CN108795182A - A kind of Interior decorative paints capable of purifying air and preparation method thereof - Google Patents
A kind of Interior decorative paints capable of purifying air and preparation method thereof Download PDFInfo
- Publication number
- CN108795182A CN108795182A CN201810722190.6A CN201810722190A CN108795182A CN 108795182 A CN108795182 A CN 108795182A CN 201810722190 A CN201810722190 A CN 201810722190A CN 108795182 A CN108795182 A CN 108795182A
- Authority
- CN
- China
- Prior art keywords
- parts
- interior decorative
- purifying air
- decorative paints
- pretreatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of Interior decorative paints capable of purifying air, include the raw material of following parts by weight：32-38 parts of aqueous acrylic emulsion, 18-22 parts of linseed oil fatty acid, 18-22 parts of catalysis material of pretreatment volcano float stone doping, 6-10 parts of modification biological charcoal, 5-9 parts of dimethylbenzene, 2-6 parts of bamboo charcoal, 3-5 parts of nano phase ag_2 o, 3-5 parts of tourmaline powder, 1-3 parts of turpentine oil, 3-6 parts of rosin, 18-24 parts of deionized water.The object of the present invention is to provide a kind of Interior decorative paints capable of purifying air, the paint is good except aldehyde, bactericidal effect, has higher use value and good application prospect.
Description
Technical field
The present invention relates to interior paint technical fields, and in particular to a kind of Interior decorative paints and its system capable of purifying air
Preparation Method.
Background technology
Paint be thickness oil colour, it is inflammable in the case of not dry, it is not soluble in water, be slightly soluble in fat, dissolve in alcohol, aldehyde, ether,
Benzene, alkane are soluble in gasoline, kerosene, diesel oil, no matter paint kind or form, are all by film forming matter, subsidiary film forming matter
With three kinds of base substance compositions of auxiliary film forming matter, subsidiary film forming matter：Including various pigment, extender pigment, rust resisting pigment, face
Material provides color and covering power for paint film, improves the protective value and decorative effect of paint, oil can be improved in the pigment of good weatherability
The service life of paint, extender pigment can increase the thickness of paint film, and using itself sheet, the performance of acicular texture passes through face
The accumulation of material is folded multiple, forms the paint film of fish scale-shaped, improves the service life of paint film, improves water proofing property and rust-proof effect；Antirust face
Material prevents body surface by air, chemicals attack, metal surface is become rusty by itself physics and chemical anti-rust action
Erosion.
Existing Chinese patent literature（Publication number：CN105400244B）Disclose a kind of waterborne inorganic einc-rich primer and preparation
Method, wherein waterborne inorganic einc-rich primer, including first component and second component；The first component includes the raw material group of following parts by weight
At：60~95 parts of high mode aqueous inorganic zinc-rich coating resins, 1~20 part of water-compatible amino resin, 0.1~1 part of antifoaming agent；The second
Component includes the raw material composition of following parts by weight：40~90 parts of zinc powder, 10~60 parts of filler, 0.5~10 part of anti-settling agent, wherein filling out
Material is nano-calcination-kaolinite can greatly increase the anticorrosive property of paint film, while by nanometer by adding nano-calcination-kaolinite
Calcined kaolin participates in the fine and close paint film to be formed, and road paints under energy direct spraying, not will produce bubble and pin hole, which adopts
Raw material is mainly high mode aqueous inorganic zinc-rich coating resins, water-compatible amino resin, and raw material does not have purification air effect.
Chinese patent literature（Publication number：CN104327571B）Disclose a kind of wrinkle paint, it is characterised in that including with
The component of lower mass percent：60-65% acrylic resins, 20-25% amine resins, 8-10% acrylic acid, 3-4% enclosed type sulphur
Acid, 2-3% ammonium hydroxide and the anti-settling waxes of 1-2%, though the raw material environmental protection of the invention, except formaldehyde, bactericidal effect are poor.
Invention content
In view of the drawbacks of the prior art, the object of the present invention is to provide a kind of Interior decorative paints capable of purifying air, should
Paint is good except aldehyde, bactericidal effect, has higher use value and good application prospect.
The present invention solves technical problem and adopts the following technical scheme that：
The present invention provides a kind of Interior decorative paints capable of purifying air, include the raw material of following parts by weight：
32-38 parts of aqueous acrylic emulsion, 18-22 parts of linseed oil fatty acid, pretreatment volcano float stone doping catalysis material 18-
22 parts, 6-10 parts of modification biological charcoal, 5-9 parts of dimethylbenzene, 2-6 parts of bamboo charcoal, 3-5 parts of nano phase ag_2 o, 3-5 parts of tourmaline powder, pine
1-3 parts of fuel-economizing, 3-6 parts of rosin, 18-24 parts of deionized water.
Preferably, the Interior decorative paints capable of purifying air include the raw material of following parts by weight：
34-38 parts of aqueous acrylic emulsion, 20-22 parts of linseed oil fatty acid, pretreatment volcano float stone doping catalysis material 19-
22 parts, 8-10 parts of modification biological charcoal, 6-9 parts of dimethylbenzene, 3-6 parts of bamboo charcoal, 4-5 parts of nano phase ag_2 o, 4-5 parts of tourmaline powder, pine
2-3 parts of fuel-economizing, 4-6 parts of rosin, 20-24 parts of deionized water.
Preferably, the Interior decorative paints capable of purifying air include the raw material of following parts by weight：
35 parts of aqueous acrylic emulsion, 20 parts of catalysis material of pretreatment volcano float stone doping, is modified 20 parts of linseed oil fatty acid
8 parts of charcoal, 4 parts of bamboo charcoal, 4 parts of nano phase ag_2 o, 4 parts of tourmaline powder, 2 parts of turpentine oil, 4.5 parts of rosin, is gone 7 parts of dimethylbenzene
21 parts of ionized water.
Preferably, pretreatment volcano float stone doping catalysis material is pretreatment volcano float stone, nano-photo catalytic material
Material is according to weight ratio 5:1 is mixed.
Preferably, pretreatment volcano float stone is added to the water for volcano float stone and carries out ultrasonic disperse, disperses 6-
10min, it is 10-20% ferric chloride solutions that mass fraction, which is then added, is stirred 12-16min to get pretreatment volcano float stone.
Preferably, the nano-photocatalyst material is nano titanic oxide sol, cross-linked chitosan according to weight ratio
3:The mixture of 2 compositions.
Preferably, it is matrix that the cross-linked chitosan preparation method, which is chitosan acetic acid solution, and polyethoxy fatty alcohol is
Dispersant, glutaraldehyde as cross linker are crosslinked by lotion and are made.
Preferably, the modification biological charcoal preparation method is that charcoal reacts 1-2h in nitration mixture, is then re-fed into microwave
Expansion 35-45min is carried out in stove, expansion temperature is 225-235 DEG C.
Preferably, the nitration mixture is the concentrated sulfuric acid, concentrated nitric acid according to weight ratio 3:The mixture of 2 compositions.
The present invention also provides a kind of methods preparing Interior decorative paints capable of purifying air, include the following steps：
Step 1 weighs each component raw material as required；
Step 2 sequentially adds aqueous acrylic emulsion, linseed oil fatty acid, dimethylbenzene, turpentine oil, rosin, deionized water
In homogenizer, rotating speed 210-220r/min stirs 35-45min, and mixture A is made；
Step 3, by mixture A, modification biological charcoal, pretreatment volcano float stone doping catalysis material, bamboo charcoal, nano phase ag_2 o,
Tourmaline powder sequentially adds in high-speed mixer, be sufficiently stirred so that all material be uniformly mixed, mixing speed 750-850r/
Min, mixing time 1-2 hours to get the present invention Interior decorative paints capable of purifying air.
Compared with prior art, the present invention has following advantageous effect：
（1）Using aqueous acrylic emulsion, linseed oil fatty acid, dimethylbenzene, turpentine oil etc. as paint base, addition changes the present invention
Property charcoal, pretreatment volcano float stone doping catalysis material, bamboo charcoal, nano phase ag_2 o, tourmaline powder be formaldehyde absorbing, sterilization
Play respective action, formaldehyde absorbing, sterilization and other effects then can be improved in mutual associated between each raw material.
（2）Charcoal is bio-organic materials high temperature pyrolysis product under anaerobic environment, is commonly used for heavy metal absorbent, and
Modification biological charcoal is improved surface area by the present invention by enhancing its surface-active, then by expansion, then can effectively improve suction
The impurity such as attached formaldehyde, harmful substance.
（3）Volcano float stone have good weatherability, corrosion resistance is good, have it is wear-resistant, after iron chloride is handled, carry
High porosity, nano-photocatalyst material are the compound of nano titanic oxide sol, cross-linked chitosan composition, promote pretreatment fire
Dispersion of the mountain float stone in paint then improves formaldehyde adsorption effect, pre-processes volcano float stone dopen Nano photocatalysis material in addition
Material activity is strong, plays synergistic effect with sterilization materials such as nano silvers on dispersion base, then enhances antibacterial effect.
（4）3 purifying formaldehyde rate of the embodiment of the present invention is relative to comparative example 4, and purifying rate improves 45.9%, golden yellow grape
Coccus sterilizing rate improves 47.7%, is obtained from comparative example 1-3, pretreatment volcano float stone doping catalysis material, modification biological
Charcoal can PARA FORMALDEHYDE PRILLS(91,95) purifies, synergistic effect is played in staphylococcus aureus sterilization.
Specific implementation mode
With reference to specific embodiment, technical scheme in the embodiment of the invention is clearly and completely described, shows
So, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based on the reality in the present invention
Example is applied, every other embodiment obtained by those of ordinary skill in the art without making creative efforts all belongs to
In the scope of protection of the invention.
Embodiment 1.
A kind of Interior decorative paints capable of purifying air of the present embodiment, include the raw material of following parts by weight：
32 parts of aqueous acrylic emulsion, 18 parts of catalysis material of pretreatment volcano float stone doping, is modified 18 parts of linseed oil fatty acid
6 parts of charcoal, 5 parts of dimethylbenzene, 2 parts of bamboo charcoal, 3 parts of nano phase ag_2 o, 3 parts of tourmaline powder, 1 part of turpentine oil, 3 parts of rosin, go from
18 parts of sub- water.
The pretreatment volcano float stone doping catalysis material of the present embodiment is pretreatment volcano float stone, nano-photocatalyst material
According to weight ratio 5:1 is mixed.
The pretreatment volcano float stone of the present embodiment is added to the water for volcano float stone and carries out ultrasonic disperse, disperses 6-10min,
It is 10% ferric chloride solution that mass fraction, which is then added, is stirred 12min to get pretreatment volcano float stone.
The nano-photocatalyst material of the present embodiment is nano titanic oxide sol, cross-linked chitosan according to weight ratio 3:2 groups
At mixture.
The cross-linked chitosan preparation method of the present embodiment is that chitosan acetic acid solution is matrix, and polyethoxy fatty alcohol is point
Powder, glutaraldehyde as cross linker are crosslinked by lotion and are made.
The modification biological charcoal preparation method of the present embodiment is that charcoal reacts 1h in nitration mixture, is then re-fed into micro-wave oven
Expansion 35min is carried out, expansion temperature is 225 DEG C.
The nitration mixture of the present embodiment is the concentrated sulfuric acid, concentrated nitric acid according to weight ratio 3:The mixture of 2 compositions.
A kind of method preparing Interior decorative paints capable of purifying air of the present embodiment, includes the following steps：
Step 1 weighs each component raw material as required；
Step 2 sequentially adds aqueous acrylic emulsion, linseed oil fatty acid, dimethylbenzene, turpentine oil, rosin, deionized water
In homogenizer, rotating speed 210r/min stirs 35min, and mixture A is made；
Step 3, by mixture A, modification biological charcoal, pretreatment volcano float stone doping catalysis material, bamboo charcoal, nano phase ag_2 o,
Tourmaline powder sequentially adds in high-speed mixer, is sufficiently stirred so that all material is uniformly mixed, mixing speed 750r/min is stirred
1 hour time is mixed to get the Interior decorative paints capable of purifying air of the present invention.
Embodiment 2.
A kind of Interior decorative paints capable of purifying air of the present embodiment, include the raw material of following parts by weight：
38 parts of aqueous acrylic emulsion, 22 parts of catalysis material of pretreatment volcano float stone doping, is modified 22 parts of linseed oil fatty acid
10 parts of charcoal, 9 parts of dimethylbenzene, 6 parts of bamboo charcoal, 5 parts of nano phase ag_2 o, 5 parts of tourmaline powder, 3 parts of turpentine oil, 6 parts of rosin, go from
24 parts of sub- water.
The pretreatment volcano float stone doping catalysis material of the present embodiment is pretreatment volcano float stone, nano-photocatalyst material
According to weight ratio 5:1 is mixed.
The pretreatment volcano float stone of the present embodiment is added to the water for volcano float stone and carries out ultrasonic disperse, disperses 10min, with
It is 20% ferric chloride solution that mass fraction is added afterwards, is stirred 16min to get pretreatment volcano float stone.
The nano-photocatalyst material of the present embodiment is nano titanic oxide sol, cross-linked chitosan according to weight ratio 3:2 groups
At mixture.
The cross-linked chitosan preparation method of the present embodiment is that chitosan acetic acid solution is matrix, and polyethoxy fatty alcohol is point
Powder, glutaraldehyde as cross linker are crosslinked by lotion and are made.
The modification biological charcoal preparation method of the present embodiment is that charcoal reacts 2h in nitration mixture, is then re-fed into micro-wave oven
Expansion 45min is carried out, expansion temperature is 235 DEG C.
The nitration mixture of the present embodiment is the concentrated sulfuric acid, concentrated nitric acid according to weight ratio 3:The mixture of 2 compositions.
A kind of method preparing Interior decorative paints capable of purifying air of the present embodiment, includes the following steps：
Step 1 weighs each component raw material as required；
Step 2 sequentially adds aqueous acrylic emulsion, linseed oil fatty acid, dimethylbenzene, turpentine oil, rosin, deionized water
In homogenizer, rotating speed 220r/min stirs 45min, and mixture A is made；
Step 3, by mixture A, modification biological charcoal, pretreatment volcano float stone doping catalysis material, bamboo charcoal, nano phase ag_2 o,
Tourmaline powder sequentially adds in high-speed mixer, is sufficiently stirred so that all material is uniformly mixed, mixing speed 850r/min is stirred
Time 2 h is mixed to get the Interior decorative paints capable of purifying air of the present invention.
Embodiment 3.
A kind of Interior decorative paints capable of purifying air of the present embodiment, include the raw material of following parts by weight：
35 parts of aqueous acrylic emulsion, 20 parts of catalysis material of pretreatment volcano float stone doping, is modified 20 parts of linseed oil fatty acid
8 parts of charcoal, 4 parts of bamboo charcoal, 4 parts of nano phase ag_2 o, 4 parts of tourmaline powder, 2 parts of turpentine oil, 4.5 parts of rosin, is gone 7 parts of dimethylbenzene
21 parts of ionized water.
The pretreatment volcano float stone doping catalysis material of the present embodiment is pretreatment volcano float stone, nano-photocatalyst material
According to weight ratio 5:1 is mixed.
The pretreatment volcano float stone of the present embodiment is added to the water for volcano float stone and carries out ultrasonic disperse, divides 8min, then
Addition mass fraction is 15% ferric chloride solution, is stirred 14min to get pretreatment volcano float stone.
The nano-photocatalyst material of the present embodiment is nano titanic oxide sol, cross-linked chitosan according to weight ratio 3:2 groups
At mixture.
The cross-linked chitosan preparation method of the present embodiment is that chitosan acetic acid solution is matrix, and polyethoxy fatty alcohol is point
Powder, glutaraldehyde as cross linker are crosslinked by lotion and are made.
The modification biological charcoal preparation method of the present embodiment is that charcoal reacts 1.5h in nitration mixture, is then re-fed into micro-wave oven
In carry out expansion 40min, expansion temperature is 230 DEG C.
The nitration mixture of the present embodiment is the concentrated sulfuric acid, concentrated nitric acid according to weight ratio 3:The mixture of 2 compositions.
A kind of method preparing Interior decorative paints capable of purifying air of the present embodiment, includes the following steps：
Step 1 weighs each component raw material as required；
Step 2 sequentially adds aqueous acrylic emulsion, linseed oil fatty acid, dimethylbenzene, turpentine oil, rosin, deionized water
In homogenizer, rotating speed 215r/min stirs 40min, and mixture A is made；
Step 3, by mixture A, modification biological charcoal, pretreatment volcano float stone doping catalysis material, bamboo charcoal, nano phase ag_2 o,
Tourmaline powder sequentially adds in high-speed mixer, is sufficiently stirred so that all material is uniformly mixed, mixing speed 800r/min is stirred
1.5 hours time is mixed to get the Interior decorative paints capable of purifying air of the present invention.
Comparative example 1.
It is essentially identical with the material and preparation process of embodiment 3, it has only the difference is that being not added with pretreatment volcano float stone doping light
Catalysis material.
Comparative example 2.
It is essentially identical with the material and preparation process of embodiment 3, it has only the difference is that being not added with modification biological charcoal.
Comparative example 3.
It is essentially identical with the material and preparation process of embodiment 3, it has only the difference is that being not added with pretreatment volcano float stone doping light
Catalysis material, modification biological charcoal.
Comparative example 4.
Chinese patent literature（Publication number：CN105400244B）It discloses real in a kind of waterborne inorganic einc-rich primer and preparation method
Apply the raw material and method of example 1.
Embodiment 3 and comparative example 1-4 the performance test results are as follows
| Purifying formaldehyde rate（%） | Staphylococcus aureus sterilizing rate（%） | |
| Embodiment 3 | 67.2 | 99.4 |
| Comparative example 1 | 55.4 | 97.6 |
| Comparative example 2 | 61.7 | 98.8 |
| Comparative example 3 | 45.1 | 93.2 |
| Comparative example 4 | 21.3 | 51.7 |
3 purifying formaldehyde rate of the embodiment of the present invention is relative to comparative example 4, and purifying rate improves 45.9%, staphylococcus aureus sterilization
Rate improves 47.7%, is obtained from comparative example 1-3, and pretreatment volcano float stone doping catalysis material, modification biological charcoal can be right
Synergistic effect is played in purifying formaldehyde, staphylococcus aureus sterilization.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Profit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent requirements of the claims
Variation is included within the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiment being appreciated that.
Claims (10)
1. a kind of Interior decorative paints capable of purifying air, which is characterized in that include the raw material of following parts by weight：
32-38 parts of aqueous acrylic emulsion, 18-22 parts of linseed oil fatty acid, pretreatment volcano float stone doping catalysis material 18-
22 parts, 6-10 parts of modification biological charcoal, 5-9 parts of dimethylbenzene, 2-6 parts of bamboo charcoal, 3-5 parts of nano phase ag_2 o, 3-5 parts of tourmaline powder, pine
1-3 parts of fuel-economizing, 3-6 parts of rosin, 18-24 parts of deionized water.
2. a kind of Interior decorative paints capable of purifying air according to claim 1, which is characterized in that described to purify sky
The Interior decorative paints of gas include the raw material of following parts by weight：
34-38 parts of aqueous acrylic emulsion, 20-22 parts of linseed oil fatty acid, pretreatment volcano float stone doping catalysis material 19-
22 parts, 8-10 parts of modification biological charcoal, 6-9 parts of dimethylbenzene, 3-6 parts of bamboo charcoal, 4-5 parts of nano phase ag_2 o, 4-5 parts of tourmaline powder, pine
2-3 parts of fuel-economizing, 4-6 parts of rosin, 20-24 parts of deionized water.
3. a kind of Interior decorative paints capable of purifying air according to claim 2, which is characterized in that described to purify sky
The Interior decorative paints of gas include the raw material of following parts by weight：
35 parts of aqueous acrylic emulsion, 20 parts of catalysis material of pretreatment volcano float stone doping, is modified 20 parts of linseed oil fatty acid
8 parts of charcoal, 4 parts of bamboo charcoal, 4 parts of nano phase ag_2 o, 4 parts of tourmaline powder, 2 parts of turpentine oil, 4.5 parts of rosin, is gone 7 parts of dimethylbenzene
21 parts of ionized water.
4. a kind of Interior decorative paints capable of purifying air according to claim 1, which is characterized in that the pretreatment fire
Mountain float stone doping catalysis material is pretreatment volcano float stone, nano-photocatalyst material according to weight ratio 5:1 is mixed.
5. a kind of Interior decorative paints capable of purifying air according to claim 4, which is characterized in that the pretreatment fire
Mountain float stone is added to the water for volcano float stone and carries out ultrasonic disperse, disperses 6-10min, and mass fraction is then added as 10-20% chlorine
Change ferrous solution, is stirred 12-16min to get pretreatment volcano float stone.
6. a kind of Interior decorative paints capable of purifying air according to claim 4, which is characterized in that the nanometer
Catalysis material is nano titanic oxide sol, cross-linked chitosan according to weight ratio 3:The mixture of 2 compositions.
7. a kind of Interior decorative paints capable of purifying air according to claim 6, which is characterized in that the crosslinking shell is poly-
Sugared preparation method is that chitosan acetic acid solution is matrix, and polyethoxy fatty alcohol is dispersant, glutaraldehyde as cross linker, by breast
Liquid crosslinking is made.
8. a kind of Interior decorative paints capable of purifying air according to claim 1, which is characterized in that the modification biological
Charcoal preparation method is that charcoal reacts 1-2h in nitration mixture, is then re-fed into micro-wave oven and carries out expansion 35-45min, expansion temperature
Degree is 225-235 DEG C.
9. a kind of Interior decorative paints capable of purifying air according to claim 8, which is characterized in that described mixed
Acid is the concentrated sulfuric acid, concentrated nitric acid according to weight ratio 3:The mixture of 2 compositions.
10. a kind of method preparing Interior decorative paints capable of purifying air as claimed in claim 1 or 2, which is characterized in that
Include the following steps：
Step 1 weighs each component raw material as required；
Step 2 sequentially adds aqueous acrylic emulsion, linseed oil fatty acid, dimethylbenzene, turpentine oil, rosin, deionized water
In homogenizer, rotating speed 210-220r/min stirs 35-45min, and mixture A is made；
Step 3, by mixture A, modification biological charcoal, pretreatment volcano float stone doping catalysis material, bamboo charcoal, nano phase ag_2 o,
Tourmaline powder sequentially adds in high-speed mixer, be sufficiently stirred so that all material be uniformly mixed, mixing speed 750-850r/
Min, mixing time 1-2 hours to get the present invention Interior decorative paints capable of purifying air.