CN108794819A - 一种防水型变压器输油管用新型橡胶材料 - Google Patents

一种防水型变压器输油管用新型橡胶材料 Download PDF

Info

Publication number
CN108794819A
CN108794819A CN201810505586.5A CN201810505586A CN108794819A CN 108794819 A CN108794819 A CN 108794819A CN 201810505586 A CN201810505586 A CN 201810505586A CN 108794819 A CN108794819 A CN 108794819A
Authority
CN
China
Prior art keywords
parts
rubber
polyvinyl alcohol
filler
oil
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810505586.5A
Other languages
English (en)
Inventor
姜影洲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201810505586.5A priority Critical patent/CN108794819A/zh
Publication of CN108794819A publication Critical patent/CN108794819A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种防水型变压器输油管用新型橡胶材料，按照重量份有以下原料组成：锭子油7‑12份、顺丁橡胶8‑12份、聚乙烯醇0.3‑0.8份、天然橡胶20‑30份、顺丁橡胶13‑19份、茂金属乙烯‑已烯共聚物0.8‑1.8份、纳米二氧化钛0.2‑0.6份、聚烯烃弹性体0.4‑0.8份、丁基橡胶10‑20份、增塑剂10‑15份、黄原酸改性的氯丁橡胶13‑18份、三元乙丙橡胶12‑18份、聚苯乙烯磺酸0.1‑0.5份、端羧基丁腈橡胶16‑20份、交联剂12‑16份、填充补强料9‑16份、聚乙烯醇0.5‑0.8份、大豆油6‑15份、硫化促进剂5‑9份、防老剂2‑7份、硫化剂3‑7份、乙丙橡胶9‑15份、三烯丙基异氰脲酸酯0.3‑0.8份、硅酸钾钠0.3‑0.7份、氧化锌0.4‑1份、复配填充剂4‑8份、滑石粉6‑10份和三聚氰胺占0.2‑0.7份。本发明所述的一种橡胶材料具有良好的绝缘性能，且使用寿命较长等优点。

Description

一种防水型变压器输油管用新型橡胶材料
技术领域
本发明涉及变压器相关技术领域，尤其涉及一种防水型变压器输油管用新型橡胶材料。
背景技术
市场上传统的绝缘橡胶，以橡胶为主体材料，加入相关配合剂后所制成的，具有高弹性及良好的防水性，目前现有的绝缘橡胶，绝缘性能及耐候性能差，适用的温度范围比较小，不能得到广泛应用。
发明内容
本发明的目的是为了解决现有技术中存在的缺点，而提出的一种防水型变压器输油管用新型橡胶材料。
为了实现上述目的，本发明采用了如下技术方案：
一种防水型变压器输油管用新型橡胶材料，按照重量份有以下原料组成：锭子油7-12份、顺丁橡胶8-12份、聚乙烯醇0.3-0.8份、天然橡胶20-30份、顺丁橡胶13-19份、茂金属乙烯-已烯共聚物0.8-1.8份、纳米二氧化钛0.2-0.6份、聚烯烃弹性体0.4-0.8份、丁基橡胶10-20份、增塑剂10-15份、黄原酸改性的氯丁橡胶13-18份、三元乙丙橡胶12-18份、聚苯乙烯磺酸0.1-0.5份、端羧基丁腈橡胶16-20份、交联剂12-16份、填充补强料9-16份、聚乙烯醇0.5-0.8份、大豆油6-15份、硫化促进剂5-9份、防老剂2-7份、硫化剂3-7份、乙丙橡胶9-15份、三烯丙基异氰脲酸酯0.3-0.8份、硅酸钾钠0.3-0.7份、氧化锌0.4-1份、复配填充剂4-8份、滑石粉6-10份和三聚氰胺占0.2-0.7份。
上述的一种防水型变压器输油管用新型橡胶材料，按照重量份有以下原料组成：锭子油7-11份、顺丁橡胶8-11份、聚乙烯醇0.3-0.7份、天然橡胶20-29份、顺丁橡胶13-18份、茂金属乙烯-已烯共聚物0.8-1.7份、纳米二氧化钛0.2-0.5份、聚烯烃弹性体0.4-0.7份、丁基橡胶10-19份、增塑剂10-14份、黄原酸改性的氯丁橡胶13-17份、三元乙丙橡胶12-17份、聚苯乙烯磺酸0.1-0.4份、端羧基丁腈橡胶16-19份、交联剂12-15份、填充补强料9-15份、聚乙烯醇0.5-0.7份、大豆油6-14份、硫化促进剂5-8份、防老剂2-6份、硫化剂3-6份、乙丙橡胶9-14份、三烯丙基异氰脲酸酯0.3-0.7份、硅酸钾钠0.3-0.6份、氧化锌0.4-0.9份、复配填充剂4-7份、滑石粉6-9份和三聚氰胺占0.2-0.6份。
上述的一种防水型变压器输油管用新型橡胶材料，按照重量份有以下原料组成：锭子油8-11份、顺丁橡胶9-11份、聚乙烯醇0.4-0.7份、天然橡胶21-29份、顺丁橡胶14-18份、茂金属乙烯-已烯共聚物0.9-1.7份、纳米二氧化钛0.3-0.5份、聚烯烃弹性体0.5-0.7份、丁基橡胶11-19份、增塑剂11-14份、黄原酸改性的氯丁橡胶14-17份、三元乙丙橡胶13-17份、聚苯乙烯磺酸0.2-0.4份、端羧基丁腈橡胶17-19份、交联剂13-15份、填充补强料10-15份、聚乙烯醇0.6-0.7份、大豆油7-14份、硫化促进剂6-8份、防老剂3-6份、硫化剂4-6份、乙丙橡胶10-14份、三烯丙基异氰脲酸酯0.4-0.7份、硅酸钾钠0.4-0.6份、氧化锌0.5-0.9份、复配填充剂5-7份、滑石粉7-9份和三聚氰胺占0.3-0.6份。
上述的一种防水型变压器输油管用新型橡胶材料，按照重量份有以下原料组成：锭子油9.5份、顺丁橡胶10份、聚乙烯醇0.55份、天然橡胶25份、顺丁橡胶16份、茂金属乙烯-已烯共聚物1.3份、纳米二氧化钛0.4份、聚烯烃弹性体0.6份、丁基橡胶15份、增塑剂12.5份、黄原酸改性的氯丁橡胶15.5份、三元乙丙橡胶15份、聚苯乙烯磺酸0.3份、端羧基丁腈橡胶18份、交联剂14份、填充补强料12.5份、聚乙烯醇0.65份、大豆油10.5份、硫化促进剂7份、防老剂4.5份、硫化剂5份、乙丙橡胶12份、三烯丙基异氰脲酸酯0.55份、硅酸钾钠0.5份、氧化锌0.7份、复配填充剂6份、滑石粉8份和三聚氰胺占0.45份。
与现有技术相比，本发明的有益效果为：
本发明的一种防水型变压器输油管用新型橡胶材料与传统橡胶相比，具有良好的绝缘性能且耐候性好，在空气中不易老化分解，使用范围广，大大增加了使用寿命；另，具有良好的韧性和强度，适用于各种环境等优点；该橡胶生产工艺简单，材料易得，成本低廉。
具体实施方式
实施例1
一种防水型变压器输油管用新型橡胶材料，按照重量份有以下原料组成：锭子油7份、顺丁橡胶8份、聚乙烯醇0.3份、天然橡胶20份、顺丁橡胶13份、茂金属乙烯-已烯共聚物0.8份、纳米二氧化钛0.2份、聚烯烃弹性体0.4份、丁基橡胶10份、增塑剂10份、黄原酸改性的氯丁橡胶13份、三元乙丙橡胶12份、聚苯乙烯磺酸0.1份、端羧基丁腈橡胶16份、交联剂12份、填充补强料9份、聚乙烯醇0.5份、大豆油6份、硫化促进剂5份、防老剂2份、硫化剂3份、乙丙橡胶9份、三烯丙基异氰脲酸酯0.3份、硅酸钾钠0.3份、氧化锌0.4份、复配填充剂4份、滑石粉6份和三聚氰胺占0.2份。
实施例2
上述的一种防水型变压器输油管用新型橡胶材料，按照重量份有以下原料组成：锭子油12份、顺丁橡胶12份、聚乙烯醇0.8份、天然橡胶30份、顺丁橡胶19份、茂金属乙烯-已烯共聚物1.8份、纳米二氧化钛0.6份、聚烯烃弹性体0.8份、丁基橡胶20份、增塑剂15份、黄原酸改性的氯丁橡胶18份、三元乙丙橡胶18份、聚苯乙烯磺酸0.5份、端羧基丁腈橡胶20份、交联剂16份、填充补强料16份、聚乙烯醇0.8份、大豆油15份、硫化促进剂9份、防老剂7份、硫化剂7份、乙丙橡胶15份、三烯丙基异氰脲酸酯0.8份、硅酸钾钠0.7份、氧化锌1份、复配填充剂8份、滑石粉10份和三聚氰胺占0.7份。
实施例3
上述的一种防水型变压器输油管用新型橡胶材料，按照重量份有以下原料组成：锭子油9.5份、顺丁橡胶10份、聚乙烯醇0.55份、天然橡胶25份、顺丁橡胶16份、茂金属乙烯-已烯共聚物1.3份、纳米二氧化钛0.4份、聚烯烃弹性体0.6份、丁基橡胶15份、增塑剂12.5份、黄原酸改性的氯丁橡胶15.5份、三元乙丙橡胶15份、聚苯乙烯磺酸0.3份、端羧基丁腈橡胶18份、交联剂14份、填充补强料12.5份、聚乙烯醇0.65份、大豆油10.5份、硫化促进剂7份、防老剂4.5份、硫化剂5份、乙丙橡胶12份、三烯丙基异氰脲酸酯0.55份、硅酸钾钠0.5份、氧化锌0.7份、复配填充剂6份、滑石粉8份和三聚氰胺占0.45份。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。

Claims (4)

1.一种防水型变压器输油管用新型橡胶材料，其特征在于，按照重量份有以下原料组成：锭子油7-12份、顺丁橡胶8-12份、聚乙烯醇0.3-0.8份、天然橡胶20-30份、顺丁橡胶13-19份、茂金属乙烯-已烯共聚物0.8-1.8份、纳米二氧化钛0.2-0.6份、聚烯烃弹性体0.4-0.8份、丁基橡胶10-20份、增塑剂10-15份、黄原酸改性的氯丁橡胶13-18份、三元乙丙橡胶12-18份、聚苯乙烯磺酸0.1-0.5份、端羧基丁腈橡胶16-20份、交联剂12-16份、填充补强料9-16份、聚乙烯醇0.5-0.8份、大豆油6-15份、硫化促进剂5-9份、防老剂2-7份、硫化剂3-7份、乙丙橡胶9-15份、三烯丙基异氰脲酸酯0.3-0.8份、硅酸钾钠0.3-0.7份、氧化锌0.4-1份、复配填充剂4-8份、滑石粉6-10份和三聚氰胺占0.2-0.7份。
2.根据权利要求1所述的一种防水型变压器输油管用新型橡胶材料，其特征在于，按照重量份有以下原料组成：锭子油7-11份、顺丁橡胶8-11份、聚乙烯醇0.3-0.7份、天然橡胶20-29份、顺丁橡胶13-18份、茂金属乙烯-已烯共聚物0.8-1.7份、纳米二氧化钛0.2-0.5份、聚烯烃弹性体0.4-0.7份、丁基橡胶10-19份、增塑剂10-14份、黄原酸改性的氯丁橡胶13-17份、三元乙丙橡胶12-17份、聚苯乙烯磺酸0.1-0.4份、端羧基丁腈橡胶16-19份、交联剂12-15份、填充补强料9-15份、聚乙烯醇0.5-0.7份、大豆油6-14份、硫化促进剂5-8份、防老剂2-6份、硫化剂3-6份、乙丙橡胶9-14份、三烯丙基异氰脲酸酯0.3-0.7份、硅酸钾钠0.3-0.6份、氧化锌0.4-0.9份、复配填充剂4-7份、滑石粉6-9份和三聚氰胺占0.2-0.6份。
3.根据权利要求1所述的一种防水型变压器输油管用新型橡胶材料，其特征在于，按照重量份有以下原料组成：锭子油8-11份、顺丁橡胶9-11份、聚乙烯醇0.4-0.7份、天然橡胶21-29份、顺丁橡胶14-18份、茂金属乙烯-已烯共聚物0.9-1.7份、纳米二氧化钛0.3-0.5份、聚烯烃弹性体0.5-0.7份、丁基橡胶11-19份、增塑剂11-14份、黄原酸改性的氯丁橡胶14-17份、三元乙丙橡胶13-17份、聚苯乙烯磺酸0.2-0.4份、端羧基丁腈橡胶17-19份、交联剂13-15份、填充补强料10-15份、聚乙烯醇0.6-0.7份、大豆油7-14份、硫化促进剂6-8份、防老剂3-6份、硫化剂4-6份、乙丙橡胶10-14份、三烯丙基异氰脲酸酯0.4-0.7份、硅酸钾钠0.4-0.6份、氧化锌0.5-0.9份、复配填充剂5-7份、滑石粉7-9份和三聚氰胺占0.3-0.6份。
4.根据权利要求1所述的一种防水型变压器输油管用新型橡胶材料，其特征在于，按照重量份有以下原料组成：锭子油9.5份、顺丁橡胶10份、聚乙烯醇0.55份、天然橡胶25份、顺丁橡胶16份、茂金属乙烯-已烯共聚物1.3份、纳米二氧化钛0.4份、聚烯烃弹性体0.6份、丁基橡胶15份、增塑剂12.5份、黄原酸改性的氯丁橡胶15.5份、三元乙丙橡胶15份、聚苯乙烯磺酸0.3份、端羧基丁腈橡胶18份、交联剂14份、填充补强料12.5份、聚乙烯醇0.65份、大豆油10.5份、硫化促进剂7份、防老剂4.5份、硫化剂5份、乙丙橡胶12份、三烯丙基异氰脲酸酯0.55份、硅酸钾钠0.5份、氧化锌0.7份、复配填充剂6份、滑石粉8份和三聚氰胺占0.45份。
CN201810505586.5A 2018-05-24 2018-05-24 一种防水型变压器输油管用新型橡胶材料 Withdrawn CN108794819A (zh)