CN108727907A - A kind of long-acting mosquito-driving muscid-type environmental protection coating material and method - Google Patents
A kind of long-acting mosquito-driving muscid-type environmental protection coating material and method Download PDFInfo
- Publication number
- CN108727907A CN108727907A CN201810580120.1A CN201810580120A CN108727907A CN 108727907 A CN108727907 A CN 108727907A CN 201810580120 A CN201810580120 A CN 201810580120A CN 108727907 A CN108727907 A CN 108727907A
- Authority
- CN
- China
- Prior art keywords
- parts
- environmental protection
- coating material
- powder
- long
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of long-acting mosquito-driving muscid-type environmental protection coating material and methods.Environmental protection coating material is made of the substance of following mass parts：20-30 parts of modified corn starch fat resin, 25-35 parts of clear water, 5-15 parts of plant gum, 10-15 parts of powder of Chinese mugwort, 1-3 parts of ultrafine carbon fiber particle, 10-15 parts of diatomite, 4-10 parts of titanium dioxide, 1-4 parts of ceramic powder.The preparation method of environmental protection coating material is：First group glue composition and second group powder liquid composition are individually prepared, is then uniformly mixed two parts of compositions.The coating of the present invention can give out plant folium artemisiae argyi faint scent, environment protection health, and can long-acting mosquito-driving fly be up to 20 years；And has the advantages that wear-resisting, scrub resistance is strong, flexibility is strong, purposes is wide, be suitable for the coating of wall, furniture, office accommodation, toilet wash platform and other body surfaces.
Description
Technical field
The present invention relates to a kind of coating and method more particularly to a kind of long-acting mosquito-driving muscid-type environmental protection coating material and methods.
Background technology
Coating is to be coated in the body surface protected or decorated, and can form the continuous of firm attachment with coated article
Film all has very extensive application in fields such as machinery, household, building, techniques, closely bound up with people's lives.Mesh
Preceding waterproof in the market mainly has two major classes：First, polyurethanes water-repellent paint, this kind of material is usually by polyurethane and coal tar
Oil is made as raw material, and the tar gas toxicity that it is volatilized is big, and does not allow easy-clear, therefore banned in China in 2000
Only use, and still in the polyurethane waterproofing coating of sale, it is to use pitch to replace coal tar as raw material, but this coating makes
It is used time, general using being diluted containing organic solvents such as toluene, dimethylbenzene, thus also containing toxic；Second is that polyalcohol cement basis
Water-repellent paint, the lotion that this coating is synthesized by a variety of waterborne polymerics are formed with the high grade cement mixed with various additives, though
So it is showed excellent in terms of impermeability is with stability, but it does not have any environment-friendly function, and extension and resistance to
Mill property is slightly poor.
Reinforcement with people to environmental protection consciousness researches and develops novel environmentally friendly functional coating by the body to safeguarding people
Body health and high standard quality of life require significance.
Invention content
In order to solve the shortcoming present in above-mentioned technology, the present invention provides a kind of long-acting mosquito-driving muscid-type environmental protection coating materials
And method.
In order to solve the above technical problems, the technical solution adopted by the present invention is：A kind of long-acting mosquito-driving muscid-type environmental protection coating material,
It is made of the substance of following mass parts：
Preferably, a kind of long-acting mosquito-driving muscid-type environmental protection coating material is made of the substance of following mass parts：Modified corn starch fat
25 parts of resin, 31 parts of clear water, 10 parts of plant gum, 12 parts of powder of Chinese mugwort, 2 parts of ultrafine carbon fiber particle, 12 parts of diatomite, titanium dioxide 6
Part, 2 parts of ceramic powder.
Preferably, a kind of long-acting mosquito-driving muscid-type environmental protection coating material is made of the substance of following mass parts：Modified corn starch fat
28 parts of resin, 28 parts of clear water, 12 parts of plant gum, 14 parts of powder of Chinese mugwort, 2 parts of ultrafine carbon fiber particle, 11 parts of diatomite, titanium dioxide 5
Part, 3 parts of ceramic powder.
A kind of preparation method of long-acting mosquito-driving muscid-type environmental protection coating material, overall step are：
A, the preparation of first group glue composition：
By mass parts be respectively 20-30 parts of modified corn starch fat resin, 20-30 parts of clear water is added to mixing vessel
In, add 5-15 parts of plant gum；200r/min mechanical agitation 30min, above-mentioned substance is uniformly mixed, and forms first group glue
Liquid composition；
B, the preparation of second group powder liquid composition：
Sequentially added into another mixing vessel 4-10 parts of titanium dioxide, 1-4 parts of ceramic powder, 10-15 parts Chinese mugwort powder,
1-3 parts of ultrafine carbon fiber particle, 10-15 parts of diatomite and 5-10 parts of clear water, stirring 30min to uniform mixing, shape
At second group powder liquid composition；
C, second group powder liquid composition is added in first group glue composition, stirs 30min, be uniformly mixed；Then exist
Composition is ground to 5 microns of fineness on horizontal sand mill；Fineness is detected, is all filtered after qualification filling.
The total amount of adding of clear water is 25-35 mass parts twice.
The coating of the present invention can give out plant folium artemisiae argyi faint scent, environment protection health, and can long-acting mosquito-driving fly be up to 20 years；And
And have the advantages that wear-resisting, scrub resistance is strong, flexibility is strong, purposes is wide, it is suitable for wall, furniture, office accommodation, toilet horse
The coating of bucket wash platform and other body surfaces.
Specific implementation mode
The present invention will be further described in detail with reference to the specific embodiments.
A kind of long-acting mosquito-driving muscid-type environmental protection coating material, is made of the substance of following mass parts：
A kind of preparation method of long-acting mosquito-driving muscid-type environmental protection coating material, overall step are：
A, the preparation of first group glue composition：
By mass parts be respectively 20-30 parts of modified corn starch fat resin, 20-30 parts of clear water is added to mixing vessel
In, add 5-15 parts of plant gum；200r/min mechanical agitation 30min, above-mentioned substance is uniformly mixed, and forms first group glue
Liquid composition；
B, the preparation of second group powder liquid composition：
Sequentially added into another mixing vessel 4-10 parts of titanium dioxide, 1-4 parts of ceramic powder, 10-15 parts Chinese mugwort powder,
1-3 parts of ultrafine carbon fiber particle, 10-15 parts of diatomite and 5-10 parts of clear water, stirring 30min to uniform mixing, shape
At second group powder liquid composition；
C, second group powder liquid composition is added in first group glue composition, stirs 30min, be uniformly mixed；Then exist
Composition is ground to 5 microns of fineness on horizontal sand mill；Fineness is detected, is all filtered after qualification filling.
The total amount of adding of clear water is 25-35 mass parts twice.
In the present invention, modified corn starch fat resin can effectively improve the bonding strength of this product and comprehensive mechanical property
Energy；Plant gum is used as adhesive and curing agent, has the characteristic of film forming.The addition of Chinese mugwort powder, can not only promote product
Faint scent, functional functionality can be kept stronger with long-acting mosquito-driving fly.Ultrafine carbon fiber particle, titanium dioxide, ceramic powder
All have effects that enhance wearability and corrosion resistance, the mechanical property of product can be further strengthened, to increase substantially it
Service life.On the one hand diatomite can be used as stabilizer for improving the dispersion degrees of other each substances, on the other hand due to it is light,
It is fine and smooth, porous, the flexibility of product can also be significantly increased.
The Specific construction parameter of coating is as follows in the present invention：
(1) dosage is referred to：When 100 μm of thickness of dry film, dosage is 0.25kg/ ㎡.
(2) performance parameter：
Solid content：Quality solid content：>=90%；
Surface drying time：Temperature is 5 DEG C：≤ 60 minutes；Temperature is 40 DEG C：≤ 30 minutes；
Do solid work the time：Temperature is 5 DEG C：≤ 8 hours；Temperature is 40 DEG C：≤ 4 hours；
Tearing strength：≥120N/mm；
Hardness：>=60 (shore D)；
Wearability：After 1000 turns being ground with the w/H-10 grinding wheels of 1000g weights on Taber grinding wheels, mass loss≤0.7g；
Adhesive force：The concrete of coating prime lacquer：>=5MPa or concrete destruction；
Peeling force：With 180 ° of strippings of concrete of coating prime lacquer：>=6.0N/mm or concrete destruction；
Chemical reagent-resistant performance：It is impregnated for a long time in diesel oil, gasoline, machine oil, saturated brine, anti-icing fluid without exception；
The bonding force of freeze-thawing resistant cyclicity and concrete：>=0.8MPa or concrete destruction；
Chloride permeability rate：<0.04%；
Impermeability：0.5Mpa is for 24 hours, waterproof；
Heat ageing：80 DEG C of heat ageing, 1000h.
Alkali resistance：It is saturated Ca (OH)2Solution impregnates 500h, and no cracking is peeled off without peeling；
Normal use temperature range：- 10 DEG C~45 DEG C
Certain performances (such as intensity, elongation percentage, hardness and lower temperature resistance etc.) can also according to the environment of practice come into
Row adjustment only need to slightly adjust formula and can be achieved with.
The test temperature of the above performance display parameters is 25 DEG C.
(3) product surface pre-processes：
Concrete surface processing：Newly-built concrete slab should be at least 7 days curing age；Basal plane must it is clean,
It is dry and firm；Basal plane must not have laitance, grease and other surface contaminants.
Steel surface processing：All iron rust of steel surface, dust and pollutant must be removed, and bright metal is exposed
Surface reaches the surface derusting grade of 2 grades of sandblasting.
(4) it constructs：
Priming paint：Must construct suitable basal plane inorganic agent before, it is proposed that use natural plants folium artemisiae argyi carbon fiber diatomite
Bottom layer treatment agent is as basal plane inorganic agent, which can use brushing or spraying process handles basal plane, and construction can spray after 1 hour
Apply this product.
Work progress needs uniformly, and film is without hole, pin hole or drum blister.Coating the natural point of interruption for example expansion joint, corner,
Wall side, tank skin lid etc. can be from interruptions.If the region of application does not form nature interruption, width and depth need to be cut out in advance
At least 6 millimeters of sawtooth, then construction paint again, makes film be interrupted at sawtooth.By the neighboring edge glue around sawtooth
Tape erasure falls the film of overspray, makes surface smooth clean.
Bi-component airless spraying equipment can be used to be sprayed, blade coating or roller coating by hand can also be used, it at room temperature can be fast
Speed forms high richness film.It needs to be checked as early as possible after having constructed, ensure surface pore-free, drum blister or sprays phenomena such as irregular
Occur.Any defective spraying area should again spray after spraying completion for the first time in 48 hours.
According to construction method, the difference of construction site situation and environmental condition, reach the painting needed for required coating thickness
Layer road number is also different.It often constructs one of environmental protection coating material, it is necessary to assure preceding one of film has reached dry to touch.It can after construction
The thickness of dry film of 100 μm of -3mm of minimum is obtained, spreading rate is different according to the degree of roughness of substrate surface.
(5) technique effect：
1, there is long-acting mosquito-driving fly characteristic, longest was up to 20 years；2, it is clear to distribute fragrance plant folium artemisiae argyi for environment protection health
It is fragrant；3, can 8 hours it is fast curing-formed；4, it is added to ultrafine carbon fiber particle, the superpower temperature tolerance, superpower soft with carbon fiber
Toughness and superpower intensity；5, high solids content, resistance of chloride ion penetration is strong, anti acid alkali performance is strong, scrub resistance is strong, superpower wear-resistant
Property；6, it is rich in diatomite, titanium dioxide, ceramic powder, fabulous physical property, including stretches tensile strength, adhesion strength, ageing-resistant, resistance to
Burn into against weather etc.；7, multiple color, such as Transparent color can be made, white, grey is green, and yellow, red etc. in this way may be used
Need to select different colors according to use environment；8, easy to use, there are a variety of application methods such as spraying, blade coating, roller coating；
9, widely used, it is suitable for wall, furniture, office accommodation, toilet wash platform and other body surfaces.
The technical scheme of the invention is described in detail through specific implementation examples：
Embodiment one,
A kind of long-acting mosquito-driving muscid-type environmental protection coating material, is made of the substance of following mass parts：Modified corn starch fat resin 25
Part, 31 parts of clear water, 10 parts of plant gum, 12 parts of powder of Chinese mugwort, 2 parts of ultrafine carbon fiber particle, 12 parts of diatomite, 6 parts of titanium dioxide, ceramics
2 parts of powder.
The preparation process of environmental protection coating material is in the present embodiment：
A, the preparation of first group glue composition：
By mass parts be respectively 25 parts modified corn starch fat resin, 25 parts of clear water be added into mixing vessel, then
10 parts of plant gum is added；200r/min mechanical agitation 30min, above-mentioned substance is uniformly mixed, and forms the combination of first group glue
Object；
B, the preparation of second group powder liquid composition：
6 parts of titanium dioxide, 2 parts of ceramic powder, 12 parts of Chinese mugwort powder, 2 parts super are sequentially added into another mixing vessel
Fine carbon particle, 12 parts of diatomite and 6 parts of clear water, stirring 30min to uniform mixing, form the combination of second group powder liquid
Object；
C, second group powder liquid composition is added in first group glue composition, stirs 30min, be uniformly mixed；Then exist
Composition is ground to 5 microns of fineness on horizontal sand mill；Fineness is detected, is all filtered after qualification filling.
Embodiment two,
A kind of long-acting mosquito-driving muscid-type environmental protection coating material, is made of the substance of following mass parts：Modified corn starch fat resin 28
Part, 28 parts of clear water, 12 parts of plant gum, 14 parts of powder of Chinese mugwort, 2 parts of ultrafine carbon fiber particle, 11 parts of diatomite, 5 parts of titanium dioxide, ceramics
3 parts of powder.
The preparation process of environmental protection coating material is other in addition to difference in the mass parts of each substance and embodiment one in the present embodiment
It is identical as embodiment one.Wherein, when first, second composition is prepared, the additive amount of clear water is respectively 20 parts, 8 parts.
Embodiment three,
A kind of long-acting mosquito-driving muscid-type environmental protection coating material, is made of the substance of following mass parts：Modified corn starch fat resin 20
Part, 35 parts of clear water, 5 parts of plant gum, 15 parts of powder of Chinese mugwort, 1 part of ultrafine carbon fiber particle, 15 parts of diatomite, 4 parts of titanium dioxide, ceramics
4 parts of powder.
The preparation process of environmental protection coating material is other in addition to difference in the mass parts of each substance and embodiment one in the present embodiment
It is identical as embodiment one.Wherein, when first, second composition is prepared, the additive amount of clear water is respectively 30 parts, 5 parts.
Example IV,
A kind of long-acting mosquito-driving muscid-type environmental protection coating material, is made of the substance of following mass parts：Modified corn starch fat resin 30
Part, 25 parts of clear water, 15 parts of plant gum, 10 parts of powder of Chinese mugwort, 3 parts of ultrafine carbon fiber particle, 10 parts of diatomite, 10 parts of titanium dioxide, pottery
1 part of porcelain powder.
The preparation process of environmental protection coating material is other in addition to difference in the mass parts of each substance and embodiment one in the present embodiment
It is identical as embodiment one.Wherein, when first, second composition is prepared, the additive amount of clear water is respectively 20 parts, 5 parts.
Embodiment five,
A kind of long-acting mosquito-driving muscid-type environmental protection coating material, is made of the substance of following mass parts：Modified corn starch fat resin 30
Part, 35 parts of clear water, 5 parts of plant gum, 10 parts of powder of Chinese mugwort, 1 part of ultrafine carbon fiber particle, 10 parts of diatomite, 10 parts of titanium dioxide, ceramics
4 parts of powder.
The preparation process of environmental protection coating material is other in addition to difference in the mass parts of each substance and embodiment one in the present embodiment
It is identical as embodiment one.Wherein, when first, second composition is prepared, the additive amount of clear water is respectively 25 parts, 10 parts.
Embodiment six,
A kind of long-acting mosquito-driving muscid-type environmental protection coating material, is made of the substance of following mass parts：Modified corn starch fat resin 23
Part, 30 parts of clear water, 8 parts of plant gum, 13 parts of powder of Chinese mugwort, 3 parts of ultrafine carbon fiber particle, 13 parts of diatomite, 8 parts of titanium dioxide, ceramics
2 parts of powder.
The preparation process of environmental protection coating material is other in addition to difference in the mass parts of each substance and embodiment one in the present embodiment
It is identical as embodiment one.Wherein, when first, second composition is prepared, the additive amount of clear water is respectively 24 parts, 6 parts.
Embodiment seven,
A kind of long-acting mosquito-driving muscid-type environmental protection coating material, is made of the substance of following mass parts：Modified corn starch fat resin 26
Part, 32 parts of clear water, 6 parts of plant gum, 13 parts of powder of Chinese mugwort, 1 part of ultrafine carbon fiber particle, 14 parts of diatomite, 9 parts of titanium dioxide, ceramics
3 parts of powder.
The preparation process of environmental protection coating material is other in addition to difference in the mass parts of each substance and embodiment one in the present embodiment
It is identical as embodiment one.Wherein, when first, second composition is prepared, the additive amount of clear water is respectively 26 parts, 6 parts.
The composition of the present invention has long-acting mosquito-driving fly characteristic longest up to 20 years spies compared with previous common coating
Property, and it is wear-resisting, scrub resistance is stronger, flexibility is stronger, purposes is wider, be suitable for wall, furniture, office accommodation, toilet
Closestool wash platform and other body surfaces, under three kinds of spraying, blade coating, roller coating coating methods can in 8 hours curing moldings,
And fragrance smell, environment protection health can be distributed.
The above embodiment is not limitation of the present invention, and the present invention is also not limited to the example above, this technology neck
The variations, modifications, additions or substitutions that the technical staff in domain is made within the scope of technical scheme of the present invention, also belong to this hair
Bright protection domain.
Claims (5)
1. a kind of long-acting mosquito-driving muscid-type environmental protection coating material, it is characterised in that：The coating is made of the substance of following mass parts：
2. long-acting mosquito-driving muscid-type environmental protection coating material according to claim 1, it is characterised in that：The coating is by following mass parts
Substance be made：25 parts of modified corn starch fat resin, 31 parts of clear water, 10 parts of plant gum, 12 parts of powder of Chinese mugwort, ultrafine carbon fiber
2 parts of grain, 12 parts of diatomite, 6 parts of titanium dioxide, 2 parts of ceramic powder.
3. long-acting mosquito-driving muscid-type environmental protection coating material according to claim 1, it is characterised in that：The coating is by following mass parts
Substance be made：28 parts of modified corn starch fat resin, 28 parts of clear water, 12 parts of plant gum, 14 parts of powder of Chinese mugwort, ultrafine carbon fiber
2 parts of grain, 11 parts of diatomite, 5 parts of titanium dioxide, 3 parts of ceramic powder.
4. a kind of preparation method of long-acting mosquito-driving muscid-type environmental protection coating material as described in claim 1, it is characterised in that：The method
Overall step be：
A, the preparation of first group glue composition：
By mass parts be respectively 20-30 parts modified corn starch fat resin, 20-30 parts of clear water be added into mixing vessel,
Add 5-15 parts of plant gum；200r/min mechanical agitation 30min, above-mentioned substance is uniformly mixed, and forms first group glue
Composition；
B, the preparation of second group powder liquid composition：
4-10 parts of titanium dioxide, 1-4 parts of ceramic powder, 10-15 parts of Chinese mugwort powder, 1-3 are sequentially added into another mixing vessel
The ultrafine carbon fiber particle, 10-15 parts of diatomite and 5-10 parts of clear water of part, stirring 30min form second to uniform mixing
Group powder liquid composition；
C, second group powder liquid composition is added in first group glue composition, stirs 30min, be uniformly mixed；Then horizontal
Composition is ground to 5 microns of fineness on sand mill；Fineness is detected, is all filtered after qualification filling.
5. the preparation method of long-acting mosquito-driving muscid-type environmental protection coating material according to claim 4, it is characterised in that：In the method
The total amount of adding of clear water is 25-35 mass parts twice.