CN108818863A - A kind of drying anticorrosion process of solid wooden floor board - Google Patents
A kind of drying anticorrosion process of solid wooden floor board Download PDFInfo
- Publication number
- CN108818863A CN108818863A CN201810537298.8A CN201810537298A CN108818863A CN 108818863 A CN108818863 A CN 108818863A CN 201810537298 A CN201810537298 A CN 201810537298A CN 108818863 A CN108818863 A CN 108818863A
- Authority
- CN
- China
- Prior art keywords
- wood flooring
- drying
- flooring cants
- cants
- floor board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of drying anticorrosion process of solid wooden floor board, specific steps include：Plate cutting, blank immersion, blank boiling, primary drying, redrying and post-processing.The present invention sequentially dries Wood flooring cants by high temperature evaporation and infra-red radiation two ways and greatly improves the rate of drying of Wood flooring cants compared to natural drying, is conducive to solid wooden floor board manufacturing enterprise and improves production efficiency, increases the market competitiveness of enterprise.The present invention makes the micropore generated carry out closure reparation using tung oil is dry to Wood flooring cants in time simultaneously, effectively prevents Wood flooring cants and a possibility that dry and cracked occurs in post-processing, improve the quality of solid wooden floor board.
Description
Technical field
The present invention relates to timber manufacture fields, more particularly, to a kind of drying anticorrosion process of solid wooden floor board.
Background technique
Solid wooden floor board is the floor formed after natural timber drying, processing.The natural wood line that solid wooden floor board shows
Reason and colour image, give nature, soft, rich in affinity texture, simultaneously because the characteristic that it is cool in summer and warm in winter, sense of touch is good
Become the ideal material of the ground surface finishings such as bedroom, parlor, study.
In the process of solid wooden floor board, the Wood flooring cants for finishing cutting is needed to be dried, to reduce
The water content of Wood flooring cants, the degree of drying of Wood flooring cants directly affect the stability of solid wooden floor board finished product.Meanwhile
To in the drying process of Wood flooring cants, it is also noted that preservative treatment is carried out to Wood flooring cants, to prevent solid wooden floor board finished product
In the normal use process after selling, lead to rotten damage because of itself quality problem.
Existing timber drying process, majority take a long time, and are unfavorable for the quick production of enterprise.
Summary of the invention
The present invention is to overcome above situation insufficient, it is desirable to provide a kind of technical solution that can solve the above problem.
A kind of drying anticorrosion process of solid wooden floor board, specific step is as follows：
S1, plate cutting：Cutting process is carried out to log, the rectangular plate of 15~20mm of thickness is finally made, as timber floor base
Material；
S2, blank impregnate：Wood flooring cants are immersed in thimerosal 5~6 hours, so that thimerosal can be impregnated with the wooden ground completely
Plate blank material, while sterilization processing is made to Wood flooring cants by thimerosal；
S3, blank boiling：It will be impregnated in the Wood flooring cants merging water of thimerosal, boiling heated, in dilution Wood flooring cants
While sterilizing liquid hold-up, additionally it is possible to soften Wood flooring cants, reduce timber color difference, beautify the appearance of Wood flooring cants, work as water
After boiling, continuous heating is kept for fluidized state 6~8 hours；
S4, primary drying：The outer surface moisture of Wood flooring cants after boiling is dried, then the timber floor base after drying
Material is put into hothouse, and dry room temperature is slowly promoted to 75~85 degrees Celsius, and slow cooling after holding 8~10 hours,
Region drying by Wood flooring cants close to outer surface finishes；
S5, redrying：Wood flooring cants after primary drying are taken out, and are put into infra-red drying room, infra-red radiation 3
~4 hours, by vaporizing the moisture in Wood flooring cants using infrared radiation, reaching reduced Wood flooring cants inner aqueous
The purpose of amount；
S6, post-processing：Wood flooring cants after redrying are immersed in tung oil 2~3 hours, tung oil is made to block timber floor
The micropore left after blank dehydration and drying, prevents Wood flooring cants from occurring in post-processing dry and cracked, then takes out timber floor base
Material, carries out further deep processing, and the Wood flooring cants surface after completion of processing sprays potassium silicate fire resistant coating, most end form
At solid wooden floor board finished product.
As a further solution of the present invention：In the step S1, in cutting process log, it will include and be not limited to worm
Moth, rotten and burr region unqualified part are given up.
As a further solution of the present invention：In the step S2, using glutaraldehyde solution as thimerosal, to timber floor
Blank makees sterilization processing by impregnating.
As a further solution of the present invention：In the step S3, using 4 degrees Celsius of cold water soak Wood flooring cants,
Wood flooring cants are heated with the heating rate of 10~15 degrees Celsius/hour again.
As a further solution of the present invention：In the step S4, high-temperature resistant fan is provided in hothouse, it is dry to promote
The air circulation of dry chamber interior accelerates the drying to Wood flooring cants.
As a further solution of the present invention：In the step S5, infra-red drying room uses 10 μm of infrared rays of launch wavelength
Fuel plate.
As a further solution of the present invention：In the step S6, potassium silicate fire resistant coating with a thickness of 0.3~0.6mm.
Compared with prior art, the beneficial effects of the invention are as follows：
The present invention sequentially dries Wood flooring cants by high temperature evaporation and infra-red radiation two ways, compared to natural drying, pole
The big rate of drying for improving Wood flooring cants is conducive to solid wooden floor board manufacturing enterprise and improves production efficiency, increases enterprise
The market competitiveness.The present invention makes the micropore generated carry out closure reparation using tung oil is dry to Wood flooring cants in time simultaneously, has
Effect prevents Wood flooring cants that a possibility that dry and cracked occurs in post-processing, improves the quality of solid wooden floor board.
Additional aspect and advantage of the invention will be set forth in part in the description, and will partially become from the following description
Obviously, or practice through the invention is recognized.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
In the embodiment of the present invention 1, a kind of drying anticorrosion process of solid wooden floor board, specific step is as follows：
S1, plate cutting：Cutting process is carried out to log, the rectangular plate of thick 20mm is finally made, as Wood flooring cants；
S2, blank impregnate：Wood flooring cants are immersed in thimerosal 6 hours, so that thimerosal can be impregnated with timber floor completely
Blank, while sterilization processing is made to Wood flooring cants by thimerosal；
S3, blank boiling：It will be impregnated in the Wood flooring cants merging water of thimerosal, boiling heated, in dilution Wood flooring cants
While sterilizing liquid hold-up, additionally it is possible to soften Wood flooring cants, reduce timber color difference, beautify the appearance of Wood flooring cants, work as water
After boiling, continuous heating is kept for fluidized state 8 hours；
S4, primary drying：The outer surface moisture of Wood flooring cants after boiling is dried, then the timber floor base after drying
Material is put into hothouse, and dry room temperature is slowly promoted to 75 degrees Celsius, and slow cooling after holding 10 hours, by timber floor
Region drying of the blank close to outer surface finishes；
S5, redrying：Wood flooring cants after primary drying are taken out, and are put into infra-red drying room, infra-red radiation 4
Hour, by vaporizing the moisture in Wood flooring cants using infrared radiation, reaching reduces Wood flooring cants interior moisture content
Purpose；
S6, post-processing：Wood flooring cants after redrying are immersed in tung oil 3 hours, tung oil is made to block timber floor base
The micropore left after material dehydration and drying, prevents Wood flooring cants from occurring in post-processing dry and cracked, then takes out Wood flooring cants,
Further deep processing is carried out, and the Wood flooring cants surface after completion of processing sprays potassium silicate fire resistant coating, ultimately forms
Solid wooden floor board finished product.
In the embodiment of the present invention 2, a kind of drying anticorrosion process of solid wooden floor board, specific step is as follows：
S1, plate cutting：Cutting process is carried out to log, the rectangular plate of thick 18mm is finally made, as Wood flooring cants；
S2, blank impregnate：Wood flooring cants are immersed in thimerosal 5.5 hours, so that thimerosal can be impregnated with the wooden ground completely
Plate blank material, while sterilization processing is made to Wood flooring cants by thimerosal；
S3, blank boiling：It will be impregnated in the Wood flooring cants merging water of thimerosal, boiling heated, in dilution Wood flooring cants
While sterilizing liquid hold-up, additionally it is possible to soften Wood flooring cants, reduce timber color difference, beautify the appearance of Wood flooring cants, work as water
After boiling, continuous heating is kept for fluidized state 7 hours；
S4, primary drying：The outer surface moisture of Wood flooring cants after boiling is dried, then the timber floor base after drying
Material is put into hothouse, and dry room temperature is slowly promoted to 80 degrees Celsius, and slow cooling after holding 9 hours, by timber floor
Region drying of the blank close to outer surface finishes；
S5, redrying：Wood flooring cants after primary drying are taken out, and are put into infra-red drying room, infra-red radiation
3.5 hours, by vaporizing the moisture in Wood flooring cants using infrared radiation, reaching reduced Wood flooring cants inner aqueous
The purpose of amount；
S6, post-processing：Wood flooring cants after redrying are immersed in tung oil 2.5 hours, tung oil is made to block timber floor
The micropore left after blank dehydration and drying, prevents Wood flooring cants from occurring in post-processing dry and cracked, then takes out timber floor base
Material, carries out further deep processing, and the Wood flooring cants surface after completion of processing sprays potassium silicate fire resistant coating, most end form
At solid wooden floor board finished product.
In the embodiment of the present invention 3, a kind of drying anticorrosion process of solid wooden floor board, specific step is as follows：
S1, plate cutting：Cutting process is carried out to log, the rectangular plate of thick 15mm is finally made, as Wood flooring cants；
S2, blank impregnate：Wood flooring cants are immersed in thimerosal 5 hours, so that thimerosal can be impregnated with timber floor completely
Blank, while sterilization processing is made to Wood flooring cants by thimerosal；
S3, blank boiling：It will be impregnated in the Wood flooring cants merging water of thimerosal, boiling heated, in dilution Wood flooring cants
While sterilizing liquid hold-up, additionally it is possible to soften Wood flooring cants, reduce timber color difference, beautify the appearance of Wood flooring cants, work as water
After boiling, continuous heating is kept for fluidized state 6 hours；
S4, primary drying：The outer surface moisture of Wood flooring cants after boiling is dried, then the timber floor base after drying
Material is put into hothouse, and dry room temperature is slowly promoted to 85 degrees Celsius, and slow cooling after holding 8 hours, by timber floor
Region drying of the blank close to outer surface finishes；
S5, redrying：Wood flooring cants after primary drying are taken out, and are put into infra-red drying room, infra-red radiation 3
Hour, by vaporizing the moisture in Wood flooring cants using infrared radiation, reaching reduces Wood flooring cants interior moisture content
Purpose；
S6, post-processing：Wood flooring cants after redrying are immersed in tung oil 2 hours, tung oil is made to block timber floor base
The micropore left after material dehydration and drying, prevents Wood flooring cants from occurring in post-processing dry and cracked, then takes out Wood flooring cants,
Further deep processing is carried out, and the Wood flooring cants surface after completion of processing sprays potassium silicate fire resistant coating, ultimately forms
Solid wooden floor board finished product.
The working principle of the invention is：
The present invention sequentially dries Wood flooring cants by high temperature evaporation and infra-red radiation two ways, compared to natural drying, pole
The big rate of drying for improving Wood flooring cants is conducive to solid wooden floor board manufacturing enterprise and improves production efficiency, increases enterprise
The market competitiveness.The present invention makes the micropore generated carry out closure reparation using tung oil is dry to Wood flooring cants in time simultaneously, has
Effect prevents Wood flooring cants that a possibility that dry and cracked occurs in post-processing, improves the quality of solid wooden floor board.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.
Claims (7)
1. a kind of drying anticorrosion process of solid wooden floor board, which is characterized in that specific step is as follows for it：
S1, plate cutting：Cutting process is carried out to log, the rectangular plate of thick 20mm is finally made, as Wood flooring cants；
S2, blank impregnate：Wood flooring cants are immersed in thimerosal 6 hours, so that thimerosal can be impregnated with timber floor completely
Blank, while sterilization processing is made to Wood flooring cants by thimerosal；
S3, blank boiling：It will be impregnated in the Wood flooring cants merging water of thimerosal, boiling heated, in dilution Wood flooring cants
While sterilizing liquid hold-up, additionally it is possible to soften Wood flooring cants, reduce timber color difference, beautify the appearance of Wood flooring cants, work as water
After boiling, continuous heating is kept for fluidized state 8 hours；
S4, primary drying：The outer surface moisture of Wood flooring cants after boiling is dried, then the timber floor base after drying
Material is put into hothouse, and dry room temperature is slowly promoted to 75 degrees Celsius, and slow cooling after holding 10 hours, by timber floor
Region drying of the blank close to outer surface finishes；
S5, redrying：Wood flooring cants after primary drying are taken out, and are put into infra-red drying room, infra-red radiation 4
Hour, by vaporizing the moisture in Wood flooring cants using infrared radiation, reaching reduces Wood flooring cants interior moisture content
Purpose；
S6, post-processing：Wood flooring cants after redrying are immersed in tung oil 3 hours, tung oil is made to block timber floor base
The micropore left after material dehydration and drying, prevents Wood flooring cants from occurring in post-processing dry and cracked, then takes out Wood flooring cants,
Further deep processing is carried out, and the Wood flooring cants surface after completion of processing sprays potassium silicate fire resistant coating, ultimately forms
Solid wooden floor board finished product.
2. the drying anticorrosion process of solid wooden floor board according to claim 1, which is characterized in that in the step S1, cutting
When cutting processing logs, it will include and be not limited to damage by worms, rot and the unqualified part in burr region is given up.
3. the drying anticorrosion process of solid wooden floor board according to claim 1, which is characterized in that in the step S2, use
Glutaraldehyde solution makees sterilization processing by impregnating as thimerosal, to Wood flooring cants.
4. the drying anticorrosion process of solid wooden floor board according to claim 1, which is characterized in that in the step S3, use 4
Degree Celsius cold water soak Wood flooring cants, then Wood flooring cants are added with the heating rate of 10~15 degrees Celsius/hour
Heat.
5. the drying anticorrosion process of solid wooden floor board according to claim 1, which is characterized in that dry in the step S4
Interior is provided with high-temperature resistant fan, to promote the air circulation inside hothouse, accelerates the drying to Wood flooring cants.
6. the drying anticorrosion process of solid wooden floor board according to claim 1, which is characterized in that infrared in the step S5
Hothouse uses the fuel plate of 10 μm of infrared rays of launch wavelength.
7. the drying anticorrosion process of solid wooden floor board according to claim 1, which is characterized in that in the step S6, silicic acid
Potassium fire resistant coating with a thickness of 0.3~0.6mm.