CN108745839A - 一种提升钻井机卸杆机构零件使用寿命的处理方法 - Google Patents

一种提升钻井机卸杆机构零件使用寿命的处理方法 Download PDF

Info

Publication number
CN108745839A
CN108745839A CN201810568669.9A CN201810568669A CN108745839A CN 108745839 A CN108745839 A CN 108745839A CN 201810568669 A CN201810568669 A CN 201810568669A CN 108745839 A CN108745839 A CN 108745839A
Authority
CN
China
Prior art keywords
parts
trepan
service life
processing method
promoting
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810568669.9A
Other languages
English (en)
Inventor
丁恩亚
丁庆平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FUNAN COUNTY FENJIN MACHINERY MANUFACTURING Co Ltd
Original Assignee
FUNAN COUNTY FENJIN MACHINERY MANUFACTURING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FUNAN COUNTY FENJIN MACHINERY MANUFACTURING Co Ltd filed Critical FUNAN COUNTY FENJIN MACHINERY MANUFACTURING Co Ltd
Priority to CN201810568669.9A priority Critical patent/CN108745839A/zh
Publication of CN108745839A publication Critical patent/CN108745839A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种提升钻井机卸杆机构零件使用寿命的处理方法，包括如下步骤：（1）除油处理、（2）喷丸处理、（3）涂料涂覆处理、（4）冷却处理。本发明处理方法能够有效的改善钻井机卸杆机构零件的表面特性，增强了其耐腐、耐温、耐磨能力，很好的延长了其使用寿命，极具推广应用价值。

Description

一种提升钻井机卸杆机构零件使用寿命的处理方法
技术领域
本发明属于农业机械加工处理技术领域，具体涉及一种提升钻井机卸杆机构零件使用寿命的处理方法。
背景技术
申请号为：201310260785.1公开了一种车载 电动液压振动式钻井机，包括有底座，底座的前端固定安装在车体上，底座的后端安装有可调式支腿，底座前端部的上端面架设有两并列的立柱，立柱内侧配合有可上下移动的导轨，导轨的移动由液压缸驱动，导轨之间设有固定支座，固定支座上架设有驱动齿轮箱，后端部有连接管穿过，连接管的上端安装有抽泥水接头，钻杆接头转动安装在齿轮箱底端，钻杆接头的转动由电机驱动，底座的中部设有两可对合的挡板，挡板中部分别设有相互对应的半圆形凹槽，半圆形凹槽对合后与钻杆接头顶端的台阶配合。其具有移动方便、噪音小、运行稳定、散热效果好的特点，需要动力小，可节能 50％，钻杆装卸时人工劳动强度小，省时省力，提高了钻杆的装卸效率。但此机在卸杆时还不能达到自动化操作，钻杆接头很容易磨损，需要经常更换，拆卸也较为繁琐。对此申请号为：201410632986.4公开了一种车载电动液压振动式钻井机卸杆机构，其中是由多种机构零件组成，而此组成零件多由不锈钢等金属材质制成，长期在潮湿条件下工作会发生锈蚀，需要进行防护处理。目前对于构成上述组成零件的防护处理效果不佳，导致使用寿命不长，影响了使用的价值。
发明内容
本发明的目的是针对现有的问题，提供了一种提升钻井机卸杆机构零件使用寿命的处理方法。
本发明是通过以下技术方案实现的：
一种提升钻井机卸杆机构零件使用寿命的处理方法，包括如下步骤：
（1）除油处理：
先将零件放入到丙酮中浸泡除油处理15~20min后取出，然后用去离子水冲洗一遍后备用；
（2）喷丸处理：
将步骤（1）处理后的零件放入到喷丸机内进行喷丸处理，完成后取出备用；
（3）涂料涂覆处理：
a.向步骤（2）处理后的零件的表面上涂覆一层专用涂料，完成后将零件放入到干燥箱内干燥固化处理；所述的专用涂料由如下重量份的物质组成：95~100份环氧树脂、28~32份酚醛树脂、7~10份C9石油树脂、4~6份硅溶胶、6~8份玻璃纤维、5~7份栲胶、2.5~3.5份壳聚糖、0.5~1.5份乙二胺四乙酸四钠、7~10份十二烷基二甲基苄基溴化铵、7~9份乙酸乙酯、10~14份丙三醇、0.1~0.2份硝酸镧、8~10份碳酸钙、1~2份纳米碳粉、2~3份颜填料、3~5份增韧剂；
b.待操作a处理后的零件表面的专用涂料涂层半干后，对零件施加交流电处理，直至专用涂料涂层完全干燥固化；
（4）冷却处理：
将步骤（3）处理后的零件取出自然冷却至室温即可。
进一步的，步骤（2）中所述的喷丸处理时喷丸的介质选择二氧化硅颗粒，其直径为0.7~0.8mm，喷嘴离零件表面的距离为95~105mm，喷丸的流速为170~175m/s。
进一步的，步骤（3）操作a中所述的碳酸钙的颗粒粒径为400~500目。
进一步的，步骤（3）操作a中所述的纳米碳粉的颗粒粒径为20~80nm。
进一步的，步骤（3）操作a中所述的颜填料为铬黄、酞菁蓝、氧化铬绿中的任意一种。
进一步的，步骤（3）操作a中所述的增韧剂为丁腈橡胶。
进一步的，步骤（3）操作b中所述的交流电处理时控制电流强度为35~40mA。
本发明对零件的处理方法进行了特殊的改进，其中进行的喷丸处理很好的细化了零件表面的晶粒，并适度提高了零件表面的粗糙度，为后续的处理奠定了基础，随后又用专用涂料进行了涂覆处理，专用涂料是以环氧树脂作为基体物质，又复配添加了酚醛树脂和C9石油树脂，很好的提升了整体的铺展、成膜特性，为了进一步改善整体的品质，又添加了硅溶胶、玻璃纤维、栲胶和壳聚糖成分，其中硅溶胶、玻璃纤维能有效的提高涂料整体的致密性，耐温、耐磨性，添加的栲胶和壳聚糖能够通过疏水键和盐键络合形成高活性复合物，结合固定于玻璃纤维的表面，提升了与树脂高分子间的结合强度，提升了涂料的品质，此专用专用涂料粘结性好、致密度高，涂覆于零件表面半干后，又进行了交流电处理，在专用涂料内部纳米碳粉导流的作用下，专用涂料各组分的活性提升，相互间及其与金属零件表面间的结合能力和强度提升，进一步提升了处理的效果。
本发明相比现有技术具有以下优点：
本发明处理方法能够有效的改善钻井机卸杆机构零件的表面特性，增强了其耐腐、耐温、耐磨能力，很好的延长了其使用寿命，极具推广应用价值。
具体实施方式
实施例1
一种提升钻井机卸杆机构零件使用寿命的处理方法，包括如下步骤：
（1）除油处理：
先将零件放入到丙酮中浸泡除油处理15min后取出，然后用去离子水冲洗一遍后备用；
（2）喷丸处理：
将步骤（1）处理后的零件放入到喷丸机内进行喷丸处理，完成后取出备用；
（3）涂料涂覆处理：
a.向步骤（2）处理后的零件的表面上涂覆一层专用涂料，完成后将零件放入到干燥箱内干燥固化处理；所述的专用涂料由如下重量份的物质组成：95份环氧树脂、28份酚醛树脂、7份C9石油树脂、4份硅溶胶、6份玻璃纤维、5份栲胶、2.5份壳聚糖、0.5份乙二胺四乙酸四钠、7份十二烷基二甲基苄基溴化铵、7份乙酸乙酯、10份丙三醇、0.1份硝酸镧、8份碳酸钙、1份纳米碳粉、2份颜填料、3份增韧剂；
b.待操作a处理后的零件表面的专用涂料涂层半干后，对零件施加交流电处理，直至专用涂料涂层完全干燥固化；
（4）冷却处理：
将步骤（3）处理后的零件取出自然冷却至室温即可。
进一步的，步骤（2）中所述的喷丸处理时喷丸的介质选择二氧化硅颗粒，其直径为0.7~0.8mm，喷嘴离零件表面的距离为95~105mm，喷丸的流速为170~175m/s。
进一步的，步骤（3）操作a中所述的碳酸钙的颗粒粒径为400目。
进一步的，步骤（3）操作a中所述的纳米碳粉的颗粒粒径为20~80nm。
进一步的，步骤（3）操作a中所述的颜填料为铬黄。
进一步的，步骤（3）操作a中所述的增韧剂为丁腈橡胶。
进一步的，步骤（3）操作b中所述的交流电处理时控制电流强度为35mA。
实施例2
一种提升钻井机卸杆机构零件使用寿命的处理方法，包括如下步骤：
（1）除油处理：
先将零件放入到丙酮中浸泡除油处理18min后取出，然后用去离子水冲洗一遍后备用；
（2）喷丸处理：
将步骤（1）处理后的零件放入到喷丸机内进行喷丸处理，完成后取出备用；
（3）涂料涂覆处理：
a.向步骤（2）处理后的零件的表面上涂覆一层专用涂料，完成后将零件放入到干燥箱内干燥固化处理；所述的专用涂料由如下重量份的物质组成：97份环氧树脂、30份酚醛树脂、8份C9石油树脂、5份硅溶胶、7份玻璃纤维、6份栲胶、3份壳聚糖、1份乙二胺四乙酸四钠、9份十二烷基二甲基苄基溴化铵、8份乙酸乙酯、12份丙三醇、0.15份硝酸镧、9份碳酸钙、1.5份纳米碳粉、2.5份颜填料、4份增韧剂；
b.待操作a处理后的零件表面的专用涂料涂层半干后，对零件施加交流电处理，直至专用涂料涂层完全干燥固化；
（4）冷却处理：
将步骤（3）处理后的零件取出自然冷却至室温即可。
进一步的，步骤（2）中所述的喷丸处理时喷丸的介质选择二氧化硅颗粒，其直径为0.7~0.8mm，喷嘴离零件表面的距离为95~105mm，喷丸的流速为170~175m/s。
进一步的，步骤（3）操作a中所述的碳酸钙的颗粒粒径为450目。
进一步的，步骤（3）操作a中所述的纳米碳粉的颗粒粒径为20~80nm。
进一步的，步骤（3）操作a中所述的颜填料为酞菁蓝。
进一步的，步骤（3）操作a中所述的增韧剂为丁腈橡胶。
进一步的，步骤（3）操作b中所述的交流电处理时控制电流强度为38mA。
实施例3
一种提升钻井机卸杆机构零件使用寿命的处理方法，包括如下步骤：
（1）除油处理：
先将零件放入到丙酮中浸泡除油处理20min后取出，然后用去离子水冲洗一遍后备用；
（2）喷丸处理：
将步骤（1）处理后的零件放入到喷丸机内进行喷丸处理，完成后取出备用；
（3）涂料涂覆处理：
a.向步骤（2）处理后的零件的表面上涂覆一层专用涂料，完成后将零件放入到干燥箱内干燥固化处理；所述的专用涂料由如下重量份的物质组成：100份环氧树脂、32份酚醛树脂、10份C9石油树脂、6份硅溶胶、8份玻璃纤维、7份栲胶、3.5份壳聚糖、1.5份乙二胺四乙酸四钠、10份十二烷基二甲基苄基溴化铵、9份乙酸乙酯、14份丙三醇、0.2份硝酸镧、10份碳酸钙、2份纳米碳粉、3份颜填料、5份增韧剂；
b.待操作a处理后的零件表面的专用涂料涂层半干后，对零件施加交流电处理，直至专用涂料涂层完全干燥固化；
（4）冷却处理：
将步骤（3）处理后的零件取出自然冷却至室温即可。
进一步的，步骤（2）中所述的喷丸处理时喷丸的介质选择二氧化硅颗粒，其直径为0.7~0.8mm，喷嘴离零件表面的距离为95~105mm，喷丸的流速为170~175m/s。
进一步的，步骤（3）操作a中所述的碳酸钙的颗粒粒径为500目。
进一步的，步骤（3）操作a中所述的纳米碳粉的颗粒粒径为20~80nm。
进一步的，步骤（3）操作a中所述的颜填料为氧化铬绿。
进一步的，步骤（3）操作a中所述的增韧剂为丁腈橡胶。
进一步的，步骤（3）操作b中所述的交流电处理时控制电流强度为40mA。
对比实施例1
本对比实施例1与实施例2相比，省去了步骤（3）涂料涂覆处理操作a中专用涂料中的栲胶和壳聚糖成分，除此外的方法步骤均相同。
对比实施例2
本对比实施例2与实施例2相比，省去了步骤（3）涂料涂覆处理操作b中的交流电处理操作，除此外的方法步骤均相同。
对比实施例3
本对比实施例3与实施例2相比，省去了步骤（3）涂料涂覆处理操作a中专用涂料中的栲胶和壳聚糖成分，同时还省去了步骤（3）涂料涂覆处理操作b中的交流电处理操作，除此外的方法步骤均相同。
为了简化对比本发明效果，选用304号不锈钢作为实验对象，分别用上述实施例2、对比实施例1、对比实施例2、对比实施例3所述的方法进行处理，完成后对各组处理后的304号不锈钢试样进行性能测试，具体对比数据如下表1所示：
表1
注：上表1中所述的耐应力腐蚀时长参照GB/T17898-1999进行测试；所述的模拟海水浸泡中模拟海水中的各成分及含量为：氯化钠28.2g/L，氯化钾0.9 g/L，氯化钙1.5g/L，碳酸氢钠0.3 g/L，氯化镁2.3 g/L，硫酸镁3.2 g/L，余量为水，且模拟海水的pH值为6.5~7.2，温度为常温。
由上表1可以看出，本发明处理方法能够有效的改善零件的表面特性，提升了其耐腐能力，在实际使用时其寿命延长了30%以上，极具推广应用价值。

Claims (7)

1.一种提升钻井机卸杆机构零件使用寿命的处理方法，其特征在于，包括如下步骤：
（1）除油处理：
先将零件放入到丙酮中浸泡除油处理15~20min后取出，然后用去离子水冲洗一遍后备用；
（2）喷丸处理：
将步骤（1）处理后的零件放入到喷丸机内进行喷丸处理，完成后取出备用；
（3）涂料涂覆处理：
a.向步骤（2）处理后的零件的表面上涂覆一层专用涂料，完成后将零件放入到干燥箱内干燥固化处理；所述的专用涂料由如下重量份的物质组成：95~100份环氧树脂、28~32份酚醛树脂、7~10份C9石油树脂、4~6份硅溶胶、6~8份玻璃纤维、5~7份栲胶、2.5~3.5份壳聚糖、0.5~1.5份乙二胺四乙酸四钠、7~10份十二烷基二甲基苄基溴化铵、7~9份乙酸乙酯、10~14份丙三醇、0.1~0.2份硝酸镧、8~10份碳酸钙、1~2份纳米碳粉、2~3份颜填料、3~5份增韧剂；
b.待操作a处理后的零件表面的专用涂料涂层半干后，对零件施加交流电处理，直至专用涂料涂层完全干燥固化；
（4）冷却处理：
将步骤（3）处理后的零件取出自然冷却至室温即可。
2.根据权利要求1所述的一种提升钻井机卸杆机构零件使用寿命的处理方法，其特征在于，步骤（2）中所述的喷丸处理时喷丸的介质选择二氧化硅颗粒，其直径为0.7~0.8mm，喷嘴离零件表面的距离为95~105mm，喷丸的流速为170~175m/s。
3.根据权利要求1所述的一种提升钻井机卸杆机构零件使用寿命的处理方法，其特征在于，步骤（3）操作a中所述的碳酸钙的颗粒粒径为400~500目。
4.根据权利要求1所述的一种提升钻井机卸杆机构零件使用寿命的处理方法，其特征在于，步骤（3）操作a中所述的纳米碳粉的颗粒粒径为20~80nm。
5.根据权利要求1所述的一种提升钻井机卸杆机构零件使用寿命的处理方法，其特征在于，步骤（3）操作a中所述的颜填料为铬黄、酞菁蓝、氧化铬绿中的任意一种。
6.根据权利要求1所述的一种提升钻井机卸杆机构零件使用寿命的处理方法，其特征在于，步骤（3）操作a中所述的增韧剂为丁腈橡胶。
7.根据权利要求1所述的一种提升钻井机卸杆机构零件使用寿命的处理方法，其特征在于，步骤（3）操作b中所述的交流电处理时控制电流强度为35~40mA。
CN201810568669.9A 2018-06-05 2018-06-05 一种提升钻井机卸杆机构零件使用寿命的处理方法 Pending CN108745839A (zh)