CN104446230A - Tile adhesive - Google Patents
Tile adhesive Download PDFInfo
- Publication number
- CN104446230A CN104446230A CN201410820384.1A CN201410820384A CN104446230A CN 104446230 A CN104446230 A CN 104446230A CN 201410820384 A CN201410820384 A CN 201410820384A CN 104446230 A CN104446230 A CN 104446230A
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- sizing agent
- tile sizing
- agent according
- sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to the field of building materials, and particularly relates to a tile adhesive. The tile adhesive comprises the following components in parts by weight: 35-45 parts of cement, 0.1-1 part of basalt fibers and 45-65 parts of sand. The heat-resistant adhesive strength and the flexibility of the tile adhesive are improved by introducing the basalt fibers into the formula of a traditional tile adhesive. After the tile adhesive is mixed with water in a mass ratio of 4:1, performance detection results show that the transverse deformation of the tile adhesive is more than 2.2mm, and the tensile adhesive strength of the thermally aged tile adhesive is more than 1.1MPa.
Description
Technical field
The invention belongs to building material field, particularly relate to a kind of ceramic tile sizing agent.
Background technology
Ceramic tile sizing agent has been applied very general in European and American developed countries, substantially account for 50% of all dry-mixed mortars, and due to the scope of application and applied environment different, the kind of glue for tile and classification are also very many.The product standard of China's ceramic tile sizing agent was just introduced from Europe in 1994, and carried out revising several times, but the popularization of product and application popularization are in progress slower always, until in recent years because the application of the quick growth of labor cost and low water absorption, large size porcelain brick gets more and more, ceramic tile sizing agent product has just had the application of certain scale in some economically developed cities, overall application rate is still relatively low, according to incompletely statistics, the ratio of current domestic employing ceramic tile sizing agent patch block is less than 10%.
According to related statistics; the output of annual Chinese pottery brick product in 2013 reaches 9,800,000,000 square meters; wherein water-intake rate lower than 0.5% porcelain brick (being commonly called as vitrified tile) account for 68.07 hundred million square meters, increased during the year 9.7% than 2012, account for 70% of total amount.These low water absorptions and the increasing vitrified tile of size will realize safe bonding, the only way out is exactly the ceramic tile bond selecting reliable in quality.In addition, along with transition of China's economy and only-child of new generation enter labour market, the cost of labor in cost of labor, especially construction site increases quickly, the simpler and speed of application of operation faster thin layer ceramic tile sizing agent application also will more and more accept by building site.
Although the product of ceramic tile sizing agents existing a lot of is in the market in sale, but there is the requirement that a considerable amount of quality product does not reach ceramic tile sizing agent industry standard JC/T547-2005, be in particular in the heat-resisting adhesive strength of a considerable amount of product and snappiness defective.Some patch block engineerings, especially exterior wall patch block engineering, even if having employed thin-layer method technique and glue for tile product, but still there is the hollowing of ceramic tile after several years and come off in last use, a very important reason is exactly heat-resisting adhesive strength and the poor in flexibility of glue for tile, namely ceramic tile is when different temperature fields is expanded with heat and contract with cold, lack enough adhesive strengths and snappiness due to ceramic tile sizing agent and the internal stress of the condensing generation of ceramic tile heat expansion can not be discharged well, finally cause going out little crack between glue for tile and ceramic tile, hollowing can be formed gradually after these cracks run up to certain quantity, and cause final coming off.
Summary of the invention
In view of this, the object of the present invention is to provide a kind of ceramic tile sizing agent, the heat-resisting adhesive strength of ceramic tile sizing agent provided by the invention is high, snappiness good.
The invention provides a kind of ceramic tile sizing agent, with weight parts, comprise following component:
Cement 35 ~ 45 parts;
Basalt fibre 0.1 ~ 1 part;
45 ~ 65 parts, sand.
Preferably, the filament diameter of described basalt fibre is 3 ~ 23 μm.
Preferably, the filament length of described basalt fibre is 3 ~ 15mm.
Preferably, described ceramic tile sizing agent also comprises one or more in dicalcium powder, latex powder, water-retaining admixture, hardening accelerator and thixotropic lubricant.
Preferably, the fineness of described dicalcium powder is 250 ~ 500 orders.
Preferably, described latex powder is one or more in VAE, vinylacetate-ethylene-tertiary ethylene carbonate polymkeric substance, copolymer in cinnamic acrylic ester, vinyl acetate-tertiary ethylene carbonate-acrylic acid ethylene, vinyl chloride-ethylene-laurate copolymer and vinyl acetate-vinyl chloride-ethylene copolymer.
Preferably, described water-retaining admixture is ethoxyl methyl cellulose ether and/or hydroxypropyl methyl cellulose ether.
Preferably, described hardening accelerator is one or more in calcium formiate, calcium chloride and sodium sulfate.
Preferably, described thixotropic lubricant is wilkinite.
Preferably, with weight parts, described ceramic tile sizing agent comprises following component:
Compared with prior art, the invention provides a kind of ceramic tile sizing agent, ceramic tile sizing agent provided by the invention, with weight parts, comprise following component: cement 35 ~ 45 parts; Basalt fibre 0.1 ~ 1 part; 45 ~ 65 parts, sand.The present invention, by introducing basalt fibre component in traditional ceramic tile sizing agent formula, improves heat-resisting adhesive strength and the snappiness of ceramic tile sizing agent.After being mixed according to mass ratio 4:1 with water by ceramic tile sizing agent provided by the invention, carry out Performance Detection, result shows, the transverse deformation of ceramic tile sizing agent provided by the invention is greater than 2.2mm, and the stretching adhesive strength after thermal ageing is greater than 1.1MPa.
Accompanying drawing explanation
In order to be illustrated more clearly in the embodiment of the present invention or technical scheme of the prior art, be briefly described to the accompanying drawing used required in embodiment or description of the prior art below, apparently, accompanying drawing in the following describes is only embodiments of the invention, for those of ordinary skill in the art, under the prerequisite not paying creative work, other accompanying drawing can also be obtained according to the accompanying drawing provided.
Fig. 1 is the wettability test pattern that the embodiment of the present invention 1 obtains ceramic tile sizing agent;
Fig. 2 is the wettability test pattern that comparative example of the present invention obtains ceramic tile sizing agent.
Embodiment
Be clearly and completely described the technical scheme in the embodiment of the present invention below, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
The invention provides a kind of ceramic tile sizing agent, with weight parts, comprise following component:
Cement 35 ~ 45 parts;
Basalt fibre 0.1 ~ 1 part;
45 ~ 65 parts, sand.
Ceramic tile sizing agent provided by the invention comprises cement, basalt fibre and sand.Wherein, described cement is most important inorganic coagulation material in ceramic tile gluing agent prescription, is the important foundation of the various mechanical property of ceramic tile sizing agent, and the quality of cement and volume directly have influence on water-fast adhesive strength and the freeze-thawing resistant adhesive strength of ceramic tile sizing agent.In an embodiment provided by the invention, described cement is ordinary Portland cement; In another embodiment provided by the invention, described cement is 42.5R ordinary Portland cement and/or 52.5R ordinary Portland cement; In other embodiments provided by the invention, described cement is white portland cement; In other embodiments provided by the invention, described cement is 42.5R white portland cement and/or 52.5R white portland cement.In an embodiment provided by the invention, the content of described cement in ceramic tile sizing agent is 35 ~ 45 weight parts; In another embodiment provided by the invention, the content of described cement in ceramic tile sizing agent is 37 ~ 45 weight parts.
Described basalt fibre is a kind of fiber reinforced material be added in ceramic tile sizing agent provided by the invention.In an embodiment provided by the invention, the filament diameter of described basalt fibre is 3 ~ 23 μm; In another embodiment provided by the invention, the filament diameter of described basalt fibre is 9 ~ 17 μm; In other embodiments provided by the invention, the filament diameter of described basalt fibre is 9 μm, 11 μm, 12 μm, 13 μm, 15 μm or 17 μm.In an embodiment provided by the invention, the filament length of described basalt fibre is 3 ~ 15mm; In another embodiment provided by the invention, the filament length of described basalt fibre is 3 ~ 6mm.In an embodiment provided by the invention, the content of described basalt fibre in ceramic tile sizing agent is 0.1 ~ 1 weight part; In another embodiment provided by the invention, the content of described basalt fibre in ceramic tile sizing agent is 0.1 ~ 0.3 weight part.The source of the present invention to described basalt fibre is not particularly limited, and selects commercially available basalt fibre.
Described sand is the coarse aggregate in ceramic tile sizing agent.In an embodiment provided by the invention, described sand is one or more in washed-out sand, aeolian sand and Machine-made Sand.In an embodiment provided by the invention, described in face, the fineness of sand is 10 ~ 200 orders; In another embodiment provided by the invention, the fineness of described sand is 40 ~ 140 orders.In an embodiment provided by the invention, described sand is graded sand; In another embodiment provided by the invention, described sand is continuous grading sand.In an embodiment provided by the invention, the content of described sand in ceramic tile sizing agent is 45 ~ 65 weight parts; In another embodiment provided by the invention, the content of described sand in ceramic tile sizing agent is 45 ~ 55 weight parts; In other embodiments provided by the invention, the content of described sand in ceramic tile sizing agent is 46 ~ 53 weight parts.
In an embodiment provided by the invention, described ceramic tile sizing agent also comprise in dicalcium powder, latex powder, water-retaining admixture, hardening accelerator and thixotropic lubricant one or more.
In an embodiment provided by the invention, the fineness of described dicalcium powder is 250 ~ 500 orders; In another embodiment provided by the invention, the fineness of described dicalcium powder is 250 ~ 325 orders.In an embodiment provided by the invention, the content of described dicalcium powder in ceramic tile sizing agent is 5 ~ 10 weight parts; In another embodiment provided by the invention, the content of described dicalcium powder in ceramic tile sizing agent is 6 ~ 10 weight parts.In the present invention, the effect of described dicalcium powder in glue for tile formula is the space of the grain composition optimizing glue for tile further, filler sand, in addition, dicalcium powder add the denseness and serviceability that can also improve glue for tile.
In an embodiment provided by the invention, described latex powder is one or more in VAE, vinylacetate-ethylene-tertiary ethylene carbonate polymkeric substance, copolymer in cinnamic acrylic ester, vinyl acetate-tertiary ethylene carbonate-acrylic acid ethylene, vinyl chloride-ethylene-laurate copolymer and vinyl acetate-vinyl chloride-ethylene copolymer.In an embodiment provided by the invention, the second-order transition temperature of described latex powder is 10 ~ 30 DEG C, and minimum film-forming temperature is 2 ~ 10 DEG C, and Dominant particle size is 0.1 ~ 10 μm; In another embodiment provided by the invention, the second-order transition temperature of described latex powder is 14 ~ 20 DEG C, and minimum film-forming temperature is 4 ~ 6 DEG C, and Dominant particle size is 0.5 ~ 8 μm.In an embodiment provided by the invention, the content of described latex powder in ceramic tile sizing agent is 1 ~ 5 weight part; In another embodiment provided by the invention, the content of described latex powder in ceramic tile sizing agent is 3 ~ 5 weight parts.In the present invention; after the ceramic tile sizing agent being added with latex powder adds water and stirs; latex powder again can be dispersed into little emulsion particle and be evenly distributed in wet mortar; when ceramic tile sizing agent by thin layer process by tile paste on base material time; again the latex powder emulsion particle disperseed can be assembled and film forming inner at glue for tile and glue for tile and ceramic tile (basal plane) interface; the force of cohesion of glue for tile and the cohesive force of glue for tile and ceramic tile (base material) are provided, thus the adhesive strength of ceramic tile sizing agent, snappiness, wettability and open hour can be improved further.
In an embodiment provided by the invention, described water-retaining admixture is ethoxyl methyl cellulose ether and/or hydroxypropyl methyl cellulose ether.In an embodiment provided by the invention, the viscosity of described water-retaining admixture is 10000 ~ 100000mPa.s; In another embodiment provided by the invention, the viscosity of described water-retaining admixture is 10000 ~ 20000mPa.s.In an embodiment provided by the invention, described in face, the content of water-retaining admixture in ceramic tile sizing agent is 0.1 ~ 1 weight part; In another embodiment provided by the invention, the content of described water-retaining admixture in ceramic tile sizing agent is 0.5 ~ 1 weight part.In the present invention, in ceramic tile sizing agent, add water-retaining admixture can improve the blade coating performance of ceramic tile sizing agent, wet viscosity energy, open hour and resistant slide performance, after can ensureing that ceramic tile sizing agent mixes with water, cement wherein obtains abundant aquation simultaneously.
In an embodiment provided by the invention, described hardening accelerator is one or more in calcium formiate, calcium chloride and sodium sulfate.In an embodiment provided by the invention, described in face, the content of hardening accelerator in ceramic tile sizing agent is 0.1 ~ 1 weight part; In another embodiment provided by the invention, the content of described hardening accelerator in ceramic tile sizing agent is 0.5 ~ 1 weight part.In the present invention, in ceramic tile bond, add hardening accelerator after ceramic tile sizing agent mixes with water, the aquation of cement in ceramic tile bond can be accelerated, accelerate the bonding strength development that ceramic tile sizing agent is early stage, improve the early mechanics characteristics of ceramic tile sizing agent.
In an embodiment provided by the invention, described thixotropic lubricant is wilkinite; In another embodiment provided by the invention, described thixotropic lubricant is calcium-base bentonite.In an embodiment provided by the invention, the content of described thixotropic lubricant in ceramic tile sizing agent is 0.05 ~ 0.5 weight part; In another embodiment provided by the invention, the content of described thixotropic lubricant in ceramic tile sizing agent is 0.15 ~ 0.5 weight part.
In an embodiment provided by the invention, with weight parts, described ceramic tile sizing agent comprises following component:
In the present invention, directly above-mentioned raw materials is mixed in proportion, ceramic tile sizing agent provided by the invention can be obtained.
The present invention, by introducing basalt fibre component in traditional ceramic tile sizing agent formula, improves heat-resisting adhesive strength and the snappiness of ceramic tile sizing agent.Basalt fibre is easy to dispersion, and good with the consistency of hydrolysis product of cement, be entrained in glue for tile the water-fast adhesive strength that can not affect glue for tile, basalt fibre is cheap in addition, is easy to obtain, contributes to the reduction of ceramic tile sizing agent production cost.Ceramic tile sizing agent provided by the invention can improve the security of tile bonding; reduce the hollowing of water-intake rate large size vitrified tile stickup and the risk that comes off; reduce ceramic tile hollowing and come off the various losses that may bring; as property damage, personnel safety loss etc., there is obvious social benefit and economic benefit.After being mixed according to mass ratio 4:1 with water by ceramic tile sizing agent provided by the invention, carry out Performance Detection, result shows, the transverse deformation of ceramic tile sizing agent provided by the invention is greater than 2.2mm, and the stretching adhesive strength after thermal ageing is greater than 1.1MPa.In addition, in optimal technical scheme provided by the invention, ceramic tile sizing agent provided by the invention also has the longer open hour, good water-fast adhesive strength, freeze-thawing resistant adhesive strength, anti-slipping property and wettability.After ceramic tile sizing agent optimal technical scheme of the present invention provided mixes according to mass ratio 4:1 with water, carry out Performance Detection, result shows, this ceramic tile sizing agent hangs the stretching adhesive strength after 20min higher than 1.0MPa, stretching adhesive strength after water inlet is higher than 1.0MPa, stretching adhesive strength after freeze-thaw cycle is higher than 1.2MPa, and adopt 200g brick to carry out resistant slide performance test, the downslide displacement of ceramic tile sizing agent is less than 0.5mm.
Embodiment 1
By 370g 52.5R ordinary Portland cement (Jidong Cement Co., Ltd., Tangshan), 250g washed-out sand (Chengde thick source natural siliceous sand company limited, 40 ~ 70 orders), 275.5g washed-out sand (Chengde thick source natural siliceous sand company limited, 70 ~ 140 orders), (Beijing benefits the nation great achievement superfine powder company limited 60g dicalcium powder, 325 orders), 5g ethoxyl methyl cellulose ether (Beijing Long Hu scientific & technical corporation, viscosity is 10000mPa.s ~ 20000mPa.s), 30g VAE (Beijing Long Hu scientific & technical corporation, second-order transition temperature is 16 DEG C), 5g calcium formiate (Beijing Long Hu scientific & technical corporation, industry calcium formiate), 1.5g wilkinite (Beijing Long Hu scientific & technical corporation, calcium-base bentonite) and 3g basalt fibre (Sichuan Aerospace Tuoxin Basalt Industrial Co., Ltd., filament length 3mm, filament diameter 9 μm) mix, obtain 1000g ceramic tile sizing agent.
Embodiment 2
By 370g 52.5R ordinary Portland cement (Jidong Cement Co., Ltd., Tangshan), 250g washed-out sand (Chengde thick source natural siliceous sand company limited, 40 ~ 70 orders), 277.5g washed-out sand (Chengde thick source natural siliceous sand company limited, 70 ~ 140 orders), (Beijing benefits the nation great achievement superfine powder company limited 60g dicalcium powder, 325 orders), 5g ethoxyl methyl cellulose ether (Beijing Long Hu scientific & technical corporation, viscosity is 10000mPa.s ~ 20000mPa.s), 30g VAE (Beijing Long Hu scientific & technical corporation, second-order transition temperature is 16 DEG C), 5g calcium formiate (Beijing Long Hu scientific & technical corporation, industry calcium formiate), 1.5g wilkinite (Beijing Long Hu scientific & technical corporation, calcium-base bentonite) and 1g basalt fibre (Sichuan Aerospace Tuoxin Basalt Industrial Co., Ltd., filament length 3mm, filament diameter 9 μm) mix, obtain 1000g ceramic tile sizing agent.
Embodiment 3
By 370g 52.5R white portland cement (A Erbo Portland (Anqing) company limited), 250g washed-out sand (Chengde thick source natural siliceous sand company limited, 40 ~ 70 orders), 277.5g washed-out sand (Chengde thick source natural siliceous sand company limited, 70 ~ 140 orders), (Beijing benefits the nation great achievement superfine powder company limited 60g dicalcium powder, 325 orders), 5g ethoxyl methyl cellulose ether (Beijing Long Hu scientific & technical corporation, viscosity is 10000mPa.s ~ 20000mPa.s), 30g VAE (Beijing Long Hu scientific & technical corporation, second-order transition temperature is 16 DEG C), 5g calcium formiate (Beijing Long Hu scientific & technical corporation, industry calcium formiate), 1.5g wilkinite (Beijing Long Hu scientific & technical corporation, calcium-base bentonite) and 1g basalt fibre (Sichuan Aerospace Tuoxin Basalt Industrial Co., Ltd., filament length 3mm, filament diameter 9 μm) mix, obtain 1000g ceramic tile sizing agent.
Embodiment 4
By 450g 42.5R ordinary Portland cement (Jidong Cement Co., Ltd., Tangshan), 220g washed-out sand (Chengde thick source natural siliceous sand company limited, 40 ~ 70 orders), 247.5g washed-out sand (Chengde thick source natural siliceous sand company limited, 70 ~ 140 orders), (Beijing benefits the nation great achievement superfine powder company limited 60g dicalcium powder, 325 orders), 5g ethoxyl methyl cellulose ether (Beijing Long Hu scientific & technical corporation, viscosity is 10000mPa.s ~ 20000mPa.s), 30g VAE (Beijing Long Hu scientific & technical corporation, second-order transition temperature is 16 DEG C), 5g calcium formiate (Beijing Long Hu scientific & technical corporation, industry calcium formiate), 1.5g wilkinite (Beijing Long Hu scientific & technical corporation, calcium-base bentonite) and 1g basalt fibre (Sichuan Aerospace Tuoxin Basalt Industrial Co., Ltd., filament length 6mm, filament diameter is 13 μm) mix, obtain 1020g ceramic tile sizing agent.
Embodiment 5
By 450g 42.5R ordinary Portland cement (Jidong Cement Co., Ltd., Tangshan), 220g washed-out sand (Chengde thick source natural siliceous sand company limited, 40 ~ 70 orders), 247.5g washed-out sand (Chengde thick source natural siliceous sand company limited, 70 ~ 140 orders), (Beijing great achievement superfine powder that benefits the nation is limited for 60g dicalcium powder, 325 orders), 5g ethoxyl methyl cellulose ether (Beijing Long Hu scientific & technical corporation, viscosity is 10000mPa.s ~ 20000mPa.s), 30g vinyl acetate-vinyl chloride-ethylene-dien terpolymer (Beijing Long Hu scientific & technical corporation, second-order transition temperature is 14 DEG C), 5g calcium formiate (Beijing Long Hu scientific & technical corporation, industry calcium formiate), 1.5g wilkinite (Beijing Long Hu scientific & technical corporation, calcium-base bentonite) and 1g basalt fibre (Sichuan Aerospace Tuoxin Basalt Industrial Co., Ltd., filament length 3mm, filament diameter is 17 μm) mix, obtain 1020g ceramic tile sizing agent.
Comparative example
By 370g 52.5R ordinary Portland cement (Jidong Cement Co., Ltd., Tangshan), 250g washed-out sand (Chengde thick source natural siliceous sand company limited, 40 ~ 70 orders), 275.5g washed-out sand (Chengde thick source natural siliceous sand company limited, 70 ~ 140 orders), (Beijing benefits the nation great achievement superfine powder company limited 60g dicalcium powder, 325 orders), 5g ethoxyl methyl cellulose ether (Beijing Long Hu scientific & technical corporation, viscosity is 10000mPa.s ~ 20000mPa.s), 30g VAE (Beijing Long Hu scientific & technical corporation, second-order transition temperature is 16 DEG C), 5g calcium formiate (Beijing Long Hu scientific & technical corporation, industry calcium formiate) and 1.5g wilkinite (Beijing Long Hu scientific & technical corporation, calcium-base bentonite) mix, obtain 997g ceramic tile sizing agent.
Embodiment 6
Performance test
Embodiment 1 ~ 3 and comparative example are obtained ceramic tile sizing agent 500g to mix with 125g water respectively, carry out the test of resistant slide performance, adhesive strength and transverse deformation according to JC/T547-2005 standard, result is as shown in table 1, and table 1 is ceramic tile sizing agent the performance test results.
Table 1 ceramic tile sizing agent the performance test results
Can be found out by table 1, performance test is carried out according to JC/T547-2005 standard, the performance of the ceramic tile sizing agent that embodiment 1 ~ 5 is obtained all reaches the technical requirements of C2T, and wherein the performance of embodiment 1 and the obtained ceramic tile sizing agent of embodiment 5 has reached the technical requirements of flexible ceramic tile glue C2TS1.
Carry out wettability test to the ceramic tile sizing agent that embodiment 1 and comparative example obtain, concrete grammar is:
Glue for tile is stirred the combing of rear flute profile scraper on base material, every 10min, 20min; vitrified tile and earthenware brick is put after 30min; and press 30 seconds with the iron pressure head of 2kg respectively, finally vitrified tile and earthenware brick are opened and observe the area that the wet mortar got off is glued at the brick back side, result is as depicted in figs. 1 and 2.Fig. 1 is the wettability test pattern that the embodiment of the present invention 1 obtains ceramic tile sizing agent, and wherein left side is vitrified tile, and right side is earthenware brick, is followed successively by the test fragment of brick every 10min, 20min, 30min from top to bottom; Fig. 2 is the wettability test pattern that comparative example of the present invention obtains ceramic tile sizing agent, and wherein left side is vitrified tile, and right side is earthenware brick, is followed successively by the test fragment of brick every 10min, 20min, 30min from top to bottom.
Relatively can find out by Fig. 1 and Fig. 2, in Fig. 1, the brick back side is glued the wet mortar area got off and is obviously greater than Fig. 2, illustrates that the wettability of the ceramic tile sizing agent that embodiment 1 is obtained is all obviously better than the obtained ceramic tile sizing agent of comparative example.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the premise without departing from the principles of the invention; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (10)
1. a ceramic tile sizing agent, with weight parts, comprises following component:
Cement 35 ~ 45 parts;
Basalt fibre 0.1 ~ 1 part;
45 ~ 65 parts, sand.
2. ceramic tile sizing agent according to claim 1, is characterized in that, the filament diameter of described basalt fibre is 3 ~ 23 μm.
3. ceramic tile sizing agent according to claim 1, is characterized in that, the filament length of described basalt fibre is 3 ~ 15mm.
4. ceramic tile sizing agent according to claim 1, is characterized in that, described ceramic tile sizing agent also comprise in dicalcium powder, latex powder, water-retaining admixture, hardening accelerator and thixotropic lubricant one or more.
5. ceramic tile sizing agent according to claim 4, is characterized in that, the fineness of described dicalcium powder is 250 ~ 500 orders.
6. ceramic tile sizing agent according to claim 4, it is characterized in that, described latex powder is one or more in VAE, vinylacetate-ethylene-tertiary ethylene carbonate polymkeric substance, copolymer in cinnamic acrylic ester, vinyl acetate-tertiary ethylene carbonate-acrylic acid ethylene, vinyl chloride-ethylene-laurate copolymer and vinyl acetate-vinyl chloride-ethylene copolymer.
7. ceramic tile sizing agent according to claim 4, is characterized in that, described water-retaining admixture is ethoxyl methyl cellulose ether and/or hydroxypropyl methyl cellulose ether.
8. ceramic tile sizing agent according to claim 4, is characterized in that, described hardening accelerator is one or more in calcium formiate, calcium chloride and sodium sulfate.
9. ceramic tile sizing agent according to claim 4, is characterized in that, described thixotropic lubricant is wilkinite.
10. ceramic tile sizing agent according to claim 4, is characterized in that, with weight parts, described ceramic tile sizing agent comprises following component: