CN108753174A - High osmosis consolidates wall alkali-resistant sealing primer - Google Patents
High osmosis consolidates wall alkali-resistant sealing primer Download PDFInfo
- Publication number
- CN108753174A CN108753174A CN201810645258.5A CN201810645258A CN108753174A CN 108753174 A CN108753174 A CN 108753174A CN 201810645258 A CN201810645258 A CN 201810645258A CN 108753174 A CN108753174 A CN 108753174A
- Authority
- CN
- China
- Prior art keywords
- parts
- resistant sealing
- high osmosis
- weight proportion
- sealing primer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high osmosis to consolidate wall alkali-resistant sealing primer, including constituent weight proportion range it is as follows：Water：34~35 parts；Substrate wetting agents：0.1~0.3 part；Lotion：64~66 parts；Propylene glycol：1.0~1.5 parts；Coalescents：1.0~2.0 parts；Antifoaming agent：0.1~0.3 part；Preservative：0.2~0.3 part.The present invention can make loose, dusting metope solid very well, without rooting out the metope of loose dusting, greatly save human and material resources.
Description
Technical field
The present invention relates to constructional ornamental material technology, refers specifically to a kind of high osmosis and consolidate wall alkali-resistant sealing primer.
Background technology
Oxidation and ultraviolet irradiation of the metope by oxygen, aging can all occur, metope all can loose and powder after aging
Change, and directly brush common seal coat all and peeling can occur and fall off, is all loose and dusting wall for renovation
Face is rooted out, and criticizes putty again, then applies seal coat and finishing coat.It is time-consuming and laborious, not due to loose and dusting metope sometimes
Cleaning it is very clean, batch putty can also hollowing fall off.
Invention content
The present invention proposes that a kind of permeability is very strong, and the high high osmosis of adhesive strength consolidates wall alkali-resistant sealing primer, can be very
Make loose, dusting metope solid well, without rooting out the metope of loose dusting, greatlys save human and material resources.
The technical proposal of the invention is realized in this way：
A kind of high osmosis consolidates wall alkali-resistant sealing primer, including constituent weight proportion range it is as follows：
Water：34~35 parts；
Substrate wetting agents：0.1~0.3 part；
Lotion：64~66 parts；
Propylene glycol：1.0~1.5 parts；
Coalescents：1.0~2.0 parts；
Antifoaming agent：0.1~0.3 part；
Preservative：0.2~0.3 part.
Preferably, the weight proportion of water is 34.5 parts.
Preferably, the weight proportion of substrate wetting agents is 0.2 part.
Preferably, the weight proportion of lotion is 65 parts.
Preferably, ranging from 1.2~1.4 parts of the weight proportion of propylene glycol.
Preferably, the weight proportion of coalescents is 1.5 parts.
Preferably, the weight proportion of antifoaming agent is 0.2 part.
Preferably, the weight proportion of preservative is 0.25 part.
The beneficial effects of the present invention are：Loose, dusting metope can be made solid very well, without by loose dusting
Metope root out, greatly save human and material resources.
Specific implementation mode
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field
The every other embodiment that art personnel are obtained without creative efforts belongs to the model that the present invention protects
It encloses.
The present invention proposes a kind of high osmosis and consolidates wall alkali-resistant sealing primer, including constituent weight proportion range such as
Under：
Water：34~35 parts；
Substrate wetting agents：0.1~0.3 part；
Lotion：64~66 parts；
Propylene glycol：1.0~1.5 parts；
Coalescents：1.0~2.0 parts；
Antifoaming agent：0.1~0.3 part；
Preservative：0.2~0.3 part.
The high osmosis of the present invention consolidates wall alkali-resistant sealing primer, and wherein substrate wetting agents can reduce the surface of priming paint very well
Tension, enhancing priming paint are soaked and are permeated to wall, and the lotion for selecting grain size small can pass through the hole of loose dusting wall very well
Gap penetrates into the absorption of wall and quickly crosslinking curing and prevents the infiltration of priming paint, therefore the high osmosis Gu Qiang of the present invention is anti-
Alkali seal coat can make the metope of loose dusting become solid metope, just not because of the loose dusting of wall in old-wall renewing
And it is rooted out, it can solve as long as consolidating wall alkali-resistant sealing primer using this high osmosis, greatly save manpower, object
Power.
Wherein, the weight proportion of water ranges preferably from 34.2~34.8 parts, preferably 34.3~34.7 parts, preferably 34.4
~34.6 parts, specifically, the weight proportion of water can be 34.5 parts.
Wherein, the weight proportion of substrate wetting agents ranges preferably from 0.15~0.25, and the weight proportion of substrate wetting agents is
0.2 part.
Wherein, the weight proportion of lotion ranges preferably from 64.5~65.5, and the weight proportion of lotion is 65 parts.
Wherein, the weight proportion of propylene glycol ranges preferably from 1.2~1.4 parts, more preferably 1.3~1.4 parts.
Wherein, the weight proportion of coalescents is preferably 1.2~1.8 parts, more preferably 1.4~1.6 parts, coalescents
Weight proportion is 1.5 parts.
Wherein, the weight proportion of antifoaming agent ranges preferably from 0.15~0.25 part, more preferably 0.18~0.22 part, defoaming
The weight proportion of agent is 0.2 part.
Wherein, the weight proportion of preservative is preferably 0.22~0.27 part, more preferably 0.24~0.26 part, preservative
Weight proportion is 0.25 part.
The embodiment of the present invention compared with prior art, has the advantages that：
1, high osmosis of the invention, which consolidates wall alkali-resistant sealing primer, has high osmosis, without loose, dusting metope
Loose, dusting metope hardening, densification can be made by rooting out.
2, easy for construction, saving human and material resources.
Consolidating wall alkali-resistant sealing primer in order to ensure the high osmosis of the embodiment of the present invention can be in wide in range environment into enforcement
With, also need be added part of auxiliary, these auxiliary agents can ensure that coating uses within the scope of different temperatures, different humidity, in this hair
In another bright embodiment, it is as follows that high osmosis of the present invention consolidates wall alkali-resistant sealing primer proportioning：
The making step of the present embodiment is as follows：
Water is added to the container by step 1 by requirement, starts dispersion machine, rotating speed 400RPM；
Step 2 sequentially adds wetting agent, lotion, propylene glycol, coalescents, antifoaming agent, preservative, dispersing speed
It is transferred to 600RPM, is disperseed 10 minutes.
High osmosis, which is made, in the embodiment of the present invention, which consolidates wall alkali-resistant sealing primer, can reach performance indicator below
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention
With within principle, any modification, equivalent replacement, improvement and so on should all be included in the protection scope of the present invention god.
Claims (8)
1. a kind of high osmosis consolidates wall alkali-resistant sealing primer, it is characterised in that：Including constituent weight proportion range it is as follows：
Water：34~35 parts；
Substrate wetting agents：0.1~0.3 part；
Lotion：64~66 parts；
Propylene glycol：1.0~1.5 parts；
Coalescents：1.0~2.0 parts；
Antifoaming agent：0.1~0.3 part；
Preservative：0.2~0.3 part.
2. high osmosis according to claim 1 consolidates wall alkali-resistant sealing primer, it is characterised in that：The weight proportion of water is
34.5 parts.
3. high osmosis according to claim 1 consolidates wall alkali-resistant sealing primer, it is characterised in that：The weight of substrate wetting agents
Proportioning is 0.2 part.
4. high osmosis according to claim 1 consolidates wall alkali-resistant sealing primer, it is characterised in that：The weight proportion of lotion is
65 parts.
5. high osmosis according to claim 1 consolidates wall alkali-resistant sealing primer, it is characterised in that：The weight proportion of propylene glycol
Ranging from 1.2~1.4 parts.
6. high osmosis according to claim 1 consolidates wall alkali-resistant sealing primer, it is characterised in that：The weight of coalescents is matched
Than being 1.5 parts.
7. high osmosis according to claim 1 consolidates wall alkali-resistant sealing primer, it is characterised in that：The weight proportion of antifoaming agent
It is 0.2 part.
8. high osmosis according to claim 1 consolidates wall alkali-resistant sealing primer, it is characterised in that：The weight proportion of preservative
It is 0.25 part.