CN108707297A - A kind of heat-proof combustion-resistant PVC injection molding materials - Google Patents
A kind of heat-proof combustion-resistant PVC injection molding materials Download PDFInfo
- Publication number
- CN108707297A CN108707297A CN201810621858.8A CN201810621858A CN108707297A CN 108707297 A CN108707297 A CN 108707297A CN 201810621858 A CN201810621858 A CN 201810621858A CN 108707297 A CN108707297 A CN 108707297A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- heat
- injection molding
- molding materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to PVC material field more particularly to a kind of heat-proof combustion-resistant PVC injection molding materials, the heat-proof combustion-resistant PVC injection molding materials prepare the substance that raw material includes following parts by weight:100~120 parts by weight of polyvinyl chloride resin, 25~35 parts by weight of epoxy modified silicone resin, 15~40 parts by weight of schmigel, 15~35 parts by weight of compounded mix, 10~15 parts by weight of plasticizer, 7~12 parts by weight of lubricant, 5~12 parts by weight of heat stabilizer, 15~22 parts by weight of 2~6 parts by weight of flow ability modifying agent and oxidic polyethylene alcohol.
Description
Technical field
The present invention relates to PVC material field more particularly to a kind of heat-proof combustion-resistant PVC injection molding materials.
Background technology
In the prior art, cable industry generally use PVC is as the insulated pipes used on the outside of cable, but due to polyvinyl chloride resin
Self shortcoming, flame retardant property is poor, and on flame burn when can release a large amount of hydrogen chloride gas, hydrogen chloride gas
Have certain toxicity and corrosivity, left with it " self-extinguishment " for having due to it after flame can automatic distinguishing, but it still holds
Easily drip, drippage caused to be lighted, in addition except open fire other than, polyvinyl chloride resin in 100 DEG C or more of hot environment also easily
It decomposes, generate discoloration and releases hydrogen chloride toxic gas simultaneously, with its decomposition of temperature rise and release hydrogen chloride gas
Speed can also further speed up, and when as insulated pipes used on the outside of cable its inevitably can duration work under the high temperature conditions,
And there is certain probability to touch open fire, therefore since the common PVC material of disadvantages mentioned above is difficult to meet the needs of existing industry.
Certainly, there are also the PVC cable injection molding materials with fire retardation in the prior art, but the fire-retardant of its addition helps
Agent, some are that have the fire retardant containing halogen, have larger damaging effect, then flame retardant effect is poor for other;In addition, existing
Some PVC cable insulations tubing is generally harder, it is difficult to be suitable for certain use environments, improve it by adding existing plasticizer
Pliability can then influence the flame retardant property of tubing again;Therefore, being badly in need of one kind can be made both fire-retardant simultaneously with preferable pliability
The flame-proof PVC injection molding material for the PVC insulating materials haveing excellent performance.
Patent Office of the People's Republic of China discloses a kind of application for a patent for invention of flame-proof PVC injection molding material on January 30th, 2018, and application is public
Announcement number is CN107641270A, and discloses a kind of flame-proof PVC on January 23rd, 2018 in Patent Office of the People's Republic of China more in early time
The application for a patent for invention of the preparation method of injection molding material, application notification number are CN107619559A, and both of which is using modified diatom
Soil carries out the improvement of flame retardant property to it, is second to pass through tool one is by the absorption of the ammonium carbonate with flame retardant property
There is the surface of the polysiloxanes fire retardant of flame retarding function to coat, plays the role of isolation burning, but its high temperature resistance does not obtain
To significantly improving, it is heated and is still easy aging.
Invention content
For solve in the prior art, cable industry generally use PVC as the insulated pipes used on the outside of cable, but due to
The self shortcoming of polyvinyl chloride resin, flame retardant property is poor, and can release a large amount of hydrogen chloride gas, chlorine when burning on flame
Change hydrogen and have certain toxicity and corrosivity, left with it " self-extinguishment " for having due to it after flame can automatic distinguishing,
But it is still easy to happen drippage, cause drippage light, in addition except open fire other than, hot environment of the polyvinyl chloride resin at 100 DEG C or more
In also easily decompose, generate discoloration and simultaneously releases hydrogen chloride toxic gas, with temperature rise its decompose and release chlorine
Changing the speed of hydrogen can also further speed up, and when as insulated pipes used on the outside of cable its inevitably can duration in hot conditions
Lower work, and there is certain probability to touch open fire, therefore the problem of common PVC material is difficult to meet existing industry requirement, this
Invention provides a kind of heat-proof combustion-resistant PVC injection molding materials.
To achieve the above object, the present invention uses following technical scheme:
A kind of heat-proof combustion-resistant PVC injection molding materials, the heat-proof combustion-resistant PVC injection molding materials prepare the object that raw material includes following parts by weight
Matter:100~120 parts by weight of polyvinyl chloride resin, 25~35 parts by weight of epoxy modified silicone resin, 15~40 parts by weight of schmigel are multiple
Conjunction 15~35 parts by weight of filler, 10~15 parts by weight of plasticizer, 7~12 parts by weight of lubricant, 5~12 parts by weight of heat stabilizer,
15~22 parts by weight of 2~6 parts by weight of flow ability modifying agent and oxidic polyethylene alcohol.
Preferably, the heat-proof combustion-resistant PVC injection molding materials prepare the substance that raw material includes following parts by weight:PVC trees
110~115 parts by weight of fat, 28~32 parts by weight of epoxy modified silicone resin, 28~35 parts by weight of schmigel, compounded mix 23
~28 parts by weight, 11~13 parts by weight of plasticizer, 9~11 parts by weight of lubricant, 7~9 parts by weight of heat stabilizer, flow ability modifying agent
18~20 parts by weight of 3~4 parts by weight and oxidic polyethylene alcohol.
Preferably, the heat-proof combustion-resistant PVC injection molding materials prepare the substance that raw material includes following parts by weight:PVC trees
113 parts by weight of fat, 31 parts by weight of epoxy modified silicone resin, 34 parts by weight of schmigel, 26 parts by weight of compounded mix, plasticizer
12 parts by weight, 10.5 parts by weight of lubricant, 8.5 parts by weight of heat stabilizer, 3.75 parts by weight of flow ability modifying agent and oxidic polyethylene
18 parts by weight of alcohol.
Wherein, epoxy modified silicone resin is preferably any one in ES-1001N, ES-1001T and ES-1023 resin
Kind is several, has preferably heat resistance, especially excellent compared to general organic resin, can be under the conditions of 200~250 DEG C
It is used for a long time and decomposes or change colour without generating, and 300 DEG C can be resistant in a short time, and in schmigel, titanium dioxide and glass powder
Under the filling effect of equal heat-resistant fillers, heat resistance can dramatically get a promotion, up to 500 DEG C or more, as auxiliary
Material can greatly improve the heat resistance of prepared product, and wherein ES-1001N is a kind of typical epoxy modified silicone
Resin has good heat resistance, and ES-1001T is also equipped with certain enhancing admittedly on the basis of ES-1001N had performances
The effect for changing effect, improves the mechanical property of material and accelerates curing rate, optimize solidification effect, ES-1023 is in ES-
The filling of the characteristics of low in acidity value is also equipped in the performance basis that 1001N has, schmigel makes its oxidation resistance also into one
Step gets a promotion, and mobility modifying agent can improve the processability of injection molding material so that can be more effective prepare cable
Outer rubber etc., film forming agent enable injection molding material surface to form one layer of film that can play waterproof action, but also through injection molding
The outside of cable rubber obtained etc. forms one layer of film with waterproof action afterwards, improves its humidity resistance, oxidic polyethylene
Alcohol can be effectively distributed in the surface of PVC Insulation Materials, play the role of protecting film, to substantially increase the anti-of PVC Insulation Materials
Damp performance extends the shelf-life of PVC Insulation Materials.
Preferably, the compounded mix is improved silica filler.
Silica have good heat-proof combustion-resistant performance and can in resin oxygen-containing group and hydroxyl can produce
Raw good link effect, improves the stability of improved silica filler and matrix resin, and silica is easy setting
Formed evenly dispersed in fat, filling effect is more preferably.
Preferably, the improved silica filler is prepared by following methods:
1) mesoporous nano silicon dioxide is placed in the tetrahydrofuran of its 3~5 times of parts by weight and carries out ultrasonic vibration, ultrasonic vibration work(
Rate is 70~85kW, and the time is 10~15min, obtains suspension;
2) 0.2~0.5 times of mesoporous nano silicon dioxide is added into step 1) suspension just obtained after ultrasonic vibration
The OP-10 non-ionic surfactants of 0.03~0.1 times of parts by weight of organic filler and mesoporous nano silicon dioxide of parts by weight
Agent is stirred under the conditions of being placed in 45~65 DEG C to thick shape liquid is formed, and dry 3~6h is modified under the conditions of being placed in 80~120 DEG C
Silica filler.
Wherein be added organic filler after stirring can be carried out under the conditions of low pressure or vacuum, be conducive to organic filler into
Enter inside the gap of mesoporous nano silicon dioxide, prepared by improved silica filler using mesoporous nano silicon dioxide as
The micropore of main base ingredient, meso-hole structure is filled by organic filler, and nano level silica more preferably has
Conducive to evenly dispersed, optimization filling effect.
Preferably, the organic filler is KR-242A organic siliconresins, KR-511 modified silicone resins and JP-R035
At least one of acrylic silicon resin.
Above-mentioned organic filler is provided with preferable mobility, heat resistance and a degree of flame retardant property and has and two
The height suitability of silica, improved silica filler in the base its heat-proof combustion-resistant modifying function when, if moment is by strong
High temperature impact, structure are more easily damaged, the heat-proof combustion-resistant that common silica filler generates after its structure is destroyed
Effect can quickly and significantly decline, and improved silica filler, when by strong high temperature impact, structure can also be destroyed,
But the organic filler for being destroyed its rear intension leaks, and the organic filler after leaking can be to the position that is damaged, is destroyed
Filling effect is generated, and then continues to play the effect for strengthening heat-proof combustion-resistant performance, and the organic filler is silicones,
It also further can convert to form silica under certain condition, the structure to being damaged, being destroyed part reconnected,
Structure and repairing, since its chain length increases, toughness can be also improved the structure re-formed after repairing, be realized in breakage
Selfreparing and reinforcing in short time afterwards improves using effect and extends its service life.
Preferably, the plasticizer is at least one of dioctyl phthalate and dioctyl terephthalate.
Preferably, the lubricant is any one in stearic acid or stearate.
Preferably, the heat stabilizer is tribasic lead sulfate, dibasic lead phosphite, dibasic lead stearate, two
At least one of isooctyl thioglycolate dioctyltin and dimethyl dimercapto 2-ethyl hexyl ethanoate tin.
Preferably, the flow ability modifying agent is EMI resins.
EMI resins are a kind of using styrene and acrylonitrile as the low molecular weight random copolymer of main monomer, show excess of export
High mobility, thermal stability and good dispersibility can significantly reduce the viscosity of plastic melt, promote plasticizing, reduce injection molding
Processing and forming temperature shortens the processing and forming period.
The beneficial effects of the invention are as follows:
1) product heat-proof combustion-resistant PVC injection molding materials of the present invention have excellent injection molding performance;
2) product of the present invention has good heat-proof combustion-resistant performance;
3) it can realize selfreparing in a short time after internal structure is destroyed, its heat-proof combustion-resistant performance is avoided to decline.
Specific implementation mode
Present invention work is further clearly described in detail below in conjunction with specific embodiment
Embodiment 1
A kind of heat-proof combustion-resistant PVC injection molding materials prepare the substance that raw material includes following parts by weight:
100 parts by weight of polyvinyl chloride resin, 25 parts by weight of epoxy modified silicone resin, 15 parts by weight of schmigel, 15 weight of compounded mix
Part, 10 parts by weight of dioctyl phthalate, 7 parts by weight of stearic acid, 5:1:The tribasic lead sulfate of 2 mass ratioes, two alkali formulas are sub-
5 parts by weight of lead phosphate and dibasic lead stearate, 15 parts by weight of 2 parts by weight of EMI resins and oxidic polyethylene alcohol.
Wherein compounded mix is improved silica filler, and improved silica filler is prepared by following methods:
1) mesoporous nano silicon dioxide is placed in the tetrahydrofuran of its 3 times of parts by weight and carries out ultrasonic vibration, ultrasonic vibration power
Suspension is obtained for 70kW, time 10min;
2) 0.2 times of parts by weight of mesoporous nano silicon dioxide are added into step 1) suspension just obtained after ultrasonic vibration
0.03 times of parts by weight of organic filler and mesoporous nano silicon dioxide OP-10 nonionic surface active agent, be placed in low pressure
It is stirred under the conditions of 45 DEG C to thick shape liquid is formed, dry 6h obtains improved silica filler under the conditions of being placed in 80 DEG C.
Embodiment 2
A kind of heat-proof combustion-resistant PVC injection molding materials prepare the substance that raw material includes following parts by weight:
120 parts by weight of polyvinyl chloride resin, 35 parts by weight of epoxy modified silicone resin, 40 parts by weight of schmigel, 35 weight of compounded mix
Part, 1:15 parts by weight of dioctyl phthalate and dioctyl terephthalate of 1 mass ratio, 12 parts by weight of stearic acid sodium, two
12 parts by weight of isooctyl thioglycolate dioctyltin, 22 parts by weight of 6 parts by weight of EMI resins and oxidic polyethylene alcohol.
Wherein compounded mix is improved silica filler, and improved silica filler is prepared by following methods:
1) mesoporous nano silicon dioxide is placed in the tetrahydrofuran of its 5 times of parts by weight and carries out ultrasonic vibration, ultrasonic vibration power
Suspension is obtained for 85kW, time 15min;
2) 0.5 times of parts by weight of mesoporous nano silicon dioxide are added into step 1) suspension just obtained after ultrasonic vibration
0.1 times of parts by weight of organic filler and mesoporous nano silicon dioxide OP-10 nonionic surface active agent, be placed in and vacuumize
It is stirred under the conditions of 65 DEG C to thick shape liquid is formed, dry 6h obtains improved silica filler under the conditions of being placed in 120 DEG C.
Embodiment 3
A kind of heat-proof combustion-resistant PVC injection molding materials prepare the substance that raw material includes following parts by weight:
110 parts by weight of polyvinyl chloride resin, 28 parts by weight of epoxy modified silicone resin, 28 parts by weight of schmigel, 23 weight of compounded mix
Part, 11 parts by weight of dioctyl phthalate, 9 parts by weight of barium stearate, 7 parts by weight of dimethyl dimercapto 2-ethyl hexyl ethanoate tin,
18 parts by weight of 3 parts by weight of EMI resins and oxidic polyethylene alcohol.
Wherein compounded mix is improved silica filler, and improved silica filler is prepared by following methods:
1) mesoporous nano silicon dioxide is placed in the tetrahydrofuran of its 3 times of parts by weight and carries out ultrasonic vibration, ultrasonic vibration power
Suspension is obtained for 75kW, time 15min;
2) 0.5 times of parts by weight of mesoporous nano silicon dioxide are added into step 1) suspension just obtained after ultrasonic vibration
0.05 times of parts by weight of organic filler and mesoporous nano silicon dioxide OP-10 nonionic surface active agent, be placed in
It is stirred under the conditions of 55 DEG C in 0.5atm air pressure environment to thick shape liquid is formed, dry 6h obtains modified two under the conditions of being placed in 120 DEG C
Cilicon oxide filler.
Embodiment 4
A kind of heat-proof combustion-resistant PVC injection molding materials prepare the substance that raw material includes following parts by weight:
115 parts by weight of polyvinyl chloride resin, 32 parts by weight of epoxy modified silicone resin, 35 parts by weight of schmigel, 28 weight of compounded mix
Part, 13 parts by weight of dioctyl phthalate, 11 parts by weight of stearic acid, 9 parts by weight of dimercapto 2-ethyl hexyl ethanoate dioctyltin,
20 parts by weight of 4 parts by weight of EMI resins and oxidic polyethylene alcohol.
Wherein compounded mix is improved silica filler, and improved silica filler is prepared by following methods:
1) mesoporous nano silicon dioxide is placed in the tetrahydrofuran of its 3.5 times of parts by weight and carries out ultrasonic vibration, ultrasonic vibration work(
Rate is 85kW, and time 10min obtains suspension;
2) 0.45 times of weight of mesoporous nano silicon dioxide is added into step 1) suspension just obtained after ultrasonic vibration
The OP-10 nonionic surface active agent of 0.045 times of parts by weight of organic filler and mesoporous nano silicon dioxide of part, is placed in
It is stirred under the conditions of 65 DEG C in 0.45atm environment to thick shape liquid is formed, dry 4h obtains modified titanium dioxide under the conditions of being placed in 100 DEG C
Silicon filler.
Embodiment 5
A kind of heat-proof combustion-resistant PVC injection molding materials prepare the substance that raw material includes following parts by weight:
113 parts by weight of polyvinyl chloride resin, 31 parts by weight of epoxy modified silicone resin, 34 parts by weight of schmigel, 26 weight of compounded mix
Part, 12 parts by weight of dioctyl terephthalate, 10.5 parts by weight of stearic acid, 5:The dimercapto 2-ethyl hexyl ethanoate two of 1 mass ratio is just
8.5 parts by weight of tin octylate and dimethyl dimercapto 2-ethyl hexyl ethanoate tin, 18 weight of 3.75 parts by weight of EMI resins and oxidic polyethylene alcohol
Measure part.
Wherein compounded mix is improved silica filler, and improved silica filler is prepared by following methods:
1) mesoporous nano silicon dioxide is placed in the tetrahydrofuran of its 5 times of parts by weight and carries out ultrasonic vibration, ultrasonic vibration power
Suspension is obtained for 85kW, time 15min;
2) 0.35 times of weight of mesoporous nano silicon dioxide is added into step 1) suspension just obtained after ultrasonic vibration
The OP-10 nonionic surface active agent of 0.055 times of parts by weight of organic filler and mesoporous nano silicon dioxide of part, is placed in
It is stirred under the conditions of 60 DEG C in 0.7atm environment to thick shape liquid is formed, dry 6h obtains modified titanium dioxide under the conditions of being placed in 110 DEG C
Silicon filler.
Technical indicator:
It is fire-retardant:V0 grades (UL94 fire-retardant fireproofs level estimates);
Heat resistance:Constant temperature placement 3d is non-discolouring under the conditions of 280 DEG C, mass change < 1.2%.
Claims (10)
1. a kind of heat-proof combustion-resistant PVC injection molding materials, which is characterized in that the heat-proof combustion-resistant PVC injection molding materials prepare raw material include with
The substance of lower parts by weight:100~120 parts by weight of polyvinyl chloride resin, 25~35 parts by weight of epoxy modified silicone resin, schmigel
15~40 parts by weight, 15~35 parts by weight of compounded mix, 10~15 parts by weight of plasticizer, 7~12 parts by weight of lubricant, thermostabilization
5~12 parts by weight of agent, 15~22 parts by weight of 2~6 parts by weight of flow ability modifying agent and oxidic polyethylene alcohol.
2. a kind of heat-proof combustion-resistant PVC injection molding materials according to claim 1, which is characterized in that the heat-proof combustion-resistant PVC injection moldings
Material prepares the substance that raw material includes following parts by weight:110~115 parts by weight of polyvinyl chloride resin, epoxy modified silicone resin 28
~32 parts by weight, 28~35 parts by weight of schmigel, 23~28 parts by weight of compounded mix, 11~13 parts by weight of plasticizer, lubricant 9
~11 parts by weight, 7~9 parts by weight of heat stabilizer, 18~20 parts by weight of 3~4 parts by weight of flow ability modifying agent and oxidic polyethylene alcohol.
3. a kind of heat-proof combustion-resistant PVC injection molding materials according to claim 1, which is characterized in that the heat-proof combustion-resistant PVC injection moldings
Material prepares the substance that raw material includes following parts by weight:113 parts by weight of polyvinyl chloride resin, 31 weight of epoxy modified silicone resin
Part, 34 parts by weight of schmigel, 26 parts by weight of compounded mix, 12 parts by weight of plasticizer, 10.5 parts by weight of lubricant, heat stabilizer
8.5 parts by weight, 18 parts by weight of 3.75 parts by weight of flow ability modifying agent and oxidic polyethylene alcohol.
4. a kind of heat-proof combustion-resistant PVC injection molding materials according to claim 1 or 2 or 3, which is characterized in that the compounded mix
For improved silica filler.
5. a kind of heat-proof combustion-resistant PVC injection molding materials according to claim 4, which is characterized in that the improved silica is filled out
Material is prepared by following methods:
1) mesoporous nano silicon dioxide is placed in the tetrahydrofuran of its 3~5 times of parts by weight and carries out ultrasonic vibration, ultrasonic vibration work(
Rate is 70~85kW, and the time is 10~15min, obtains suspension;
2) 0.2~0.5 times of mesoporous nano silicon dioxide is added into step 1) suspension just obtained after ultrasonic vibration
The OP-10 non-ionic surfactants of 0.03~0.1 times of parts by weight of organic filler and mesoporous nano silicon dioxide of parts by weight
Agent is stirred under the conditions of being placed in 45~65 DEG C to thick shape liquid is formed, and dry 3~6h is modified under the conditions of being placed in 80~120 DEG C
Silica filler.
6. a kind of heat-proof combustion-resistant PVC injection molding materials according to claim 5, which is characterized in that the organic filler is KR-
At least one of 242A organic siliconresins, KR-511 modified silicone resins and JP-R035 acrylic silicon resins.
7. a kind of heat-proof combustion-resistant PVC injection molding materials according to claim 1 or 2 or 3, which is characterized in that the plasticizer is
At least one of dioctyl phthalate and dioctyl terephthalate.
8. a kind of heat-proof combustion-resistant PVC injection molding materials according to claim 1 or 2 or 3, which is characterized in that the lubricant is
Any one in stearic acid or stearate.
9. a kind of heat-proof combustion-resistant PVC injection molding materials according to claim 1 or 2 or 3, which is characterized in that the heat stabilizer
For tribasic lead sulfate, dibasic lead phosphite, dibasic lead stearate, dimercapto 2-ethyl hexyl ethanoate dioctyltin and diformazan
At least one of base dimercapto 2-ethyl hexyl ethanoate tin.
10. a kind of heat-proof combustion-resistant PVC injection molding materials according to claim 1 or 2 or 3, which is characterized in that the flow modifier
Agent is EMI resins.