CN108796722A - A kind of fire-retardant day wire production method - Google Patents
A kind of fire-retardant day wire production method Download PDFInfo
- Publication number
- CN108796722A CN108796722A CN201810703711.3A CN201810703711A CN108796722A CN 108796722 A CN108796722 A CN 108796722A CN 201810703711 A CN201810703711 A CN 201810703711A CN 108796722 A CN108796722 A CN 108796722A
- Authority
- CN
- China
- Prior art keywords
- yarn
- tencel
- retardant
- fire
- flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fire-retardant day wire production method of spinninging technical field, the production method of the fire-retardant tencel includes the following steps:S1, raw material selection:The raw material for selecting tencel yarn, linen thread and yarn and flame-retardant yarn to be made as tencel;S2, pre-treatment:Clear up the impurity of tencel yarn, linen thread and yarn and the attachment of flame-retardant yarn surface;S3, spinning:Tencel yarn, linen thread and yarn and flame-retardant yarn are spun into tencel blended yarn using ring spinner;S4 pads processing:It is placed into fermentation vat after tencel blended yarn finish after the completion of will be blended in step S3 is good, it is easy to operate, by selecting tencel yarn, linen thread and yarn and flame-retardant yarn to be used as the raw material of tencel making, ensure that fibrillation will not occur for tencel blended yarn, it is not easy to fluff so that fabric obtained will not fade, and there is good anti-flaming thermal-insulation effect, and by padding processing, drying, cleaning and cleaning again so that scribbled is with excellent flexibility and comfort.
Description
Technical field
The present invention relates to spinninging technical field, specially a kind of fire-retardant day wire production method.
Background technology
Tencel is a kind of cellulose fibre, using solvent spining technology, does by force slightly below terylene, but be apparently higher than general
Viscose rayon, it is wet to improve significantly than viscose glue by force, there is very high rigidity, good washing dimensional stability(Washing shrinkage
Only 2%), there is higher hygroscopicity, fiber cross section to be round or oval, gloss is graceful, and soft, drapability is good,
Elegant property is good, and Tencel fibers can decompose completely in soil, environmentally safe, no matter in the state of dry or wet, equal poles
Have toughness, in a wet state, it is the cellulose fibre that the first wet strength outclass cotton, a hundred percent natural material,
In addition the manufacturing process of environmental protection, allows life style, for this, to cater to the demand of modern consumer completely with conservation of nature environment, and
It is environmentally protective, it can be rated as the green fiber of 21 century, manufactured fabric has that feel is smooth, moisture absorption is ventilative and other effects, is high-grade
Clothes fabric, and the raising of the requirement with people to quality of the life, traditional tencel do not have the effect of heat-resistant fireproof
Fruit, for this purpose, it is proposed that a kind of fire-retardant day wire production method.
Invention content
The purpose of the present invention is to provide a kind of fire-retardant day wire production methods, to solve mentioned above in the background art ask
Topic.
To achieve the above object, the present invention provides the following technical solutions:A kind of fire-retardant day wire production method, the fire-retardant tencel
Production method include the following steps:
S1, raw material selection:The raw material for selecting tencel yarn, linen thread and yarn and flame-retardant yarn to be made as tencel, and component ratio
For tencel yarn:Linen thread and yarn:Flame-retardant yarn=4.5-5.5:0.7-1.4:2.5-3.5;
S2, pre-treatment:Clear up the impurity of tencel yarn, linen thread and yarn and the attachment of flame-retardant yarn surface;
S3, spinning:Tencel yarn, linen thread and yarn and flame-retardant yarn are spun into tencel blended yarn using ring spinner;
S4 pads processing:It is placed into fermentation vat after tencel blended yarn finish after the completion of will be blended in step S3 is good, by thing
First ready dressing liquid pours into fermentation vat, the dressing liquid in fermentation vat is carried out heat treatment so that temperature is controlled 65
Between DEG C -80 DEG C, tencel blended yarn is carried out to pad processing;
S5, drying:The tencel blended yarn that will pad that treated in step S4 is sent as in high temperature drying unit, adjustment drying dress
It sets, temperature rises to 80-90 DEG C, and drying operation is carried out to tencel blended yarn;
S6, cleaning:Will be cooling under the tencel blended yarn to room temperature after drying, tencel blended yarn after cooling is put into 40 DEG C
Clear water in clean;
S7, secondary drying:Scribbled after clear water is cleaned is placed again into high temperature drying unit and carries out secondary baking
Dry run, and temperature rises to 120 DEG C;
S8, it is cooling:Scribbled placement after secondary drying is cooled down at room temperature, obtains finished product.
Preferably, the flame-retardant yarn is by fire-retardant nylon fiber line, eyeball polyvinyl chloride fibre fiber line, fire resistant viscose acetal fibre line or fire-retardant
One kind in dacron thread is arbitrarily formed.
Preferably, the collagen solution that the dressing liquid in the step S4 is extracted using natural materials is base fluid, and concentration
For 20-25 parts of the collagen solution of 40-70g/l;100 parts of water;5-8 parts of polyether silicone oil;1-3 parts of lecithin;Glacial acetic acid 1-2
Part.
Preferably, the preparation method of the dressing liquid is:The collagen solution 20-25 of a concentration of 40-70g/l is taken respectively
Part, 90-100 parts of water, 5-8 parts of polyether silicone oil, 1-3 parts of lecithin and 1-2 parts of glacial acetic acid are spare, are poured into agitating device appropriate
The water of component, and suitable collagen solution, polyether silicone oil, lecithin and glacial acetic acid solution are poured into water successively, add
Heat is stirred operation to 45 DEG C, mixing time 20min, will under the dressing liquid to room temperature that be stirred cooling it is spare.
Preferably, fire-retardant tencel can also carry out it dying operation in making, and dual-active may be used after step S3
The reactive dye of property agent or more activating agents carry out dyeing processing to obtained tencel blended yarn.
Compared with prior art, the beneficial effects of the invention are as follows:The fire-retardant day wire production method, it is easy to operate, pass through choosing
The raw material for using tencel yarn, linen thread and yarn and flame-retardant yarn to be made as tencel, it is ensured that fibril will not occur for tencel blended yarn
Change, be not easy to fluff so that fabric obtained will not fade, and there is good anti-flaming thermal-insulation effect, and by padding
Processing, drying, cleaning and cleaning again so that scribbled has excellent flexibility and comfort.
Specific implementation mode
Below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described,
Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based in the present invention
Embodiment, every other embodiment obtained by those of ordinary skill in the art without making creative efforts, all
Belong to the scope of protection of the invention.
Embodiment 1
A kind of fire-retardant day wire production method, it is characterised in that:The production method of the fire-retardant tencel includes the following steps:
S1, raw material selection:The raw material for selecting tencel yarn, linen thread and yarn and flame-retardant yarn to be made as tencel, and component ratio
For tencel yarn:Linen thread and yarn:Flame-retardant yarn=4.5:0.7:2.5, the flame-retardant yarn is by fire-retardant nylon fiber line, eyeball polyvinyl chloride fibre
Fiber line, fire resistant viscose acetal fibre line or one kind in flame-resistant terylene silk are arbitrarily formed;
S2, pre-treatment:Clear up the impurity of tencel yarn, linen thread and yarn and the attachment of flame-retardant yarn surface;
S3, spinning:Tencel yarn, linen thread and yarn and flame-retardant yarn are spun into tencel blended yarn using ring spinner;
S4 pads processing:It is placed into fermentation vat after tencel blended yarn finish after the completion of will be blended in step S3 is good, by thing
First ready dressing liquid pours into fermentation vat, the dressing liquid in fermentation vat is carried out heat treatment so that temperature is controlled 65
Between DEG C, tencel blended yarn is carried out to pad processing, the collagen egg that the dressing liquid in the step S4 is extracted with natural materials
White solution is base fluid, and 20 parts of the collagen solution of a concentration of 40-70g/l;100 parts of water;5 parts of polyether silicone oil;Lecithin 1
Part;1 part of glacial acetic acid, the preparation method of the dressing liquid are:20 parts of collagen solution, the water of a concentration of 40-70g/l are taken respectively
1 part of 100 parts, 5 parts of polyether silicone oil, 1 part of lecithin and glacial acetic acid are spare, and the water of appropriate amount of components is poured into agitating device, and
Suitable collagen solution, polyether silicone oil, lecithin and glacial acetic acid solution are poured into water successively, 45 DEG C is heated to and is stirred
Operation is mixed, mixing time 20min is spare by cooling under the dressing liquid to room temperature being stirred;
S5, drying:The tencel blended yarn that will pad that treated in step S4 is sent as in high temperature drying unit, adjustment drying dress
It sets, temperature rises to 80 DEG C, and drying operation is carried out to tencel blended yarn;
S6, cleaning:Will be cooling under the tencel blended yarn to room temperature after drying, tencel blended yarn after cooling is put into 40 DEG C
Clear water in clean;
S7, secondary drying:Scribbled after clear water is cleaned is placed again into high temperature drying unit and carries out secondary baking
Dry run, and temperature rises to 120 DEG C;
S8, it is cooling:Scribbled placement after secondary drying is cooled down at room temperature, obtains finished product;
Fire-retardant tencel can also carry out it dying operation in making, and double activated agent or mostly active may be used after step S3
The reactive dye of agent carry out dyeing processing to obtained tencel blended yarn.
Embodiment 2
A kind of fire-retardant day wire production method, it is characterised in that:The production method of the fire-retardant tencel includes the following steps:
S1, raw material selection:The raw material for selecting tencel yarn, linen thread and yarn and flame-retardant yarn to be made as tencel, and component ratio
For tencel yarn:Linen thread and yarn:Flame-retardant yarn=5.5:1.4:3.5, the flame-retardant yarn is by fire-retardant nylon fiber line, eyeball polyvinyl chloride fibre
Fiber line, fire resistant viscose acetal fibre line or one kind in flame-resistant terylene silk are arbitrarily formed;
S2, pre-treatment:Clear up the impurity of tencel yarn, linen thread and yarn and the attachment of flame-retardant yarn surface;
S3, spinning:Tencel yarn, linen thread and yarn and flame-retardant yarn are spun into tencel blended yarn using ring spinner;
S4 pads processing:It is placed into fermentation vat after tencel blended yarn finish after the completion of will be blended in step S3 is good, by thing
First ready dressing liquid pours into fermentation vat, the dressing liquid in fermentation vat is carried out heat treatment so that temperature is controlled 80
Between DEG C, tencel blended yarn is carried out to pad processing, the collagen egg that the dressing liquid in the step S4 is extracted with natural materials
White solution is base fluid, and 25 parts of the collagen solution of a concentration of 40-70g/l;100 parts of water;8 parts of polyether silicone oil;Lecithin 3
Part;2 parts of glacial acetic acid, the preparation method of the dressing liquid are:25 parts of collagen solution, the water of a concentration of 40-70g/l are taken respectively
2 parts of 100 parts, 8 parts of polyether silicone oil, 3 parts of lecithin and glacial acetic acid are spare, and the water of appropriate amount of components is poured into agitating device, and
Suitable collagen solution, polyether silicone oil, lecithin and glacial acetic acid solution are poured into water successively, 45 DEG C is heated to and is stirred
Operation is mixed, mixing time 20min is spare by cooling under the dressing liquid to room temperature being stirred;
S5, drying:The tencel blended yarn that will pad that treated in step S4 is sent as in high temperature drying unit, adjustment drying dress
It sets, temperature rises to 90 DEG C, and drying operation is carried out to tencel blended yarn;
S6, cleaning:Will be cooling under the tencel blended yarn to room temperature after drying, tencel blended yarn after cooling is put into 40 DEG C
Clear water in clean;
S7, secondary drying:Scribbled after clear water is cleaned is placed again into high temperature drying unit and carries out secondary baking
Dry run, and temperature rises to 120 DEG C;
S8, it is cooling:Scribbled placement after secondary drying is cooled down at room temperature, obtains finished product;
Fire-retardant tencel can also carry out it dying operation in making, and double activated agent or mostly active may be used after step S3
The reactive dye of agent carry out dyeing processing to obtained tencel blended yarn.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (5)
1. a kind of fire-retardant day wire production method, it is characterised in that:The production method of the fire-retardant tencel includes the following steps:
S1, raw material selection:The raw material for selecting tencel yarn, linen thread and yarn and flame-retardant yarn to be made as tencel, and component ratio
For tencel yarn:Linen thread and yarn:Flame-retardant yarn=4.5-5.5:0.7-1.4:2.5-3.5;
S2, pre-treatment:Clear up the impurity of tencel yarn, linen thread and yarn and the attachment of flame-retardant yarn surface;
S3, spinning:Tencel yarn, linen thread and yarn and flame-retardant yarn are spun into tencel blended yarn using ring spinner;
S4 pads processing:It is placed into fermentation vat after tencel blended yarn finish after the completion of will be blended in step S3 is good, by thing
First ready dressing liquid pours into fermentation vat, the dressing liquid in fermentation vat is carried out heat treatment so that temperature is controlled 65
Between DEG C -80 DEG C, tencel blended yarn is carried out to pad processing;
S5, drying:The tencel blended yarn that will pad that treated in step S4 is sent as in high temperature drying unit, adjustment drying dress
It sets, temperature rises to 80-90 DEG C, and drying operation is carried out to tencel blended yarn;
S6, cleaning:Will be cooling under the tencel blended yarn to room temperature after drying, tencel blended yarn after cooling is put into 40 DEG C
Clear water in clean;
S7, secondary drying:Scribbled after clear water is cleaned is placed again into high temperature drying unit and carries out secondary baking
Dry run, and temperature rises to 120 DEG C;
S8, it is cooling:Scribbled placement after secondary drying is cooled down at room temperature, obtains finished product.
2. a kind of fire-retardant day wire production method according to claim 1, it is characterised in that:The flame-retardant yarn is by fire-retardant Buddhist nun
Imperial fiber line, eyeball polyvinyl chloride fibre fiber line, fire resistant viscose acetal fibre line or one kind in flame-resistant terylene silk are arbitrarily formed.
3. a kind of fire-retardant day wire production method according to claim 1, it is characterised in that:Dressing liquid in the step S4
Using the collagen solution of natural materials extraction as base fluid, and 20-25 parts of the collagen solution of a concentration of 40-70g/l;Water
100 parts;5-8 parts of polyether silicone oil;1-3 parts of lecithin;1-2 parts of glacial acetic acid.
4. a kind of fire-retardant day wire production method according to claim 1 and 3, it is characterised in that:The dressing liquid is produced
Method is:5-8 parts of 100 parts of 20-25 parts of collagen solution, water, polyether silicone oil, the lecithin of a concentration of 40-70g/l are taken respectively
1-3 parts and 1-2 parts of glacial acetic acid it is spare, pour into the water of appropriate amount of components into agitating device, and pour into successively into water suitable
Collagen solution, polyether silicone oil, lecithin and glacial acetic acid solution are heated to 45 DEG C and are stirred operation, and mixing time is
20min, cooling under the dressing liquid to room temperature being stirred is spare.
5. a kind of fire-retardant day wire production method according to claim 1, it is characterised in that:Fire-retardant tencel can be in making
To its into
Row dying operation, and the reactive dye of double activated agent or more activating agents may be used to obtained tencel after step S3
Scribbled carries out dyeing processing.