CN108703216A - A kind of fruit preservative paper - Google Patents
A kind of fruit preservative paper Download PDFInfo
- Publication number
- CN108703216A CN108703216A CN201810537201.3A CN201810537201A CN108703216A CN 108703216 A CN108703216 A CN 108703216A CN 201810537201 A CN201810537201 A CN 201810537201A CN 108703216 A CN108703216 A CN 108703216A
- Authority
- CN
- China
- Prior art keywords
- mass ratio
- take
- mixed
- parts
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of fruit preservative papers, belong to paper product field.The present invention is in 40 ~ 55 DEG C, take ethyl cellulose, inorganic powder, composite modified constituent of chitosan that 1 ~ 2h is mixed in reaction kettle, after be cooled to 20 ~ 25 DEG C plasticizer, spinach compound extracted solution, polylysines mixing be added, 40 ~ 60min is stirred with 300 ~ 350r/min, obtains antistaling coating; antistaling coating is taken to be sprayed on the side of individual wood pulp body paper; stands 5 ~ 10min, sprays antistaling coating again in wood pulp body paper homonymy, stand 5 ~ 10min; drying is to get fruit preservative paper.It is short that the present invention solves the current fruit preservative paper function time, the inapparent problem of preservation.
Description
Technical field
The invention belongs to paper product fields, and in particular to a kind of fruit preservative paper.
Background technology
In recent years, Chinese fruit industry development is very fast, however preserving fruit and vegetable utilizing storage capacity seriously falls behind, and the shelf-life is shorter,
It is difficult to ensure the freshness of fruit.Fruits and vegetables rot to be the basic reason for causing the preserving fruit and vegetable utilizing phase short, and fruits and vegetables storage condition is wet
Degree, temperature, cleannes and oxygen concentration are the principal element for causing fruits and vegetables rotten, the rotten speed and aforementioned four of fruits and vegetables
The value of factor is directly proportional, i.e., temperature is higher, and humidity is bigger, and cleannes are poorer, and oxygen concentration is bigger, the rotten speed of fruits and vegetables
Degree is faster.So-called cleannes refer mainly to the bacterial content in storage condition air（Mainly mould）, these bacterium parts
In natural air, a part is contained on the epidermis of fruits and vegetables, and humidity, temperature, oxygen are the hotbeds of bacterial reproduction.It changes
Yan Zhi, temperature is higher, humidity is bigger, oxygen is more sufficient, and the speed of bacterial reproduction is faster.It is well known that for most of food
For, the exceeded growth and breeding of microorganism is the main reason for leading to food spoilage.In the storage and transport of food, if warm
Degree, humidity and gas flow it is suitable, microorganism will raised growth breeding, accelerate food spoilage.Food packaging is as food and outside
Last one of barrier of boundary's environment has particularly important relationship to the holding of food quality.As people anticipate to environment protection health
The enhancing of knowledge, the requirement to packaging are also higher and higher.Tin foil has become the country as a kind of environmentally protective Perserving materials
The research emphasis of outer researcher.
Antistaling agent is mainly added in paper substrate or is coated on paper substrate surface for the preparation of tin foil, makes it have certain
Fresh-keeping effect, packaging of the tin foil as fruits and vegetables can not only enable the freshness date of fruits and vegetables extend, moreover it is possible to reduce the machine of fruit
Tool damages, and is a kind of effective preserving fruit and vegetable utilizing measure, but the fruit preservative paper function time current in actual use
Short, preservation is not notable.Therefore, before producing a kind of fruit preservative paper that can be solved the above problems there is prodigious market
Scape.
Invention content
The technical problems to be solved by the invention：Short, the preservation for the current fruit preservative paper function time
Inapparent problem provides a kind of fruit preservative paper.
In order to solve the above technical problems, the present invention is using technical solution as described below：
A kind of fruit preservative paper includes following component according to the mass fraction：15 ~ 25 parts of ethyl celluloses, 2 ~ 5 parts of plasticizer, 2 ~ 5
Part inorganic powder, 15 ~ 20 parts of epsilon-polylysines, 40 ~ 60 parts of water, which is characterized in that further include 25 ~ 35 parts of composite modified chitosans
Ingredient, 20 ~ 40 parts of spinach compound extracted solutions；
The preparation method of the composite modified constituent of chitosan, includes the following steps：
（1）The chitosan taken in mass ratio 1：10 ~ 15, which are added acetic acid solution, is mixed, and stands, obtains chitosan liquid, in mass ratio
1：10 ~ 15 take sodium alginate to be mixed with water, obtain sodium alginate soln, take sodium alginate soln in mass ratio 1：1 ~ 2 is added
Gelatin solution is uniformly mixed, and ultrasonic wave defoaming obtains mixed liquor, takes mixed liquor in mass ratio 1：0.3：2 ~ 4 are added crosslinking agent, shell gathers
Liquid glucose is mixed, and stands, obtains modification of chitosan solution, spare；
（2）In mass ratio 1：1：15 ~ 20 take zeolite, sepiolite, saturation liquor potassic permanganate to be mixed, and in 100 ~ 110 DEG C, add
3 ~ 5h of heat is stood, cooling, and filtering takes filter residue and drying, obtains pretreatment building stones；
（3）Pretreatment stone pulverizing sieving is taken, sieving particle in mass ratio 1 is taken:3~5：2：7 ~ 8 are added step（1）In it is spare
Modification of chitosan solution, epoxychloropropane, acetic acid solution obtain mixture in 25 ~ 40 DEG C of mixings, take mixture to be added mixed
The NaOH solution for closing material quality 5 ~ 10% is mixed, and stands, and filtering takes filter residue in mass ratio 1:3 ~ 5 wash with water, dry, i.e.,
Obtain composite modified constituent of chitosan；
The preparation method of the spinach compound extracted solution, includes the following steps：
S1. it is 1 in mass ratio with sodium bicarbonate solution to take spinach cleaning, go root segment, scalding：3 ~ 5 mixing, stand, obtain
Object is stood, takes the fructose for standing object addition standing amount of substance 5 ~ 10%, the sodium chloride of standing amount of substance 5 ~ 10% to be uniformly mixed, smashs to pieces
Homogenate, is concentrated under reduced pressure into the 20 ~ 30% of original volume, obtains spinach concentrate；
S2. it is 1 to take carbomer and water in mass ratio：20 ~ 30 are mixed, cooling, stand, and 2 ~ 3 times of carbomer quality is added
Chrysanthemum essential oil, the phosphatide that 1 ~ 4 times of carbomer quality, obtains viscous fluid, and it is 3 ~ 5 to take spinach concentrate and viscous fluid in mass ratio:1 is mixed
After conjunction, vacuum defoamation is to get spinach compound extracted solution.
Institute's gelatine solution：Take gelatin and water in mass ratio 1：20 ~ 30 mixing, stand swelling, and constant temperature stirs to get gelatin
Liquid.
The step（1）The crosslinking agent is in mass ratio 1：8 ~ 12 take Geniposide, absolute ethyl alcohol mixing, i.e. crosslinking agent.
The plasticizer is in mass ratio 1:1:2~3:8 take sorbierite, polyethylene glycol, glycerine, water mixing to get plasticising
Agent.
The inorganic powder is according to the mass fraction, to take 3 ~ 5 parts of magnesia, 8 ~ 15 parts of calcium hydroxy phosphates, 5 ~ 10 parts of pearls
Powder, 10 ~ 20 parts of bone meal, the mixing of 50 ~ 60 ethanol solutions are to get inorganic powder.
Compared with other methods, advantageous effects are the present invention：
The present invention is preprocessed as raw material using zeolite, sepiolite, can form high-voidage structural load potassium permanganate, can absorb fruit
The ethylene of ripe Surface Creation coordinates chitosan liquid-sodium alginate-gelatin structure gel rubber system, can strengthen and is melted into fresh-keeping antioxygen
Point and antipathogenic composition slow releasing function, to reach fresh-keeping, long-term antibacterial, the effect of Shelf-life, the ingredient in chrysanthemum essential oil
The position that the part functional group in skeleton of the present invention can be occupied promotes mechanical property to reduce the oscillation intensity of whole covalent bond
Can, the group that gained fruit preservative paper forms hydrophilic bond is reduced, and can assign its anti-moisture absorption, humidity resistance, has excellent antioxygen
The performances such as change, antibacterial pass through to improve fresh-keeping effect when packaging paper product uses to food and add a small amount of carbomer, profit
With a large amount of acid groups carried in carbomer molecular structure, hydrogen bond is formed with the glycosyl group in system, reinforces chitosan liquid-seaweed
Sour sodium-gelatin network, to improve the mechanical property of system, in addition, the active carbonyl group of fructose can obtain amine root with epsilon-polylysine
The schiff bases generated are reacted, carbomer molecule institute band acid groups can combine again with schiff bases, make schiff bases in rearrangement process
In, be arranged in gel network structure and fixed, improve the stability of tin foil system, persistence, can synergy it is fresh-keeping, it is long
Phase is antibacterial, Shelf-life.
Specific implementation mode
Polylysine：It is purchased from Jiangsu Fu Shengde bioengineering Co., Ltd.
Carbomer：Molecular weight is 940, is purchased from Xi Xing pharmaceutcal corporation, Ltds of Guan County.
Gelatin solution：Take gelatin and water in mass ratio 1：20 ~ 30 mixing, stand swelling, in 20 ~ 25 DEG C of constant temperature stirring 40 ~
60min is to get gelatin solution.
Crosslinking agent：In mass ratio 1：8 ~ 12 take Geniposide, absolute ethyl alcohol mixing, i.e. crosslinking agent.
Plasticizer：In 90 ~ 100 DEG C in mass ratio 1 of water-bath:1:2~3:8 take sorbierite, polyethylene glycol, glycerine, water mixing,
40 ~ 60min is stirred to get plasticizer with 200 ~ 300r/min.
Inorganic powder：According to the mass fraction, take 3 ~ 5 parts of magnesia, 8 ~ 15 parts of calcium hydroxy phosphates, 5 ~ 10 parts of pearl powders, 10 ~
20 parts of bone meal, 50 ~ 60 parts of mass fractions are that 75% ethanol solution mixes to get inorganic powder.
The preparation method of composite modified constituent of chitosan, includes the following steps：
（1）It is 95% chitosan in mass ratio 1 to take deacetylation：The acetic acid solution mixing that 10 ~ 15 addition mass fractions are 8% is set
In magnetic stirring apparatus, 1 ~ 2h is stirred with 220 ~ 250r/min in 25 ~ 35 DEG C, 2 ~ 3h of swelling is stood, obtains chitosan liquid, in mass ratio
1：10 ~ 15 take sodium alginate to be mixed with water, and the rear gelatin solution that is added is uniformly mixed, and ultrasonic wave defoams 5 ~ 7h, obtains mixed liquor,
Take mixed liquor in mass ratio 1：0.3：2 ~ 4 are added crosslinking agent, chitosan liquid, stir 40 ~ 60min with 300 ~ 350r/min, stand 1
~ 2h obtains modification of chitosan solution, spare；
（2）In mass ratio 1：1：15 ~ 20 take zeolite, sepiolite, saturation potassium permanganate to be mixed, and are bathed in 100 ~ 110 DEG C of greases,
3 ~ 5h is heated, rear standing of taking out is cooled to room temperature, filters, take filter residue in 70 ~ 80 DEG C of oven dryings, obtain pretreatment building stones；
（3）It takes pretreatment stone pulverizing to cross 80 mesh sieve, takes sieving particle in mass ratio 1:3~5：2：7 ~ 8 are added step（1）In it is standby
Modification of chitosan solution, epoxychloropropane, the acetic acid solution that mass fraction is 10%, 2 are mixed in 25 ~ 40 DEG C of water-bath ~
3h obtains mixture, takes mixture that the NaOH solution that the mass fraction of mixture quality 5 ~ 10% is 40% is added and is mixed, stands
20 ~ for 24 hours, filtering takes filter residue in mass ratio 1:3 ~ 5 are cleaned with deionized water, in 70 ~ 85 DEG C of oven dryings to get composite modified
Constituent of chitosan.
The preparation method of spinach compound extracted solution, includes the following steps：
S1. it is that 2 ~ 5cm segments are with mass fraction through 85 ~ 95 DEG C of 3 ~ 7min of scalding to take spinach cleaning, root is gone to cut spinach
20% sodium bicarbonate solution is 1 in mass ratio：3 ~ 5 mixing, stand 2 ~ 3h, obtain standing object, take and stand object addition standing amount of substance
5 ~ 10% fructose, the sodium chloride for standing amount of substance 5 ~ 10% are uniformly mixed, and are placed in tissue mashing machine and are smashed homogenate to pieces, are concentrated under reduced pressure into
The 20 ~ 30% of original volume obtain spinach concentrate；
S2. it is 1 to take carbomer and water in mass ratio：20 ~ 30 are mixed in 40 ~ 50 DEG C of water-bath heating stirring 20 ~ 40min, naturally cold
But, 1 ~ 2h of swelling is stood, the chrysanthemum essential oil of 2 ~ 3 times of carbomer quality is added, the phosphatide that 1 ~ 4 times of carbomer quality obtains viscous fluid,
It is 3 ~ 5 to take spinach concentrate and viscous fluid in mass ratio:1 mixing, vacuum defoamation is to get spinach compound extracted solution.
A kind of preparation method of fruit preservative paper, includes the following steps：
（1）According to the mass fraction, take 15 ~ 25 parts of ethyl celluloses, 2 ~ 5 parts of plasticizer, 2 ~ 5 parts of inorganic powders, 15 ~ 20 parts poly- rely
Propylhomoserin, 40 ~ 60 parts of water, 25 ~ 35 parts of composite modified constituent of chitosan, 20 ~ 40 parts of spinach compound extracted solutions；
（2）In 40 ~ 55 DEG C, take ethyl cellulose, inorganic powder, composite modified constituent of chitosan in reaction kettle be mixed 1 ~
2h, after be cooled to 20 ~ 25 DEG C be added plasticizer, spinach compound extracted solution, epsilon-polylysines mixing, with 300 ~ 350r/min stir
40 ~ 60min obtains antistaling coating, and antistaling coating is taken to be sprayed on the side of individual wood pulp body paper, stands 5 ~ 10min, and spraying again is protected
Fresh coating stands 5 ~ 10min in wood pulp body paper homonymy, dries to get fruit preservative paper.
Polylysine：It is purchased from Jiangsu Fu Shengde bioengineering Co., Ltd.
Carbomer：Molecular weight is 940, is purchased from Xi Xing pharmaceutcal corporation, Ltds of Guan County.
Gelatin solution：Take gelatin and water in mass ratio 1：20 mixing, stand swelling, in 20 DEG C of constant temperature stirring 40min to get
Gelatin solution.
Crosslinking agent：In mass ratio 1：8 take Geniposide, absolute ethyl alcohol mixing, i.e. crosslinking agent.
Plasticizer：In 90 DEG C in mass ratio 1 of water-bath:1:2:8 take sorbierite, polyethylene glycol, glycerine, water mixing, with 200r/
Min stirs 40min to get plasticizer.
Inorganic powder：According to the mass fraction, 3 parts of magnesia, 8 parts of calcium hydroxy phosphates, 5 parts of pearl powders, 10 parts of bone meal, 50 are taken
Part mass fraction is that 75% ethanol solution mixes to get inorganic powder.
The preparation method of composite modified constituent of chitosan, includes the following steps：
（1）It is 95% chitosan in mass ratio 1 to take deacetylation：The acetic acid solution mixing that 10 addition mass fractions are 8% is placed in
Magnetic stirring apparatus stirs 1h in 25 DEG C with 220r/min, stands swelling 2h, obtains chitosan liquid, in mass ratio 1：10 take alginic acid
Sodium is mixed with water, and the rear gelatin solution that is added is uniformly mixed, and ultrasonic wave defoams 5h, obtains mixed liquor, takes mixed liquor in mass ratio
1：0.3：2 are added crosslinking agent, chitosan liquid, stir 40min with 300r/min, stand 1h, obtain modification of chitosan solution, spare；
（2）In mass ratio 1：1：15 take zeolite, sepiolite, saturation potassium permanganate to be mixed, and are bathed in 100 DEG C of greases, heat 3h,
It takes out to stand afterwards and be cooled to room temperature, filter, take filter residue in 70 DEG C of oven dryings, obtain pretreatment building stones；
（3）It takes pretreatment stone pulverizing to cross 80 mesh sieve, takes sieving particle in mass ratio 1:3：2：7 are added step（1）In it is spare
Modification of chitosan solution, epoxychloropropane, the acetic acid solution that mass fraction is 10% must be mixed in 25 DEG C of mixing 2h of water-bath
Material takes mixture that the NaOH solution that the mass fraction of mixture quality 5% is 40% is added and is mixed, stands 20h, filtering takes
Filter residue in mass ratio 1:3 are cleaned with deionized water, in 70 DEG C of oven dryings to get composite modified constituent of chitosan.
The preparation method of spinach compound extracted solution, includes the following steps：
S1. it is 2cm segments to take spinach cleaning, root is gone to cut spinach, through 85 DEG C of scalding 3min, the carbon for being 20% with mass fraction
Sour hydrogen sodium solution is 1 in mass ratio：3 mixing, stand 2h, obtain standing object, take and stand object the fructose, quiet for standing amount of substance 5% is added
The sodium chloride of glove quality 5% is uniformly mixed, and is placed in tissue mashing machine and is smashed homogenate to pieces, is concentrated under reduced pressure into the 20% of original volume, obtains spinach
Dish concentrate；
S2. it is 1 to take carbomer and water in mass ratio：20 are mixed in 40 DEG C of heating stirring 20min of water-bath, and natural cooling is stood molten
The chrysanthemum essential oil of 2 times of carbomer quality is added in swollen 1h, and the phosphatide that 1 times of carbomer quality obtains viscous fluid, take spinach concentrate with
Viscous fluid is 3 in mass ratio:1 mixing, vacuum defoamation is to get spinach compound extracted solution.
A kind of preparation method of fruit preservative paper, includes the following steps：
（1）According to the mass fraction, 15 parts of ethyl celluloses, 2 parts of plasticizer, 2 parts of inorganic powders, 15 parts of epsilon-polylysines, 40 are taken
Part water, 25 parts of composite modified constituent of chitosan, 20 parts of spinach compound extracted solutions；
（2）In 40 DEG C, take ethyl cellulose, inorganic powder, composite modified constituent of chitosan that 1h is mixed in reaction kettle, it is rear to drop
Temperature is added plasticizer, spinach compound extracted solution, epsilon-polylysine to 20 DEG C and mixes, and stirs 40min with 300r/min, obtains fresh-keeping painting
Material takes antistaling coating to be sprayed on the side of individual wood pulp body paper, stands 5min, and it is same in wood pulp body paper to spray antistaling coating again
Side stands 5min, dries to get fruit preservative paper.
Polylysine：It is purchased from Jiangsu Fu Shengde bioengineering Co., Ltd.
Carbomer：Molecular weight is 940, is purchased from Xi Xing pharmaceutcal corporation, Ltds of Guan County.
Gelatin solution：Take gelatin and water in mass ratio 1：30 mixing, stand swelling, in 25 DEG C of constant temperature stirring 60min to get
Gelatin solution.
Crosslinking agent：In mass ratio 1：12 take Geniposide, absolute ethyl alcohol mixing, i.e. crosslinking agent.
Plasticizer：In 100 DEG C in mass ratio 1 of water-bath:1:3:8 take sorbierite, polyethylene glycol, glycerine, water mixing, with
300r/min stirs 60min to get plasticizer.
Inorganic powder：According to the mass fraction, take 5 parts of magnesia, 15 parts of calcium hydroxy phosphates, 10 parts of pearl powders, 20 parts of bone meal,
60 parts of mass fractions are that 75% ethanol solution mixes to get inorganic powder.
The preparation method of composite modified constituent of chitosan, includes the following steps：
（1）It is 95% chitosan in mass ratio 1 to take deacetylation：The acetic acid solution mixing that 15 addition mass fractions are 8% is placed in
Magnetic stirring apparatus stirs 2h in 35 DEG C with 250r/min, stands swelling 3h, obtains chitosan liquid, in mass ratio 1：15 take alginic acid
Sodium is mixed with water, and the rear gelatin solution that is added is uniformly mixed, and ultrasonic wave defoams 7h, obtains mixed liquor, takes mixed liquor in mass ratio
1：0.3：4 are added crosslinking agent, chitosan liquid, stir 60min with 350r/min, stand 2h, obtain modification of chitosan solution, spare；
（2）In mass ratio 1：1：20 take zeolite, sepiolite, saturation potassium permanganate to be mixed, and are bathed in 110 DEG C of greases, heat 5h,
It takes out to stand afterwards and be cooled to room temperature, filter, take filter residue in 80 DEG C of oven dryings, obtain pretreatment building stones；
（3）It takes pretreatment stone pulverizing to cross 80 mesh sieve, takes sieving particle in mass ratio 1:5：2：8 are added step（1）In it is spare
Modification of chitosan solution, epoxychloropropane, the acetic acid solution that mass fraction is 10% must be mixed in 40 DEG C of mixing 3h of water-bath
Material takes mixture that the NaOH solution that the mass fraction of mixture quality 10% is 40% is added and is mixed, stands for 24 hours, filtering takes
Filter residue in mass ratio 1:5 are cleaned with deionized water, in 85 DEG C of oven dryings to get composite modified constituent of chitosan.
The preparation method of spinach compound extracted solution, includes the following steps：
S1. it is 5cm segments to take spinach cleaning, root is gone to cut spinach, through 95 DEG C of scalding 7min, the carbon for being 20% with mass fraction
Sour hydrogen sodium solution is 1 in mass ratio：5 mixing, stand 3h, obtain standing object, take stand object be added stand amount of substance 10% fructose,
The sodium chloride for standing amount of substance 10% is uniformly mixed, and is placed in tissue mashing machine and is smashed homogenate to pieces, is concentrated under reduced pressure into the 30% of original volume, obtains
Spinach concentrate；
S2. it is 1 to take carbomer and water in mass ratio：30 are mixed in 50 DEG C of heating stirring 40min of water-bath, and natural cooling is stood molten
The chrysanthemum essential oil of 3 times of carbomer quality is added in swollen 2h, and the phosphatide that 4 times of carbomer quality obtains viscous fluid, take spinach concentrate with
Viscous fluid is 5 in mass ratio:1 mixing, vacuum defoamation is to get spinach compound extracted solution.
A kind of preparation method of fruit preservative paper, includes the following steps：
（1）According to the mass fraction, 25 parts of ethyl celluloses, 5 parts of plasticizer, 5 parts of inorganic powders, 20 parts of epsilon-polylysines, 60 are taken
Part water, 35 parts of composite modified constituent of chitosan, 40 parts of spinach compound extracted solutions；
（2）In 55 DEG C, take ethyl cellulose, inorganic powder, composite modified constituent of chitosan that 2h is mixed in reaction kettle, it is rear to drop
Temperature is added plasticizer, spinach compound extracted solution, epsilon-polylysine to 25 DEG C and mixes, and stirs 60min with 350r/min, obtains fresh-keeping painting
Material takes antistaling coating to be sprayed on the side of individual wood pulp body paper, stands 10min, and it is same in wood pulp body paper to spray antistaling coating again
Side stands 10min, dries to get fruit preservative paper.
Polylysine：It is purchased from Jiangsu Fu Shengde bioengineering Co., Ltd.
Carbomer：Molecular weight is 940, is purchased from Xi Xing pharmaceutcal corporation, Ltds of Guan County.
Gelatin solution：Take gelatin and water in mass ratio 1：25 mixing, stand swelling, in 23 DEG C of constant temperature stirring 50min to get
Gelatin solution.
Crosslinking agent：In mass ratio 1：10 take Geniposide, absolute ethyl alcohol mixing, i.e. crosslinking agent.
Plasticizer：In 95 DEG C in mass ratio 1 of water-bath:1:2:8 take sorbierite, polyethylene glycol, glycerine, water mixing, with 250r/
Min stirs 50min to get plasticizer.
Inorganic powder：According to the mass fraction, take 4 parts of magnesia, 12 parts of calcium hydroxy phosphates, 7 parts of pearl powders, 15 parts of bone meal,
55 parts of mass fractions are that 75% ethanol solution mixes to get inorganic powder.
The preparation method of composite modified constituent of chitosan, includes the following steps：
（1）It is 95% chitosan in mass ratio 1 to take deacetylation：The acetic acid solution mixing that 13 addition mass fractions are 8% is placed in
Magnetic stirring apparatus stirs 1h in 30 DEG C with 235r/min, stands swelling 2h, obtains chitosan liquid, in mass ratio 1：13 take alginic acid
Sodium is mixed with water, and the rear gelatin solution that is added is uniformly mixed, and ultrasonic wave defoams 6h, obtains mixed liquor, takes mixed liquor in mass ratio
1：0.3：3 are added crosslinking agent, chitosan liquid, stir 50min with 325r/min, stand 1h, obtain modification of chitosan solution, spare；
（2）In mass ratio 1：1：17 take zeolite, sepiolite, saturation potassium permanganate to be mixed, and are bathed in 105 DEG C of greases, heat 4h,
It takes out to stand afterwards and be cooled to room temperature, filter, take filter residue in 75 DEG C of oven dryings, obtain pretreatment building stones；
（3）It takes pretreatment stone pulverizing to cross 80 mesh sieve, takes sieving particle in mass ratio 1:4：2：7 are added step（1）In it is spare
Modification of chitosan solution, epoxychloropropane, the acetic acid solution that mass fraction is 10% must be mixed in 33 DEG C of mixing 2h of water-bath
Material takes mixture that the NaOH solution that the mass fraction of mixture quality 7% is 40% is added and is mixed, stands 22h, filtering takes
Filter residue in mass ratio 1:4 are cleaned with deionized water, in 77 DEG C of oven dryings to get composite modified constituent of chitosan.
The preparation method of spinach compound extracted solution, includes the following steps：
S1. it is 4cm segments to take spinach cleaning, root is gone to cut spinach, through 90 DEG C of scalding 5min, the carbon for being 20% with mass fraction
Sour hydrogen sodium solution is 1 in mass ratio：4 mixing, stand 2h, obtain standing object, take and stand object the fructose, quiet for standing amount of substance 7% is added
The sodium chloride of glove quality 7% is uniformly mixed, and is placed in tissue mashing machine and is smashed homogenate to pieces, is concentrated under reduced pressure into the 25% of original volume, obtains spinach
Dish concentrate；
S2. it is 1 to take carbomer and water in mass ratio：25 are mixed in 45 DEG C of heating stirring 30min of water-bath, and natural cooling is stood molten
The chrysanthemum essential oil of 2 times of carbomer quality is added in swollen 1h, and the phosphatide that 2 times of carbomer quality obtains viscous fluid, take spinach concentrate with
Viscous fluid is 4 in mass ratio:1 mixing, vacuum defoamation is to get spinach compound extracted solution.
A kind of preparation method of fruit preservative paper, includes the following steps：
（1）According to the mass fraction, 20 parts of ethyl celluloses, 3 parts of plasticizer, 3 parts of inorganic powders, 17 parts of epsilon-polylysines, 50 are taken
Part water, 30 parts of composite modified constituent of chitosan, 30 parts of spinach compound extracted solutions；
（2）In 47 DEG C, take ethyl cellulose, inorganic powder, composite modified constituent of chitosan that 1h is mixed in reaction kettle, it is rear to drop
Temperature is added plasticizer, spinach compound extracted solution, epsilon-polylysine to 23 DEG C and mixes, and stirs 50min with 325r/min, obtains fresh-keeping painting
Material takes antistaling coating to be sprayed on the side of individual wood pulp body paper, stands 7min, and it is same in wood pulp body paper to spray antistaling coating again
Side stands 7min, dries to get fruit preservative paper.
Comparative example 1：It is essentially identical with the preparation method of embodiment 1, have only unlike lack composite modified chitosan at
Point.
Comparative example 2：It is essentially identical with the preparation method of embodiment 1, it has only the difference is that lacking spinach compound extracted solution.
Comparative example 3：The tin foil of company of Weifang City production.
Tin foil in the tin foil and comparative example that are obtained respectively using above-described embodiment wraps up honey peach, fresh-keeping comparison inspection
Survey result such as table 1.
Table 1：
| Detection project | Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative example 1 | Comparative example 2 | Comparative example 3 |
| Wrap up fruit | Honey peach | Honey peach | Honey peach | Honey peach | Honey peach | Honey peach |
| Standing time（It） | 14 | 15 | 15 | 13 | 10 | 4~5 |
| Temperature in use DEG C | 25 | 25 | 25 | 25 | 25 | 25 |
| As a result | Without rotten | Without rotten | Without rotten | Without rotten | It is slight to rot | It rots apparent |
In summary, tin foil of the invention is of good preservation effect, and action time is longer, and comprehensive performance is better than presently commercially available product,
It is worth of widely use.
Claims (5)
1. a kind of fruit preservative paper includes following component according to the mass fraction：15 ~ 25 parts of ethyl celluloses, 2 ~ 5 parts of plasticizer, 2
~ 5 parts of inorganic powders, 15 ~ 20 parts of polylysines, 40 ~ 60 parts of water, which is characterized in that further include 25 ~ 35 parts of composite modified chitosans
Ingredient, 20 ~ 40 parts of spinach compound extracted solutions；
The preparation method of the composite modified constituent of chitosan, includes the following steps：
（1）The chitosan taken in mass ratio 1：10 ~ 15, which are added acetic acid solution, is mixed, and stands, obtains chitosan liquid, in mass ratio
1：10 ~ 15 take sodium alginate to be mixed with water, obtain sodium alginate soln, take sodium alginate soln in mass ratio 1：1 ~ 2 is added
Gelatin solution is uniformly mixed, and ultrasonic wave defoaming obtains mixed liquor, takes mixed liquor in mass ratio 1：0.3：2 ~ 4 are added crosslinking agent, shell gathers
Liquid glucose is mixed, and stands, obtains modification of chitosan solution, spare；
（2）In mass ratio 1：1：15 ~ 20 take zeolite, sepiolite, saturation liquor potassic permanganate to be mixed, and in 100 ~ 110 DEG C, add
3 ~ 5h of heat is stood, cooling, and filtering takes filter residue and drying, obtains pretreatment building stones；
（3）Pretreatment stone pulverizing sieving is taken, sieving particle in mass ratio 1 is taken:3~5：2：7 ~ 8 are added step（1）In it is spare
Modification of chitosan solution, epoxychloropropane, acetic acid solution obtain mixture in 25 ~ 40 DEG C of mixings, take mixture to be added mixed
The NaOH solution for closing material quality 5 ~ 10% is mixed, and stands, and filtering takes filter residue in mass ratio 1:3 ~ 5 wash with water, dry, i.e.,
Obtain composite modified constituent of chitosan；
The preparation method of the spinach compound extracted solution, includes the following steps：
S1. it is 1 in mass ratio with sodium bicarbonate solution to take spinach cleaning, go root segment, scalding：3 ~ 5 mixing, stand, obtain
Object is stood, takes the fructose for standing object addition standing amount of substance 5 ~ 10%, the sodium chloride of standing amount of substance 5 ~ 10% to be uniformly mixed, smashs to pieces
Homogenate, is concentrated under reduced pressure into the 20 ~ 30% of original volume, obtains spinach concentrate；
S2. it is 1 to take carbomer and water in mass ratio：20 ~ 30 are mixed, cooling, stand, and 2 ~ 3 times of carbomer quality is added
Chrysanthemum essential oil, the phosphatide that 1 ~ 4 times of carbomer quality, obtains viscous fluid, and it is 3 ~ 5 to take spinach concentrate and viscous fluid in mass ratio:1 is mixed
After conjunction, vacuum defoamation is to get spinach compound extracted solution.
2. fruit preservative paper according to claim 1, which is characterized in that institute's gelatine solution：Take gelatin and water in mass ratio
1：20 ~ 30 mixing, stand swelling, and constant temperature stirs to get gelatin solution.
3. fruit preservative paper according to claim 1, which is characterized in that the step（1）The crosslinking agent is in mass ratio
1：8 ~ 12 take Geniposide, absolute ethyl alcohol mixing, i.e. crosslinking agent.
4. fruit preservative paper according to claim 1, which is characterized in that the plasticizer is in mass ratio 1:1:2~3:8 take
Sorbierite, polyethylene glycol, glycerine, water mixing are to get plasticizer.
5. fruit preservative paper according to claim 1, which is characterized in that the inorganic powder is according to the mass fraction, to take 3 ~ 5
Part magnesia, 8 ~ 15 parts of calcium hydroxy phosphates, 5 ~ 10 parts of pearl powders, 10 ~ 20 parts of bone meal, the mixing of 50 ~ 60 ethanol solutions are to get inorganic
Powder.