CN107326223A - A kind of bicycle use alloy material - Google Patents
A kind of bicycle use alloy material Download PDFInfo
- Publication number
- CN107326223A CN107326223A CN201710430764.8A CN201710430764A CN107326223A CN 107326223 A CN107326223 A CN 107326223A CN 201710430764 A CN201710430764 A CN 201710430764A CN 107326223 A CN107326223 A CN 107326223A
- Authority
- CN
- China
- Prior art keywords
- parts
- aluminium
- bicycle use
- alloy material
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of bicycle use alloy material, using aluminium as raw material, include the component of following parts by weight：25 parts of nitrogen；0.8 1.5 parts of gold；0.13 0.24 parts of phosphorus；0.1 0.3 parts of magnesium；0.2 0.35 parts of palladium.The beneficial effects of the invention are as follows：Using aluminium as primary raw material, proportioning is scientific and reasonable, and the phosphorus and magnesium metallic element of addition increase the mechanical strength of parts, enhance the mechanical property of aluminium alloy plate, can improve filiform corrosion resistance, improve the stability of metal material.
Description
Technical field
The present invention relates to a kind of metal material, more particularly to a kind of bicycle use alloy material.
Background technology
In bicycle many parts be all by the bicycle stamping parts for welding or being machined after stamped or punching press,
The bicycle hardware stamping part of different purposes selects the metal material of different mechanical properties according to its handling characteristics, so as to ensure it
Product quality.In recent years, bicycle trade energy-saving and emission-reduction policy is widelyd popularize so that the alternative materials such as high strength steel are in vehicle
Begin to use in manufacture, high strength steel can mitigate part quality by reducing the modes such as thickness of slab or sectional dimension, in reality
Had a clear superiority in terms of existing vehicle lightweight and raising security performance, current steel bicycle use material generally existing wearability
The problem of difference, difference of hardness.
Therefore, to solve the above problems, special provide a kind of new technical scheme.
The content of the invention
The present invention provides a kind of bicycle use alloy material.
The technical solution adopted by the present invention is：
A kind of bicycle use alloy material, using aluminium as raw material, includes the component of following parts by weight：2-5 parts of nitrogen；0.8-1.5
The gold of part；0.13-0.24 parts of phosphorus；0.1-0.3 parts of magnesium；0.2-0.35 parts of palladium.
Further, the parts by weight of the aluminium are 70-80 parts.
Further, the parts by weight of the magnesium are 0.19 part.
Further, the parts by weight of the palladium are 0.25-0.3 parts.
Further, the golden parts by weight are 0.9-1.2 parts.
The beneficial effects of the invention are as follows：Using aluminium as primary raw material, proportioning is scientific and reasonable, and the phosphorus and magnesium metallic element of addition add
The big mechanical strength of parts, enhances the mechanical property of aluminium alloy plate, can improve filiform corrosion resistance, improve gold
Belong to the stability of material.
Embodiment
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, the embodiment
It is only used for explaining the present invention, does not constitute the restriction to protection scope of the present invention.
Embodiment 1
A kind of bicycle use alloy material, using aluminium as raw material, includes the component of following parts by weight：2 parts of nitrogen；0.8 part of gold；
0.13 part of phosphorus；0.1 part of magnesium；0.2 part of palladium.
The beneficial effects of the invention are as follows：Using aluminium as primary raw material, proportioning is scientific and reasonable, and the phosphorus and magnesium metallic element of addition add
The big mechanical strength of parts, enhances the mechanical property of aluminium alloy plate, can improve filiform corrosion resistance, improve gold
Belong to the stability of material.
Embodiment 2
A kind of bicycle use alloy material, using aluminium as raw material, includes the component of following parts by weight：3.5 parts of nitrogen；1.2 parts
Gold；0.19 part of phosphorus；0.2 part of magnesium；0.28 part of palladium.
The beneficial effects of the invention are as follows：Using aluminium as primary raw material, proportioning is scientific and reasonable, and the phosphorus and magnesium metallic element of addition add
The big mechanical strength of parts, enhances the mechanical property of aluminium alloy plate, can improve filiform corrosion resistance, improve gold
Belong to the stability of material.
Embodiment 3
A kind of bicycle use alloy material, using aluminium as raw material, includes the component of following parts by weight：5 parts of nitrogen；1.5 parts
Gold；0.24 part of phosphorus；0.3 part of magnesium；0.35 part of palladium.
The beneficial effects of the invention are as follows：Using aluminium as primary raw material, proportioning is scientific and reasonable, and the phosphorus and magnesium metallic element of addition add
The big mechanical strength of parts, enhances the mechanical property of aluminium alloy plate, can improve filiform corrosion resistance, improve gold
Belong to the stability of material.
The above described is only a preferred embodiment of the present invention, being not the limit for making any other form to the present invention
System, and any modification made according to technical spirit of the invention or equivalent variations, still fall within model claimed of the invention
Enclose.
Claims (5)
1. a kind of bicycle use alloy material, it is characterised in that：Using aluminium as raw material, include the component of following parts by weight：2-5 parts
Nitrogen；0.8-1.5 parts of gold；0.13-0.24 parts of phosphorus；0.1-0.3 parts of magnesium；0.2-0.35 parts of palladium.
2. a kind of bicycle use alloy material according to claim 1, it is characterised in that：The parts by weight of the aluminium are
70-80 parts.
3. a kind of bicycle use alloy material according to claim 1, it is characterised in that：The parts by weight of the magnesium are
0.19 part.
4. a kind of bicycle use alloy material according to claim 1, it is characterised in that：The parts by weight of the palladium are
0.25-0.3 parts.
5. a kind of bicycle use alloy material according to claim 1, it is characterised in that：The golden parts by weight are
0.9-1.2 parts.