CN108772542A - The method that bloom continuous casting produces 20CrMo pinion steels - Google Patents
The method that bloom continuous casting produces 20CrMo pinion steels Download PDFInfo
- Publication number
- CN108772542A CN108772542A CN201810700018.0A CN201810700018A CN108772542A CN 108772542 A CN108772542 A CN 108772542A CN 201810700018 A CN201810700018 A CN 201810700018A CN 108772542 A CN108772542 A CN 108772542A
- Authority
- CN
- China
- Prior art keywords
- steel
- 20crmo
- continuous casting
- bloom
- control
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of methods that bloom continuous casting produces 20CrMo pinion steels, are suitable for 360mm × 450mm section bloom pinion steel strands, belong to bloom pinion steel production technical field.The present invention is on the basis of M-EMS, electromagnetic agitation equipment is additionally arranged between two cold-zones and solidification end, and the installation site and running parameter of the two are rationally designed, in conjunction with control cast superheat of liquid steel, poring rate, cooling parameter etc., the compactness and homogenieity of bloom 20CrMo gear steel continuous casting billets are improved, in addition, passing through the fillet parameter designing to tube type mold, optimize the cooling of strand corner, improves the control of strand corner defect.By the improvement to cooling water channel, to ensure uniformity of conducting heat so that crystallizer exit casting blank shell thickness is uniform.Present invention can ensure that bloom 20CrMo gear steel continuous casting billet comprehensive quality high levels control.
Description
Technical field
The present invention relates to a kind of methods that bloom continuous casting produces 20CrMo pinion steels, are suitable for 360mm × 450mm sections
Bloom pinion steel strand belongs to bloom pinion steel production technical field.
Background technology
Gear is important power and transmits mechanical component, and different operating modes, its stressing conditions of the gear of different parts are different, lose
Effect pattern can also have different degrees of difference, and by gear material, processing technology, lubrication circumstances, frictional force and gear
The influence of the factors such as geometry parameter and load modes.Its dominant failure mode has:Tooth caused by tooth root fracture, flank of tooth recess
Facial contour deformation, fatigue flake, abrasion are divided into adhesion wear and abrasive wear etc..It is right according to above-mentioned main failure mode
The performance requirement of pinion steel is that high conquassation drag and the good impact resistance ability of anti-spot corrosion peel-ability and bending resistance rush ability.It closes
Suitable quenching degree and case depth and the good processing performance of centre hardness and machinability and deformation and dimensionally stable
Property.Automobile gear has the function of that power transmits and change speed, is a big important representative of gear.Gear making with steel not only
There are good obdurability, wearability, can absorb impact, be bent and contact stress well, but also require to deform small.In tooth
In the manufacturing process of wheel, except requiring reasonably to design and machining is outer, also to carry out carburizing and quenching or it is quenched etc. be heat-treated, make it
Surface hardened layer is wear-resisting, matrix shock resistance.And the quality of Gear Processing blank then largely determines the effect of Gear Production
Rate and quality control.
With the continuous development of continuous casting technology, slab quality control technology level is continuously improved.Domestic automobile at present
Based on the production of gear blank is mainly produced with continuous small-billet casting, with the continuous improvement that gear quality requires, gear steel blank
Compactness, the requirement also higher of homogenieity.For small billet, bloom pinion steel strand rolling reduction bigger is high
The bloom of quality promotes advantageously the compactness and homogenieity of gear product.But the high quality of production of bloom continuous casting
There are certain technical difficulty, and strand center portion setting time first is long, and liquid core length increases, and the feeding of solidification latter stage is difficult, strand
Center segregation seriousness promoted, strand corner quality to subsequently solidify differentiation influence increase, this need to continuous cast mold,
Interference control is given in intensity of secondary cooling and casting blank solidification differentiation.Both at home and abroad have some scholars to bloom slab quality control equipment and
Technology has carried out corresponding research, mainly for bloom Properties of Heavy Rail Steel and small billet pinion steel, and for 360mm × 450mm sections
The research of bloom pinion steel slab quality control, has no substantially.
Such as:
CN107262689A discloses convex sufficient roll structure and soft reduction process, especially one kind under a kind of bloom two is cold-pressed and relates to
And convex sufficient roll structure and soft reduction process under the cold pressing of bloom two of technical field of ferrous metallurgy.Under the bloom two of the present invention is cold-pressed
Convex foot roll structure, including sufficient roller and sufficient roller under pressure area in area are depressed, it is described to depress sufficient roller sufficient roller in pressure area under area
Lower section is provided with boss in the pressure area in the middle part of sufficient roller, sufficient roller middle part is provided with boss, the pressure area under the pressure area
The boss of lower foot roller is longer than the boss of sufficient roller in pressure area.The lower area's soft reduction process of the cold pressing of bloom two of the present invention, setting are multigroup
It depresses sufficient roller in area and depresses sufficient roller under area, the drafts of sufficient roller gradually increases in throwing direction in the pressure area.The application
It can effectively solve the problems, such as bloom continuous casting base center segregation and center porosity.But it is generous for 360mm × 450mm sections
Some crucial particular contents of base pinion steel slab quality control are not directed to.
CN106735013A discloses a kind of continuous casting process improving bloom quality of primary blank, this is simple for process, changes
It is kind to open the contact for pouring molten steel with copper plate of crystallizer, increase lubrication, prevent angle seam and scrape steel phenomenon, effectively avoids opening base surface of gravying with meat or vegetables poured over rice or noodles and lack
It falls into, ensures excellent bloom quality of primary blank, while also improving the service life of copper plate of crystallizer.It is characterized in that including following
Step:(1) casting machine starts the preceding 40 ± 5min of cast, lubrication of crystallizer agent is smeared on crystallizer copper wall, and fill, especially tied
Brilliant device corner;Mode is smeared in the lubrication of crystallizer agent:It is uniformly smeared using roller, primary to smear, natural wind
Dry 5 ± 1min, then carries out secondary smearing, and other preparations opened and pour preceding routine are carried out after natural air drying;(2) casting process
In, open when pouring filled graphite at copper plate of crystallizer angle seam, control stopper open degree is 30~45% when cast, and steel stream is normally to pour
The 40~60% of casting, after the operation, other open of normal control pours work, to starting to walk, pulling rate stabilization in 0.45m/min or
0.48m/min.But for the specific interior of some keys of 360mm × 450mm section bloom pinion steel slab qualities control
Appearance is not directed to.
CN107225148A disclose it is a kind of providing a kind of milling method of 22CrMoH pinion steels, by cogging temperature
The adjusting of degree, final rolling temperature, finishing temperature, pass deformation, the cold technique of control, can effectively reduce the length/width ratio of MnS field trashes,
The austenite structure that state is organized as flattening is rolled according to the pinion steel that the method obtains, precipitate size is 20~25nm, is precipitated
It is 0.31~0.38% to measure weight fraction;After heat treatment, austenite grain size is 5~7 μm, impact of collision toughness ratio approach
In 1.It is characterized in that the milling method includes the following steps:(1) the heated stove heat of continuous casting billet, goes through high-pressure water descaling
Except iron scale;(2) continuous casting billet after dephosphorization carries out cogging and obtains bloom;(3) bloom is rolled into Continuous mill train;(4) go out
Water mist cooling is carried out after Continuous mill train;(5) enter slow cooling bed after water mist cooling and carry out slow cooling;(6) enter burial pit and carry out slow cooling;
(7) air-cooled, it can be obtained hot rolling 22CrMoH gear round steel.But for 360mm × 450mm section bloom pinion steel strands
The crucial particular content of some of quality control is not directed to.
CN106967931A discloses a kind of 20Cr2Ni4 pinion steels and its production technology, which uses
20Cr2Ni4 is made, and the mass percentage of Mo is in 20Cr2Ni4:0.15~0.30%.Its production technology include dispensing,
Electric arc furnace smelting, refining furnace are smelted, and molten steel melts in arc furnace smelting procedure, and temperature reaches 1570~1590 DEG C, and sampling carries out
Detection and analysis, make the mass percentage of Mo reach 0.15~0.30%;In refining furnace smelting process, temperature reaches 1570~
1590 DEG C, sampling is detected analysis, and the mass percentage of Mo is made to reach 0.15~0.30%.The present invention reduces to be mingled in steel
Object reduces H, O, N gas content in steel, reduces harmful element P, S, As, Sn in steel, appropriate Mo is added, and can improve steel use
In components such as large gear, axis, in quenching degree, heat resistance, crystal grain thinning, the improved combination properties such as hardness of steel are improved.Its feature
It is, the mass percentage of Mo is in 20Cr2Ni4:0.15~0.30%.But it is generous for 360mm × 450mm sections
Some crucial particular contents of base pinion steel slab quality control are not directed to.
CN106566998A discloses a kind of manufacturing method of CrMo systems gear round steel, it is characterised in that its component is by weight
Percentage is:C:0.22%~0.27%, Si:0.03%~0.12%, Mn:1.20~1.45%, S≤0.020%, P≤
0.020%, Cr:0.30%~0.60%, Mo:≤ 0.20%, Al:0.015~0.040%, Ni≤0.10%, O≤15 × 10
~6%, remainder is Fe and inevitable impurity.A classes and type impurity≤1.5 grade D, the B classes and C classes of round steel wherein obtained
Field trash≤1.0 grade, round steel hardenability:J5mm is 42~50HRC, and J9mm is 38~46HRC, and J15mm is 32~40HRC.
It change it is traditional improve the technical thought of the quenching degree of steel by adding the alloying elements such as a large amount of addition Cr, Ni, Mo, pass through
C, Mn content are properly increased, Mo contents and Cr contents is greatly lowered, replaces Ni alloys, is not dropped in the quenching degree for ensuring pinion steel
Under the premise of low, the production cost of product is considerably reduced, improves the competitiveness of product.But for 360mm ×
Some crucial particular contents of 450mm section bloom pinion steel slab qualities control are not directed to.
Invention content
The technical problem to be solved by the present invention is to:A kind of method of bloom continuous casting production 20CrMo pinion steels is provided,
Suitable for 360mm × 450mm section blooms, bloom 20CrMo gear steel continuous casting billets compactness, homogenieity can be promoted, it is ensured that
Bloom 20CrMo gear steel continuous casting billet comprehensive quality high levels control.
The technical solution adopted in the present invention is to solve above-mentioned technical problem:
(1) tube type mold is used, the corner fillet size of tube type mold is R20mm, can optimize strand corner in this way
It is cooling, improve the control of strand corner defect;Cooling water channel is two into two times, and there are two water inlet and two water outlets for tool, simultaneously
DN250 regulating valves are installed at water inlet position, realize accurately controlling for crystallizer intensity of cooling;The work of the cooling water of crystallizer
Skill state modulator is water flow 3157L/min~3340L/min, and hydraulic pressure 0.82MPa~0.87MPa ensures the casting of crystallizer exit
The thickness and uniformity of base green shell, shell thickness size are preferably controlled in 16mm~20mm.
(2) M-EMS is that the low level in crystallizer exit is installed, and M-EMS equips cover height
For 350mm, lower end is flushed with mouth under crystallizer;M-EMS true field gaussian intensity is measured, magnetic is stirred with practical
Field gaussian intensity is that 280 ± 5Gs is stirred electric current setting, stir current frequency 2.4Hz;
(3) electromagnetic agitation equipment is installed between two cold-zones and solidification end, electromagnetic agitation equipment installation site is
The region that linear ratio is 0.45~0.47 is solidified, specially apart from the sections crystallizer molten steel surface 10.0m~11.0m;Actual measurement stirring
Magnetic field gaussian intensity is that 200 ± 25Gs is stirred current strength setting by true field gaussian intensity, and stir current frequency is
7.0Hz;
(4) Water Rate for Secondary Cooling Water presses 0.311Lkg-1 Steel~0.320Lkg-1 SteelIt is configured;
Furthermore, it is necessary to which middle Baogang's liquid has certain degree of superheat to meet casting demand.The 1st heat cast is wrapped for middle,
Superheat of liquid steel control is poured into a mould at 27 DEG C~43 DEG C;For 2~N heats of middle packet casting, cast superheat of liquid steel control exists
15 DEG C~35 DEG C;
Casting speed control can according to target pulling rate 0.50m/min constant speed be poured into a mould in 0.45m/min~0.55m/min.
The beneficial effects of the invention are as follows:On the basis of M-EMS, increase between two cold-zones and solidification end
If electromagnetic agitation equipment, and the installation site and running parameter of the two rationally designed, pour into a mould steel in conjunction with control
The liquid degree of superheat, poring rate, cooling parameter etc. improve the compactness and homogenieity of bloom 20CrMo gear steel continuous casting billets,
In addition, by the fillet parameter designing to tube type mold, the cooling of optimization strand corner improves the control of strand corner defect.
By the improvement to cooling water channel, to ensure uniformity of conducting heat so that crystallizer exit casting blank shell thickness is uniform.The present invention
It can ensure that bloom 20CrMo gear steel continuous casting billet comprehensive quality high levels control.
Specific implementation mode
With reference to embodiment, the invention will be further described.
In embodiment, the electromagnetic agitation equipment installed between two cold-zones and solidification end, referred to as " between two cold and solidifications
End electromagnetic agitation " (S~F-EMS).
Embodiment 1
The embodiment is certain steel mill method production 360mm × 450mm section 20CrMo Series Gears using the present invention
Steel continuous casting blooms.The specific implementation mode of the technology of the present invention is:Using tube type mold, corner fillet size is R20mm;If
It is two into two times to count tube type mold water route, ensures heat transfer uniformity;Crystallizer be equipped with cooling water inflow be 3160L/min~
3340L/min, hydraulic pressure 0.84MPa~0.87MPa fine-tune crystallizer cooling water using DN250 regulating valves;Crystallizer electromagnetism
Stirring is that the low level in crystallizer exit is installed, and M-EMS equips cover height 350mm, lower end and mouth under crystallizer
It flushes;M-EMS true field 280 ± 5Gs of gaussian intensity, stir current are set as 495A~500A, stir current
Frequency 2.4Hz.Installation " cold with solidification end electromagnetic agitations between two " position (S~F-EMS) be solidification linear ratio be 0.45~
0.47 region, specially apart from the sections crystallizer molten steel surface 10.0m~11.0m, stirring magnetic field gaussian intensity is 200 ±
25Gs, stir current intensity are 215A~218A, and stir current frequency is 7.0Hz;Water Rate for Secondary Cooling Water is 0.315Lkg-1 Steel~
0.320L·kg-1 Steel。
In addition, control is at 17 DEG C~35 DEG C, the first heat of middle packet, degree of superheat control for cast superheat of liquid steel (middle packet casting)
At 30 DEG C~43 DEG C;By casting speed control in 0.45m/min~0.55m/min, target pull rate 0.50m/min constant speed duration of pouring ratios
Example is 91%.
Casting process Mold liquid level stabilizing, covering slag thickness distribution are uniform.Low power is carried out to continuous casting blooms
Detection;Corroded using cold sour dendrite, detection strand cross section shell thickness distribution situation, the results show that the technology was produced
20CrMo Series Gears steel continuous casting blooms shell thickness is circumferentially distributed uniformly along section, and whole control is in 16mm~20mm;Casting
Base corner quality is good, to continuous casting billet tunneling boring carry out in-situ metal Scanning Detction, strand tunneling boring homogeneity be 0.910~
0.922, center portion consistency is 0.913~0.941, and corresponding bite low power grading center segregation, center porosity are ≤0.5
Grade, non-stop layer shrinkage cavity.
Embodiment 2
The embodiment is certain steel mill method production 360mm × 450mm section 20CrMo Series Gears using the present invention
Steel continuous casting blooms.The present invention specific implementation mode be:Using tube type mold, corner fillet size is R20mm;Design pipe
Formula crystallizer water route is two into two times, ensures heat transfer uniformity;It is 3157L/min~3340L/ that crystallizer, which is equipped with cooling water inflow,
Min, hydraulic pressure 0.82MPa~0.87MPa fine-tune crystallizer cooling water using DN250 regulating valves;M-EMS is
The low level in crystallizer exit is installed, and M-EMS equips cover height 350mm, and lower end is flushed with mouth under crystallizer;
M-EMS true field 280 ± 5Gs of gaussian intensity, stir current are set as 491A~495A, stir current frequency
2.4Hz.Installation " between two cold and solidification end electromagnetic agitations " position (S~F-EMS) is that solidification linear ratio is 0.45~0.47
Region, specially apart from the sections crystallizer molten steel surface 10.0m~11.0m, stirring magnetic field gaussian intensity is 200 ± 25Gs, is stirred
It is 214A~217A to mix current strength, and stir current frequency is 7.0Hz;Water Rate for Secondary Cooling Water is 0.311Lkg-1 Steel~0.318L
kg-1 Steel。
In addition, control is at 16 DEG C~33 DEG C, the first heat of middle packet, degree of superheat control for cast superheat of liquid steel (middle packet casting)
At 27 DEG C~42 DEG C;By casting speed control in 0.47m/min~0.53m/min, target pull rate 0.50m/min constant speed duration of pouring ratios
Example is 95%.
Casting process Mold liquid level stabilizing, covering slag thickness distribution are uniform.Low power is carried out to continuous casting blooms
Detection;Corroded using cold sour dendrite, detection strand cross section shell thickness distribution situation, the results show that the technology was produced
20CrMo Series Gears steel continuous casting blooms shell thickness is circumferentially distributed uniformly along section, and whole control is in 17mm~18.6mm;
Strand corner quality is good, carries out in-situ metal Scanning Detction to continuous casting billet tunneling boring, strand tunneling boring homogeneity is 0.900
~0.934, center portion consistency is 0.902~0.931, and corresponding bite low power grading center segregation, center porosity are ≤0.5
Grade, non-stop layer shrinkage cavity.
Embodiment 3
The embodiment is certain steel mill method production 360mm × 450mm section 20CrMo Series Gears using the present invention
Steel continuous casting blooms.The present invention specific implementation mode be:Using tube type mold, corner fillet size is R20mm;Design pipe
Formula crystallizer water route is two into two times, ensures heat transfer uniformity;It is 3255L/min~3330L/ that crystallizer, which is equipped with cooling water inflow,
Min, hydraulic pressure 0.84MPa~0.87MPa fine-tune crystallizer cooling water using DN250 regulating valves;M-EMS is
The low level in crystallizer exit is installed, and M-EMS equips cover height 350mm, and lower end is flushed with mouth under crystallizer;
M-EMS true field 280 ± 5Gs of gaussian intensity, stir current are set as 492A~495A, stir current frequency
2.4Hz.Installation " between two cold and solidification end electromagnetic agitations " position (S~F-EMS) is that solidification linear ratio is 0.45~0.47
Region, specially apart from the sections crystallizer molten steel surface 10.0m~11.0m, stirring magnetic field gaussian intensity is 200 ± 25Gs, is stirred
It is 214A~217A to mix current strength, and stir current frequency is 7.0Hz;Water Rate for Secondary Cooling Water is 0.313Lkg-1 Steel~0.319L
kg-1 Steel。
In addition, control is at 17 DEG C~35 DEG C, the first heat of middle packet, degree of superheat control for cast superheat of liquid steel (middle packet casting)
At 29 DEG C~41 DEG C;By casting speed control in 0.46m/min~0.55m/min, target pull rate 0.50m/min constant speed duration of pouring ratios
Example is 90.3%.
Casting process Mold liquid level stabilizing, covering slag thickness distribution are uniform.Low power is carried out to continuous casting blooms
Detection;Corroded using cold sour dendrite, detection strand cross section shell thickness distribution situation, the results show that the technology was produced
20CrMo Series Gears steel continuous casting blooms shell thickness is circumferentially distributed uniformly along section, and whole control is in 17.8mm~20mm;
Strand corner quality is good, carries out in-situ metal Scanning Detction to continuous casting billet tunneling boring, strand tunneling boring homogeneity is 0.901
~0.931, center portion consistency is 0.921~0.933, and corresponding bite low power grading center segregation, center porosity are ≤0.5
Grade, non-stop layer shrinkage cavity.
Above-mentioned embodiment explanation, after technical scheme of the present invention, 360mm × 450mm section 20CrMo teeth
Take turns the control of steel bloom slab quality well, strand corner zero-fault, shell thickness is uniformly distributed circumferentially, and strand tunneling boring is equal
Matter is preferable, and internal rarefaction and shrinkage cavity are effectively controlled, the high-caliber control of strand center portion consistency, center porosity, center
It is more excellent to be segregated the control of low multiple quality standard diagrams, other capability and performances are whole qualified.
Claims (5)
1. the method that bloom continuous casting produces 20CrMo pinion steels, it is characterised in that:Using tube type mold, the cooling of crystallizer
The process parameter control of water is water flow 3157L/min~3340L/min, hydraulic pressure 0.82MPa~0.87MPa;
M-EMS is that the low level in crystallizer exit is installed, and it is 350mm that M-EMS, which equips cover height,
Lower end is flushed with mouth under crystallizer;M-EMS true field gaussian intensity is measured, it is strong with practical stirring magnetic field Gauss
Degree is that 280 ± 5Gs is stirred electric current setting, stir current frequency 2.4Hz;
Electromagnetic agitation equipment is installed between two cold-zones and solidification end, it is that solidification is linear which, which equips installation site,
Than the region for 0.45~0.47;Actual measurement stirring magnetic field gaussian intensity is that 200 ± 25Gs is stirred by true field gaussian intensity
Current strength setting is mixed, stir current frequency is 7.0Hz;Water Rate for Secondary Cooling Water presses 0.311Lkg-1 Steel~0.320Lkg-1 SteelInto
Row setting;
For the 1st heat of middle packet casting, cast superheat of liquid steel control is at 27 DEG C~43 DEG C;For 2~N of middle packet casting
Heat, cast superheat of liquid steel control is at 15 DEG C~35 DEG C;
Casting speed control is in 0.45m/min~0.55m/min.
2. the method for bloom continuous casting production 20CrMo pinion steels as described in claim 1, it is characterised in that:Tube type mold
Corner fillet size be R20mm.
3. the method for bloom continuous casting production 20CrMo pinion steels as described in claim 1, it is characterised in that:Tube type mold
Cooling water channel be two into two times, tool is there are two water inlet and two water outlets.
4. the method for the bloom continuous casting production 20CrMo pinion steels as described in any one of claims 1 to 3, feature exist
In:Shell thickness size Control is in 16mm~20mm.
5. the method for the bloom continuous casting production 20CrMo pinion steels as described in any one of claims 1 to 3, feature exist
In:Electromagnetic agitation equipment installation site between two cold-zones and solidification end is apart from crystallizer molten steel surface 10.0m~11.0m
Section.