CN108727876A - A kind of preparation method for the filler promoting fishing lines intensity and rotproofness - Google Patents
A kind of preparation method for the filler promoting fishing lines intensity and rotproofness Download PDFInfo
- Publication number
- CN108727876A CN108727876A CN201810483951.7A CN201810483951A CN108727876A CN 108727876 A CN108727876 A CN 108727876A CN 201810483951 A CN201810483951 A CN 201810483951A CN 108727876 A CN108727876 A CN 108727876A
- Authority
- CN
- China
- Prior art keywords
- parts
- rotproofness
- montmorillonite
- fishing lines
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of preparation methods of the filler of promotion fishing lines intensity and rotproofness, include the following steps:(1)Cleaning treatment,(2)High-temperature process,(3)Modification,(4)It is dried.The present invention provides a kind of preparation methods of filler, and integrated artistic is simple, and reasonable standard is arranged in process, the characteristics such as corrosion resistant, heatproof, the intensity of fishing lines can be effectively promoted conducive to duplication and batch operation, filler stay in grade obtained, extend its service life, great application value.
Description
Technical field
The invention belongs to fishing lines processing and manufacturing technologies, and in particular to a kind of fishing lines intensity and rotproofness of being promoted
The preparation method of filler.
Background technology
Fishing lines is basic material common in fishing gear field, is initially mostly made of linen-cotton material, as people make it
With the continuous promotion and the continuous enhancing of production technology of characteristic, existing fishing lines is mostly Plastic artificial synthetic fiber,
The accounting of middle nylon fishing net line is larger.Although the usage amount of nylon fishing net line is larger, production and processing is more mature, with people
Continuous promotion for product demand so that the performance requirement produced and processed to it constantly enhances.
For qualities such as the intensity, corrosion resistant, the heatproofs that improve nylon fishing net line, now many techniques by add filler ingredient come
Improve, common filler has kaolin, attapulgite etc., although playing certain improvement, because filler grain is easy to
Reunite, dispersibility is bad, with the compatibility of high molecular material matrix it is bad, itself have a single function the problems such as, limit filler
Using effect.
Invention content
The purpose of the present invention is for existing problem, provide the filler of a kind of promotion fishing lines intensity and rotproofness
Preparation method.
The present invention is achieved by the following technical solutions:
A kind of preparation method for the filler promoting fishing lines intensity and rotproofness, includes the following steps:
(1)Cleaning treatment:
5 ~ 7min of immersion treatment in tartaric acid solution first is put into montmorillonite, then takes out to be put into sodium hydroxide solution and soak
Bubble 7 ~ 10min of processing, finally taking-up are spare after being rinsed one time with deionized water;
(2)High-temperature process:
By step(1)Montmorillonite after cleaning, which is put into high-temperature calcination stove, carries out calcination processing, is taken out after 1 ~ 2h spare;
(3)Modification:
A. by step(2)Montmorillonite that treated, which is put into ultraviolet irradiation instrument, carries out radiation treatment, is taken out after 25 ~ 30min
It is spare;
B. will operation a treated that montmorillonite is immersed in modification solution A, ultrasonic vibration handle take out after 1 ~ 2h it is spare;
The modification solution A by following parts by weight material composition:20 ~ 25 parts of polyoxylethylene abietates, 7 ~ 12 parts of metatitanic acids
Ester coupling agent, 4 ~ 8 parts of magnesium thiosulfates, 300 ~ 350 parts of deionized waters;
C. will operation b treated that montmorillonite is immersed in modification solution B, ultrasonic vibration handle take out after 2 ~ 3h it is spare;
The modification solution B by following parts by weight material composition:4 ~ 6 parts of nano-titanium dioxides, 3 ~ 5 parts of detergent alkylate sulphurs
Sour sodium, 2 ~ 4 parts of calcium stearates, 0.5 ~ 1 part of disodium ethylene diamine tetraacetate, 90 ~ 100 parts of deionized waters;
(4)It is dried:
By step(3)Montmorillonite that treated, which is put into drying box, is dried processing, is taken out after 1.5 ~ 2.5h.
Further, step(1)Described in tartaric acid solution mesotartaric acid mass fraction be 6 ~ 9%;The hydrogen-oxygen
The mass fraction for changing sodium hydroxide in sodium solution is 8 ~ 10%.
Further, step(2)Described in calcination processing when keep high-temperature calcination stove in temperature be 800 ~ 900 DEG C.
Further, step(3)Operate a described in radiation treatment when control ultraviolet irradiation instrument in power be 900 ~
1000W, the wavelength for controlling ultraviolet light are 260 ~ 320nm.
Further, step(3)The supersonic frequency for operating the ultrasonic vibration processing described in b is 180 ~ 200kHz.
Further, step(3)The supersonic frequency for operating the ultrasonic vibration processing described in c is 300 ~ 400kHz.
Further, step(3)The grain diameter for operating the nano-titanium dioxide described in c is 20 ~ 70nm.
Further, step(4)Described in drying process when control drying box in temperature be 83 ~ 88 DEG C.
The present invention provides a kind of preparation methods of filler, effectively improve the use characteristic of filler, enhance fishing net
The use quality of line is modified and is handled using montmorillonite as matrix composition, the cleaning treatment and high temperature first carried out
Calcination processing effectively improves the specific surface area and adsorption capacity of montmorillonite, lays a good foundation for subsequent processing, with laggard
Gone modification, radiation treatment first during which carried out to montmorillonite with ultraviolet light, improve montmorillonite surface group content and
Structure enhances its respond, then carries out immersion modification, modification with the modification solution A of formulated
Two kinds of ingredients of polyoxylethylene abietate and magnesium thiosulfate in solution A can penetrate into infiltration to the interlayer of montmorillonite, weaken
Its lamella mutual hydrogen bond and polarity effect are subsequent place to which create the effect of swollen, expanding interfloor distance
Reason is laid a good foundation, and the titanate coupling agent of addition can effectively improve the surface characteristic of montmorillonite, improve itself and height
Compatibility between molecular chaperones and remaining ingredient has then been carried out impregnating modification again with modification solution B, at modification
In reason solution B the nano-titanium dioxide ingredient that adds can the intercalated grafted interlayer to montmorillonite, improve montmorillonite particle
Corrosion resistant, resistance to mild granule stability, and the specific surface area and adsorption capacity of montmorillonite are enhanced, improve what filling used
Effect.
The present invention has the following advantages compared with prior art:
The present invention provides a kind of preparation methods of filler, and integrated artistic is simple, and reasonable standard is arranged in process, are conducive to replicate
And batch operation, filler stay in grade obtained can effectively promote the characteristics such as corrosion resistant, heatproof, the intensity of fishing lines, extend
Its service life, great application value.
Specific implementation mode
Embodiment 1
A kind of preparation method for the filler promoting fishing lines intensity and rotproofness, includes the following steps:
(1)Cleaning treatment:
Immersion treatment 5min in tartaric acid solution first is put into montmorillonite, then takes out to be put into sodium hydroxide solution and impregnate
7min is handled, finally taking-up is spare after being rinsed one time with deionized water;
(2)High-temperature process:
By step(1)Montmorillonite after cleaning, which is put into high-temperature calcination stove, carries out calcination processing, is taken out after 1h spare;
(3)Modification:
A. by step(2)Montmorillonite that treated, which is put into ultraviolet irradiation instrument, carries out radiation treatment, is taken out after 25min standby
With;
B. will operation a treated that montmorillonite is immersed in modification solution A, taken out after ultrasonic vibration processing 1h spare;Institute
The modification solution A stated by following parts by weight material composition:20 parts of polyoxylethylene abietates, 7 parts of titanate coupling agents,
4 parts of magnesium thiosulfates, 300 parts of deionized waters;
C. will operation b treated that montmorillonite is immersed in modification solution B, taken out after ultrasonic vibration processing 2h spare;Institute
The modification solution B stated by following parts by weight material composition:4 parts of nano-titanium dioxides, 3 parts of neopelexes, 2
Part calcium stearate, 0.5 part of disodium ethylene diamine tetraacetate, 90 parts of deionized waters;
(4)It is dried:
By step(3)Montmorillonite that treated, which is put into drying box, is dried processing, is taken out after 1.5h.
Further, step(1)Described in tartaric acid solution mesotartaric acid mass fraction be 6%;The hydroxide
The mass fraction of sodium hydroxide is 8% in sodium solution.
Further, step(2)Described in calcination processing when keep high-temperature calcination stove in temperature be 800 DEG C.
Further, step(3)Operation a described in radiation treatment when control ultraviolet irradiation instrument in power be
900W, the wavelength for controlling ultraviolet light are 260 ~ 320nm.
Further, step(3)The supersonic frequency for operating the ultrasonic vibration processing described in b is 180kHz.
Further, step(3)The supersonic frequency for operating the ultrasonic vibration processing described in c is 300kHz.
Further, step(3)The grain diameter for operating the nano-titanium dioxide described in c is 20 ~ 70nm.
Further, step(4)Described in drying process when control drying box in temperature be 83 DEG C.
Embodiment 2
A kind of preparation method for the filler promoting fishing lines intensity and rotproofness, includes the following steps:
(1)Cleaning treatment:
Immersion treatment 6min in tartaric acid solution first is put into montmorillonite, then takes out to be put into sodium hydroxide solution and impregnate
9min is handled, finally taking-up is spare after being rinsed one time with deionized water;
(2)High-temperature process:
By step(1)Montmorillonite after cleaning, which is put into high-temperature calcination stove, carries out calcination processing, is taken out after 1.5h spare;
(3)Modification:
A. by step(2)Montmorillonite that treated, which is put into ultraviolet irradiation instrument, carries out radiation treatment, is taken out after 28min standby
With;
B. will operation a treated that montmorillonite is immersed in modification solution A, taken out after ultrasonic vibration processing 1.6h spare;
The modification solution A by following parts by weight material composition:23 parts of polyoxylethylene abietates, 10 parts of titanate esters couplings
Agent, 6 parts of magnesium thiosulfates, 330 parts of deionized waters;
C. will operation b treated that montmorillonite is immersed in modification solution B, taken out after ultrasonic vibration processing 2.5h spare;
The modification solution B by following parts by weight material composition:5 parts of nano-titanium dioxides, 4 parts of dodecyl benzene sulfonic acid
Sodium, 3 parts of calcium stearates, 0.8 part of disodium ethylene diamine tetraacetate, 95 parts of deionized waters;
(4)It is dried:
By step(3)Montmorillonite that treated, which is put into drying box, is dried processing, is taken out after 2h.
Further, step(1)Described in tartaric acid solution mesotartaric acid mass fraction be 8%;The hydroxide
The mass fraction of sodium hydroxide is 9% in sodium solution.
Further, step(2)Described in calcination processing when keep high-temperature calcination stove in temperature be 860 DEG C.
Further, step(3)Operation a described in radiation treatment when control ultraviolet irradiation instrument in power be
970W, the wavelength for controlling ultraviolet light are 260 ~ 320nm.
Further, step(3)The supersonic frequency for operating the ultrasonic vibration processing described in b is 190kHz.
Further, step(3)The supersonic frequency for operating the ultrasonic vibration processing described in c is 360kHz.
Further, step(3)The grain diameter for operating the nano-titanium dioxide described in c is 20 ~ 70nm.
Further, step(4)Described in drying process when control drying box in temperature be 85 DEG C.
Embodiment 3
A kind of preparation method for the filler promoting fishing lines intensity and rotproofness, includes the following steps:
(1)Cleaning treatment:
Immersion treatment 7min in tartaric acid solution first is put into montmorillonite, then takes out to be put into sodium hydroxide solution and impregnate
10min is handled, finally taking-up is spare after being rinsed one time with deionized water;
(2)High-temperature process:
By step(1)Montmorillonite after cleaning, which is put into high-temperature calcination stove, carries out calcination processing, is taken out after 2h spare;
(3)Modification:
A. by step(2)Montmorillonite that treated, which is put into ultraviolet irradiation instrument, carries out radiation treatment, is taken out after 30min standby
With;
B. will operation a treated that montmorillonite is immersed in modification solution A, taken out after ultrasonic vibration processing 2h spare;Institute
The modification solution A stated by following parts by weight material composition:25 parts of polyoxylethylene abietates, 12 parts of titanate esters couplings
Agent, 8 parts of magnesium thiosulfates, 350 parts of deionized waters;
C. will operation b treated that montmorillonite is immersed in modification solution B, taken out after ultrasonic vibration processing 3h spare;Institute
The modification solution B stated by following parts by weight material composition:6 parts of nano-titanium dioxides, 5 parts of neopelexes, 4
Part calcium stearate, 1 part of disodium ethylene diamine tetraacetate, 100 parts of deionized waters;
(4)It is dried:
By step(3)Montmorillonite that treated, which is put into drying box, is dried processing, is taken out after 2.5h.
Further, step(1)Described in tartaric acid solution mesotartaric acid mass fraction be 9%;The hydroxide
The mass fraction of sodium hydroxide is 10% in sodium solution.
Further, step(2)Described in calcination processing when keep high-temperature calcination stove in temperature be 900 DEG C.
Further, step(3)Operation a described in radiation treatment when control ultraviolet irradiation instrument in power be
1000W, the wavelength for controlling ultraviolet light are 260 ~ 320nm.
Further, step(3)The supersonic frequency for operating the ultrasonic vibration processing described in b is 200kHz.
Further, step(3)The supersonic frequency for operating the ultrasonic vibration processing described in c is 400kHz.
Further, step(3)The grain diameter for operating the nano-titanium dioxide described in c is 20 ~ 70nm.
Further, step(4)Described in drying process when control drying box in temperature be 88 DEG C.
Comparative example 1
This comparative example 1 compared with Example 2, eliminates step(3)Operation b processing in modification, side in addition to this
Method step all same.
Comparative example 2
This comparative example 2 compared with Example 2, eliminates step(3)Operation c processing in modification, side in addition to this
Method step all same.
Comparative example 3
This comparative example 3 compared with Example 2, eliminates step(3)The whole operation of modification, method step in addition to this
Rapid all same.
Control group
Existing commercially available montmorillonite filler.
In order to compare effect of the present invention, by above-described embodiment 2, comparative example 1, comparative example 2, comparative example 3,
Control group corresponds to filler ingredient obtained in the manufacture of nylon fishing net line, the weight percent of addition to be 7%, after the completion
To nylon fishing net line made from each group(Filament diameter specification is 0.20 ± 0.01mm)It is tested for the property, specific correction data
As shown in table 1 below:
Table 1
Note:Fracture strength described in upper table 1 is measured by Britain INSTRON-4466 type strength testers, and when test controls
Temperature condition is 20 ± 2 DEG C, and relative humidity control is 65 ± 5%, and the speed for controlling stretching is 330mm/min, and the length of monofilament is
600mm;The knot strength retention is that the nylon fishing net line after each group alignment processing is put in temperature as 35 DEG C, relative humidity
After exposure under 85% natural conditions 12 months, tests it and tie the conservation rate of strength, to react the anti-aging characteristic of its corrosion resistant.
Filler produced by the present invention can effectively promote the intensity of fishing lines, the anti-aging product of corrosion resistant it can be seen from upper table 1
Matter, hence it is evident that improve the use characteristic of fishing lines, there is good application value.
Claims (8)
1. a kind of preparation method for the filler promoting fishing lines intensity and rotproofness, which is characterized in that include the following steps:
(1)Cleaning treatment:
5 ~ 7min of immersion treatment in tartaric acid solution first is put into montmorillonite, then takes out to be put into sodium hydroxide solution and soak
Bubble 7 ~ 10min of processing, finally taking-up are spare after being rinsed one time with deionized water;
(2)High-temperature process:
By step(1)Montmorillonite after cleaning, which is put into high-temperature calcination stove, carries out calcination processing, is taken out after 1 ~ 2h spare;
(3)Modification:
A. by step(2)Montmorillonite that treated, which is put into ultraviolet irradiation instrument, carries out radiation treatment, is taken out after 25 ~ 30min
It is spare;
B. will operation a treated that montmorillonite is immersed in modification solution A, ultrasonic vibration handle take out after 1 ~ 2h it is spare;
The modification solution A by following parts by weight material composition:20 ~ 25 parts of polyoxylethylene abietates, 7 ~ 12 parts of metatitanic acids
Ester coupling agent, 4 ~ 8 parts of magnesium thiosulfates, 300 ~ 350 parts of deionized waters;
C. will operation b treated that montmorillonite is immersed in modification solution B, ultrasonic vibration handle take out after 2 ~ 3h it is spare;
The modification solution B by following parts by weight material composition:4 ~ 6 parts of nano-titanium dioxides, 3 ~ 5 parts of detergent alkylate sulphurs
Sour sodium, 2 ~ 4 parts of calcium stearates, 0.5 ~ 1 part of disodium ethylene diamine tetraacetate, 90 ~ 100 parts of deionized waters;
(4)It is dried:
By step(3)Montmorillonite that treated, which is put into drying box, is dried processing, is taken out after 1.5 ~ 2.5h.
2. a kind of preparation method of filler promoting fishing lines intensity and rotproofness according to claim 1, feature exist
In step(1)Described in tartaric acid solution mesotartaric acid mass fraction be 6 ~ 9%;Hydrogen-oxygen in the sodium hydroxide solution
The mass fraction for changing sodium is 8 ~ 10%.
3. a kind of preparation method of filler promoting fishing lines intensity and rotproofness according to claim 1, feature exist
In step(2)Described in calcination processing when keep high-temperature calcination stove in temperature be 800 ~ 900 DEG C.
4. a kind of preparation method of filler promoting fishing lines intensity and rotproofness according to claim 1, feature exist
In step(3)Power when operating the radiation treatment described in a in control ultraviolet irradiation instrument is 900 ~ 1000W, and control is ultraviolet
The wavelength of line is 260 ~ 320nm.
5. a kind of preparation method of filler promoting fishing lines intensity and rotproofness according to claim 1, feature exist
In step(3)The supersonic frequency for operating the ultrasonic vibration processing described in b is 180 ~ 200kHz.
6. a kind of preparation method of filler promoting fishing lines intensity and rotproofness according to claim 1, feature exist
In step(3)The supersonic frequency for operating the ultrasonic vibration processing described in c is 300 ~ 400kHz.
7. a kind of preparation method of filler promoting fishing lines intensity and rotproofness according to claim 1, feature exist
In step(3)The grain diameter for operating the nano-titanium dioxide described in c is 20 ~ 70nm.
8. a kind of preparation method of filler promoting fishing lines intensity and rotproofness according to claim 1, feature exist
In step(4)Described in drying process when control drying box in temperature be 83 ~ 88 DEG C.