CN104446230B - A kind of ceramic tile adhesive - Google Patents
A kind of ceramic tile adhesive Download PDFInfo
- Publication number
- CN104446230B CN104446230B CN201410820384.1A CN201410820384A CN104446230B CN 104446230 B CN104446230 B CN 104446230B CN 201410820384 A CN201410820384 A CN 201410820384A CN 104446230 B CN104446230 B CN 104446230B
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- tile adhesive
- adhesive
- present
- ethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention belongs to building material field, particularly relate to a kind of ceramic tile adhesive.The ceramic tile adhesive that the application provides, in terms of parts by weight, including following components: cement 35～45 parts；Basalt fibre 0.1～1 part；Sand 45～65 parts.The application, by introducing basalt fibre component in tradition ceramic tile adhesive formula, improves heat-resisting adhesive strength and the pliability of ceramic tile adhesive.After being mixed according to mass ratio 4:1 with water by the ceramic tile adhesive that the present invention provides, carrying out performance detection, result shows, the transverse deformation of the ceramic tile adhesive that the application provides is more than 1.1MPa more than 2.2mm, the stretching adhesive strength after heat ageing.
Description
Technical field
The invention belongs to building material field, particularly relate to a kind of ceramic tile adhesive.
Background technology
Ceramic tile adhesive has been applied very universal in European and American developed countries, substantially accounts for all dry-mixed mortars
50%, and owing to scope and the applied environment of application are different, kind and the classification of glue for tile are the most.
The product standard of China's ceramic tile adhesive was just introduced from Europe in 1994, and carried out repairing several times
Order, but the popularization of product and application popularization are in progress relatively slower always, until in recent years due to labour force
The application of the quickly growth of cost and low water absorption, large scale Imitation Rock Porcelain Tiles gets more and more, and ceramic tile adhesive produces
Product have just had the application of certain scale in some economically developed cities, and overall application rate is the most relatively low,
According to incompletely statistics, the ratio of current domestic employing ceramic tile adhesive patch block is less than 10%.
According to related statistics, the yield of annual Chinese pottery brick product in 2013 reaches 9,800,000,000 square meters,
Wherein the water absorption rate Imitation Rock Porcelain Tiles (being commonly called as vitrified tile) less than 0.5% accounts for 68.07 hundred million square meters, more complete than 2012
Year increases by 9.7%, accounts for the 70% of total amount.These low water absorptions and the increasing vitrified tile of size are wanted
Realizing the bonding of safety, the only way out is exactly the ceramic tile bond selecting reliable in quality.It addition, along with
Transition and a new generation only child of China's economy enter labour market, cost of labor, especially build
The cost of labor in building site increases very fast, operates simpler and speed of application faster thin layer ceramic tile adhesive
Application also will increasingly be accepted by building site.
Although the product of existing a lot of ceramic tile adhesive is being sold in the market, but exists a great deal of
Product quality do not reach the requirement of ceramic tile adhesive industry standard JC/T547-2005, be in particular in quite
The heat-resisting adhesive strength of product of quantity and pliability are defective.Some patch block engineerings, especially exterior wall patch block
Engineering, even if having employed thin-layer method technique and glue for tile product, but still occurs in that porcelain after finally using several years
The hollowing of brick and coming off, a very important reason is exactly heat-resisting adhesive strength and the pliability of glue for tile
Bad, i.e. ceramic tile is when different temperature fields is expanded with heat and contract with cold, owing to ceramic tile adhesive lacks enough glue
Glue intensity and pliability and the internal stress of the condensing generation of ceramic tile flatulence of heat type can not be discharged well, ultimately result in porcelain
Going out little crack between brick glue and ceramic tile, these cracks can gradually form hollowing after running up to certain quantity,
And cause final coming off.
Summary of the invention
In view of this, it is an object of the invention to provide a kind of ceramic tile adhesive, the ceramic tile that the present invention provides
The heat-resisting adhesive strength of adhesive is high, pliability is good.
The invention provides a kind of ceramic tile adhesive, in terms of parts by weight, including following components:
Cement 35～45 parts；
Basalt fibre 0.1～1 part；
Sand 45～65 parts.
Preferably, the filament diameter of described basalt fibre is 3～23 μm.
Preferably, the filament length of described basalt fibre is 3～15mm.
Preferably, described ceramic tile adhesive also includes dicalcium powder, latex powder, water-retaining admixture, early strength agent
With one or more in thixotropic lubricant.
Preferably, the fineness of described dicalcium powder is 250～500 mesh.
Preferably, described latex powder is VAE, vinylacetate-ethylene-tertiary carbon
Vinyl acetate polymer, copolymer in cinnamic acrylic ester, vinylacetate-tertiary ethylene carbonate-propylene
Acid-ethylene copolymer, vinyl chloride-ethylene-laurate copolymer and vinyl acetate-vinyl chloride-ethylene
One or more in copolymer.
Preferably, described water-retaining admixture is ethoxyl methyl cellulose ether and/or hydroxypropyl methyl cellulose
Ether.
Preferably, one or more during described early strength agent is calcium formate, calcium chloride and sodium sulfate.
Preferably, described thixotropic lubricant is bentonite.
Preferably, in terms of parts by weight, described ceramic tile adhesive includes following components:
Compared with prior art, the invention provides a kind of ceramic tile adhesive, the glue for tile that the present invention provides
Glutinous agent, in terms of parts by weight, including following components: cement 35～45 parts；Basalt fibre 0.1～1 part；
Sand 45～65 parts.The present invention, by introducing basalt fibre component in tradition ceramic tile adhesive formula, carries
The heat-resisting adhesive strength of high ceramic tile adhesive and pliability.The ceramic tile adhesive that the present invention is provided and water
After mixing according to mass ratio 4:1, carrying out performance detection, result shows, the ceramic tile adhesive that the present invention provides
Transverse deformation more than 2.2mm, the stretching adhesive strength after heat ageing is more than 1.1MPa.
Accompanying drawing explanation
In order to be illustrated more clearly that the embodiment of the present invention or technical scheme of the prior art, below will be to reality
Execute the required accompanying drawing used in example or description of the prior art to be briefly described, it should be apparent that below,
Accompanying drawing in description is only embodiments of the invention, for those of ordinary skill in the art, not
On the premise of paying creative work, it is also possible to obtain other accompanying drawing according to the accompanying drawing provided.
Fig. 1 is the wettability test figure that the embodiment of the present invention 1 prepares ceramic tile adhesive；
Fig. 2 is the wettability test figure that comparative example of the present invention prepares ceramic tile adhesive.
Detailed description of the invention
Below the technical scheme in the embodiment of the present invention is clearly and completely described, it is clear that retouched
The embodiment stated is only a part of embodiment of the present invention rather than whole embodiments.Based on the present invention
In embodiment, the institute that those of ordinary skill in the art are obtained under not making creative work premise
There are other embodiments, broadly fall into the scope of protection of the invention.
The invention provides a kind of ceramic tile adhesive, in terms of parts by weight, including following components:
Cement 35～45 parts；
Basalt fibre 0.1～1 part；
Sand 45～65 parts.
The ceramic tile adhesive that the present invention provides includes cement, basalt fibre and sand.Wherein, described cement
It is most important inorganic coagulation material in ceramic tile gluing agent prescription, is the various mechanical property of ceramic tile adhesive
Important foundation, the quality of cement and volume directly influence the water-fast adhesive strength of ceramic tile adhesive and resistance to freeze
Melt adhesive strength.In the embodiment that the present invention provides, described cement is Portland cement；
The present invention provide another embodiment in, described cement be 42.5R Portland cement and/or
52.5R Portland cement；In other embodiments that the present invention provides, described cement is white silicic acid
Salt cement；The present invention provide other embodiments in, described cement be 42.5R white portland cement and
/ or 52.5R white portland cement.In the embodiment that the present invention provides, described cement is at glue for tile
Content in glutinous agent is 35～45 weight portions；In another embodiment that the present invention provides, described cement exists
Content in ceramic tile adhesive is 37～45 weight portions.
Described basalt fibre is a kind of fiber reinforcement material being added in the ceramic tile adhesive that the present invention provides
Material.In the embodiment that the present invention provides, the filament diameter of described basalt fibre is 3～23 μm；
In another embodiment that the present invention provides, the filament diameter of described basalt fibre is 9～17 μm；?
The present invention provide other embodiments in, the filament diameter of described basalt fibre be 9 μm, 11 μm,
12 μm, 13 μm, 15 μm or 17 μm.In the embodiment that the present invention provides, the described Black Warrior
The filament length of rock fiber is 3～15mm；In another embodiment that the present invention provides, described basalt
The filament length of fiber is 3～6mm.In the embodiment that the present invention provides, described basalt fibre
Content in ceramic tile adhesive is 0.1～1 weight portion；In another embodiment that the present invention provides, institute
Stating basalt fibre content in ceramic tile adhesive is 0.1～0.3 weight portion.The present invention is to described basalt
The source of fiber is not particularly limited, and selects commercially available basalt fibre.
Described sand is the coarse aggregate in ceramic tile adhesive.In the embodiment that the present invention provides, described
Sand is one or more in washed-out sand, aeolian sand and Machine-made Sand.In the embodiment that the present invention provides
The fineness of middle described sand is 10～200 mesh；In another embodiment that the present invention provides, described sand
Fineness is 40～140 mesh.In the embodiment that the present invention provides, described sand is graded sand；At this
In another embodiment of bright offer, described sand is continuous grading sand.In the enforcement that the present invention provides
In example, described sand content in ceramic tile adhesive is 45～65 weight portions；The present invention provide another
In embodiment, described sand content in ceramic tile adhesive is 45～55 weight portions；The present invention provide its
In his embodiment, described sand content in ceramic tile adhesive is 46～53 weight portions.
The present invention provide an embodiment in, described ceramic tile adhesive also include dicalcium powder, latex powder,
One or more in water-retaining admixture, early strength agent and thixotropic lubricant.
In the embodiment that the present invention provides, the fineness of described dicalcium powder is 250～500 mesh；At this
In another embodiment of bright offer, the fineness of described dicalcium powder is 250～325 mesh.There is provided in the present invention
In one embodiment, described dicalcium powder content in ceramic tile adhesive is 5～10 weight portions；In the present invention
In another embodiment provided, described dicalcium powder content in ceramic tile adhesive is 6～10 weight portions.
In the present invention, the effect in glue for tile formula of the described dicalcium powder is the granule optimizing glue for tile further
Grating, fills the space of sand, additionally, the addition of dicalcium powder can also improve denseness and the workability of glue for tile
Energy.
The present invention provide an embodiment in, described latex powder be VAE,
Vinylacetate-ethylene-tertiary ethylene carbonate polymer, copolymer in cinnamic acrylic ester, vinyl acetate
Ester-tertiary ethylene carbonate-acrylic acid ethylene, vinyl chloride-ethylene-laurate copolymer and vinegar
One or more in vinyl acetate-vinyl chloride-ethylene copolymer.In the embodiment that the present invention provides
In, the glass transition temperature of described latex powder is 10～30 DEG C, and minimum film formation temperature is 2～10 DEG C, mainly
Particle size is 0.1～10 μm；In another embodiment that the present invention provides, the glass of described latex powder
Changing transition temperature is 14～20 DEG C, and minimum film formation temperature is 4～6 DEG C, and Dominant particle size is 0.5～8 μm.
In the embodiment that the present invention provides, described latex powder content in ceramic tile adhesive is 1～5 weight
Part；In another embodiment that the present invention provides, described latex powder content in ceramic tile adhesive is
3～5 weight portions.In the present invention, it is added with the ceramic tile adhesive of latex powder and adds water after stirring, latex powder meeting
Again it is dispersed into little emulsion particle to be evenly distributed in wet mortar, when ceramic tile adhesive passes through thin layer process
During by tile paste on base material, the most scattered latex powder emulsion particle can be at glue for tile inside and ceramic tile
The interface of glue and ceramic tile (basal plane) is assembled and film forming, it is provided that the cohesiveness of glue for tile and glue for tile and porcelain
The cohesive force of brick (base material), such that it is able to improve further the adhesive strength of ceramic tile adhesive, pliability,
Wettability and open hour.
In the embodiment that the present invention provides, described water-retaining admixture is ethoxyl methyl cellulose ether
And/or hydroxypropyl methyl cellulose ether.In the embodiment that the present invention provides, described water-retaining admixture
Viscosity be 10000～100000mPa.s；In another embodiment that the present invention provides, described water conservation increases
The viscosity of thick dose is 10000～20000mPa.s.Water conservation described in face in the embodiment that the present invention provides
Thickening agent content in ceramic tile adhesive is 0.1～1 weight portion；In another embodiment that the present invention provides
In, described water-retaining admixture content in ceramic tile adhesive is 0.5～1 weight portion.In the present invention, exist
In ceramic tile adhesive add water-retaining admixture can improve the blade coating performance of ceramic tile adhesive, wet viscosity energy,
Open hour and resistant slide performance, after can ensure that ceramic tile adhesive mixes with water simultaneously, cement therein
Obtain abundant aquation.
In the embodiment that the present invention provides, described early strength agent is calcium formate, calcium chloride and sodium sulfate
In one or more.In the embodiment that the present invention provides, early strength agent described in face is at ceramic tile adhesive
In content be 0.1～1 weight portion；In another embodiment that the present invention provides, described early strength agent is at porcelain
Content in brick adhesive is 0.5～1 weight portion.In the present invention, ceramic tile bond adds early strength agent
The aquation of cement in ceramic tile bond can be accelerated, accelerates glue for tile after ceramic tile adhesive mixes with water
Glutinous agent adhesive strength development in early days, improves the early mechanics characteristics of ceramic tile adhesive.
In the embodiment that the present invention provides, described thixotropic lubricant is bentonite；Carry in the present invention
In another embodiment of confession, described thixotropic lubricant is calcium-base bentonite.One provided in the present invention
In embodiment, described thixotropic lubricant content in ceramic tile adhesive is 0.05～0.5 weight portion；At this
In another embodiment of bright offer, described thixotropic lubricant content in ceramic tile adhesive is 0.15～0.5
Weight portion.
The present invention provide an embodiment in, in terms of parts by weight, described ceramic tile adhesive include with
Lower component:
In the present invention, directly above-mentioned raw materials is mixed in proportion, i.e. can get what the present invention provided
Ceramic tile adhesive.
The present invention, by introducing basalt fibre component in tradition ceramic tile adhesive formula, improves ceramic tile
The heat-resisting adhesive strength of adhesive and pliability.Basalt fibre is easily dispersed, with hydrolysis product of cement
The compatibility is good, is entrained in glue for tile the water-fast adhesive strength not interfering with glue for tile, basalt in addition
Fiber is cheap, it is easy to obtains, contributes to the reduction of ceramic tile adhesive production cost.The present invention provides
Ceramic tile adhesive can improve the safety of tile bonding, reduce what water absorption rate large scale vitrified tile was pasted
Hollowing and the risk that comes off, reduce ceramic tile hollowing and the various losses that may bring that come off, as property loss,
Personal safety losses etc., have obvious social benefit and economic benefit.The glue for tile that the present invention is provided
After glutinous agent mixes according to mass ratio 4:1 with water, carrying out performance detection, result shows, the porcelain that the present invention provides
The transverse deformation of brick adhesive is more than 2.2mm, and the stretching adhesive strength after heat ageing is more than 1.1MPa.This
Outward, in the optimal technical scheme that the present invention provides, the ceramic tile adhesive that the present invention provides also has longer
Open hour, good water-fast adhesive strength, freeze-thawing resistant adhesive strength, anti-slipping property and wettability.
After the ceramic tile adhesive that optimal technical scheme of the present invention provides is mixed according to mass ratio 4:1 with water, Progressive symmetric erythrokeratodermia
Can detect, result shows, this ceramic tile adhesive hangs the stretching adhesive strength after 20min and is higher than 1.0MPa,
Stretching adhesive strength after water inlet is higher than 1.0MPa, and the stretching adhesive strength after freeze-thaw cycle is higher than 1.2MPa,
Using 200g brick to carry out resistant slide performance test, the downslide displacement of ceramic tile adhesive is less than 0.5mm.
Embodiment 1
370g 52.5R Portland cement (Jidong Cement Co., Ltd., Tangshan), 250g are washed
Sand (Chengde thick source natural siliceous sand company limited, 40～70 mesh), 275.5g washed-out sand (thick source sky, Chengde
So quartz sand company limited, 70～140 mesh), (Beijing benefits the nation great achievement superfine powder limited public affairs 60g dicalcium powder
Department, 325 mesh), (Beijing Long Hu scientific & technical corporation, viscosity is 5g ethoxyl methyl cellulose ether
10000mPa.s～20000mPa.s), 30g VAE (Beijing Long Hu scientific & technical corporation,
Glass transition temperature is 16 DEG C), 5g calcium formate (Beijing Long Hu scientific & technical corporation, industry calcium formate),
(Sichuan space flight is opened up for 1.5g bentonite (Beijing Long Hu scientific & technical corporation, calcium-base bentonite) and 3g basalt fibre
Prosperous basalt Industrial Co., Ltd., filament length 3mm, filament diameter 9 μm) mix homogeneously, obtain 1000g
Ceramic tile adhesive.
Embodiment 2
370g 52.5R Portland cement (Jidong Cement Co., Ltd., Tangshan), 250g are washed
Sand (Chengde thick source natural siliceous sand company limited, 40～70 mesh), 277.5g washed-out sand (thick source sky, Chengde
So quartz sand company limited, 70～140 mesh), (Beijing benefits the nation great achievement superfine powder limited public affairs 60g dicalcium powder
Department, 325 mesh), (Beijing Long Hu scientific & technical corporation, viscosity is 5g ethoxyl methyl cellulose ether
10000mPa.s～20000mPa.s), 30g VAE (Beijing Long Hu scientific & technical corporation,
Glass transition temperature is 16 DEG C), 5g calcium formate (Beijing Long Hu scientific & technical corporation, industry calcium formate),
(Sichuan space flight is opened up for 1.5g bentonite (Beijing Long Hu scientific & technical corporation, calcium-base bentonite) and 1g basalt fibre
Prosperous basalt Industrial Co., Ltd., filament length 3mm, filament diameter 9 μm) mix homogeneously, obtain 1000g
Ceramic tile adhesive.
Embodiment 3
By 370g 52.5R white portland cement (A Erbo Portland (Anqing) company limited), 250g water
Washed-out sand (Chengde thick source natural siliceous sand company limited, 40～70 mesh), 277.5g washed-out sand (Chengde thick source
Natural siliceous sand company limited, 70～140 mesh), (Beijing great achievement superfine powder that benefits the nation is limited for 60g dicalcium powder
Company, 325 mesh), (Beijing Long Hu scientific & technical corporation, viscosity is 5g ethoxyl methyl cellulose ether
10000mPa.s～20000mPa.s), 30g VAE (Beijing Long Hu scientific & technical corporation,
Glass transition temperature is 16 DEG C), 5g calcium formate (Beijing Long Hu scientific & technical corporation, industry calcium formate),
(Sichuan space flight is opened up for 1.5g bentonite (Beijing Long Hu scientific & technical corporation, calcium-base bentonite) and 1g basalt fibre
Prosperous basalt Industrial Co., Ltd., filament length 3mm, filament diameter 9 μm) mix homogeneously, obtain 1000g
Ceramic tile adhesive.
Embodiment 4
450g 42.5R Portland cement (Jidong Cement Co., Ltd., Tangshan), 220g are washed
Sand (Chengde thick source natural siliceous sand company limited, 40～70 mesh), 247.5g washed-out sand (thick source sky, Chengde
So quartz sand company limited, 70～140 mesh), (Beijing benefits the nation great achievement superfine powder limited public affairs 60g dicalcium powder
Department, 325 mesh), (Beijing Long Hu scientific & technical corporation, viscosity is 5g ethoxyl methyl cellulose ether
10000mPa.s～20000mPa.s), 30g VAE (Beijing Long Hu scientific & technical corporation,
Vitrification point is 16 DEG C), 5g calcium formate (Beijing Long Hu scientific & technical corporation, industry calcium formate), 1.5g
(Sichuan space flight is opened up prosperous for bentonite (Beijing Long Hu scientific & technical corporation, calcium-base bentonite) and 1g basalt fibre
Basalt Industrial Co., Ltd., filament length 6mm, filament diameter is 13 μm) mix homogeneously, obtain 1020g
Ceramic tile adhesive.
Embodiment 5
450g 42.5R Portland cement (Jidong Cement Co., Ltd., Tangshan), 220g are washed
Sand (Chengde thick source natural siliceous sand company limited, 40～70 mesh), 247.5g washed-out sand (thick source sky, Chengde
So quartz sand company limited, 70～140 mesh), 60g dicalcium powder (Beijing great achievement superfine powder that benefits the nation is limited, 325
Mesh), (Beijing Long Hu scientific & technical corporation, viscosity is 5g ethoxyl methyl cellulose ether
10000mPa.s～20000mPa.s), 30g vinyl acetate-vinyl chloride-ethylene-dien terpolymer (Beijing dragon
Lake scientific & technical corporation, vitrification point is 14 DEG C), 5g calcium formate (Beijing Long Hu scientific & technical corporation, industry first
Acid calcium), 1.5g bentonite (Beijing Long Hu scientific & technical corporation, calcium-base bentonite) and 1g basalt fibre (four
River space flight Tuo Xin basalt Industrial Co., Ltd., filament length 3mm, filament diameter is 17 μm) mixing is all
Even, obtain 1020g ceramic tile adhesive.
Comparative example
370g 52.5R Portland cement (Jidong Cement Co., Ltd., Tangshan), 250g are washed
Sand (Chengde thick source natural siliceous sand company limited, 40～70 mesh), 275.5g washed-out sand (thick source sky, Chengde
So quartz sand company limited, 70～140 mesh), (Beijing benefits the nation great achievement superfine powder limited public affairs 60g dicalcium powder
Department, 325 mesh), (Beijing Long Hu scientific & technical corporation, viscosity is 5g ethoxyl methyl cellulose ether
10000mPa.s～20000mPa.s), 30g VAE (Beijing Long Hu scientific & technical corporation,
Glass transition temperature is 16 DEG C), 5g calcium formate (Beijing Long Hu scientific & technical corporation, industry calcium formate) and
1.5g bentonite (Beijing Long Hu scientific & technical corporation, calcium-base bentonite) mix homogeneously, obtains 997g ceramic tile gluing
Agent.
Embodiment 6
Performance test
By embodiment 1～3 and comparative example prepare ceramic tile adhesive 500g and mix with 125g water respectively, according to
JC/T547-2005 standard carries out resistant slide performance, adhesive strength and transverse deformation test, result such as table 1 institute
Showing, table 1 is ceramic tile adhesive the performance test results.
Table 1 ceramic tile adhesive the performance test results
By table 1 it can be seen that carry out performance test according to JC/T547-2005 standard, embodiment 1～5 prepares
The performance of ceramic tile adhesive all reach the technology requirement of C2T, the porcelain that wherein embodiment 1 and embodiment 5 prepare
The performance of brick adhesive has reached the technology requirement of flexible ceramic tile glue C2TS1.
The ceramic tile adhesive preparing embodiment 1 and comparative example carries out wettability test, method particularly includes:
After glue for tile is stirred with flute profile scraper combing on base material, after 10min, 20min, 30min
Put vitrified tile and earthenware brick, and press 30 seconds with the ferrum pressure head of 2kg respectively, finally vitrified tile and earthenware brick are opened
Observing the brick back side and glue the area of the wet mortar got off, result is as depicted in figs. 1 and 2.Fig. 1 is that the present invention implements
Example 1 prepares the wettability test figure of ceramic tile adhesive, and wherein left side is vitrified tile, and right side is earthenware brick, from upper
The test fragment of brick every 10min, 20min, 30min it is followed successively by under to；Fig. 2 is that comparative example of the present invention prepares
The wettability test figure of ceramic tile adhesive, wherein left side is vitrified tile, and right side is earthenware brick, depends on from top to bottom
Secondary for the test fragment of brick every 10min, 20min, 30min.
By the comparison of Fig. 1 and Fig. 2 it can be seen that in Fig. 1 to glue the wet mortar area got off the biggest at the brick back side
In Fig. 2, illustrate that the wettability of the prepared ceramic tile adhesive of embodiment 1 is significantly better than that the porcelain that comparative example prepares
Brick adhesive.
The above is only the preferred embodiment of the present invention, it is noted that general for the art
For logical technical staff, under the premise without departing from the principles of the invention, it is also possible to make some improvement and profit
Decorations, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (7)
1. a ceramic tile adhesive, in terms of parts by weight, including following components:
Described early strength agent is one or more in calcium formate, calcium chloride and sodium sulfate.
Ceramic tile adhesive the most according to claim 1, it is characterised in that described basalt fibre
Filament diameter is 3～23 μm.
Ceramic tile adhesive the most according to claim 1, it is characterised in that described basalt fibre
Filament length is 3～15mm.
Ceramic tile adhesive the most according to claim 1, it is characterised in that the fineness of described dicalcium powder
It is 250～500 mesh.
Ceramic tile adhesive the most according to claim 1, it is characterised in that described latex powder is acetic acid
Vinyl acetate-ethylene copolymer, vinylacetate-ethylene-tertiary ethylene carbonate polymer, Styrene And Chloroalkyl Acrylates
Ester copolymer, vinylacetate-tertiary ethylene carbonate-acrylic acid ethylene, vinyl chloride-ethylene-Laurel
One or more in vinyl acetate copolymer and vinyl acetate-vinyl chloride-ethylene copolymer.
Ceramic tile adhesive the most according to claim 1, it is characterised in that described water-retaining admixture is
Ethoxyl methyl cellulose ether and/or hydroxypropyl methyl cellulose ether.
Ceramic tile adhesive the most according to claim 1, it is characterised in that described thixotropic lubricant is
Bentonite.