CN108793833A - A kind of environment-friendly sheet and its production method - Google Patents
A kind of environment-friendly sheet and its production method Download PDFInfo
- Publication number
- CN108793833A CN108793833A CN201810522192.0A CN201810522192A CN108793833A CN 108793833 A CN108793833 A CN 108793833A CN 201810522192 A CN201810522192 A CN 201810522192A CN 108793833 A CN108793833 A CN 108793833A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- auxiliary agent
- silica
- friendly sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of environment-friendly sheet of the present invention, according to parts by weight, raw material includes 10-15 parts of calcium carbonate, 20-40 parts of diatomite, 10-25 parts of flyash, 8-15 parts of silica, 8-16 parts of epoxy resin, 5-10 parts of fibrous material, 2-6 parts of carboxymethyl cellulose, 0.2-0.3 parts of lauryl sodium sulfate, 0.2-0.4 parts of coupling agent, 2-5 parts of auxiliary agent, the present invention have the performances such as heat preservation, fire prevention, and it is environmentally safe, it is harmless.
Description
Technical field
The present invention relates to a kind of planks, specifically, being related to a kind of environment-friendly sheet and its production method.
Background technology
With the development of society, building is more and more diversified, the requirement to construction material is also higher and higher, now, people
Increasingly focus on environmental protection, the requirement for whether belonging to environment-friendly materials of construction material is also increasingly paid close attention to.
Plank is a kind of important construction material, particularly for interior decoration field;With Ecology in China, green, environmental protection
The development of house necessarily promotes the sustainable development of environment-friendly building materials energy-saving material.Vast in territory, the climate difference in north and south in China
Greatly, general plank is difficult to meet the requirement of north-south climate difference.
Invention content
The present invention overcomes the disadvantages of the prior art, a kind of environment-friendly sheet and its production method is provided, to environment
It is pollution-free, it is harmless, and also good weatherability, property are stablized.
In order to solve the above-mentioned technical problem, the present invention is achieved by the following technical solutions:
A kind of environment-friendly sheet, according to parts by weight, raw material includes 10-15 parts of calcium carbonate, 20-40 parts of diatomite, flyash
10-25 parts, 8-15 parts of silica, 8-16 parts of epoxy resin, 5-10 parts of fibrous material, 2-6 parts of carboxymethyl cellulose, dodecane
0.2-0.3 parts of base sodium sulphate, 0.2-0.4 parts of coupling agent, 2-5 parts of auxiliary agent.
Further, the auxiliary agent includes 0.5-1 parts of mould inhibitor, 0.2~0.4 part of graphene, 0.5-1 parts of oleamide, stream
Flat auxiliary agent 0.5-1 parts;0.8-1.5 parts of thickening aids;0.5-1.5 parts of antifoam additives.
Further, according to parts by weight, raw material includes 12 parts of calcium carbonate, 25 parts of diatomite, 18 parts of flyash, silica
10 parts, 12 parts of epoxy resin, 8 parts of fibrous material, 4 parts of carboxymethyl cellulose, 0.25 part of lauryl sodium sulfate, coupling agent 0.3
Part, 4 parts of auxiliary agent, wherein the auxiliary agent includes 0.6 part of mould inhibitor, 0.3 part of graphene, 0.8 part of oleamide, leveling auxiliary agent 0.6
Part;1 part of thickening aids;0.7 part of antifoam additives.
Further, the fibrous material is wood-fibred, bamboo fibre or flaxen fiber.
A kind of production method of environment-friendly sheet, includes the following steps:
1) silica is by pretreatment;
2) calcium carbonate, diatomite, flyash, silica, epoxy resin are firstly added into dispersion cylinder by measuring requirement,
Fibrous material and carboxymethyl cellulose, then start dispersion machine, and rotating speed is maintained at 1500~2200r/min, then decelerates to 600
~800r/min sequentially adds mould inhibitor, graphene, oleamide, 1-2 parts of leveling auxiliary agent, antifoam additives under stirring, stirs
After mixing 5~10min, thickening aids being added, and carry out viscosity test, viscosity, which reaches, applies -4 glasss of 70~120s, finally, filtering,
Packaging.
Further, the silica includes by pretreatment:The silica dioxide granule, which is added to the water, to be stirred, water
In simultaneously lauryl sodium sulfate and coupling agent is added, persistently stir 30min or more in this process, carried out after stirring
Filter, the filter residue of filtering is dried in vacuo, and drying temperature is 50 DEG C, vacuum degree≤100pa.
Compared with prior art, the beneficial effects of the invention are as follows:
A kind of environment-friendly sheet of the present invention, according to parts by weight, raw material includes 10-15 parts of calcium carbonate, diatomite 20-40
Part, 10-25 parts of flyash, 8-15 parts of silica, 8-16 parts of epoxy resin, 5-10 parts of fibrous material, carboxymethyl cellulose 2-6
Part, 0.2-0.3 parts of lauryl sodium sulfate, 0.2-0.4 parts of coupling agent, 2-5 parts of auxiliary agent, the present invention, which has, the property such as keeps the temperature, prevents fires
Can, and it is environmentally safe, it is harmless.
Specific implementation mode
Hereinafter, preferred embodiments of the present invention will be described, it should be understood that preferred embodiment described herein is only used
In the description and interpretation present invention, it is not intended to limit the present invention.
A kind of environment-friendly sheet, according to parts by weight, raw material includes 12 parts of calcium carbonate, 25 parts of diatomite, 18 parts of flyash, two
10 parts of silica, 12 parts of epoxy resin, 8 parts of fibrous material, 4 parts of carboxymethyl cellulose, 0.25 part of lauryl sodium sulfate, coupling
0.3 part of agent, 4 parts of auxiliary agent, wherein the auxiliary agent includes 0.6 part of mould inhibitor, 0.3 part of graphene, and 0.8 part of oleamide, levelling helps
0.6 part of agent;1 part of thickening aids;0.7 part of antifoam additives.Wherein, fibrous material is wood-fibred, bamboo fibre or flaxen fiber.
A kind of production method of environment-friendly sheet, includes the following steps:
1) silica is by pretreatment;
2) calcium carbonate, diatomite, flyash, silica, epoxy resin are firstly added into dispersion cylinder by measuring requirement,
Fibrous material and carboxymethyl cellulose, then start dispersion machine, and rotating speed is maintained at 1500~2200r/min, then decelerates to 600
~800r/min sequentially adds mould inhibitor, graphene, oleamide, 1-2 parts of leveling auxiliary agent, antifoam additives under stirring, stirs
After mixing 5~10min, thickening aids being added, and carry out viscosity test, viscosity, which reaches, applies -4 glasss of 70~120s, finally, filtering,
Packaging.
Further, the silica includes by pretreatment:The silica dioxide granule, which is added to the water, to be stirred, water
In simultaneously lauryl sodium sulfate and coupling agent is added, persistently stir 30min or more in this process, carried out after stirring
Filter, the filter residue of filtering is dried in vacuo, and drying temperature is 50 DEG C, vacuum degree≤100pa.
Testing result such as table 1:
Table 1
Embodiment 2:
According to parts by weight, raw material includes calcium carbonate:14 parts, 33 parts of diatomite, 12 parts of flyash, 2 parts of silica 1,
10 parts of epoxy resin, 6 parts of fibrous material, 3 parts of carboxymethyl cellulose, 0.28 part of lauryl sodium sulfate, 0.32 part of coupling agent help
3.52 parts of agent, wherein auxiliary agent includes 0.5-1 parts of mould inhibitor, 0.2~0.4 part of graphene, 0.5-1 parts of oleamide, leveling auxiliary agent
0.5-1 parts;0.8-1.5 parts of thickening aids;0.5-1.5 parts of antifoam additives.
Finally it should be noted that:It these are only the preferred embodiment of the present invention, be not intended to restrict the invention, although
With reference to embodiment, invention is explained in detail, for those skilled in the art, still can be to aforementioned
Technical solution recorded in each embodiment is modified or equivalent replacement of some of the technical features, but it is all
Within the spirit and principles in the present invention, any modification, equivalent replacement, improvement and so on should be included in the protection of the present invention
Within the scope of.
Claims (6)
1. a kind of environment-friendly sheet, which is characterized in that according to parts by weight, raw material includes 10-15 parts of calcium carbonate, diatomite 20-40
Part, 10-25 parts of flyash, 8-15 parts of silica, 8-16 parts of epoxy resin, 5-10 parts of fibrous material, carboxymethyl cellulose 2-6
Part, 0.2-0.3 parts of lauryl sodium sulfate, 0.2-0.4 parts of coupling agent, 2-5 parts of auxiliary agent.
2. a kind of environment-friendly sheet according to claim 1, which is characterized in that the auxiliary agent includes 0.5-1 parts of mould inhibitor, graphite
0.2~0.4 part of alkene, 0.5-1 parts of oleamide, 0.5-1 parts of leveling auxiliary agent;0.8-1.5 parts of thickening aids;Antifoam additives 0.5-
1.5 part.
3. a kind of environment-friendly sheet according to claim 2, which is characterized in that according to parts by weight, raw material includes calcium carbonate 12
Part, 25 parts of diatomite, 18 parts of flyash, 0 part of silica 1,12 parts of epoxy resin, 8 parts of fibrous material, carboxymethyl cellulose 4
Part, 0.25 part of lauryl sodium sulfate, 0.3 part of coupling agent, 4 parts of auxiliary agent, wherein the auxiliary agent includes 0.6 part of mould inhibitor, graphite
0.3 part of alkene, 0.8 part of oleamide, 0.6 part of leveling auxiliary agent;1 part of thickening aids;0.7 part of antifoam additives.
4. a kind of environment-friendly sheet according to claim 1, which is characterized in that the fibrous material be wood-fibred, bamboo fibre or
Person's flaxen fiber.
5. a kind of production method of environment-friendly sheet according to claim 1, which is characterized in that include the following steps:
1) silica is by pretreatment;
2) calcium carbonate, diatomite, flyash, silica, epoxy resin, fiber are firstly added into dispersion cylinder by measuring requirement
Then material and carboxymethyl cellulose start dispersion machine, rotating speed is maintained at 1500~2200r/min, then decelerate to 600~
800r/min sequentially adds mould inhibitor, graphene, oleamide, 1-2 parts of leveling auxiliary agent, antifoam additives under stirring, stirs
After 5~10min, thickening aids being added, and carry out viscosity test, viscosity, which reaches, applies -4 glasss of 70~120s, finally, filtering, packet
Dress.
6. a kind of production method of environment-friendly sheet according to claim 5, which is characterized in that the silica is by pre- place
Reason includes:The silica dioxide granule, which is added to the water, to be stirred, and lauryl sodium sulfate and coupling agent is added simultaneously in water,
This process persistently stirs 30min or more, is filtered after stirring, the filter residue of filtering is dried in vacuo, drying temperature
It is 50 DEG C, vacuum degree≤100pa.