CN108759567A - A kind of environmental protection flame retardant armour and preparation method thereof - Google Patents
A kind of environmental protection flame retardant armour and preparation method thereof Download PDFInfo
- Publication number
- CN108759567A CN108759567A CN201810644814.7A CN201810644814A CN108759567A CN 108759567 A CN108759567 A CN 108759567A CN 201810644814 A CN201810644814 A CN 201810644814A CN 108759567 A CN108759567 A CN 108759567A
- Authority
- CN
- China
- Prior art keywords
- layer
- armour
- environmental protection
- unit fibers
- flame retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of environmental protection flame retardant armour and preparation method thereof, wherein environmental protection flame retardant armour includes：Flame-retardant layer, several unit fibers layers and the articulamentum between unit fibers layer；Several unit fibers layers are stacked from top to bottom, adjacent unit fibers layer is mutually bonded by articulamentum, each unit fibrous layer passes through laminar manner compression moulding, any cell fibrous layer has several filaments unidirectionally arranged being mutually parallel, in two adjacent unit fibers layers, the filament of the filament and another unit fibers layer of one of unit fibers layer is arranged in a crossed manner, flame-retardant layer is compound in the one side for the unit fibers layer being stacked, and flame-retardant layer is glass fiber resin layer or anti-stab coating cloth.The present invention not only enhances the ballistic performance of armour, but also armour is made to have both fire protecting performance, copes with complicated objective environment to be conducive to armour, facilitate the use of armour to a certain extent by the way that flame-retardant layer is arranged.
Description
Technical field
The present invention relates to shellproof technical field technical field more particularly to a kind of environmental protection flame retardant armour and its making sides
Method.
Background technology
Armour can be applied in the ballistic resistant products such as bullet-proof vest, shield use as burster course.Currently, bullet-proof vest,
The ballistic resistant products such as shield usually only have bulletproof function.However, due to the complexity of objective environment, when ballistic resistant products are on fire,
User can not then continue to hold the ballistic resistant products, affect the use of ballistic resistant products.Therefore, in view of the above-mentioned problems, it is necessary to
It is proposed further solution.
Invention content
The purpose of the present invention is to provide a kind of environmental protection flame retardant armours and preparation method thereof, are deposited in the prior art with overcoming
Deficiency.
For achieving the above object, the present invention provides a kind of environmental protection flame retardant armour comprising：Flame-retardant layer, Ruo Gandan
First fibrous layer and the articulamentum between unit fibers layer；
Several unit fibers layers are stacked from top to bottom, and adjacent unit fibers layer is mutually bonded by articulamentum,
Each unit fibrous layer has several fibres unidirectionally arranged being mutually parallel by laminar manner compression moulding, any cell fibrous layer
Tie up silk, in adjacent two unit fibers layers, the fibre of the filament and another unit fibers layer of one of unit fibers layer
Dimension silk is arranged in a crossed manner, and the flame-retardant layer is compound in the one side for the unit fibers layer being stacked, and the flame-retardant layer is glass fibers
Tie up resin layer or anti-stab coating cloth.
The improvement of environmental protection flame retardant armour as the present invention, the unit fibers layer are polyethylene fiber layer or aramid fiber
Ballistic fiber layer, the articulamentum are adhesive tie.
The improvement of environmental protection flame retardant armour as the present invention, in adjacent two unit fibers layers, the filament of intersection
Angle be 90 °.
For achieving the above object, the present invention provides a kind of production method of environmental protection flame retardant armour comprising as follows
Step：
S1, offer are attached with the unit fibers layer of viscose glue thereon, and placement is laminated in multilevel-cell fiber from top to bottom；
S2, the multilevel-cell fiber for placing stacking are sent into press die, and set temperature is heated to；
S3, multilevel-cell fiber laminated into type is cooled to room temperature；
S4, the one side fixation flame-retardant layer in multilevel-cell fiber laminated into type, the flame-retardant layer is glass fiber resin
Layer or anti-stab coating cloth.
The improvement of the production method of environmental protection flame retardant armour as the present invention in the step S2, is placed in stacking
Release film is placed respectively above and below multilevel-cell fiber.
The improvement of the production method of environmental protection flame retardant armour as the present invention, in the step S2, the set temperature
It is 120-135 DEG C.
The improvement of the production method of environmental protection flame retardant armour as the present invention in the step S2, is laminated by multistage
Mode to multilevel-cell fiber carry out lamination treatment.
The improvement of the production method of environmental protection flame retardant armour as the present invention, in multistage lamination, one section of solidifying pressure is
6Mpa, two sections of solidifying pressures are 10Mpa, and three sections of solidifying pressures are 16Mpa, and four sections of solidifying pressures are set as 16Mpa.
The improvement of the production method of environmental protection flame retardant armour as the present invention, in multistage lamination, one section of hardening time is
Thermocouple assay temperature is from room temperature to 90 DEG C, and two sections of hardening times are 90 DEG C and are warming up to 90-128 DEG C, and three sections of hardening times are to protect
Warm pressurize 3 hours, four sections of hardening times are to be cooled to room temperature the required time.
The improvement of the production method of environmental protection flame retardant armour as the present invention, the unit fibers layer are polyethylene fibre
Layer or aramid fiber ballistic fiber layer, the viscose glue are the glue that can make fiber strong bond.
Compared with prior art, the beneficial effects of the invention are as follows：The environmental protection flame retardant armour of the present invention is fire-retardant by being arranged
Layer not only enhances the ballistic performance of armour, but also armour is made to have both fire protecting performance to a certain extent, to advantageous
Complicated objective environment is coped in armour, facilitates the use of armour.
Description of the drawings
In order to more clearly explain the embodiment of the invention or the technical proposal in the existing technology, to embodiment or will show below
There is attached drawing needed in technology description to be briefly described, it should be apparent that, the accompanying drawings in the following description is only this
Some embodiments described in invention, for those of ordinary skill in the art, without creative efforts,
Other drawings may also be obtained based on these drawings.
Fig. 1 is the schematic diagram of a layer structure of one specific implementation mode of environmental protection flame retardant armour of the present invention；
Fig. 2 is the vertical view of the adjacent two unit fibers layers being stacked together.
Specific implementation mode
The present invention is described in detail for each embodiment shown in below in conjunction with the accompanying drawings, but it should explanation, these
Embodiment is not limitation of the present invention, those of ordinary skill in the art according to function, method made by these embodiments,
Or the equivalent transformation in structure or replacement, all belong to the scope of protection of the present invention within.
As shown in Figure 1, the environmental protection flame retardant armour of the present invention includes：Flame-retardant layer 1, several unit fibers layers 2 and it is located at
Articulamentum between unit fibers layer 2.The unit fibers layer 2 is polyethylene fiber layer or nonwoven phenolic aldehyde layer of cloth.
Several unit fibers layers 2 are stacked from top to bottom, and adjacent unit fibers layer 2 is mutually glued by articulamentum
It connects.Preferably, the articulamentum is thermosetting glue bonding layer.In addition, other viscose glues, which also may be selected, realizes the connection of each unit fibrous layer
It is fixed.
Each unit fibrous layer 2 has several lists being mutually parallel by laminar manner compression moulding, any cell fibrous layer 2
To the filament of arrangement, in adjacent two unit fibers layers 2, filament and another list of one of unit fibers layer 2
The filament of first fibrous layer 2 is arranged in a crossed manner.Preferably, in two adjacent unit fibers layers 2, the filametntary angle of intersection is
90°.So set, it makes the environmental protection flame retardant armour of the present invention have preferable ballistic performance.
The flame-retardant layer 1 is compound in the one side for the unit fibers layer 2 being stacked, and the flame-retardant layer 1 is glass fibre
Resin layer or anti-stab coating cloth.It is arranged such so that armour has both fire protecting performance, is coped with to be conducive to armour
Complicated objective environment, facilitates the use of armour.
Based on environmental protection flame retardant armour as described above, the present invention also provides a kind of making sides of environmental protection flame retardant armour
Method comprising following steps：
S1, offer are attached with the unit fibers layer of viscose glue thereon, and placement is laminated in multilevel-cell fiber from top to bottom；
S2, the multilevel-cell fiber for placing stacking are sent into press die, and set temperature is heated to；
S3, multilevel-cell fiber laminated into type is cooled to room temperature；
S4, the one side fixation flame-retardant layer in multilevel-cell fiber laminated into type, the flame-retardant layer is glass fiber resin
Layer or anti-stab coating cloth.
Preferably, the unit fibers layer is polyethylene fiber layer or aramid fiber ballistic fiber layer, and the viscose glue is can
Make the glue of fiber strong bond.
With reference to embodiment specifically, the production method of the environmental protection flame retardant armour of the present invention illustrate
It is bright.
Embodiment 1
The polyethylene fiber layer for being attached with hot-setting adhesive thereon is provided, placement is laminated in multilaminar polyethylene fiber from top to bottom.
The hot-setting adhesive is phenolic hot-setting adhesive.
Release film is placed respectively above and below the multilaminar polyethylene fiber that stacking is placed, and the surrounding of release film is led to
Fluid sealant bonding is crossed, multilaminar polyethylene fiber is sent into mold, set temperature is heated to.The set temperature is 132
℃。
Lamination treatment is carried out to multilaminar polyethylene fiber by way of four sections of laminations, wherein one section of solidifying pressure is
6Mpa, two sections of solidifying pressures are 10Mpa, and three sections of solidifying pressures are 16Mpa, and four sections of solidifying pressures are set as 16Mpa.When one section of solidification
Between be thermocouple assay temperature from room temperature to 90 DEG C, two sections of hardening times are 90 DEG C and are warming up to 90 DEG C, and three sections of hardening times are to protect
Warm pressurize 3 hours, four sections of hardening times are to be cooled to room temperature the required time.Multilaminar polyethylene fiber laminated into type is cooled down
To room temperature.
Glass fiber resin layer is fixed in the one side of multilaminar polyethylene fiber laminated into type.
Embodiment 2
The nonwoven phenolic aldehyde layer of cloth for being attached with hot-setting adhesive thereon is provided, multilayer nonwoven phenolic aldehyde layer of cloth is laminated from top to bottom and is put
It sets.The hot-setting adhesive is phenolic hot-setting adhesive.
Release film is placed respectively above and below the multilayer nonwoven phenolic aldehyde layer of cloth that stacking is placed, by the surrounding of release film
By sealing glue sticking, multilayer nonwoven phenolic aldehyde layer of cloth is sent into mold, set temperature is heated to.The set temperature is
135℃。
Lamination treatment is carried out to multilayer nonwoven phenolic aldehyde layer of cloth by way of four sections of laminations, wherein one section of solidifying pressure is
6Mpa, two sections of solidifying pressures are 10Mpa, and three sections of solidifying pressures are 16Mpa, and four sections of solidifying pressures are set as 16Mpa.When one section of solidification
Between be thermocouple assay temperature from room temperature to 90 DEG C, two sections of hardening times are 90 DEG C and are warming up to 128 DEG C, and three sections of hardening times are to protect
Warm pressurize 3 hours, four sections of hardening times are to be cooled to room temperature the required time.Multilayer nonwoven phenolic aldehyde layer of cloth laminated into type is cold
But to room temperature.
Anti-stab coating cloth is fixed in the one side of multilayer nonwoven phenolic aldehyde layer of cloth laminated into type.
In conclusion the environmental protection flame retardant armour of the present invention improves the thermosetting performance of environmental protection flame retardant armour, be conducive to
The production and processing of environmental protection flame retardant armour.In addition, the environmental protection flame retardant armour of the present invention is laminated by multilevel-cell fiber, often
For layer of non-woven fabric using the filament unidirectionally arranged, the fibrous layer of adjacent unit fibers layer is arranged in a crossed manner, makes the present invention
Environmental protection flame retardant armour have preferable ballistic performance.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Profit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent requirements of the claims
Variation is included within the present invention.Any reference signs in the claims should not be construed as limiting the involved claims.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiment being appreciated that.
Claims (10)
1. a kind of environmental protection flame retardant armour, which is characterized in that the environmental protection flame retardant armour includes：Flame-retardant layer, several units are fine
Tie up layer and the articulamentum between unit fibers layer；
Several unit fibers layers are stacked from top to bottom, and adjacent unit fibers layer is mutually bonded by articulamentum, each list
First fibrous layer has several fibers unidirectionally arranged being mutually parallel by laminar manner compression moulding, any cell fibrous layer
Thread, in adjacent two unit fibers layers, the fiber of the filament and another unit fibers layer of one of unit fibers layer
Silk is arranged in a crossed manner, and the flame-retardant layer is compound in the one side for the unit fibers layer being stacked, and the flame-retardant layer is glass fibre
Resin layer or anti-stab coating cloth.
2. environmental protection flame retardant armour according to claim 1, which is characterized in that the unit fibers layer is polyethylene fibre
Layer or aramid fiber ballistic fiber layer, the articulamentum are adhesive tie.
3. environmental protection flame retardant armour according to claim 1, which is characterized in that in two adjacent unit fibers layers, hand over
The filametntary angle of fork is 90 °.
4. a kind of production method of environmental protection flame retardant armour, which is characterized in that the production method includes the following steps：
S1, offer are attached with the unit fibers layer of viscose glue thereon, and placement is laminated in multilevel-cell fiber from top to bottom；
S2, the multilevel-cell fiber for placing stacking are sent into press die, and set temperature is heated to；
S3, multilevel-cell fiber laminated into type is cooled to room temperature；
S4, multilevel-cell fiber laminated into type one side fix flame-retardant layer, the flame-retardant layer be glass fiber resin layer or
The anti-stab coating cloth of person.
5. the production method of environmental protection flame retardant armour according to claim 4, which is characterized in that in the step S2,
It is laminated above and below the multilevel-cell fiber placed and places release film respectively.
6. the production method of environmental protection flame retardant armour according to claim 4, which is characterized in that in the step S2, institute
It is 120-135 DEG C to state set temperature.
7. the production method of environmental protection flame retardant armour according to claim 4, which is characterized in that in the step S2, lead to
The mode for crossing multistage lamination carries out lamination treatment to multilevel-cell fiber.
8. the production method of environmental protection flame retardant armour according to claim 7, which is characterized in that in multistage lamination, one section
Solidifying pressure is 6Mpa, and two sections of solidifying pressures are 10Mpa, and three sections of solidifying pressures are 16Mpa, and four sections of solidifying pressures are set as 16Mpa.
9. the production method of environmental protection flame retardant armour according to claim 8, which is characterized in that in multistage lamination, one section
Hardening time is thermocouple assay temperature from room temperature to 90 DEG C, and two sections of hardening times are 90 DEG C and are warming up to 90-128 DEG C, and three sections solid
The change time is heat-insulation pressure keeping 3 hours, and four sections of hardening times are to be cooled to room temperature the required time.
10. the production method of environmental protection flame retardant armour according to claim 4, which is characterized in that the unit fibers layer
For polyethylene fiber layer or aramid fiber ballistic fiber layer, the viscose glue is the glue that can make fiber strong bond.