CN108751213A - 一种耐火材料用改性蛭石的制备方法 - Google Patents

一种耐火材料用改性蛭石的制备方法 Download PDF

Info

Publication number
CN108751213A
CN108751213A CN201810615992.7A CN201810615992A CN108751213A CN 108751213 A CN108751213 A CN 108751213A CN 201810615992 A CN201810615992 A CN 201810615992A CN 108751213 A CN108751213 A CN 108751213A
Authority
CN
China
Prior art keywords
vermiculite
performance
added
refractory material
modified
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810615992.7A
Other languages
English (en)
Inventor
刘焕章
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingdao Cree New Mstar Technology Ltd
Original Assignee
Qingdao Cree New Mstar Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingdao Cree New Mstar Technology Ltd filed Critical Qingdao Cree New Mstar Technology Ltd
Priority to CN201810615992.7A priority Critical patent/CN108751213A/zh
Publication of CN108751213A publication Critical patent/CN108751213A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种耐火材料用改性蛭石的制备方法，包括下列步骤：将蛭石研磨成粉状；将蛭石粉料放入1mol/L的氯化镁溶液中，60℃下水浴加热并充分搅拌8h，用清水冲洗3遍，放入烘箱中烘干。本发明的改性蛭石的膨胀速度快于现有技术的膨胀蛭石，可以起到更好的防火作用。用本发明的改性蛭石制成的防火材料做成的防火窗，在防火窗腔体内有一定支撑强度，在受热后迅速膨胀，充满腔体，起到很好的隔热作用。

Description

一种耐火材料用改性蛭石的制备方法
技术领域
本发明涉及耐火材料领域，尤其涉及一种改性蛭石的制备方法。
背景技术
研制与开发优质的隔热耐火材料 , 并在工业窑炉中合理配套使用 , 是行之有效的节能途径。优质的隔热耐火材料既可提高窑炉的寿命，又可提高产品的质量、减少热损失、提高热能利用效率和减少能源浪费，从而达到节约能源、降低产品成本的目的。因此，对有效的高温隔热材料的需求就愈显迫切。
发明内容
本发明要解决的问题是提供一种耐火材料用改性蛭石的制备方法。
为解决上述技术问题，本发明的耐火材料用改性蛭石的制备方法，包括下列步骤：
（1）将蛭石研磨成粉状；
（2）将蛭石粉料放入1mol/L的氯化镁溶液中，60℃下水浴加热并充分搅拌8h，用清水冲洗3遍，放入烘箱中烘干。
作为一种改进，每升氯化镁溶液中添加20-30ml质量分数为5-10%的次氯酸，然后在溶液中加入蛭石粉，在密闭容器中加压至1.5-2atm，在30-35℃下水浴加热并充分搅拌5-10分钟，冷却后泄压，然后加入氢氧化钠至溶液呈中性。上述中和后的溶液中加入可膨胀石墨粉末。60℃下水浴加热并充分搅拌8h，用清水冲洗3遍，放入烘箱中烘干。
加入次氯酸，加热并搅拌，次氯酸分解，产生氧气和盐酸，用盐酸浸泡让蛭石晶片破裂，呈现出多孔特征，颗粒通道中的杂质被溶出，孔道疏通，从而有利于吸附质分子的扩散，吸附能力得以提高。产生的氧气形成小气泡，进入蛭石的层间，产生压力，使得蛭石的壁层产生一个恰好的空间，石墨粉末进入此空间。改性后的蛭石制成的膨胀层在受热时，石墨颗粒受热膨胀撑开蛭石，使得膨胀速度更快，短时间内膨胀一定距离。使得膨胀层对火的反应更快。较之普通方法改性的膨胀层，可以起到更好的防火作用。由于石墨的作用，游离氯化镁可以更好的与蛭石结合，更好的防止防火材料受潮变形产生缝隙。本方法中，密闭的空间内加热，冷却后泄压，可以使氧气更好的打开蛭石层，产生空间。
本发明的改性蛭石的膨胀速度快于现有技术的膨胀蛭石，可以起到更好的防火作用。用本发明的改性蛭石制成的防火材料做成的防火窗，在防火窗腔体内有一定支撑强度，在受热后迅速膨胀，充满腔体，起到很好的隔热作用。经过实验测试，将插入预成型膨胀隔热条的防火窗框体放入高温炉升温至1000℃，在燃烧过程中防火窗背火面没有出现火苗，没有塌陷，框体结构依然完好。
附图说明
图1是未改性的蛭石层的显微图。
图2是本发明的蛭石层的显微图。
图3是未改性的蛭石的膨胀速率折线图。
图4是本发明的蛭石的膨胀速率折线图。
具体实施方式
本发明的本发明的本发明的耐火材料用改性蛭石的制备方法，包括下列步骤：
（1）将蛭石研磨成粉状；
（2）将蛭石粉料放入1mol/L的氯化镁溶液中，每升氯化镁溶液中添加20-30ml质量分数为5-10%的次氯酸，然后在溶液中加入蛭石粉，在密闭容器中加压至1.5-2atm，在30-35℃下水浴加热并充分搅拌5-10分钟，冷却至10-20℃后泄压，然后加入氢氧化钠并搅拌，至溶液呈中性。上述中和后的溶液中加入可膨胀石墨粉末，石墨粉100-200目。60℃下水浴加热并充分搅拌8h，用清水冲洗3遍，放入烘箱中烘干，至含水量30%以下。
加入次氯酸，加热并搅拌，次氯酸分解，产生氧气和盐酸，用盐酸浸泡让蛭石晶片破裂，呈现出多孔特征，颗粒通道中的杂质被溶出，孔道疏通，从而有利于吸附质分子的扩散，吸附能力得以提高。产生的氧气形成小气泡，进入蛭石的层间，产生压力，使得蛭石的壁层产生一个恰好的空间，石墨粉末进入此空间，如图2所示。改性后的蛭石制成的膨胀层在受热时，石墨颗粒受热膨胀撑开蛭石，使得膨胀速度更快，短时间内膨胀一定距离。使得膨胀层对火的反应更快。较之普通方法改性的膨胀层，可以起到更好的防火作用。由于石墨的作用，游离氯化镁可以更好的与蛭石结合，更好的防止防火材料受潮变形产生缝隙。本方法中，密闭的空间内加热，冷却后泄压，可以使氧气更好的打开蛭石层，产生空间。

Claims (3)

1.一种耐火材料用改性蛭石的制备方法，其特征在于：包括下列步骤：
（1）将蛭石研磨成粉状；
（2）将蛭石粉料放入1mol/L的氯化镁溶液中，60℃下水浴加热并充分搅拌8h，用清水冲洗3遍，放入烘箱中烘干。
2.按照权利要求1所述的耐火材料用改性蛭石的制备方法，其特征在于：每升氯化镁溶液中添加20-30ml质量分数为5-10%的次氯酸，然后在溶液中加入蛭石粉，在30-35℃下水浴加热并充分搅拌5-10分钟，然后加入氢氧化钠至溶液呈中性，上述中和后的溶液中加入可膨胀石墨粉末，60℃下水浴加热并充分搅拌8h，用清水冲洗3遍，放入烘箱中烘干。
3.按照权利要求2所述的耐火材料用改性蛭石的制备方法，其特征在于：在溶液中加入蛭石粉后，在密闭容器中加压至1.5-2atm，在30-35℃下水浴加热并充分搅拌5-10分钟，冷却后泄压。
CN201810615992.7A 2018-06-14 2018-06-14 一种耐火材料用改性蛭石的制备方法 Pending CN108751213A (zh)