CN108728696A - A kind of aluminum handware - Google Patents
A kind of aluminum handware Download PDFInfo
- Publication number
- CN108728696A CN108728696A CN201810653323.9A CN201810653323A CN108728696A CN 108728696 A CN108728696 A CN 108728696A CN 201810653323 A CN201810653323 A CN 201810653323A CN 108728696 A CN108728696 A CN 108728696A
- Authority
- CN
- China
- Prior art keywords
- weight percent
- account
- alloy plate
- aluminium alloy
- plate weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of aluminum handware, ingredient includes：It is 10% iron below to account for aluminium alloy plate weight percent；It is 0.5% titanium below to account for aluminium alloy plate weight percent；It is 0.45% nickel below to account for aluminium alloy plate weight percent；It is 5% copper below to account for aluminium alloy plate weight percent；Surplus is aluminium and inevitable impurity.The beneficial effects of the invention are as follows：Composition proportion is scientific and reasonable, the adjustment of iron content can increase alloy strength appropriate, the corrosion resistance and elevated temperature strength of the increase alloy of titanium, copper content can increase strength of alloy, also the machining property of alloy is substantially improved, the addition of nickel can enhance the rustless property of integral Al-alloy plate so that good product quality obtained.
Description
Technical field
The present invention relates to a kind of aluminium alloy plate more particularly to a kind of aluminum handwares.
Background technology
With the continuous improvement of science and technology, hardware industry also constantly emerges, and aluminium base handware is due to price at this stage
It is cheap therefore most widely used, while aluminium base handware also has preferable use value, then aluminium base handware makes
There are more defects during, such as：It is easily aoxidized, is easily corroded, and in view of the foregoing drawbacks, it is all made of at present copper-plated
Mode, but when copper facing in the prior art, quality is poor, density metal is insufficient, increased number of stomata, and layers of copper is loosely
Lean on so that product it is second-rate.
Therefore, to solve the above problems, providing a kind of new technical solution.
Invention content
The present invention provides a kind of aluminum handware.
The technical solution adopted by the present invention is：
A kind of aluminum handware, ingredient include：
It is 10% iron below to account for aluminium alloy plate weight percent；
It is 0.5% titanium below to account for aluminium alloy plate weight percent；
It is 0.45% nickel below to account for aluminium alloy plate weight percent；
It is 5% copper below to account for aluminium alloy plate weight percent；
Surplus is aluminium and inevitable impurity.
Further, the weight percent of the iron is 5-10%.
Further, the weight percent of the titanium is 0.2-0.5%.
Further, the weight percent of the nickel is 0.25-0.45%.
Further, the weight percent of the copper is 2-5%.
The beneficial effects of the invention are as follows：Composition proportion is scientific and reasonable, the adjustment of iron content can increase alloy appropriate it is strong
Degree, the corrosion resistance and elevated temperature strength of the increase alloy of titanium, copper content can increase strength of alloy, also substantially improve
The machining property of alloy, the addition of nickel can enhance the rustless property of integral Al-alloy plate so that good product quality obtained.
Specific implementation mode
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, the embodiment
It is only used for explaining the present invention, not restrict the protection scope of the present invention.
Embodiment 1
A kind of aluminum handware, ingredient include：
Account for the iron that aluminium alloy plate weight percent is 5%；
Account for the titanium that aluminium alloy plate weight percent is 0.2%；
Account for the nickel that aluminium alloy plate weight percent is 0.25%；
Account for the copper that aluminium alloy plate weight percent is 2%；
Surplus is aluminium and inevitable impurity.
Embodiment 2
A kind of aluminum handware, ingredient include：
Account for the iron that aluminium alloy plate weight percent is 7%；
Account for the titanium that aluminium alloy plate weight percent is 0.3%；
Account for the nickel that aluminium alloy plate weight percent is 0.3.5%；
Account for the copper that aluminium alloy plate weight percent is 3.5%；
Surplus is aluminium and inevitable impurity.
Embodiment 3
A kind of aluminum handware, ingredient include：
Account for the iron that aluminium alloy plate weight percent is 10%；
Account for the titanium that aluminium alloy plate weight percent is 0.5%；
Account for the nickel that aluminium alloy plate weight percent is 0.45%；
Account for the copper that aluminium alloy plate weight percent is 5%；
Surplus is aluminium and inevitable impurity.
The beneficial effects of the invention are as follows：Composition proportion is scientific and reasonable, the adjustment of iron content can increase alloy appropriate it is strong
Degree, the corrosion resistance and elevated temperature strength of the increase alloy of titanium, copper content can increase strength of alloy, also substantially improve
The machining property of alloy, the addition of nickel can enhance the rustless property of integral Al-alloy plate so that good product quality obtained.
The above described is only a preferred embodiment of the present invention, being not the limit for making any other form to the present invention
System, and according to the technical essence of the invention made by any modification or equivalent variations, still fall within present invention model claimed
It encloses.
Claims (5)
1. a kind of aluminum handware, it is characterised in that：Its ingredient includes：
It is 10% iron below to account for aluminium alloy plate weight percent；
It is 0.5% titanium below to account for aluminium alloy plate weight percent；
It is 0.45% nickel below to account for aluminium alloy plate weight percent；
It is 5% copper below to account for aluminium alloy plate weight percent；
Surplus is aluminium and inevitable impurity.
2. a kind of aluminum handware according to claim 1, it is characterised in that：The weight percent of the iron is 5-10%.
3. a kind of aluminum handware according to claim 1, it is characterised in that：The weight percent of the titanium is 0.2-
0.5%。
4. a kind of aluminum handware according to claim 1, it is characterised in that：The weight percent of the nickel is 0.25-
0.45%。
5. a kind of aluminum handware according to claim 1, it is characterised in that：The weight percent of the copper is 2-5%.