CN108793928A - A kind of environment protecting thermal insulating building coating and preparation method thereof - Google Patents
A kind of environment protecting thermal insulating building coating and preparation method thereof Download PDFInfo
- Publication number
- CN108793928A CN108793928A CN201710290824.0A CN201710290824A CN108793928A CN 108793928 A CN108793928 A CN 108793928A CN 201710290824 A CN201710290824 A CN 201710290824A CN 108793928 A CN108793928 A CN 108793928A
- Authority
- CN
- China
- Prior art keywords
- thermal insulating
- environment protecting
- insulating building
- building coating
- protecting thermal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environment protecting thermal insulating building coatings and preparation method thereof, it is characterised in that：Its composition of raw materials is：Asbestos wool 9~16%, PET Hollow fiber 2.5~4%, penetrant t X 0.16~0.25%, emulsifier（OP-10）0.03~0.05%, polyvinyl alcohol 0.15~0.5%, haydite（2.5mm following）0.5~1.5%, perlite 1~2.5%, porous konilite 8~22%, white carbon 2~5%, sodium metasilicate 0.7~1%, silicone emulsion 0.01%, water 76~47%.The present invention has the advantages that nontoxic, pollution-free, heat-proof quality is good, energy-saving effect is notable, corrosion-resistant, easy for construction.
Description
Technical field
The present invention relates to building material technical field more particularly to a kind of environment protecting thermal insulating building coating and its preparation sides
Method.
Background technology
Thermal insulation coatings are a kind of novel thermal insulation materials, and the one of heat-insulation and heat-preservation is realized by low thermal conductivity and high thermal resistance
Kind coating.The product adds chemical addition agent by high-quality natural mineral matter and high temperature stick enters mould, sizing, baking by slurrying
The techniques such as dry, finished product, packaging are fabricated.
The thermal insulation coatings of the prior art exist mostly toxic, pollution is big, heat-proof quality is poor, energy-saving effect is bad, it is perishable,
The inconvenient disadvantage of construction.
Invention content
In view of the drawbacks described above of the prior art, technical problem to be solved by the invention is to provide a kind of environment protecting thermal insulatings
Building coating and preparation method thereof, with nontoxic, pollution-free, heat-proof quality is good, energy-saving effect is notable, corrosion-resistant, easy for construction
The advantages of.
To achieve the above object, the present invention provides a kind of environment protecting thermal insulating building coatings, it is characterised in that：Its raw material is matched
Fang Wei：Asbestos wool 9~16%, PET Hollow fiber 2.5~4%, penetrant t X 0.16~0.25%, emulsifier（OP-10）
0.03~0.05%, polyvinyl alcohol 0.15~0.5%, haydite（2.5mm following）0.5~1.5%, perlite 1~2.5% is more
Hole konilite 8~22%, white carbon 2~5%, sodium metasilicate 0.7~1%, silicone emulsion 0.01%, water 76~47%.
A kind of above-mentioned environment protecting thermal insulating building coating preparation method, it is characterised in that：Include the following steps：
（1）First half warm water is poured into reaction kettle, after adding asbestos wool, PET Hollow fiber and penetrant t X, is intermittently stirred
Mix 4h, mixing speed 120r/min；
（2）The other half warm water and emulsifier op-10 are added later, sequentially add polyvinyl alcohol, haydite, perlite, porous
Konilite, white carbon, sodium metasilicate continue to stir 1h, mixing speed 150r/min, silicone emulsion defoaming are eventually adding, through changing
Test blowing barrelling after qualification.
The beneficial effects of the invention are as follows：
The present invention has the advantages that nontoxic, pollution-free, heat-proof quality is good, energy-saving effect is notable, corrosion-resistant, easy for construction.
Specific implementation mode
A kind of environment protecting thermal insulating building coating, it is characterised in that：Its composition of raw materials is：Asbestos wool 9~16%, PET Hollow
Fiber 2.5~4%, penetrant t X 0.16~0.25%, emulsifier（OP-10）0.03~0.05%, polyvinyl alcohol 0.15~
0.5%, haydite（2.5mm following）0.5~1.5%, perlite 1~2.5%, porous konilite 8~22%, white carbon 2~
5%, sodium metasilicate 0.7~1%, silicone emulsion 0.01%, water 76~47%.
A kind of above-mentioned environment protecting thermal insulating building coating preparation method includes the following steps：
（1）First half warm water is poured into reaction kettle, after adding asbestos wool, PET Hollow fiber and penetrant t X, is intermittently stirred
Mix 4h, mixing speed 120r/min；
（2）The other half warm water and emulsifier op-10 are added later, sequentially add polyvinyl alcohol, haydite, perlite, porous
Konilite, white carbon, sodium metasilicate continue to stir 1h, mixing speed 150r/min, silicone emulsion defoaming are eventually adding, through changing
Test blowing barrelling after qualification.
The coating of the present invention is white or the sticky shape lotion of canescence, using under rear room temperature 10~solid is congealed into for 24 hours, to new
Wall is built directly to smear without jointing；Make insulating layer use, outer cover cement mortar protective course, the service life is identical as building；If
It uses on old room body, exterior coating need to be polished clean and then smears again.
Product characteristic：First, this product is non-toxic and tasteless corrosion-free, it is environmentally safe；Second is that heat insulation effect is better than benzene plate, apply
Work cost is less than the 30%~50% of benzene plate；Third, not aging, Keep away from rain leaching solarization and cold jelly, are not protected with wall and outer cover cement mortar
Sheath associativity is good, and service life is more than 30 years；Fourth, construction is simple, it is suitable for shaping with object in any beginning complicated interface,
And closure is good, intensity is high, flawless.
The preferred embodiment of the present invention has been described in detail above.It should be appreciated that those skilled in the art without
It needs creative work according to the present invention can conceive and makes many modifications and variations.Therefore, all technologies in the art
Personnel are available by logical analysis, reasoning, or a limited experiment on the basis of existing technology under this invention's idea
Technical solution, all should be in the protection domain being defined in the patent claims.
Claims (2)
1. a kind of environment protecting thermal insulating building coating, it is characterised in that：Its composition of raw materials is：Asbestos wool 9~16%, PET Hollow are fine
Dimension 2.5~4%, penetrant t X 0.16~0.25%, emulsifier（OP-10）0.03~0.05%, polyvinyl alcohol 0.15~
0.5%, haydite（2.5mm following）0.5~1.5%, perlite 1~2.5%, porous konilite 8~22%, white carbon 2~
5%, sodium metasilicate 0.7~1%, silicone emulsion 0.01%, water 76~47%.
2. a kind of a kind of environment protecting thermal insulating building coating preparation method as described in claim 1, it is characterised in that：Including following
Step：
First half warm water is poured into reaction kettle, after adding asbestos wool, PET Hollow fiber and penetrant t X, intermittent stirring
4h, mixing speed 120r/min；
The other half warm water and emulsifier op-10 are added later, sequentially add polyvinyl alcohol, haydite, perlite, periporate stone
English, white carbon, sodium metasilicate continue to stir 1h, mixing speed 150r/min, are eventually adding silicone emulsion defoaming, are closed through chemical examination
Blowing barrelling after lattice.