CN108818832A - A kind of mildew preventing agent for wood - Google Patents
A kind of mildew preventing agent for wood Download PDFInfo
- Publication number
- CN108818832A CN108818832A CN201810714551.2A CN201810714551A CN108818832A CN 108818832 A CN108818832 A CN 108818832A CN 201810714551 A CN201810714551 A CN 201810714551A CN 108818832 A CN108818832 A CN 108818832A
- Authority
- CN
- China
- Prior art keywords
- parts
- wood
- graecum
- lily
- lavender
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of mildew preventing agent for wood, in parts by weight include the following raw material：5.5~12 parts of lily, 3.5~6.5 parts of lophatherum gracile, 6~11 parts of wormwood, 8~12 parts of Lysimachia foenum-graecum, 6.5~12.5 parts of lavender, 5~8.5 parts of dried peppermint leaf, 25~35 parts of carbendazim, 8~12 parts of sunflower oil, 9~15 parts of epoxy resin, 1.2~1.8 portions of elecampane China tree, 0.8~1.6 part of seed extract, 75~110 parts of water.After impregnating timber with the mould inhibitor, a mould situation will not occur after enabling to timber to be used for a long time, extend the service life of wood furniture.
Description
Technical field
The present invention relates to a kind for the treatment of process of timber, more particularly to a kind of mould inhibitor that can prevent timber mildew.
Background technique
The timber that wood furniture is used mainly has solid wood original plank, multi-layer solid wood plate（Multi-layer board）It is real with multilayer particieboard
The wooden original plank creates that the furniture come is durable, and appearance is beautiful, but cost is high, price height, according to different timber,
Price differs greatly, and ordinary consumer is difficult to bear.The furniture price that multilayer particieboard is created is low, and appearance is beautiful, still
After long-time service, being easy to make moist, it is mouldy to deform, and service life is shorter.The generally existing problem of wood furniture, that is, long-term
After use, wood furniture will appear mouldy situation of making moist, and the appearance of furniture and service life is caused to be affected.
Summary of the invention
In view of the deficiencies of the prior art, the present invention provides a kind of mildew preventing agent for wood, impregnate timber with the mould inhibitor
Afterwards, a mould situation will not occur after enabling to timber to be used for a long time, extend the service life of wood furniture.
To achieve the above object, the present invention provides following technical solutions：
A kind of mildew preventing agent for wood, it is characterised in that：It in parts by weight include the following raw material：
5.5~12 parts of lily
3.5~6.5 parts of lophatherum gracile
6~11 parts of wormwood
8~12 parts of Lysimachia foenum-graecum
6.5~12.5 parts of lavender
5~8.5 parts of dried peppermint leaf
25~35 parts of carbendazim
8~12 parts of sunflower oil
9~15 parts of epoxy resin
1.2~1.8 parts of elecampane
0.8~1.6 part of China tree seed extract
75~110 parts of water.
As preferred：The mould inhibitor includes the following raw material in parts by weight：
6.8 parts of lily
5 parts of lophatherum gracile
8 parts of wormwood
8 parts of Lysimachia foenum-graecum
6.5 parts of lavender
7 parts of dried peppermint leaf
28 parts of carbendazim
10 parts of sunflower oil
11 parts of epoxy resin
1.6 parts of elecampane
1.2 parts of China tree seed extract
80 parts of water.
The preparation method of the mould inhibitor is：
Step 1, above-mentioned raw materials are weighed according to parts by weight；
Step 2, lily, lophatherum gracile, wormwood, Lysimachia foenum-graecum, lavender, dried peppermint leaf are mixed and is smashed to pieces；
Step 3, sunflower oil and epoxy resin are added to the lily smashed to pieces, lophatherum gracile, wormwood, Lysimachia foenum-graecum, lavender, peppermint
Ye Zhong is stirred 10~20 minutes；
Step 4, the material Jing Guo step 3 is put into heating furnace and is heated 15~20 minutes, heating temperature is 58~62 DEG C；
Step 5, elecampane, China tree seed extract and carbendazim are added to by being put into guarantor in step 4 treated material
8~12 minutes are kept the temperature in warm furnace, holding temperature is 32 DEG C；
Step 6,65 DEG C are heated the water to, will by step 5, treated that material pours into hot water, stir 5~8 minutes, it is cooling
To room temperature；
Step 7, it is filtered through step 6 treated material, obtains filtered fluid, filtered fluid is mould inhibitor.
The invention has the advantages that：
Mould inhibitor provided by the invention includes 5.5~12 parts of lily, and 3.5~6.5 parts of lophatherum gracile, 6~11 parts of wormwood, Lysimachia foenum-graecum
8~12 parts, 6.5~12.5 parts of lavender, 5~8.5 parts of dried peppermint leaf, 25~35 parts of carbendazim, 8~12 parts of sunflower oil, asphalt mixtures modified by epoxy resin
9~15 parts of rouge, 1.2~1.8 parts of elecampane, 0.8~1.6 part of China tree seed extract, 75~110 parts of water.Above-mentioned raw materials are pure
Natural material can not only play mould proof effect, and safe without toxic side effect, moreover it is possible to give out light fragrance, use effect
Fruit is more preferable, and timber is immersed in above-mentioned mould inhibitor, and mould inhibitor slowly infiltrates in timber, connects with the everywhere tissue of timber
Touching, is incorporated in timber, firm binding force, so that timber long-time service also has the effect of mould proof, to manufacture in this way wood
The service life of matter furniture will be longer, after wood furniture damage, will not occur mildew on furniture, anti-mold effect is fine.
Mould inhibitor of the present invention includes the following raw material in parts by weight：6.8 parts of lily, 5 parts of lophatherum gracile, 8 parts of wormwood,
8 parts of Lysimachia foenum-graecum, 6.5 parts of lavender, 7 parts of dried peppermint leaf, 28 parts of carbendazim, 10 parts of sunflower oil, 11 parts of epoxy resin, elecampane 1.6
Part, 1.2 parts of China tree seed extract, 80 parts of present invention of water select these parts by weight to match the mould inhibitor anti-mold effect manufactured
Preferably, the binding force contacted with timber is maximum, most securely, mould proof time longest.
Specific embodiment
Embodiment 1
Mould inhibitor in the present embodiment includes the following raw material in parts by weight：
5.5 parts of lily
3.5 parts of lophatherum gracile
6 parts of wormwood
8 parts of Lysimachia foenum-graecum
6.5 parts of lavender
8.5 parts of dried peppermint leaf
35 parts of carbendazim
12 parts of sunflower oil
15 parts of epoxy resin
1.8 parts of elecampane
1.6 parts of China tree seed extract
110 parts of water.
The preparation method of the mould inhibitor is：
Step 1, above-mentioned raw materials are weighed according to parts by weight；
Step 2, lily, lophatherum gracile, wormwood, Lysimachia foenum-graecum, lavender, dried peppermint leaf are mixed and is smashed to pieces；
Step 3, sunflower oil and epoxy resin are added to the lily smashed to pieces, lophatherum gracile, wormwood, Lysimachia foenum-graecum, lavender, peppermint
Ye Zhong is stirred 10 minutes；
Step 4, the material Jing Guo step 3 is put into heating furnace and is heated 15 minutes, heating temperature is 62 DEG C；
Step 5, elecampane, China tree seed extract and carbendazim are added to by being put into guarantor in step 4 treated material
8 minutes are kept the temperature in warm furnace, holding temperature is 32 DEG C；
Step 6,65 DEG C are heated the water to, will by step 5, treated that material pours into hot water, stir 5 minutes, be cooled to room
Temperature；
Step 7, it is filtered through step 6 treated material, obtains filtered fluid, filtered fluid is mould inhibitor.
Embodiment 2
Mould inhibitor includes the following raw material in parts by weight in the present embodiment：
6.8 parts of lily
5 parts of lophatherum gracile
8 parts of wormwood
8 parts of Lysimachia foenum-graecum
6.5 parts of lavender
7 parts of dried peppermint leaf
28 parts of carbendazim
10 parts of sunflower oil
11 parts of epoxy resin
1.6 parts of elecampane
1.2 parts of China tree seed extract
80 parts of water.
The preparation method of the mould inhibitor is：
Step 1, above-mentioned raw materials are weighed according to parts by weight；
Step 2, lily, lophatherum gracile, wormwood, Lysimachia foenum-graecum, lavender, dried peppermint leaf are mixed and is smashed to pieces；
Step 3, sunflower oil and epoxy resin are added to the lily smashed to pieces, lophatherum gracile, wormwood, Lysimachia foenum-graecum, lavender, peppermint
Ye Zhong is stirred 15 minutes；
Step 4, the material Jing Guo step 3 is put into heating furnace and is heated 20 minutes, heating temperature is 58 DEG C；
Step 5, elecampane, China tree seed extract and carbendazim are added to by being put into guarantor in step 4 treated material
10 minutes are kept the temperature in warm furnace, holding temperature is 32 DEG C；
Step 6,65 DEG C are heated the water to, will by step 5, treated that material pours into hot water, stir 6 minutes, be cooled to room
Temperature；
Step 7, it is filtered through step 6 treated material, obtains filtered fluid, filtered fluid is mould inhibitor.
Embodiment 3
Mould inhibitor in the present embodiment includes the following raw material in parts by weight：
12 parts of lily
6.5 parts of lophatherum gracile
11 parts of wormwood
12 parts of Lysimachia foenum-graecum
12.5 parts of lavender
5 parts of dried peppermint leaf
25 parts of carbendazim
8 parts of sunflower oil
9 parts of epoxy resin
1.2 parts of elecampane
0.8 part of China tree seed extract
75 parts of water.
The preparation method of the mould inhibitor is：
Step 1, above-mentioned raw materials are weighed according to parts by weight；
Step 2, lily, lophatherum gracile, wormwood, Lysimachia foenum-graecum, lavender, dried peppermint leaf are mixed and is smashed to pieces；
Step 3, sunflower oil and epoxy resin are added to the lily smashed to pieces, lophatherum gracile, wormwood, Lysimachia foenum-graecum, lavender, peppermint
Ye Zhong is stirred 16 minutes；
Step 4, the material Jing Guo step 3 is put into heating furnace and is heated 18 minutes, heating temperature is 61 DEG C；
Step 5, elecampane, China tree seed extract and carbendazim are added to by being put into guarantor in step 4 treated material
9 minutes are kept the temperature in warm furnace, holding temperature is 32 DEG C；
Step 6,65 DEG C are heated the water to, will by step 5, treated that material pours into hot water, stir 7 minutes, be cooled to room
Temperature；
Step 7, it is filtered through step 6 treated material, obtains filtered fluid, filtered fluid is mould inhibitor.
Embodiment 4
Mould inhibitor in the present embodiment includes the following raw material in parts by weight：
6.8 parts of lily
4.5 parts of lophatherum gracile
7.5 parts of wormwood
9.5 parts of Lysimachia foenum-graecum
8 parts of lavender
7 parts of dried peppermint leaf
32 parts of carbendazim
9 parts of sunflower oil
11 parts of epoxy resin
1.6 parts of elecampane
1.1 parts of China tree seed extract
110 parts of water.
The preparation method of the mould inhibitor is：
Step 1, above-mentioned raw materials are weighed according to parts by weight；
Step 2, lily, lophatherum gracile, wormwood, Lysimachia foenum-graecum, lavender, dried peppermint leaf are mixed and is smashed to pieces；
Step 3, sunflower oil and epoxy resin are added to the lily smashed to pieces, lophatherum gracile, wormwood, Lysimachia foenum-graecum, lavender, peppermint
Ye Zhong is stirred 11 minutes；
Step 4, the material Jing Guo step 3 is put into heating furnace and is heated 19 minutes, heating temperature is 61 DEG C；
Step 5, elecampane, China tree seed extract and carbendazim are added to by being put into guarantor in step 4 treated material
9 minutes are kept the temperature in warm furnace, holding temperature is 32 DEG C；
Step 6,65 DEG C are heated the water to, will by step 5, treated that material pours into hot water, stir 7 minutes, be cooled to room
Temperature；
Step 7, it is filtered through step 6 treated material, obtains filtered fluid, filtered fluid is mould inhibitor.
After timber is according to the processing step processing of above-described embodiment, the furniture manufactured is durable, and furniture is instructed to damage
It is bad to generate mildew.
The above is only a preferred embodiment of the present invention, protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical solutions belonged under thinking of the present invention all belong to the scope of protection of the present invention.It should be pointed out that being led for this technology
For the those of ordinary skill in domain, several improvements and modifications without departing from the principles of the present invention, these improvements and modifications
Also it should be regarded as protection scope of the present invention.
Claims (2)
1. a kind of mildew preventing agent for wood, it is characterised in that：It in parts by weight include the following raw material：
5.5~12 parts of lily
3.5~6.5 parts of lophatherum gracile
6~11 parts of wormwood
8~12 parts of Lysimachia foenum-graecum
6.5~12.5 parts of lavender
5~8.5 parts of dried peppermint leaf
25~35 parts of carbendazim
8~12 parts of sunflower oil
9~15 parts of epoxy resin
1.2~1.8 parts of elecampane
0.8~1.6 part of China tree seed extract
75~110 parts of water.
2. a kind of mildew preventing agent for wood according to claim 1, it is characterised in that：The mould inhibitor is in parts by weight
Including the following raw material：
6.8 parts of lily
5 parts of lophatherum gracile
8 parts of wormwood
8 parts of Lysimachia foenum-graecum
6.5 parts of lavender
7 parts of dried peppermint leaf
28 parts of carbendazim
10 parts of sunflower oil
11 parts of epoxy resin
1.6 parts of elecampane
1.2 parts of China tree seed extract
80 parts of water.