CN108801054A - A kind of bullet proof composite plating and preparation method thereof - Google Patents
A kind of bullet proof composite plating and preparation method thereof Download PDFInfo
- Publication number
- CN108801054A CN108801054A CN201810646661.XA CN201810646661A CN108801054A CN 108801054 A CN108801054 A CN 108801054A CN 201810646661 A CN201810646661 A CN 201810646661A CN 108801054 A CN108801054 A CN 108801054A
- Authority
- CN
- China
- Prior art keywords
- layer
- composite plating
- proof composite
- bullet proof
- unit fibers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of bullet proof composite plating and preparation method thereof, wherein bullet proof composite plating includes：Cellular board, nonwoven layer, several unit fibers layers and the articulamentum between unit fibers layer；Several unit fibers layers are stacked from top to bottom, adjacent unit fibers layer is mutually bonded by articulamentum, each unit fibrous layer passes through laminar manner compression moulding, any cell fibrous layer has several filaments unidirectionally arranged being mutually parallel, in two adjacent unit fibers layers, the filament of the filament and another unit fibers layer of one of unit fibers layer is arranged in a crossed manner, cellular board be compound in the unit fibers layer being stacked while on, nonwoven layer is compound on the another side of cellular board.The present invention has effectively absorbed the impact force generated when bullet impact, has reduced armour swayback, alleviated the discomfort thus brought by the way that cellular board is arranged.In addition, the present invention under the premise of meeting certain ballistic performance, also acts as the effect of loss of weight.
Description
Technical field
The present invention relates to shellproof technical field technical field more particularly to a kind of bullet proof composite platings and preparation method thereof.
Background technology
Armour can be applied in the ballistic resistant products such as bullet-proof vest, shield use as burster course.Existing armour exists
During use, when it receives impact, due to huge recoil force effect, certain impact can be still generated to human body.Therefore,
In view of the above-mentioned problems, it is necessary to propose further solution.
Invention content
The purpose of the present invention is to provide a kind of bullet proof composite platings and preparation method thereof, existing in the prior art to overcome
It is insufficient.
For achieving the above object, the present invention provides a kind of bullet proof composite plating comprising：If cellular board, nonwoven layer,
Dry unit fibers layer and the articulamentum between unit fibers layer；
Several unit fibers layers are stacked from top to bottom, and adjacent unit fibers layer is mutually bonded by articulamentum,
Each unit fibrous layer has several fibres unidirectionally arranged being mutually parallel by laminar manner compression moulding, any cell fibrous layer
Tie up silk, in adjacent two unit fibers layers, the fibre of the filament and another unit fibers layer of one of unit fibers layer
Tie up silk it is arranged in a crossed manner, the cellular board be compound in by adhesive the unit fibers layer being stacked while on, institute
Nonwoven layer is stated to be compound on the another side of the cellular board.
The improvement of bullet proof composite plating as the present invention, the unit fibers layer are polyethylene fiber layer or nonwoven phenolic aldehyde
Layer of cloth, the articulamentum are adhesive articulamentum.
The improvement of bullet proof composite plating as the present invention, the cellular board are PP cellular boards.
For achieving the above object, the present invention provides a kind of production method of bullet proof composite plating comprising following steps：
S1, offer are attached with the unit fibers layer of viscose glue thereon, and placement is laminated in multilevel-cell fiber from top to bottom；
S2, the multilevel-cell fiber for placing stacking are sent into press die, and set temperature is heated to；
S3, multilevel-cell fiber laminated into type is cooled to room temperature；
S4, pass through adhesive fixed cellular plate in the one side of multilevel-cell fiber laminated into type；
S5, the face composite non woven layer of cloth in cellular board.
The improvement of the production method of bullet proof composite plating as the present invention, in the step S2, in the multilayer that stacking is placed
Release film is placed above and below unit fibers respectively.
The improvement of the production method of bullet proof composite plating as the present invention, in the step S2, the set temperature is
120-135℃。
The improvement of the production method of bullet proof composite plating as the present invention in the step S2, passes through the side that multistage is laminated
Formula carries out lamination treatment to multilevel-cell fiber.
The improvement of the production method of bullet proof composite plating as the present invention, in multistage lamination, one section of solidifying pressure is 6Mpa,
Two sections of solidifying pressures are 10Mpa, and three sections of solidifying pressures are 16Mpa, and four sections of solidifying pressures are set as 16Mpa.
The improvement of the production method of bullet proof composite plating as the present invention, in multistage lamination, one section of hardening time is thermoelectricity
Even test temperature is from room temperature to 90 DEG C, and two sections of hardening times are 90 DEG C and are warming up to 90-128 DEG C, and three sections of hardening times are that heat preservation is protected
Pressure 3 hours, four sections of hardening times are to be cooled to room temperature the required time.
The improvement of the production method of bullet proof composite plating as the present invention, the cellular board are PP cellular boards.
Compared with prior art, the beneficial effects of the invention are as follows：The bullet proof composite plating of the present invention has by the way that cellular board is arranged
The impact force generated when bullet impact is absorbed to effect, reduces armour swayback, alleviates the discomfort thus brought.This
Outside, bullet proof composite plating of the invention also acts as the effect of loss of weight under the premise of meeting certain ballistic performance.
Description of the drawings
In order to more clearly explain the embodiment of the invention or the technical proposal in the existing technology, to embodiment or will show below
There is attached drawing needed in technology description to be briefly described, it should be apparent that, the accompanying drawings in the following description is only this
Some embodiments described in invention, for those of ordinary skill in the art, without creative efforts,
Other drawings may also be obtained based on these drawings.
Fig. 1 is the schematic diagram of a layer structure of one specific implementation mode of bullet proof composite plating of the present invention；
Fig. 2 is the vertical view of the adjacent two unit fibers layers being stacked together.
Specific implementation mode
The present invention is described in detail for each embodiment shown in below in conjunction with the accompanying drawings, but it should explanation, these
Embodiment is not limitation of the present invention, those of ordinary skill in the art according to function, method made by these embodiments,
Or the equivalent transformation in structure or replacement, all belong to the scope of protection of the present invention within.
As shown in Figure 1, 2, bullet proof composite plating of the invention includes：Cellular board 1, nonwoven layer 2, several unit fibers layers 3
And the articulamentum between unit fibers layer 3.Wherein, the unit fibers layer 3 is polyethylene fiber layer or nonwoven phenol
Aldehyde layer of cloth.The articulamentum is adhesive articulamentum.
Several unit fibers layers 3 are stacked from top to bottom, and adjacent unit fibers layer 3 is mutually glued by articulamentum
It connects, each unit fibrous layer 3 has several unidirectional rows being mutually parallel by laminar manner compression moulding, any cell fibrous layer 3
The filament of cloth, in adjacent two unit fibers layers 3, the filament and another unit of one of unit fibers layer 3 are fine
The filament for tieing up layer 3 is arranged in a crossed manner.Preferably, in two adjacent unit fibers layers 3, the filametntary angle of intersection is 90 °.
So set, it makes the bullet proof composite plating of the present invention have preferable ballistic performance.
The cellular board 1 be compound in by adhesive the unit fibers layer 3 being stacked while on, the nothing
Woven fabric layer 2 is compound on the another side of the cellular board 1.To by the way that cellular board 1 is arranged, effectively absorb bullet impact
When the impact force that generates, reduce armour swayback, alleviate the discomfort thus brought.In addition, certain anti-meeting
Under the premise of elastic energy, the effect of loss of weight is also acted as.Preferably, the cellular board 1 is PP cellular boards.
Based on bullet proof composite plating as described above, the present invention also provides a kind of production methods of bullet proof composite plating comprising
Following steps：
S1, offer are attached with the unit fibers layer of viscose glue thereon, and placement is laminated in multilevel-cell fiber from top to bottom；
S2, the multilevel-cell fiber for placing stacking are sent into press die, and set temperature is heated to；
S3, multilevel-cell fiber laminated into type is cooled to room temperature；
S4, pass through adhesive fixed cellular plate in the one side of multilevel-cell fiber laminated into type；
S5, the face composite non woven layer of cloth in cellular board.
With reference to embodiment specifically, the production method of the bullet proof composite plating of the present invention is illustrated.
Embodiment 1
The polyethylene fiber layer for being attached with hot-setting adhesive thereon is provided, placement is laminated in multilaminar polyethylene fiber from top to bottom.
The hot-setting adhesive is phenolic hot-setting adhesive.
Release film is placed respectively above and below the multilaminar polyethylene fiber that stacking is placed, and the surrounding of release film is led to
Fluid sealant bonding is crossed, multilaminar polyethylene fiber is sent into mold, set temperature is heated to.The set temperature is 132
℃。
Lamination treatment is carried out to multilaminar polyethylene fiber by way of four sections of laminations, wherein one section of solidifying pressure is
6Mpa, two sections of solidifying pressures are 10Mpa, and three sections of solidifying pressures are 16Mpa, and four sections of solidifying pressures are set as 16Mpa.When one section of solidification
Between be thermocouple assay temperature from room temperature to 90 DEG C, two sections of hardening times are 90 DEG C and are warming up to 100 DEG C, and three sections of hardening times are to protect
Warm pressurize 3 hours, four sections of hardening times are to be cooled to room temperature the required time.Multilaminar polyethylene fibrous layer laminated into type is cold
But to room temperature.
PP cellular boards are fixed by hot-setting adhesive in the one side of multilaminar polyethylene fiber laminated into type, the one of PP cellular boards
Nonwoven layer is fixed in face by hot-setting adhesive.
Embodiment 2
The nonwoven phenolic aldehyde layer of cloth for being attached with hot-setting adhesive thereon is provided, multilayer nonwoven phenolic aldehyde layer of cloth is laminated from top to bottom and is put
It sets.The hot-setting adhesive is phenolic hot-setting adhesive.
Release film is placed respectively above and below the multilayer nonwoven phenolic aldehyde layer of cloth that stacking is placed, by the surrounding of release film
By sealing glue sticking, multilayer nonwoven phenolic aldehyde layer of cloth is sent into mold, set temperature is heated to.The set temperature is
135℃。
Lamination treatment is carried out to multilayer nonwoven phenolic aldehyde layer of cloth by way of four sections of laminations, wherein one section of solidifying pressure is
6Mpa, two sections of solidifying pressures are 10Mpa, and three sections of solidifying pressures are 16Mpa, and four sections of solidifying pressures are set as 16Mpa.When one section of solidification
Between be thermocouple assay temperature from room temperature to 90 DEG C, two sections of hardening times are 90 DEG C and are warming up to 128 DEG C, and three sections of hardening times are to protect
Warm pressurize 3 hours, four sections of hardening times are to be cooled to room temperature the required time.Multilayer nonwoven phenolic aldehyde layer of cloth laminated into type is cold
But to room temperature.
PP cellular boards are fixed by hot-setting adhesive in the one side of multilayer nonwoven phenolic aldehyde layer of cloth laminated into type, in PP cellular boards
Nonwoven layer is fixed by hot-setting adhesive on one side.
In conclusion the bullet proof composite plating of the present invention is generated by the way that cellular board is arranged when having effectively absorbed bullet impact
Impact force, reduce armour swayback, alleviate the discomfort thus brought.In addition, the bullet proof composite plating of the present invention exists
Under the premise of meeting certain ballistic performance, the effect of loss of weight is also acted as.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Profit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent requirements of the claims
Variation is included within the present invention.Any reference signs in the claims should not be construed as limiting the involved claims.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiment being appreciated that.
Claims (10)
1. a kind of bullet proof composite plating, which is characterized in that the bullet proof composite plating includes：Cellular board, nonwoven layer, several units are fine
Tie up layer and the articulamentum between unit fibers layer；
Several unit fibers layers are stacked from top to bottom, and adjacent unit fibers layer is mutually bonded by articulamentum, each list
First fibrous layer has several fibers unidirectionally arranged being mutually parallel by laminar manner compression moulding, any cell fibrous layer
Thread, in adjacent two unit fibers layers, the fiber of the filament and another unit fibers layer of one of unit fibers layer
Silk it is arranged in a crossed manner, the cellular board be compound in by adhesive the unit fibers layer being stacked while on, it is described
Nonwoven layer is compound on the another side of the cellular board.
2. bullet proof composite plating according to claim 1, which is characterized in that the unit fibers layer be polyethylene fiber layer or
Person's nonwoven phenolic aldehyde layer of cloth, the articulamentum are adhesive articulamentum.
3. bullet proof composite plating according to claim 1, which is characterized in that the cellular board is PP cellular boards.
4. a kind of production method of bullet proof composite plating, which is characterized in that the production method includes the following steps：
S1, offer are attached with the unit fibers layer of viscose glue thereon, and placement is laminated in multilevel-cell fiber from top to bottom；
S2, the multilevel-cell fiber for placing stacking are sent into press die, and set temperature is heated to；
S3, multilevel-cell fiber laminated into type is cooled to room temperature；
S4, pass through adhesive fixed cellular plate in the one side of multilevel-cell fiber laminated into type；
S5, the face composite non woven layer of cloth in cellular board.
5. the production method of bullet proof composite plating according to claim 4, which is characterized in that in the step S2, be laminated
Release film is placed respectively above and below the multilevel-cell fiber of placement.
6. the production method of bullet proof composite plating according to claim 4, which is characterized in that described to set in the step S2
Constant temperature degree is 120-135 DEG C.
7. the production method of bullet proof composite plating according to claim 4, which is characterized in that in the step S2, by more
The mode of section lamination carries out lamination treatment to multilevel-cell fiber.
8. the production method of bullet proof composite plating according to claim 7, which is characterized in that in multistage lamination, one section of solidification
Pressure is 6Mpa, and two sections of solidifying pressures are 10Mpa, and three sections of solidifying pressures are 16Mpa, and four sections of solidifying pressures are set as 16Mpa.
9. the production method of bullet proof composite plating according to claim 8, which is characterized in that in multistage lamination, one section of solidification
Time is thermocouple assay temperature from room temperature to 90 DEG C, and two sections of hardening times are 90 DEG C and are warming up to 90-128 DEG C, when three sections of solidifications
Between for heat-insulation pressure keeping 3 hours, four sections of hardening times are to be cooled to room temperature the required time.
10. the production method of bullet proof composite plating according to claim 4, which is characterized in that the cellular board is PP honeycombs
Plate.