CN108816235B - 一种可磁回收的多孔Ni@GCC复合材料及其制备方法和应用 - Google Patents
一种可磁回收的多孔Ni@GCC复合材料及其制备方法和应用 Download PDFInfo
- Publication number
- CN108816235B CN108816235B CN201810724776.6A CN201810724776A CN108816235B CN 108816235 B CN108816235 B CN 108816235B CN 201810724776 A CN201810724776 A CN 201810724776A CN 108816235 B CN108816235 B CN 108816235B
- Authority
- CN
- China
- Prior art keywords
- gcc
- norfloxacin
- magnetically
- porous
- composite material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种可磁回收的多孔Ni@GCC复合材料及其制备方法和应用。采用的技术方案是：采用水热方法合成Ni‑MOF前驱体，并衍生得到杨梅状Ni@GCC复合功能材料。本发明以Ni@GCC复合材料为催化剂，协同微波降解诺氟沙星。制备的Ni@GCC具有良好的磁性，可通过外部磁铁实现快速的分离回收，循环使用五次后，诺氟沙星降解率仍能达到96％以上，材料的高重复利用性及循环稳定性使其在实际应用中有非常好的前景。
Description
技术领域
本发明属于催化剂领域，具体的涉及一种能高效降解有机污染物的可磁回收的多孔Ni@GCC复合材料及其制备方法和应用。
背景技术
抗生素自问世以来，备受人们的关注，使用比例也相当大。其中，诺氟沙星是一种典型的喹诺酮类抗生素，因其具有广谱性抗菌、临床效果好等优点，广泛应用于医疗、畜牧养殖和水产业等领域。据统计，诺氟沙星仅2001年的产量约为3500吨，2002年增加为3600吨。人畜摄入抗生素后，在体内不能被完全代谢，其中一部分被吸收和利用，仍有大约75％以原药或代谢物的形式，经人体循环后随尿液和粪便排出体外。鉴于诺氟沙星被无节制地使用，近年来，在水环境中被频繁检出。并且，诺氟沙星半衰期较长，在自然界中能够稳定存在，短时间内无法被降解，因此，残留在环境中的诺氟沙星会对生命机体产生毒害作用，甚至诱导生物产生抗药性，造成潜在危害。因此，抗生素作为新型污染物受到人们日益关注，环境水体中残留抗生素的去除研究具有十分重要的意义。
微波驱动的催化降解技术，因其具有催化速率快(几分钟内)、矿化度高、可处理生物难降解有机污染物等特点，成为有机废水处理的新兴技术。选择合适吸波材料对降解效率的提高十分重要。目前，常用的吸波材料有活性炭，金属氧化物，聚合物等。过渡金属纳米粒子是非常优越的吸波材料，然而很少有将其作为微波催化剂降解有机污染的研究报道。尽管其具有超高的吸波能力，但其具有易于团聚、在空气中不稳定而被氧化失活等缺点，限制了其实际应用。
发明内容
本发明的目的是提供一种碳包覆的过渡金属纳米粒子作为微波催化剂。以MOFs衍生的构建方式，原位得到石墨化的碳层，保护过渡粒子不被氧化；并且可继承MOFs前驱体可变的形貌及多孔的特性，实现高度分散的碳包覆过渡金属纳米粒子。
本发明合成的可磁回收的多孔Ni@GCC复合材料作为催化剂，协同微波降解抗生素诺氟沙星，充分展示了Ni@GCC材料优异的催化性能，以及微波协同降解方法的高效性。
本发明采用的技术方案是：一种可磁回收的多孔Ni@GCC复合材料，所述的可磁回收的多孔Ni@GCC复合材料为球形，BET比表面积为110～130m2·g-1，孔径大小为12～15nm，饱和磁化量为33.71～37.8emu·g-1。
一种可磁回收的多孔Ni@GCC复合材料的制备方法，包括如下步骤：将硝酸镍、均苯三甲酸和聚乙烯吡咯烷酮溶解于混合溶剂中，然后转移到反应釜中，在140～160℃下反应9～11h，自然冷却至室温，乙醇洗涤，干燥，得Ni-MOF前驱体粉末；将所得Ni-MOF前驱体粉末置于管式炉中，在氮气保护下700℃煅烧3～4h，得到可磁回收的多孔Ni@GCC复合材料。
优选的，所述的混合溶剂为，按体积比，乙醇:水:DMF＝1:1:1。
可磁回收的多孔Ni@GCC复合材料在降解有机污染物中的应用。优选的，所述的有机污染物是喹诺酮类抗生素。更优选的，所述的喹诺酮类抗生素是诺氟沙星。
可磁回收的多孔Ni@GCC复合材料在降解有机污染物中的应用。方法如下：于含有诺氟沙星的溶液中，加入上述的可磁回收的多孔Ni@GCC复合材料，微波协同诱导催化降解。
优选的，方法如下：调节诺氟沙星的初始浓度为5mg·L-1～20mg·L-1，加入上述的可磁回收的多孔Ni@GCC复合材料，在微波功率100～700W下催化降解3～7min；每50mL初始浓度为5mg·L-1～20mg·L-1的诺氟沙星的溶液中，加入20～80mg上述的可磁回收的多孔Ni@GCC复合材料。
更优选的，方法如下：调节诺氟沙星的初始浓度为10mg·L-1，加入60mg上述的可磁回收的多孔Ni@GCC复合材料，在微波功率700W下催化降解3～7min。
本发明的有益效果是：本发明合成的可磁回收的多孔Ni@GCC复合材料作为催化剂，协同微波降解抗生素诺氟沙星，充分展示了Ni@GCC材料优异的催化性能，以及微波协同降解方法的高效性，对诺氟沙星的降解率可达97％以上，材料的高重复利用性及循环稳定性使其在实际应用中有非常好的前景。
附图说明
图1是Ni@GCC的XRD图谱。
图2是Ni@GCC的扫描电镜图。
图3是Ni@GCC的N2吸附解析曲线。
图4是Ni@GCC的孔径分布。
图5是Ni@GCC的磁滞回线图。
图6是循环前后Ni@GCC的FTIR图。
图7是循环前后Ni@GCC的XRD图。
图8是微波诱导Ni@GCC催化降解诺氟沙星机理图。
具体实施方式
实施例1
(一)可磁回收的多孔Ni@GCC复合材料的制备方法
采用金属有机框架(MOFs)材料衍生方式构建吸波材料Ni@GCC。
将0.864g硝酸镍Ni(NO3)2·6H2O，0.3g均苯三甲酸(H3BTC)和3g聚乙烯吡咯烷酮(PVP)溶解于60mL混合溶剂中(乙醇：水：DMF的体积比为1:1:1)，持续搅拌30min至完全溶解。随后，将上述溶液转移到100mL反应釜中，在150℃下反应10h。待反应结束，自然冷却至室温，产物用乙醇洗三次，并在60℃下干燥12h，得到Ni-MOF前驱体粉末。最后，将所得Ni-MOF前驱体粉末置于管式炉中进行热解，在氮气保护下，700℃煅烧3h，得到Ni@GCC复合材料。
(二)Ni@GCC的表征
由图1可知，成功的合成出了Ni-MOF前驱体，并衍生得到Ni@GCC，其衍射峰44.88°，52.16°和76.63°分别与金属Ni的(111)，(200)和(220)晶面相对应。25°左右与石墨碳的(220)面相吻合，石墨碳均匀分散于复合材料中。没有其他峰，说明本发明成功合成出Ni@GCC，且纯度很高。
图2为Ni@GCC的扫描电镜图，可以直观的展示出材料的微观形貌，由图2(a)可以清楚的看出，Ni@GCC具有球形结构，表面有很多突起，形似杨梅状，尺寸大约在3um。图2(b)是放大后表面的刺状结构，它均匀的生长在球表面。这样的形貌有助于微波的吸收，有利于催化降解。
图3是Ni@GCC的N2吸附解析曲线。催化剂的比表面积影响着目标物与活性位点的接触，通过扫描电镜照片可得知Ni@GCC具有较大的比表面积。通过N2吸附-解析曲线可以进一步的验证，由图3可知Ni@GCC的BET表面积为110m2·g-1，Ni@GCC的孔径分布图见图4，孔径大小为12nm。较大的比表面积有利于微波催化降解。
在室温下外加磁场范围-20.0kOe≤H≤20.0kOe条件下，测得Ni@GCC的磁滞回线如图5所示。由图5可见，Ni@GCC的饱和磁化量为33.71emu·g-1。Ni@GCC具有良好的磁性，这一特性尤为重要，使催化剂可以十分便利的从目标物中分离出来，有利于它的分离回收处理，简化了操作过程，这在实际应用中有很大优势，具有重要的现实意义。
实施例2可磁回收的多孔Ni@GCC复合材料降解诺氟沙星
降解实验在可控温的微波仪中进行，其上装有冷凝回流装置。
方法如下：移取50mL初始浓度为5mg·L-1～20mg·L-1的诺氟沙星溶液于250mL的三口圆底烧瓶中，加入20～80mg Ni@GC，然后置于微波仪中，在微波功率100～700W下催化降解1～7min。待反应结束后，迅速利用磁性分离取出上层清液，采用紫外光谱仪测量其紫外吸收曲线，并记录最大吸收波长处所对应的吸光度值A，计算对应的降解效率。
(一)Ni@GCC微波诱导的催化活性
为了证明微波与Ni@GCC协同催化降解作用的优越性能，分别考察了微波和Ni@GCC单独作用下，对诺氟沙星的去除效果，结果如表1。
表1不同去除方法效果对比
由表1可见，仅直接用微波辐射诺氟沙星，7min后基本不会降解；用Ni@GCC对诺氟沙星单独吸附30min达到平衡后，去除率仅为16.27％；而在MW/Ni@GCC协同作用的情况下，短短的7min内诺氟沙星的降解率即达到97.4％。表明，MW/Ni@GCC是降解诺氟沙星的有效方法，并且其协同作用效果相当显著。
(二)微波辐射时间的影响
为了考察MW/Ni@GCC协同催化降解诺氟沙星的作用效果随微波辐射时间的变化，进行了如下实验。向50mL浓度为10mg·L-1的诺氟沙星溶液中加入质量为60mg的Ni@GCC，设置微波功率700W。
表2不同微波辐射时间对诺氟沙星降解效率的影响
由表2可见，诺氟沙星在微波辐射下，30s降解率便达到60.5％，并随着微波辐射时间的增加而增大，当微波7min时其降解率可达97.4％，基本实现完全降解。
(三)Ni@GCC用量的影响
催化剂的用量直接影响着诺氟沙星的降解效率，所以对此进行了考察。实验中控制以下参数不变：诺氟沙星溶液浓度为10mg·L-1，微波功率700W，照射7min。向50mL溶液中分别加入质量为20mg，40mg，60mg和80mg的Ni@GCC，结果如表3。
表3Ni@GCC用量对诺氟沙星降解效果的影响
由表3可见，随着催化剂用量的增加，降解效率也随之增大。这是由于催化剂量的增加，会产生更多的催化活性粒子，有利于催化降解的进行。但用量由60mg增加到80mg后，降解率并没有显著的提高，因此为了节约资源，考虑成本因素，选择60mg作为Ni@GCC的最佳用量来MW/Ni@GCC协同降解诺氟沙星。
(四)诺氟沙星初始浓度的影响
初始浓度在5mg·L-1至20mg·L-1范围内的诺氟沙星，经过MW/Ni@GCC协同作用后降解率的变化展示在表4中。
表4诺氟沙星初始浓度对降解效果的影响
由表4可见，随着诺氟沙星初始浓度的增加，降解率逐渐降低。这是由于在催化剂用量及其他条相同的情况下，作用的活性位点是一定的，因此对于不同浓度的目标物，作用效果有所不同。综合考虑降解能力和效果，选择诺氟沙星溶液的初始浓度为10mg·L-1。
(五)微波功率的影响
微波协同降解过程的全部能量都是由微波辐射提供的，因此，不同微波功率提供的能量差异对于协同降解过程是至关重要的影响因素，考察微波功率与降解效率的关系如表5所示。向50mL浓度为10mg·L-1的诺氟沙星溶液中加入质量为60mg的Ni@GCC。如表5所示，微波功率为100W，300W，500W和700W，降解7min。
表5微波功率对诺氟沙星降解效果的影响
由表5可见，微波功率为100W，300W，500W和700W时，诺氟沙星的降解效率分别为83.38％，91.5％，93.8％和97.4％。这是因为更高的微波功率能够提供更大的能量，使Ni@GCC产生更多的活性粒子。优选微波功率为700W。
(六)干扰离子的影响
实际废水样品的成分复杂，许多无机离子可能会对催化降解反应带来干扰。因此，本实验考察了NO3 -，CH3COO-，SO4 2-，CO3 2-，PO4 3-等常见的干扰离子存在下的降解效率。结果如表6。
表6干扰离子对诺氟沙星降解效果的影响
由表6可见，无机离子对于MW/Ni@GCC协同催化降解诺氟沙星的反应无明显干扰，证明该催化剂应用范围广泛，可直接投入到实际有机污染废水中，这大大简化了应用中的操作过程，提高工作效率。
(七)Ni@GCC的重复利用和循环稳定性
在实际应用中，出于环保节能以及成本等因素，理想的催化剂应该是方便回收并且拥有很好的可重复利用性能，因此，对于Ni@GCC的循环利用和稳定性进行了研究。使用后的Ni@GCC，通过磁性分离，能够高效简洁快速的进行回收，仅仅需要再次通过N2保护下700℃处理后便可直接用于下一次实验。
表7Ni@GCC的循环利用
如表7所示，经五次重复使用后，诺氟沙星降解效率丝毫没有降低，与新制的催化剂具有同样出色的催化性能，仍然可达96％以上，证明了该催化剂可循环利用的特性。Ni@GCC易于回收，可重复使用，催化降解效率仍然可靠，大大控制了成本，在实际生产应用中突显优势。
为了进一步证明其稳定性，将五次循环后的Ni@GCC回收，用FTIR和XRD测定回收的Ni@GCC。由图6可知，循环前后Ni@GCC的FTIR谱图没有明显变化，表明其结构没有明显变化。图7表明，使用前后Ni@GCC在44.88°,52.16°和76.63°的Ni特征峰没有明显变化，没有NiO的特征峰的出现，再一次证明了其结构稳定性。
(八)降解动力学研究
降解过程符合一级动力学方程，速率常数k＝0.415min-1。通过自由基捕获实验，推断出Ni@GCC微波协同催化降解产生的活性物质主要是空穴，超氧自由基和羟基自由基，并通过局域表面等离子体共振理论进行进一步阐释。
为了更好的研究催化降解反应，探究了MW/Ni@GCC协同催化降解诺氟沙星的反应动力学。将实验数据根据Langmuir-Hinshelwood模型进行拟合，公式如下，并以-ln(C/C0)对t做图，结果表明该降解过程符合一级动力学方程，速率常数k＝0.415min-1。
根据自由基捕获理论来探究MW/Ni@GCC协同催化降解的机理，从微观角度解析反应过程，故考察了典型活性粒子(空穴h+，超氧自由基·O2 -，羟基自由基·OH)的作用机制。实验中加入三乙醇胺(TEOA，0.1wt％)作为h+捕获剂，通过泵入空气作为·O2 -捕获剂，碳酸氢钠(NaHCO3，0.1wt％)作为·OH捕获剂。经检测，TEOA十分明显的抑制了诺氟沙星的降解，降解率由原来的90.0％(选择降解时间为3min作为参照)减少为27.3％，这说明空穴在反应过程中是作用最大的活性粒子；NaHCO3使降解率减低至79.5％，虽然不及空穴作用明显，但也足以证明羟基自由基也是反映中的活性粒子；当向溶液中泵入空气后，增加了反应中氧气的接触量，提供了更多的超氧自由基，因此降解率增大到96.6％，同时也证明了超氧自由基是催化降解的活性粒子；另外，加入硝酸银(AgNO3，10mM)作为电子(e-)捕获剂，也对降解效果有抑制作用，这可能是因为电子数量的减少导致超氧自由基的减少，从而使降解效率降低，印证了超氧自由基为催化降解的活性粒子。综上所述，h+为MW/Ni@GCC协同催化降解的主要活性粒子，另外还有·O2 -和·OH。
综合以上的研究结果，可以用图8来阐释Ni@GCC降解诺氟沙星的反应机理。首先由石墨碳产生热点效应，这会产生较高的温度从而大大提高催化作用。另外，局域表面等离子体共振是金属纳米结构特有的性质，并且Ni是典型的等离子体激元。当微波到达界面时，可沿着入射方向透过金属粒子一定深度，并在内部传播一定距离，有助于电子与空穴的分离，从而增加了金属纳米结构催化剂的能力。在此基础上，在MW/Ni@GCC的协同效应作用下，更加有助于电子与空穴的分离，从而使催化剂具有极其优越的催化性能。Ni纳米粒子分布于碳笼中，LSPR产生的热电子会迅速向附近的石墨碳传递，并立刻与电子受体结合形成·O2 -，从而进一步抑制电子与空穴的再次复合。与此同时，生成的·O2 -和保留的h+会与有机污染物反应，从而实现催化降解的整个过程。综上所述，局域表面等离子体共振理论可以阐释Ni@GCC催化降解诺氟沙星的机理。
Claims (4)
1.可磁回收的多孔Ni@GCC复合材料在降解有机污染物中的应用，其特征在于，所述有机污染物是诺氟沙星，方法如下：于含有诺氟沙星的溶液中，加入可磁回收的多孔Ni@GCC复合材料，微波协同诱导催化降解；所述可磁回收的多孔Ni@GCC复合材料的制备方法，包括如下步骤：将硝酸镍、均苯三甲酸和聚乙烯吡咯烷酮溶解于混合溶剂中，然后转移到反应釜中，在150 ℃下反应10 h，自然冷却至室温，乙醇洗涤，干燥，得Ni-MOF前驱体粉末；将所得Ni-MOF前驱体粉末置于管式炉中，在氮气保护下700 ℃煅烧3 h，得到可磁回收的多孔Ni@GCC复合材料；所述的混合溶剂为，按体积比，乙醇:水:DMF=1:1:1。
2.根据权利要求1所述的应用，其特征在于，所述可磁回收的多孔Ni@GCC复合材料为球形，BET比表面积为110～130 m2·g-1，孔径大小为12～15nm，饱和磁化量为33.71～37.8emu·g−1。
3.根据权利要求1所述的应用，其特征在于，方法如下：调节诺氟沙星的初始浓度为5mg·L-1～20 mg·L-1，加入可磁回收的多孔Ni@GCC复合材料，在微波功率100～700 W下催化降解3～7min；每50 mL初始浓度为5 mg·L-1～20 mg·L-1的诺氟沙星的溶液中，加入20～80mg可磁回收的多孔Ni@GCC复合材料。
4.根据权利要求3所述的应用，其特征在于，方法如下：调节诺氟沙星的初始浓度为10mg·L-1，加入60mg可磁回收的多孔Ni@GCC复合材料，在微波功率700 W下催化降解3～7min。