural, more smooth, carefully
It is greasy.
Specific embodiment
Below in conjunction in the embodiment of the present invention, technical solution in the embodiment of the present invention is clearly and completely retouched
It states, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based on the present invention
In embodiment, every other implementation obtained by those of ordinary skill in the art without making creative efforts
Example, shall fall within the protection scope of the present invention.
The present invention provides a kind of technical solution：A kind of regular patterns textured man-made stone plate and preparation method thereof, including with
Lower method and step,
A, first production crystal transparent particle, are then fed into feeder；
B, mass-tone is prepared and auxiliary color is prepared, and the cooperation of prepared crystal transparent particle, mass-tone and auxiliary colorant is carried out abundant
Mixing；
Pipeline and mixer are carried out installation connection by c；
The raw material mixed is sufficiently poured into processing mold by d；
Raw material in mold is taken out by e, then carries out cutting plate；
F carries out sanding to the raw material after cutting through and polishes；
G checks appearance, and attaches protective film.
In step b, major ingredient formula includes 8-12 parts of unsaturated-resin, 12-20 parts of aluminium-hydroxide powder, yellow slurry 1.2-2.4
Part, 0.6-1.4 parts of black wash, 1-2.4 parts of red slurry, 0.8-1.6 parts of white slurry, 5-10 parts of crystal transparent particle and curing agent 1.5-3.5
Part, ratio is weighed as required, and mill base is added and stirs 1 minute, and addition unsaturated-resin stirring 2 minutes, 40 revs/min of mixing speed,
Filler aluminium hydroxide is added to stir 15 minutes, 80 revs/min of mixing speed；Then 6Pa.S/34 DEG C of slurry viscosity, when reaction is detected
Between 15-25 minutes, 118 DEG C of reaction temperature.
In step b, the auxiliary chromogen material includes 4-15 parts of unsaturated-resin, 10-18 parts of aluminium-hydroxide powder, titanium white 1.2-
2.4 parts, charcoal grind 1.6-3.4 parts, 1.8-4.2 parts of iron oxide red, 0.8-2.0 parts and 1.2-2.8 parts of thickener of middle Huang, ratio claims as required
Weight is added mill base and stirs 1 minute, and unsaturated-resin is added and stirs 2 minutes, 40 revs/min of mixing speed, filler aluminium hydroxide is added
Stirring 15 minutes, 80 revs/min of mixing speed；5.5Pa.S/34 DEG C of slurry viscosity of detection, the reaction time 17 seconds, reaction temperature 120
DEG C, it being vacuumized after detection is qualified, vacuum degree is in -0.085MPa, and the time 15 minutes.
The pipeline connection includes that major ingredient pipeline pipeline first puts on inner membrance, respectively connects 5 length of tubing；Auxiliary colour tube
Inner membrance is put in road, will be connected before mashing pump with 4 stainless steel tubes respectively, with 1.5 cun of connection peaces of wired hose behind mashing pump
Two auxiliary color mixers are filled, fill 1.2 cun of wired hoses in every kind of mixer, the separator of access 6 root canal of band on major-minor color, 6
The internal diameter of root tubule is 8mm, and secondary auxiliary color accesses the separator of 4 root canals, and the internal diameter of 4 tubules is 8mm, by 2 fixations of major ingredient pipe
On electric swing platform, after 2 major-minor colors are placed on major ingredient pipe, remaining 4 major-minor colors and 4 auxiliary colour tubes are placed on master
It is put in order before colour tube as compartment, spacing distance is that 70mm and 100mm is circuited sequentially.
In step d, in casting process, major-minor color flow is 3kg/min, and secondary auxiliary color flow is 2kg/min, when auxiliary mill base material
Start to start mass-tone when entering mixing tube, mass-tone flow is 26kg/min, and vacuum degree is fed in 0.65MPa, crystal transparent particle
Stream amount be 1.5kg/min, feeding be distributed as 0mm, 150mm, 280mm, 330mm, 390mm, 490mm, 590mm, 630mm,
750mm, 820mm open two kinds of auxiliary colors and swing, and swing interval and the time is 400mm:1min,460mm:30s,520mm:45s,
120mm:1min,70mm:1.5min,10mm:50s, every section be repeated 3 times, according to casting amount be arranged steel band speed 1.45m/min,
Check line on the reaction time be 14 points 30 seconds, temperature control at 115 DEG C.
In step e, automatic length cutting plate size 3668mm is set, checks that plate is offline having a size of length 3668mm, width
For 817mm, with a thickness of 14.5-14.7mm.
In step f, carry out repairing broadside, width 762mm, positive back side sanding, with a thickness of 12.35mm after sanding.The present invention
The artificial stone parameter table of production is as follows：Table 1
。
Traditional artificial stone parameter table is as follows：Table 2
。
To sum up, it will become apparent from the performance of artificial stone of the invention by Tables 1 and 2 better than traditional artificial stone, and this
Invent preparation artificial stone, solve the existing natural stone of entity plane materiel grain effect can accomplish again it is seamless spliced, and have resist
Bacterium, color continuity, reproducibility is radiationless, and pattern is more natural, more smooth, fine and smooth.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention, for this field skill
For art personnel, it is clear that invention is not limited to the details of the above exemplary embodiments, and without departing substantially from spirit of the invention or
In the case where essential characteristic, the present invention can be realized in other specific forms.Therefore, in all respects, should all incite somebody to action
Embodiment regards exemplary as, and is non-limiting, the scope of the present invention by appended claims rather than on state
Bright restriction, it is intended that including all changes that fall within the meaning and scope of the equivalent elements of the claims in the present invention
It is interior.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (7)
1. a kind of regular patterns textured man-made stone plate and preparation method thereof, it is characterised in that：It comprises the following methods,
A, first production crystal transparent particle, are then fed into feeder；
B, mass-tone is prepared and auxiliary color is prepared, and the cooperation of prepared crystal transparent particle, mass-tone and auxiliary colorant is adequately mixed
It closes；
Pipeline and mixer are carried out installation connection by c；
The raw material mixed is sufficiently poured into processing mold by d；
Raw material in mold is taken out by e, then carries out cutting plate；
F carries out sanding to the raw material after cutting through and polishes；
G checks appearance, and attaches protective film.
2. a kind of regular patterns textured man-made stone plate according to claim 1 and preparation method thereof, which is characterized in that step
In rapid b, major ingredient formula includes 8-12 parts of unsaturated-resin, 12-20 parts of aluminium-hydroxide powder, yellow slurry 1.2-2.4 parts, black wash
0.6-1.4 parts, 1-2.4 parts of red slurry, 0.8-1.6 parts of white slurry, 5-10 parts of crystal transparent particle and 1.5-3.5 parts of curing agent, by wanting
It asks ratio to weigh, mill base is added and stirs 1 minute, unsaturated-resin is added and stirs 2 minutes, 40 revs/min of mixing speed, filler is added
Aluminium hydroxide stirs 15 minutes, 80 revs/min of mixing speed；Then 6Pa.S/34 DEG C of slurry viscosity is detected, reaction time 15-25 point
Clock, 118 DEG C of reaction temperature.
3. a kind of regular patterns textured man-made stone plate according to claim 1 and preparation method thereof, which is characterized in that step
In rapid b, the auxiliary chromogen material includes that 4-15 parts of unsaturated-resin, 10-18 parts of aluminium-hydroxide powder, 1.2-2.4 parts of titanium white, charcoal are ground
1.6-3.4 parts, 1.8-4.2 parts of iron oxide red, 0.8-2.0 parts and 1.2-2.8 parts of thickener of middle Huang, ratio is weighed as required, and color is added
Slurry stirring 1 minute is added unsaturated-resin and stirs 2 minutes, 40 revs/min of mixing speed, filler aluminium hydroxide is added and stirs 15 points
Clock, 80 revs/min of mixing speed；5.5Pa.S/34 DEG C of slurry viscosity of detection, the reaction time 17 seconds, 120 DEG C of reaction temperature, detection was closed
It being vacuumized after lattice, vacuum degree is in -0.085MPa, and the time 15 minutes.
4. a kind of regular patterns textured man-made stone plate according to claim 1 and preparation method thereof, which is characterized in that institute
Stating pipeline connection includes that major ingredient pipeline pipeline first puts on inner membrance, respectively connects 5 length of tubing；Inner membrance is put in auxiliary colour tube road,
It will be connected before mashing pump with 4 stainless steel tubes respectively, two auxiliary color contaminations be installed with 1.5 cun of connections of wired hose behind mashing pump
Clutch fills 1.2 cun of wired hoses in every kind of mixer, and the separator of 6 root canal of band, the internal diameter of 6 tubules are accessed on major-minor color
For 8mm, secondary auxiliary color accesses the separator of 4 root canals, and the internal diameter of 4 tubules is 8mm, is fixed on electric swing for major ingredient pipe 2 and puts down
On platform, after 2 major-minor colors are placed on major ingredient pipe, time auxiliary colour tubes of remaining 4 major-minor colors and 4 be placed on before mass-tone pipe arrange it is suitable
Sequence is compartment, and spacing distance is that 70mm and 100mm is circuited sequentially.
5. a kind of regular patterns textured man-made stone plate according to claim 1 and preparation method thereof, which is characterized in that step
In rapid d, in casting process, major-minor color flow is 3kg/min, and secondary auxiliary color flow is 2kg/min, when auxiliary mill base material enters mixing
Start to start mass-tone when pipe, mass-tone flow is 26kg/min, and vacuum degree is in 0.65MPa, crystal transparent particle feeding flow
1.5kg/min, feeding be distributed as 0mm, 150mm, 280mm, 330mm, 390mm, 490mm, 590mm, 630mm, 750mm,
820mm opens two kinds of auxiliary colors and swings, and swings interval and the time is 400mm:1min,460mm:30s,520mm:45s,120mm:
1min,70mm:1.5min,10mm:50s, every section be repeated 3 times, according to casting amount be arranged steel band speed 1.45m/min, check line
The upper reaction time be 14 points 30 seconds, temperature control at 115 DEG C.
6. a kind of regular patterns textured man-made stone plate according to claim 1 and preparation method thereof, which is characterized in that step
In rapid e, automatic length cutting plate size 3668mm is set, checks that plate is offline having a size of length 3668mm, width 817mm, thickness
Degree is 14.5-14.7mm.
7. a kind of regular patterns textured man-made stone plate according to claim 1 and preparation method thereof, which is characterized in that step
In rapid f, carry out repairing broadside, width 762mm, positive back side sanding, with a thickness of 12.35mm after sanding.