CN108716466B - 隔热耐磨的空调压缩机叶片 - Google Patents
隔热耐磨的空调压缩机叶片 Download PDFInfo
- Publication number
- CN108716466B CN108716466B CN201810507028.2A CN201810507028A CN108716466B CN 108716466 B CN108716466 B CN 108716466B CN 201810507028 A CN201810507028 A CN 201810507028A CN 108716466 B CN108716466 B CN 108716466B
- Authority
- CN
- China
- Prior art keywords
- regulating roller
- temperature
- heat
- solution
- blade
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开一种隔热耐磨的空调压缩机叶片,包括叶片本体,叶片本体的一端开设有调节辊容纳槽,该调节辊容纳槽内水平设有调节辊,调节辊容纳槽的槽底正对开设有两个滑槽,两个滑槽内活动均穿设调节辊连接板,两个调节辊连接板之间连接有调节辊,调节辊的外表面覆盖有高隔热耐磨复合膜。与现有技术相比,本发明采用叶片本体与调节辊相结合的方式,将空调压缩机叶片与气缸滑槽之间的摩擦由混合摩擦变为滚动摩擦,表面覆盖有性能优异的集强韧与润滑于一体的高隔热耐磨复合膜,突破了中低温范围内使用的局限,陶瓷隔热层为表面纤维增强镍基镀层提供了良好的支撑和界面结合,降低了工件表面的导热系数,利用静电纺氧化锆纳米纤维对Ni‑P合金镀层进行增强。
Description
技术领域
本发明涉及压缩机领域,特别涉及一种隔热耐磨的空调压缩机叶片。
背景技术
压缩机作为空调系统中的核心组成部件,其内部关键零部件常处于高温、高压和高速运转状态,而新型环保冷媒在压缩机系统中的运用及压缩机朝着更高效和更高负荷方向的发展进一步加剧了压缩机关键零部件材料的摩擦磨损。传统的封闭式旋转压缩机中滑片的前端保持与环状活塞外缘紧密接触,环状活塞在气缸的工作腔内公转和自转时,滑片作径向往复运动,滑片与气缸滑片槽两侧之间的摩擦为滑动摩擦,滑片的前端与环状活塞外缘之间的摩擦为滑动及滚动混合摩擦,上述几种摩擦使压缩机功耗增大,电效率降低。汽车空调压缩机零部件通常采用轻量化设计来有效提高整机运行效率,然而,以铝质合金为代表的轻质合金取代压缩机铁质零部件仍面临严重摩擦磨损及腐蚀等问题,其中旋叶式铝合金叶片与滑槽及叶片顶部与缸体间的摩擦磨损严重影响着压缩机的可靠性和寿命。目前,使用的以Si为主要添加元素的易铸造性铝合金制的压缩机叶轮中,在使用中易产生变形、进而疲劳破坏的不良情况,不可能继续正常的旋转;在铝合金叶片表面构筑电镀金属基涂层,依然存在摩擦系数较大的缺点,从而导致较大的压缩机摩擦功耗。尤其在贫油、冷启动和间歇运行等工况下以及磨合初期,直接沉积有金属陶瓷复合镀层或者金属氮化物镀层的压缩机摩擦副之间发生冷焊或咬死的几率很大,配副间严重的磨损致使其密封功能失效。
发明内容
为解决以上技术问题,本发明提供隔热耐磨的空调压缩机叶片,以解决提高叶轮在高速运转时的稳定性、可靠性,延长服役寿命和减小功耗,减少在高冲击性的热负荷和机械负荷下,摩擦热向部件内部的传导,使其具有高承载强度、低摩擦系数和优异的抗磨损抗腐蚀性能的问题。
本发明采用的技术方案如下:一种隔热耐磨的空调压缩机叶片,关键在于:包括叶片本体,所述叶片本体的一端开设有调节辊容纳槽,该调节辊容纳槽内水平设有调节辊,所述调节辊容纳槽的槽底正对开设有两个滑槽,两个所述滑槽内活动均穿设调节辊连接板,两个所述调节辊连接板之间连接有所述调节辊;
所述叶片本体和所述调节辊的外表面覆盖有高隔热耐磨复合膜,所述复合膜包括纤维增强镍基镀层和陶瓷隔热层,所述陶瓷隔热层涂覆在叶轮叶片表面,所述纤维增强镍基镀层镀覆在所述陶瓷隔热层表面;
所述纤维增强镍基镀层为掺杂纳米纤维的Ni-P合金薄膜层,其中纳米纤维为金属氧化物纤维;所述陶瓷隔热层由以下质量份数的原料组成:氧化锆纳米微球45-58份、无机结合剂8-15份、聚乙烯醇3-10份。
优选的,所述陶瓷隔热层的质量份数为氧化锆纳米微球55份、无机结合剂12份、聚乙烯醇7份。
优选的,所述金属氧化物纤维采用以下方法获得:将聚乙烯吡咯烷酮溶于无水乙醇得到质量分数为10%~20%的透明溶液A,然后在透明溶液A中依次搅拌加入二甲基亚砜和氧氯化锆粉体后,超声处理30min,得到纺丝前驱体;将所述纺丝前驱体吸入针管后,将其固定在静电纺丝设备上,在环境温度为15℃~25℃,环境湿度为35%~60%,电压为20~40KV的条件下,进行静电纺丝得到原生纤维;将所述原生纤维在500℃~800℃下进行煅烧2h,然后自然降温至室温得到所述金属氧化物纳米纤维。
优选的,所述氧化锆纳米微球采用以下方法获得:将葡萄糖溶解于去离子水中,配置成摩尔浓度为0.5-1.5mol/L的溶液,置于水热反应釜中140-180℃进行反应,反应时间为8-20h;反应完成后,将所得混合液离心分离,并使用去离子水和无水乙醇分别洗涤,在干燥箱中干燥24h,即得碳微球;将所述碳微球加入摩尔浓度为0.1mol/L的氧氯化锆溶液中后,超声处理0.5~1h后搅拌滴加氨水,调节pH值至7,得到稳定溶胶,将得到的稳定溶胶继续超声处理0.5~1h,超声处理后,将分层的溶液离心分离,得到核壳微粒,将所得核壳微粒分别用去离子水和无水乙醇洗涤,在干燥箱中干燥12h后,然后在500℃~800℃下进行煅烧1h得到氧化锆纳米微球。
优选的,所述无机结合剂采用以下方法获得:将磷酸与水混合得到质量分数为40%~45%磷酸溶液,然后将温度升高到110~120℃后,依次加入氢氧化铝和氧化镁,反应0.5~1h,得到所述无机结合剂;所述氧化铝和磷酸的Al/P摩尔比为(0.5~1):1,所述氧化镁的加入量为氢氧化铝与磷酸质量总和的1.1~1.6%。
优选的,所述纤维增强镍基镀层的厚度为2~5μm,所述陶瓷隔热层的厚度为15~25μm。
优选的,所述滑槽内设有复位弹簧,所述复位弹簧的一端与所述滑槽的槽底固定连接,所述复位弹簧的一端与所述调节辊连接板的一端固定连接,所述调节辊连接板的另一端穿出所述调节辊容纳槽。
优选的,两个所述滑槽分别靠近所述调节辊容纳槽的槽壁设置,所述调节辊的外辊径与所述调节辊容纳槽的内槽宽相同。
优选的,所述叶片本体、所述调节辊连接板和所述调节辊(6)由Ni-Cr-Mo铸铁或添加了0.15~0.45wt%的磷的Ni-Cr-Mo铸铁形成,或者由铸铁或钢材形成。
一种隔热耐磨的空调压缩机叶片的制备方法,关键在于按以下步骤进行:
步骤一、金属工件表面预处理:将叶片本体和所述调节辊表面清洗、除油;
步骤二、涂覆陶瓷隔热层:将氧化锆纳米微球、无机结合剂和聚乙烯醇混合搅拌后,调制成料浆,然后将料浆涂覆在经过步骤一预处理后的金属工件表面,然后将涂覆料浆的金属工件进行干燥后置入气体保护炉或真空炉中,进行烧结处理,烧结处理条件为以8~15℃/min的速率升温至400~450℃,保温4~8min,再以6~10℃/min的速率从400~450℃升温至900~1000℃,接着以3~8℃/min的升温速度从900~1000℃升温至1050~1150℃,保温8~50min后,冷至室温,形成陶瓷隔热层;
步骤三、化学镀纤维增强镍基镀层:将步骤二处理后的金属工件置于装有氯化钯、盐酸、水的活化液中进行活化,然后将活化后的金属工件用去离子水冲洗,接着将冲洗后的金属工件置于装有硫酸镍浓度为200~300g/L、硫酸钴的浓度为25~40g/L,次磷酸钠的浓度为20~35g/L、乳酸的浓度为18~28g/L、丙酸的浓度为3~10g/L、无水乙酸钠的浓度为15~22g/L、硫脲的浓度为0.5~3g/L、十二烷基硫酸钠的浓度为5~15g/L和氧化锆纳米纤维的浓度为10~40g/L,在进行化学镀过程中,调节机械搅拌速度为500~1200r/min,保持镀液的pH值为5~7,保持镀液温度为70~90℃,在陶瓷隔热层表面镀覆形成纤维增强镍基镀层;
步骤四、热处理:将步骤三处理后的金属工件放入电阻炉中进行保温热处理,然后随炉冷却,得到覆有高隔热耐磨复合膜的金属工件。
步骤五、将步骤四处理后的叶片本体、调节辊与调节辊连接板、复位弹簧进行组装,得到成品。
对本发明提供的隔热耐磨的空调压缩机叶片进行如下测试:
(1)结构和成分测试:
用JSM-5600LV型扫描电子显微镜(SEM)观察本发明的空调压缩机叶片表面复合薄膜的表面微观形貌,用JSM-5600LV型扫描电子显微镜(SEM)观察本发明中氧化锆纳米纤维的微观形貌;
测试结果表明:复合薄膜表面致密光亮,无针孔、气泡,Ni-P晶粒相互紧密接触形成致密的、类似球晶堆积的沉积镀层;化学镀纤维增强镍基镀层中氧化锆纳米纤维的直径为100nm左右,且形貌均整,呈网状分布。
(2)摩擦性能测试
采用CSM摩擦磨损试验机对本发明空调压缩机叶片表面复合薄膜的干摩擦系数和磨损寿命进行评价,具体实验条件为:摩擦实验均采用球-盘往复滑动方式,摩擦对偶球为Φ3mm的GCr15钢球,滑动速度为0.05m/s,载荷为10N;
测试结果表明:(i)传统的沉积有金属镍基陶瓷镀层的压缩机零部件表面干摩擦系数变化范围为0.5~0.7,并伴随着较大幅度的波动。而沉积有本发明复合薄膜的空调压缩机叶片表面干摩擦系数稳定保持在0.04~0.06间,显示出了良好的自润滑性能,在压缩机冷启动等贫油工况能够表现出有效的防护作用;
(ii)本发明空调压缩机叶片表面复合薄膜的耐磨性是单纯镍基镀层或传统掺杂纳米陶瓷粉体镍基复合镀层的3~6倍。
(3)导热性能测试
采用DRL-III导热系数测试仪对本发明空调压缩机叶片表面复合薄膜的导热性能进行评价;
测试结果表明:陶瓷隔热层可以有效降低空调压缩机叶轮表明的导热系数,可以有效的阻挡热冲击对工件内部造成的热损伤,保护内部基体并延长其使用寿命,氧化锆纳米微球的引入为陶瓷隔热层提供大量球形空穴,因而空调压缩机叶片表面的导热系数比涂覆单纯镍基镀层或传统掺杂纳米陶瓷粉体镍基复合镀层的压缩机零部件表面的导热系数要降低30%~55%。
有益效果:与现有技术相比,本发明的隔热耐磨的空调压缩机叶片采用叶片本体与调节辊相结合的方式,将空调压缩机叶片与气缸滑槽之间的摩擦由混合摩擦变为滚动摩擦,因此,该结构大大降低了压缩机的摩擦功耗,提高了压缩机的电效率,其表面覆盖有性能优异的集强韧与润滑于一体的高隔热耐磨复合膜,采用耐高温性良好,粘结强度高的无机结合剂制备陶瓷隔热层,突破了耐热性能有限的有机结合剂所制备的陶瓷涂层只能在中低温范围内使用的局限,不仅能降低成本而且可以使其在高温环境下仍然发挥其导热性能,从而提高复合膜的耐受和腐蚀性能;陶瓷隔热层为表面纤维增强镍基镀层提供了良好的支撑和界面结合,并且有效的降低了工件表面的导热系数,克服了通常压缩机叶轮表面直接沉积镍基涂层所出现的内应力高、附着力差、承载能力弱等缺点;利用静电纺氧化锆纳米纤维对化学镀耐磨Ni-P合金镀层进行增强,镀层的硬度和耐磨性都得到明显提高,改善了单一的镍基镀层和传统掺杂纳米陶瓷粉体镍基复合镀层在高载荷下的自润滑性能和抗磨性能。
附图说明
图1为本发明的剖面结构示意图;
图2为本发明的外观结构示意图;
图3为图1中高隔热耐磨复合膜4和覆盖调节辊6的结构示意图。
具体实施方式
为使本领域技术人员更好的理解本发明的技术方案,下面结合附表和具体实施方式对本发明作详细说明。
实施例1:
如图1-3中所示,一种隔热耐磨的空调压缩机叶片,一种隔热耐磨的空调压缩机叶片,包括叶片本体1,所述叶片本体1的一端开设有调节辊容纳槽5,该调节辊容纳槽5内水平设有调节辊6,所述调节辊容纳槽5的槽底正对开设有两个滑槽2,两个所述滑槽2分别靠近所述调节辊容纳槽5的槽壁设置,所述调节辊6的外辊径与所述调节辊容纳槽5的内槽宽相同,两个所述滑槽2内活动均穿设调节辊连接板3,两个所述调节辊连接板3之间连接有所述调节辊6;所述滑槽2内设有复位弹簧7,所述复位弹簧7的一端与所述滑槽2的槽底固定连接,所述复位弹簧7的一端与所述调节辊连接板3的一端固定连接,所述调节辊连接板3的另一端穿出所述调节辊容纳槽5;所述叶片本体1、所述调节辊连接板3和所述调节辊6由Ni-Cr-Mo铸铁或添加了0.15~0.45wt%的磷的Ni-Cr-Mo铸铁形成,或者由铸铁或钢材形成;
所述叶片本体1和所述调节辊6的外表面覆盖有高隔热耐磨复合膜4,所述复合膜包括纤维增强镍基镀层4a和陶瓷隔热层4b,所述陶瓷隔热层4b涂覆在叶轮叶片表面,所述纤维增强镍基镀层4a镀覆在所述陶瓷隔热层4b表面,所述纤维增强镍基镀层4a的厚度为2~5μm,所述陶瓷隔热层4b的厚度为15~25μm,所述纤维增强镍基镀层4a为掺杂纳米纤维的Ni-P合金薄膜层,其中纳米纤维为金属氧化物纤维;所述陶瓷隔热层4b由以下质量份数的原料组成:氧化锆纳米微球45份、无机结合剂8份、聚乙烯醇3份;
所述金属氧化物纤维采用以下方法获得:将聚乙烯吡咯烷酮溶于无水乙醇得到质量分数为10%~20%的透明溶液A,然后在透明溶液A中依次搅拌加入二甲基亚砜和氧氯化锆粉体后,超声处理30min,得到纺丝前驱体;将所述纺丝前驱体吸入针管后,将其固定在静电纺丝设备上,在环境温度为15℃~25℃,环境湿度为35%~60%,电压为20~40KV的条件下,进行静电纺丝得到原生纤维;将所述原生纤维在500℃~800℃下进行煅烧2h,然后自然降温至室温得到所述金属氧化物纳米纤维;所述氧化锆纳米微球采用以下方法获得:将葡萄糖溶解于去离子水中,配置成摩尔浓度为0.5-1.5mol/L的溶液,置于水热反应釜中140-180℃进行反应,反应时间为8-20h;反应完成后,将所得混合液离心分离,并使用去离子水和无水乙醇分别洗涤,在干燥箱中干燥24h,即得碳微球;将所述碳微球加入摩尔浓度为0.1mol/L的氧氯化锆溶液中后,超声处理0.5~1h后搅拌滴加氨水,调节pH值至7,得到稳定溶胶,将得到的稳定溶胶继续超声处理0.5~1h,超声处理后,将分层的溶液离心分离,得到核壳微粒,将所得核壳微粒分别用去离子水和无水乙醇洗涤,在干燥箱中干燥12h后,然后在500℃~800℃下进行煅烧1h得到氧化锆纳米微球;所述无机结合剂采用以下方法获得:将磷酸与水混合得到质量分数为40%~45%磷酸溶液,然后将温度升高到110~120℃后,依次加入氢氧化铝和氧化镁,反应0.5~1h,得到所述无机结合剂;所述氧化铝和磷酸的Al/P摩尔比为(0.5~1):1,所述氧化镁的加入量为氢氧化铝与磷酸质量总和的1.1~1.6%。
性能测试结果:该实施例制得的空调压缩机叶片表面致密光亮,无针孔、气泡,复合薄膜的干摩擦系数稳定保持在0.06,油润滑摩擦系数甚至低于0.01,表明其具有良好的自润滑性能,其耐磨性是单纯镍基镀层或传统掺杂纳米陶瓷粉体镍基复合镀层的3倍。
实施例2:
如图1-3中所示,一种隔热耐磨的空调压缩机叶片,一种隔热耐磨的空调压缩机叶片,包括叶片本体1,所述叶片本体1的一端开设有调节辊容纳槽5,该调节辊容纳槽5内水平设有调节辊6,所述调节辊容纳槽5的槽底正对开设有两个滑槽2,两个所述滑槽2分别靠近所述调节辊容纳槽5的槽壁设置,所述调节辊6的外辊径与所述调节辊容纳槽5的内槽宽相同,两个所述滑槽2内活动均穿设调节辊连接板3,两个所述调节辊连接板3之间连接有所述调节辊6;所述滑槽2内设有复位弹簧7,所述复位弹簧7的一端与所述滑槽2的槽底固定连接,所述复位弹簧7的一端与所述调节辊连接板3的一端固定连接,所述调节辊连接板3的另一端穿出所述调节辊容纳槽5;所述叶片本体1、所述调节辊连接板3和所述调节辊6由Ni-Cr-Mo铸铁或添加了0.15~0.45wt%的磷的Ni-Cr-Mo铸铁形成,或者由铸铁或钢材形成;
所述叶片本体1和所述调节辊6的外表面覆盖有高隔热耐磨复合膜4,所述复合膜包括纤维增强镍基镀层4a和陶瓷隔热层4b,所述陶瓷隔热层4b涂覆在叶轮叶片表面,所述纤维增强镍基镀层4a镀覆在所述陶瓷隔热层4b表面,所述纤维增强镍基镀层4a的厚度为2~5μm,所述陶瓷隔热层4b的厚度为15~25μm;
所述纤维增强镍基镀层4a为掺杂纳米纤维的Ni-P合金薄膜层,其中纳米纤维为金属氧化物纤维;所述陶瓷隔热层4b由以下质量份数的原料组成:氧化锆纳米微球58份、无机结合剂15份、聚乙烯醇10份;所述金属氧化物纤维采用以下方法获得:将聚乙烯吡咯烷酮溶于无水乙醇得到质量分数为10%~20%的透明溶液A,然后在透明溶液A中依次搅拌加入二甲基亚砜和氧氯化锆粉体后,超声处理30min,得到纺丝前驱体;将所述纺丝前驱体吸入针管后,将其固定在静电纺丝设备上,在环境温度为15℃~25℃,环境湿度为35%~60%,电压为20~40KV的条件下,进行静电纺丝得到原生纤维;将所述原生纤维在500℃~800℃下进行煅烧2h,然后自然降温至室温得到所述金属氧化物纳米纤维;所述氧化锆纳米微球采用以下方法获得:将葡萄糖溶解于去离子水中,配置成摩尔浓度为0.5-1.5mol/L的溶液,置于水热反应釜中140-180℃进行反应,反应时间为8-20h;反应完成后,将所得混合液离心分离,并使用去离子水和无水乙醇分别洗涤,在干燥箱中干燥24h,即得碳微球;将所述碳微球加入摩尔浓度为0.1mol/L的氧氯化锆溶液中后,超声处理0.5~1h后搅拌滴加氨水,调节pH值至7,得到稳定溶胶,将得到的稳定溶胶继续超声处理0.5~1h,超声处理后,将分层的溶液离心分离,得到核壳微粒,将所得核壳微粒分别用去离子水和无水乙醇洗涤,在干燥箱中干燥12h后,然后在500℃~800℃下进行煅烧1h得到氧化锆纳米微球;所述无机结合剂采用以下方法获得:将磷酸与水混合得到质量分数为40%~45%磷酸溶液,然后将温度升高到110~120℃后,依次加入氢氧化铝和氧化镁,反应0.5~1h,得到所述无机结合剂;所述氧化铝和磷酸的Al/P摩尔比为(0.5~1):1,所述氧化镁的加入量为氢氧化铝与磷酸质量总和的1.1~1.6%。
性能测试结果:该实施例制得的空调压缩机叶片表面致密光亮,无针孔、气泡,其复合薄膜的干摩擦系数稳定保持在0.05,油润滑摩擦系数甚至低于0.01,表明其具有良好的自润滑性能,其耐磨性是单纯镍基镀层或传统掺杂纳米陶瓷粉体镍基复合镀层的4倍。
实施例3:
如图1-3中所示,一种隔热耐磨的空调压缩机叶片,一种隔热耐磨的空调压缩机叶片,包括叶片本体1,所述叶片本体1的一端开设有调节辊容纳槽5,该调节辊容纳槽5内水平设有调节辊6,所述调节辊容纳槽5的槽底正对开设有两个滑槽2,两个所述滑槽2分别靠近所述调节辊容纳槽5的槽壁设置,所述调节辊6的外辊径与所述调节辊容纳槽5的内槽宽相同,两个所述滑槽2内活动均穿设调节辊连接板3,两个所述调节辊连接板3之间连接有所述调节辊6;所述滑槽2内设有复位弹簧7,所述复位弹簧7的一端与所述滑槽2的槽底固定连接,所述复位弹簧7的一端与所述调节辊连接板3的一端固定连接,所述调节辊连接板3的另一端穿出所述调节辊容纳槽5;所述叶片本体1、所述调节辊连接板3和所述调节辊6由Ni-Cr-Mo铸铁或添加了0.15~0.45wt%的磷的Ni-Cr-Mo铸铁形成,或者由铸铁或钢材形成;
所述叶片本体1和所述调节辊6的外表面覆盖有高隔热耐磨复合膜4,所述复合膜包括纤维增强镍基镀层4a和陶瓷隔热层4b,所述陶瓷隔热层4b涂覆在叶轮叶片表面,所述纤维增强镍基镀层4a镀覆在所述陶瓷隔热层4b表面,所述纤维增强镍基镀层4a的厚度为2~5μm,所述陶瓷隔热层4b的厚度为15~25μm;
所述纤维增强镍基镀层4a为掺杂纳米纤维的Ni-P合金薄膜层,其中纳米纤维为金属氧化物纤维;所述陶瓷隔热层4b由以下质量份数的原料组成:氧化锆纳米微球55份、无机结合剂12份、聚乙烯醇7份;所述金属氧化物纤维采用以下方法获得:将聚乙烯吡咯烷酮溶于无水乙醇得到质量分数为10%~20%的透明溶液A,然后在透明溶液A中依次搅拌加入二甲基亚砜和氧氯化锆粉体后,超声处理30min,得到纺丝前驱体;将所述纺丝前驱体吸入针管后,将其固定在静电纺丝设备上,在环境温度为15℃~25℃,环境湿度为35%~60%,电压为20~40KV的条件下,进行静电纺丝得到原生纤维;将所述原生纤维在500℃~800℃下进行煅烧2h,然后自然降温至室温得到所述金属氧化物纳米纤维;所述氧化锆纳米微球采用以下方法获得:将葡萄糖溶解于去离子水中,配置成摩尔浓度为
0.5-1.5mol/L的溶液,置于水热反应釜中140-180℃进行反应,反应时间为8-20h;反应完成后,将所得混合液离心分离,并使用去离子水和无水乙醇分别洗涤,在干燥箱中干燥24h,即得碳微球;将所述碳微球加入摩尔浓度为0.1mol/L的氧氯化锆溶液中后,超声处理0.5~1h后搅拌滴加氨水,调节pH值至7,得到稳定溶胶,将得到的稳定溶胶继续超声处理0.5~1h,超声处理后,将分层的溶液离心分离,得到核壳微粒,将所得核壳微粒分别用去离子水和无水乙醇洗涤,在干燥箱中干燥12h后,然后在500℃~800℃下进行煅烧1h得到氧化锆纳米微球;所述无机结合剂采用以下方法获得:将磷酸与水混合得到质量分数为40%~45%磷酸溶液,然后将温度升高到110~120℃后,依次加入氢氧化铝和氧化镁,反应0.5~1h,得到所述无机结合剂;所述氧化铝和磷酸的Al/P摩尔比为(0.5~1):1,所述氧化镁的加入量为氢氧化铝与磷酸质量总和的1.1~1.6%。
性能测试结果:该实施例制得的空调压缩机叶片表面致密光亮,无针孔、气泡,其复合薄膜的干摩擦系数稳定保持在0.04,油润滑摩擦系数甚至低于0.01,表明其具有良好的自润滑性能,其耐磨性是单纯镍基镀层或传统掺杂纳米陶瓷粉体镍基复合镀层的6倍。
实施例4:隔热耐磨的空调压缩机叶片的制备方法
步骤一、金属工件表面预处理:将叶片本体1和所述调节辊6表面清洗、除油;
步骤二、涂覆陶瓷隔热层:将氧化锆纳米微球、无机结合剂和聚乙烯醇混合搅拌后,调制成料浆,然后将料浆涂覆在经过步骤一预处理后的金属工件表面,然后将涂覆料浆的金属工件进行干燥后置入气体保护炉或真空炉中,进行烧结处理,烧结处理条件为以8~15℃/min的速率升温至400~450℃,保温4~8min,再以6~10℃/min的速率从400~450℃升温至900~1000℃,接着以3~8℃/min的升温速度从900~1000℃升温至1050~1150℃,保温8~50min后,冷至室温,形成陶瓷隔热层;
步骤三、化学镀纤维增强镍基镀层:将步骤二处理后的金属工件置于装有氯化钯、盐酸、水的活化液中进行活化,然后将活化后的金属工件用去离子水冲洗,接着将冲洗后的金属工件置于装有硫酸镍浓度为200~300g/L、硫酸钴的浓度为25~40g/L,次磷酸钠的浓度为20~35g/L、乳酸的浓度为18~28g/L、丙酸的浓度为3~10g/L、无水乙酸钠的浓度为15~22g/L、硫脲的浓度为0.5~3g/L、十二烷基硫酸钠的浓度为5~15g/L和氧化锆纳米纤维的浓度为10~40g/L,在进行化学镀过程中,调节机械搅拌速度为500~1200r/min,保持镀液的pH值为5~7,保持镀液温度为70~90℃,在陶瓷隔热层表面镀覆形成纤维增强镍基镀层;
步骤四、热处理:将步骤三处理后的金属工件放入电阻炉中进行保温热处理,然后随炉冷却,得到覆有高隔热耐磨复合膜的金属工件。
步骤五、将步骤四处理后的叶片本体1、调节辊6与调节辊连接板3、复位弹簧7进行组装,得到成品。
最后需要说明,上述描述仅为本发明的优选实施例,本领域的技术人员在本发明的启示下,在不违背本发明宗旨及权利要求的前提下,可以做出多种类似的表示,这样的变换均落入本发明的保护范围之内。
Claims (6)
1.一种隔热耐磨的空调压缩机叶片,其特征在于:包括叶片本体(1),所述叶片本体(1)的一端开设有调节辊容纳槽(5),该调节辊容纳槽(5)内水平设有调节辊(6),所述调节辊容纳槽(5)的槽底正对开设有两个滑槽(2),两个所述滑槽(2)内活动均穿设调节辊连接板(3),两个所述调节辊连接板(3)之间连接有所述调节辊(6);所述滑槽(2)内设有复位弹簧(7),所述复位弹簧(7)的一端与所述滑槽(2)的槽底固定连接,所述复位弹簧(7)的一端与所述调节辊连接板(3)的一端固定连接,所述调节辊连接板(3)的另一端穿出所述调节辊容纳槽(5);所述叶片本体(1)和所述调节辊(6)的外表面覆盖有高隔热耐磨复合膜(4),所述复合膜包括纤维增强镍基镀层(4a)和陶瓷隔热层(4b),所述纤维增强镍基镀层(4a)镀覆在所述陶瓷隔热层(4b)表面;所述纤维增强镍基镀层(4a)为掺杂纳米纤维的Ni-P合金薄膜层,其中纳米纤维为金属氧化物纤维;所述陶瓷隔热层(4b)由以下质量份数的原料组成:氧化锆纳米微球45-58份、无机结合剂8-15份、聚乙烯醇3-10份;
所述空调压缩机叶片的制备方法按以下步骤进行:
步骤一、金属工件表面预处理:将叶片本体(1)和所述调节辊(6)表面清洗、除油;
步骤二、涂覆陶瓷隔热层:将氧化锆纳米微球、无机结合剂和聚乙烯醇混合搅拌后,调制成料浆,然后将料浆涂覆在经过步骤一预处理后的金属工件表面,然后将涂覆料浆的金属工件进行干燥后置入气体保护炉或真空炉中,进行烧结处理,烧结处理条件为以8~15℃/min的速率升温至400~450℃,保温4~8min,再以6~10℃/min的速率从400~450℃升温至900~1000℃,接着以3~8℃/min的升温速度从900~1000℃升温至1050~1150℃,保温8~50min后,冷至室温,形成陶瓷隔热层;
步骤三、化学镀纤维增强镍基镀层:将步骤二处理后的金属工件置于装有氯化钯、盐酸、水的活化液中进行活化,然后将活化后的金属工件用去离子水冲洗,接着将冲洗后的金属工件置于装有硫酸镍浓度为200~300g/L、硫酸钴的浓度为25~40g/L,次磷酸钠的浓度为20~35g/L、乳酸的浓度为18~28g/L、丙酸的浓度为3~10g/L、无水乙酸钠的浓度为15~22g/L、硫脲的浓度为0.5~3g/L、十二烷基硫酸钠的浓度为5~15g/L和氧化锆纳米纤维的浓度为10~40g/L的混合溶液中进行化学镀,在进行化学镀过程中,调节机械搅拌速度为500~1200r/min,保持镀液的pH值为5~7,保持镀液温度为70~90℃,在陶瓷隔热层表面镀覆形成纤维增强镍基镀层;
步骤四、热处理:将步骤三处理后的金属工件放入电阻炉中进行保温热处理,然后随炉冷却,得到覆有高隔热耐磨复合膜的金属工件;
步骤五、将步骤四处理后的叶片本体(1)、调节辊(6)与调节辊连接板(3)、复位弹簧(7)进行组装,得到成品。
2.根据权利要求1所述的隔热耐磨的空调压缩机叶片,其特征在于所述金属氧化物纤维采用以下方法获得:将聚乙烯吡咯烷酮溶于无水乙醇得到质量分数为10%~20%的透明溶液A,然后在透明溶液A中依次搅拌加入二甲基亚砜和氧氯化锆粉体后,超声处理30min,得到纺丝前驱体;将所述纺丝前驱体吸入针管后,将其固定在静电纺丝设备上,在环境温度为15℃~25℃,环境湿度为35%~60%,电压为20~40KV的条件下,进行静电纺丝得到原生纤维;将所述原生纤维在500℃~800℃下进行煅烧2h,然后自然降温至室温得到金属氧化物纳米纤维。
3.根据权利要求2所述的隔热耐磨的空调压缩机叶片,其特征在于所述氧化锆纳米微球采用以下方法获得:将葡萄糖溶解于去离子水中,配置成摩尔浓度为0.5-1.5mol/L的溶液,置于水热反应釜中140-180℃进行反应,反应时间为8-20h;反应完成后,将所得混合液离心分离,并使用去离子水和无水乙醇分别洗涤,在干燥箱中干燥24h,即得碳微球;将所述碳微球加入摩尔浓度为0.1mol/L的氧氯化锆溶液中后,超声处理0.5~1h后搅拌滴加氨水,调节pH值至7,得到稳定溶胶,将得到的稳定溶胶继续超声处理0.5~1h,超声处理后,将分层的溶液离心分离,得到核壳微粒,将所得核壳微粒分别用去离子水和无水乙醇洗涤,在干燥箱中干燥12h后,然后在500℃~800℃下进行煅烧1h得到氧化锆纳米微球。
4.根据权利要求3所述的隔热耐磨的空调压缩机叶片,其特征在于所述无机结合剂采用以下方法获得:将磷酸与水混合得到质量分数为40%~45%磷酸溶液,然后将温度升高到110~120℃后,依次加入氢氧化铝和氧化镁,反应0.5~1h,得到所述无机结合剂;所述氢氧化铝和磷酸的Al/P摩尔比为0.5~1:1,所述氧化镁的加入量为氢氧化铝与磷酸质量总和的1.1~1.6%。
5.根据权利要求1、3或4任一项所述的隔热耐磨的空调压缩机叶片,其特征在于:所述纤维增强镍基镀层(4a)的厚度为2~5μm,所述陶瓷隔热层(4b)的厚度为15~25μm。
6.根据权利要求1、3或4任一项所述的隔热耐磨的空调压缩机叶片,其特征在于:两个所述滑槽(2)分别靠近所述调节辊容纳槽(5)的槽壁设置,所述调节辊(6)的外辊径与所述调节辊容纳槽(5)的内槽宽相同。