CN108726966A - A kind of material and preparation method thereof dedicated for making sculpture - Google Patents
A kind of material and preparation method thereof dedicated for making sculpture Download PDFInfo
- Publication number
- CN108726966A CN108726966A CN201810662721.7A CN201810662721A CN108726966A CN 108726966 A CN108726966 A CN 108726966A CN 201810662721 A CN201810662721 A CN 201810662721A CN 108726966 A CN108726966 A CN 108726966A
- Authority
- CN
- China
- Prior art keywords
- parts
- dedicated
- sculpture
- mixing
- clay
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of dedicated for making the material of sculpture, and the material dedicated for making sculpture is made of the component of following parts by weight：45-68 parts of clay, 15-25 parts of nanometer agstone, 10-22 parts of magnesia, 1-5 parts of ammonium dihydrogen phosphate, 10-16 parts of polyvinyl alcohol, 1-3 parts of palm oil, 1-3 parts of graphene oxide, 0.6-1.5 parts of prodan, 1-4 parts of alum, 2-5 parts of calcium lignosulfonate, 0.5-1.6 parts of isobutyl triethoxy silane, 0.3-0.6 parts of sodium tetraborate, 0.1-0.5 parts of preservative.Hardness is high after the material solidification dedicated for making sculpture in the present invention, it is possible to prevente effectively from sculpture cracks in dry hardening process.
Description
Technical field
The present invention relates to clay sculpture field of material technology, and in particular to a kind of material and its preparation dedicated for making sculpture
Method.
Background technology
Sculpture be moulded for beautifying city or carved for commemoration meaning, the sight with certain implied meaning, symbol or pictograph
Appreciate object and souvenir.Sculpture is one kind of plastic arts, is referred to various plastic materials or the hard material creation that can be carved, can carve
Visual, the artistic image that can touch for providing certain space, so as to reflection social life, art of expression man aesthetic method, examine
The art of U.S. emotion, aesthetic ideal.Various auxiliary agents are added using clay as raw material in traditional carving material, water use regulation viscosity,
Water-saving effect is poor, is unfavorable for improving clay sculpture material plasticity, and the sculpted surface caused by inside and outside moisture evaporation speed differs
Cracking, and then influence product aesthetics.
Invention content
The purpose of the present invention is to provide a kind of dedicated for making the material and preparation method thereof of sculpture, can be effective
The technical issues of solving to be previously mentioned in background technology.
To achieve the above object, the present invention provides the following technical solutions：
A kind of material dedicated for making sculpture is made of the component of following parts by weight：45-68 parts of clay, nanometer
15-25 parts of agstone, 10-22 parts of magnesia, 1-5 parts of ammonium dihydrogen phosphate, 10-16 parts of polyvinyl alcohol, 1-3 parts of palm oil, oxygen
1-3 parts of graphite alkene, 0.6-1.5 parts of prodan, 1-4 parts of alum, 2-5 parts of calcium lignosulfonate, three ethoxy of isobutyl group
0.5-1.6 parts of base silane, 0.3-0.6 parts of sodium tetraborate, 0.1-0.5 parts of preservative.
Preferably, the material dedicated for making sculpture is made of the component of following parts by weight：60 parts of clay,
22 parts of agstone of nanometer, 14 parts of magnesia, 3 parts of ammonium dihydrogen phosphate, 13 parts of polyvinyl alcohol, 1 part of palm oil, graphene oxide 2
Part, 1 part of prodan, 3 parts of alum, 5 parts of calcium lignosulfonate, 0.8 part of isobutyl triethoxy silane, sodium tetraborate
0.5 part, 0.1 part of preservative.
Preferably, the material dedicated for making sculpture is made of the component of following parts by weight：55 parts of clay,
24 parts of agstone of nanometer, 18 parts of magnesia, 3 parts of ammonium dihydrogen phosphate, 12 parts of polyvinyl alcohol, 3 parts of palm oil, graphene oxide
1.5 parts, 1.2 parts of prodan, 2.5 parts of alum, 3 parts of calcium lignosulfonate, 1.3 parts of isobutyl triethoxy silane, four
0.6 part of Boratex, 0.3 part of preservative.
The preparation method of the material dedicated for making sculpture comprising following steps：
(1) each raw material component is weighed according to weight part ratio；
(2) clay, nanometer agstone and graphene oxide are dissolved in water, obtain first material after mixing；
(3) polyvinyl alcohol is dissolved in water, obtains second material after mixing；
(4) ammonium dihydrogen phosphate and magnesia are dissolved in water, obtain third material after mixing；
(5) after mixing first material, second material and third material, palm oil, prodan, aluminum sulfate are added
Potassium, calcium lignosulfonate, isobutyl triethoxy silane, sodium tetraborate and preservative are uniformly mixed, you can.
Compared with prior art, the beneficial effects of the invention are as follows：
Magnesia, ammonium dihydrogen phosphate, oxidation stone have been especially added in the material dedicated for making sculpture in the present invention
The raw materials such as black alkene, prodan, alum, sodium tetraborate and preservative make this between each raw material component by reasonably combined
Hardness is high after carving material solidification in invention, it is possible to prevente effectively from sculpture cracks in dry hardening process.
Specific implementation mode
With reference to the embodiment technical solution that the present invention will be described in detail, but protection domain is not limited thereto.
Embodiment one：
A kind of material dedicated for making sculpture is made of the component of following parts by weight：45 parts of clay, nanometer stone
15 parts of limestone flour, 10 parts of magnesia, 1 part of ammonium dihydrogen phosphate, 10 parts of polyvinyl alcohol, 1 part of palm oil, 1 part of graphene oxide, fluorine silicon
0.6 part of sour sodium, 1 part of alum, 2 parts of calcium lignosulfonate, 0.5 part of isobutyl triethoxy silane, 0.3 part of sodium tetraborate,
0.1 part of preservative.
The preparation method of the material dedicated for making sculpture comprising following steps：
(1) each raw material component is weighed according to weight part ratio；
(2) clay, nanometer agstone and graphene oxide are dissolved in water, obtain first material after mixing；
(3) polyvinyl alcohol is dissolved in water, obtains second material after mixing；
(4) ammonium dihydrogen phosphate and magnesia are dissolved in water, obtain third material after mixing；
(5) after mixing first material, second material and third material, palm oil, prodan, aluminum sulfate are added
Potassium, calcium lignosulfonate, isobutyl triethoxy silane, sodium tetraborate and preservative are uniformly mixed, you can.
Embodiment two：
A kind of material dedicated for making sculpture is made of the component of following parts by weight：68 parts of clay, nanometer stone
25 parts of limestone flour, 22 parts of magnesia, 5 parts of ammonium dihydrogen phosphate, 16 parts of polyvinyl alcohol, 3 parts of palm oil, 3 parts of graphene oxide, fluorine silicon
1.5 parts of sour sodium, 4 parts of alum, 5 parts of calcium lignosulfonate, 1.6 parts of isobutyl triethoxy silane, 0.6 part of sodium tetraborate,
0.5 part of preservative.
The preparation method of the material dedicated for making sculpture comprising following steps：
(1) each raw material component is weighed according to weight part ratio；
(2) clay, nanometer agstone and graphene oxide are dissolved in water, obtain first material after mixing；
(3) polyvinyl alcohol is dissolved in water, obtains second material after mixing；
(4) ammonium dihydrogen phosphate and magnesia are dissolved in water, obtain third material after mixing；
(5) after mixing first material, second material and third material, palm oil, prodan, aluminum sulfate are added
Potassium, calcium lignosulfonate, isobutyl triethoxy silane, sodium tetraborate and preservative are uniformly mixed, you can.
Embodiment three：
A kind of material dedicated for making sculpture is made of the component of following parts by weight：60 parts of clay, nanometer stone
22 parts of limestone flour, 14 parts of magnesia, 3 parts of ammonium dihydrogen phosphate, 13 parts of polyvinyl alcohol, 1 part of palm oil, 2 parts of graphene oxide, fluorine silicon
1 part of sour sodium, 3 parts of alum, 5 parts of calcium lignosulfonate, 0.8 part of isobutyl triethoxy silane, 0.5 part of sodium tetraborate are prevented
0.1 part of rotten agent.
The preparation method of the material dedicated for making sculpture comprising following steps：
(1) each raw material component is weighed according to weight part ratio；
(2) clay, nanometer agstone and graphene oxide are dissolved in water, obtain first material after mixing；
(3) polyvinyl alcohol is dissolved in water, obtains second material after mixing；
(4) ammonium dihydrogen phosphate and magnesia are dissolved in water, obtain third material after mixing；
(5) after mixing first material, second material and third material, palm oil, prodan, aluminum sulfate are added
Potassium, calcium lignosulfonate, isobutyl triethoxy silane, sodium tetraborate and preservative are uniformly mixed, you can.
Example IV：
A kind of material dedicated for making sculpture is made of the component of following parts by weight：55 parts of clay, nanometer stone
24 parts of limestone flour, 18 parts of magnesia, 3 parts of ammonium dihydrogen phosphate, 12 parts of polyvinyl alcohol, 3 parts of palm oil, 1.5 parts of graphene oxide, fluorine
1.2 parts of sodium metasilicate, 2.5 parts of alum, 3 parts of calcium lignosulfonate, 1.3 parts of isobutyl triethoxy silane, sodium tetraborate 0.6
Part, 0.3 part of preservative.
The preparation method of the material dedicated for making sculpture comprising following steps：
(1) each raw material component is weighed according to weight part ratio；
(2) clay, nanometer agstone and graphene oxide are dissolved in water, obtain first material after mixing；
(3) polyvinyl alcohol is dissolved in water, obtains second material after mixing；
(4) ammonium dihydrogen phosphate and magnesia are dissolved in water, obtain third material after mixing；
(5) after mixing first material, second material and third material, palm oil, prodan, aluminum sulfate are added
Potassium, calcium lignosulfonate, isobutyl triethoxy silane, sodium tetraborate and preservative are uniformly mixed, you can.
Embodiment five：
A kind of material dedicated for making sculpture is made of the component of following parts by weight：65 parts of clay, nanometer stone
21 parts of limestone flour, 10 parts of magnesia, 1 part of ammonium dihydrogen phosphate, 12 parts of polyvinyl alcohol, 1.8 parts of palm oil, 2.5 parts of graphene oxide,
1.3 parts of prodan, 2 parts of alum, 3 parts of calcium lignosulfonate, 1.5 parts of isobutyl triethoxy silane, sodium tetraborate 0.3
Part, 0.3 part of preservative.
The preparation method of the material dedicated for making sculpture comprising following steps：
(1) each raw material component is weighed according to weight part ratio；
(2) clay, nanometer agstone and graphene oxide are dissolved in water, obtain first material after mixing；
(3) polyvinyl alcohol is dissolved in water, obtains second material after mixing；
(4) ammonium dihydrogen phosphate and magnesia are dissolved in water, obtain third material after mixing；
(5) after mixing first material, second material and third material, palm oil, prodan, aluminum sulfate are added
Potassium, calcium lignosulfonate, isobutyl triethoxy silane, sodium tetraborate and preservative are uniformly mixed, you can.
Finally illustrate, the above examples are only used to illustrate the technical scheme of the present invention and are not limiting, although with reference to compared with
Good embodiment describes the invention in detail, it will be understood by those of ordinary skill in the art that, it can be to the skill of the present invention
Art scheme is modified or replaced equivalently, and without departing from the objective and range of the technical program, should all be covered in the present invention
Right in.
Claims (4)
1. it is a kind of dedicated for make sculpture material, which is characterized in that it is described dedicated for make sculpture material be by with
The component of lower parts by weight is made：45-68 parts of clay, 15-25 parts of nanometer agstone, 10-22 parts of magnesia, ammonium dihydrogen phosphate
1-5 parts, 10-16 parts of polyvinyl alcohol, 1-3 parts of palm oil, 1-3 parts of graphene oxide, 0.6-1.5 parts of prodan, alum
1-4 parts, 2-5 parts of calcium lignosulfonate, 0.5-1.6 parts of isobutyl triethoxy silane, 0.3-0.6 parts of sodium tetraborate, preservative
0.1-0.5 parts.
2. a kind of material dedicated for making sculpture according to claim 1, which is characterized in that described dedicated for system
The material for making sculpture is made of the component of following parts by weight：60 parts of clay, 22 parts of nanometer agstone, 14 parts of magnesia,
3 parts of ammonium dihydrogen phosphate, 13 parts of polyvinyl alcohol, 1 part of palm oil, 2 parts of graphene oxide, 1 part of prodan, 3 parts of alum, wood
5 parts of quality sulfoacid calcium, 0.8 part of isobutyl triethoxy silane, 0.5 part of sodium tetraborate, 0.1 part of preservative.
3. a kind of material dedicated for making sculpture according to claim 1, which is characterized in that described dedicated for system
The material for making sculpture is made of the component of following parts by weight：55 parts of clay, 24 parts of nanometer agstone, 18 parts of magnesia,
3 parts of ammonium dihydrogen phosphate, 12 parts of polyvinyl alcohol, 3 parts of palm oil, 1.5 parts of graphene oxide, 1.2 parts of prodan, alum
2.5 parts, 3 parts of calcium lignosulfonate, 1.3 parts of isobutyl triethoxy silane, 0.6 part of sodium tetraborate, 0.3 part of preservative.
4. the preparation method of the material as claimed in any one of claims 1-3 dedicated for making sculpture, which is characterized in that
Include the following steps：
(1) each raw material component is weighed according to weight part ratio；
(2) clay, nanometer agstone and graphene oxide are dissolved in water, obtain first material after mixing；
(3) polyvinyl alcohol is dissolved in water, obtains second material after mixing；
(4) ammonium dihydrogen phosphate and magnesia are dissolved in water, obtain third material after mixing；
(5) after mixing first material, second material and third material, palm oil, prodan, alum, wood are added
Quality sulfoacid calcium, isobutyl triethoxy silane, sodium tetraborate and preservative are uniformly mixed, you can.