CN108693574A - A kind of preparation method of optical diaphragm, back-cover and electronic equipment - Google Patents
A kind of preparation method of optical diaphragm, back-cover and electronic equipment Download PDFInfo
- Publication number
- CN108693574A CN108693574A CN201810460221.5A CN201810460221A CN108693574A CN 108693574 A CN108693574 A CN 108693574A CN 201810460221 A CN201810460221 A CN 201810460221A CN 108693574 A CN108693574 A CN 108693574A
- Authority
- CN
- China
- Prior art keywords
- pressure disc
- rupture pressure
- flash
- layer
- face
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of preparation method of optical diaphragm, back-cover and electronic equipment, this method to include:The mold of preset optical structure is obtained, preset optical structure is multi-level optical figuring structure;First rupture pressure disc of predetermined size is fitted in mold, the corresponding texture of preset optical structure is transferred on the first rupture pressure disc by transfer printing process, to form the second rupture pressure disc with texture face;By optical coating technique, it is coated with electroplated layer on the texture face of the second rupture pressure disc, to form third rupture pressure disc;By silk-screen printing technique, face where the electroplated layer of third rupture pressure disc is printed to the ink layer of pre-color, to form the 4th rupture pressure disc;4th rupture pressure disc is placed in laser carving machine platform, laser carving molding is carried out so that the optical diaphragm gloss level prepared enriches nature and has color gradient effect.
Description
Technical field
The present invention relates to a kind of manufacturing technology field more particularly to preparation method of optical diaphragm, back-cover and electronics
Equipment.
Background technology
With the rapid development of electronic equipment, electronic product update is rapid, the electronic product dog-eat-dog of each famous brand.For
The probability of transaction for improving electronic product needs the fashion perceived value for promoting electronic product.
Currently, by the way that the back-cover of electronic product is designed to various patterns, to promote the stylishness of electronic product
Know value.But the pattern displaying single effect in existing back-cover, lack stereovision.
Invention content
The embodiment of the present invention provides a kind of preparation method of optical diaphragm, back-cover and electronic equipment, to solve the prior art
The problem of optical diaphragm display effect of middle preparation is single, shortage stereovision.
In order to solve the above-mentioned technical problem, the invention is realized in this way:
In a first aspect, the present invention provides a kind of preparation method of optical diaphragm, this method includes:
The mold of preset optical structure is obtained, the preset optical structure is multi-level optical figuring structure;
In the mould by the fitting of the first rupture pressure disc of predetermined size, by transfer printing process by the preset optical structure
Corresponding texture is transferred on first rupture pressure disc, to form the second rupture pressure disc with texture face;
By optical coating technique, it is coated with electroplated layer on the texture face of second rupture pressure disc, it is explosion-proof to form third
Film;
By silk-screen printing technique, face where the electroplated layer of the third rupture pressure disc is printed to the ink of pre-color
Layer, to form the 4th rupture pressure disc;
4th rupture pressure disc is placed in laser carving machine platform, laser carving molding is carried out.
Second aspect, the present invention also provides a kind of back-cover, which includes:
The material of lid, the lid is glass or acrylic material;The top surface is covered with optical diaphragm, described
Optical diaphragm is what the preparation method based on optical diaphragm described above generated.
The third aspect, the present invention also provides a kind of electronic equipment, which includes back-cover described above.
Technical scheme of the present invention can reach following advantageous effect:
In embodiments of the present invention, by using the mold of preset optical structure so that the optical diaphragm prepared is presented
Go out multi-level optical texture, there is stereovision;Again by the way that the first rupture pressure disc of predetermined size to be fitted in the mold, pass through
The corresponding texture of preset optical structure is transferred on the first rupture pressure disc by transfer printing process, anti-to form second with texture face
Quick-fried film is coated with electroplated layer on the texture face of the second rupture pressure disc, to form third rupture pressure disc, is passed through by optical coating technique
Face where the electroplated layer of third rupture pressure disc is printed to the ink layer of pre-color by silk-screen printing technique, explosion-proof to form the 4th
4th rupture pressure disc is placed in laser carving machine platform by film, carries out laser carving molding so that the optical diaphragm gloss level prepared is rich
Rich nature and have color gradient effect, meets fashion, the appearance demand of trend of consumer's pursuit.
Description of the drawings
Fig. 1 is the flow chart of the preparation method of optical diaphragm provided in an embodiment of the present invention;
Fig. 2 is the effect diagram of back-cover provided in an embodiment of the present invention.
Specific implementation mode
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation describes, it is clear that described embodiments are some of the embodiments of the present invention, instead of all the embodiments.Based on this hair
Embodiment in bright, the every other implementation that those of ordinary skill in the art are obtained without creative efforts
Example, shall fall within the protection scope of the present invention.The technical solution provided below in conjunction with attached drawing, each embodiment that the present invention will be described in detail.
Fig. 1 is the flow chart of the preparation method of optical diaphragm provided in an embodiment of the present invention, as shown in Figure 1, this method can
To include:
Step 101, the mold for obtaining preset optical structure.
The preset optical structure is multi-level optical figuring structure.
For example, the preset optical structure can be multi-level lattice structure, alternatively, the preset optical structure can be
Multi-level dot structure, etc..Certainly, which can also be other multi-level optical figuring structures,
The present invention, which implements, will not enumerate.
First rupture pressure disc of predetermined size is bonded in the mould by step 102, will be described default by transfer printing process
The corresponding texture of optical texture is transferred on first rupture pressure disc, to form the second rupture pressure disc with texture face.
Sheet material made of first rupture pressure disc of the predetermined size can be cut by explosion-proof film coiled material.
Wherein, explosion-proof film coiled material can be 25 μ by the polyethylene terephthalate (PET) and thickness that thickness is 50 μ
Optical cement OCA (OCA) glue-line made of.
The predetermined size can be long 300MM, width 400MM.Certainly, which can also be other numerical value, this hair
Bright embodiment does not limit specifically, and when specific implementation can set according to actual demand.
In this step, which may be used existing transfer printing process.
Step 103, by optical coating technique, be coated with electroplated layer on the texture face of second rupture pressure disc, with formed
Third rupture pressure disc.
In this step, which may be used existing optical coating technique.
Wherein, the environment of the optical coating technique needs to reach thousand grades of cleanings.
Step 104, by silk-screen printing technique, face where the electroplated layer of the third rupture pressure disc is printed to pre-color
Ink layer, to form the 4th rupture pressure disc.
In this step, which may be used existing silk-screen printing technique.
Wherein, the environment of the silk-screen printing technique needs to reach thousand grades of cleanings.
4th rupture pressure disc is placed in laser carving machine platform by step 105, carries out laser carving molding.
In this step, which may be used existing numerically-controlled machine tool (CNC) laser carving technique.
In embodiments of the present invention, by using the mold of preset optical structure so that the optical diaphragm prepared is presented
Go out multi-level optical texture, there is stereovision;Again by the way that the first rupture pressure disc of predetermined size to be fitted in the mold, pass through
The corresponding texture of preset optical structure is transferred on the first rupture pressure disc by transfer printing process, anti-to form second with texture face
Quick-fried film is coated with electroplated layer on the texture face of the second rupture pressure disc, to form third rupture pressure disc, is passed through by optical coating technique
Face where the electroplated layer of third rupture pressure disc is printed to the ink layer of pre-color by silk-screen printing technique, explosion-proof to form the 4th
4th rupture pressure disc is placed in laser carving machine platform by film, carries out laser carving molding so that the optical diaphragm gloss level prepared is rich
Rich nature and have color gradient effect, meets fashion, the appearance demand of trend of consumer's pursuit.
Optionally, as one embodiment, preset optical structure described in above-described embodiment may include:Bottom, light beam
Lamina and N layers of flash-point layer.Wherein,
The bottom is the crosslamination of default geometric figure, which can be lattice or dot or small
Triangle etc..Wherein, the design of the bottom applies light and shade visual angle and interlocks principle of contrast.
In the embodiment of the present invention, by taking bottom is lattice crosslamination as an example, the lattice crosslamination is in line-of-sight distance
Remotely, it can present and indistinct set off effect.In practical applications, the size of the lattice in the lattice crosslamination
Can be 0.4*0.4mm.
The light beam lamina is laid on the bottom, and the design of the light beam lamina applies refraction and the principle of reflection of light.Edge
With above-mentioned example, bottom can be lattice crosslamination, which is laid on lattice crosslamination, can be in light and shade lattice
The sense of running that light beam is presented on son, increases the smart of bottom.In practical applications, the line of the light beam in the light beam lamina
Wide can be 40 μm, and line-spacing can be 50 μm.
The N layers of flash-point layer is laid on the light beam lamina.Wherein, the first flash-point layer in the N layers of flash-point layer to M dodge
Point layer is positive visual angle flash-point layer, and M+1 flash-points layer to P flash-point layers is left side perspective flash-point layer, and P+1 flash-points layer to Q dodges
Point layer is that right side perspective flash-point layer, N >=Q > P > M, and N, Q, P and M are positive integer.
Illustratively, it can be 5, P can be 10, Q can be 16 that N, which can be 16, M, then 16 layers of flash-point layer are laid with
On the light beam lamina.Wherein, the first flash-point layer to the 5th flash-point layer in 16 layers of flash-point layer is positive visual angle flash-point layer, the
Six flash-point layers to the tenth flash-point layer are left side perspective flash-point layer, and the 11st flash-point layer to the 16th flash-point layer is right side perspective flash-point
Layer.
Wherein, the design of the N layers of flash-point layer applies diffusing reflection principle, and controllable light is in the visible of different angle or not
It can be seen that.Therefore, which will present the bright spot of different sparkling lusters under positive visual angle;The left side perspective flash-point layer exists
It will present the bright spot of different sparkling lusters under left side perspective;The right side perspective flash-point layer will present different flickers under right side perspective
The bright spot of gloss.
In practical applications, flash-point random arrangement in the region that size is 0.4*0.4mm in the positive visual angle flash-point layer, should
Flash-point random arrangement, flash-point in the right side perspective flash-point layer in the region that size is 0.4*0.4mm in left side perspective flash-point layer
The random arrangement in the region that size is 0.4*0.4mm.
You need to add is that the design of the preset optical structure combines nanoscale ultrahigh precision processing technology.
The embodiment of the present invention, by using the mold of the preset optical structure so that the optical diaphragm prepared has ten
Kind or more different optics layer variabilities, realize that gloss changes with conversion angle, generate the bright dynamic light that gleams of light are reflecting on waves in the river
Pool, the fashion visual experience to find everything fresh and new to people meet fashion, the appearance demand of trend of consumer's pursuit.
Optionally, further include before executing step 102 as one embodiment:
First rupture pressure disc is made by fade effect face using gradient prints technique on one side;
In this step, which may be used existing gradient prints technique.
Correspondingly, step 102 specifically can be achieved be:The fade effect face of first rupture pressure disc is fitted in the mold
It is interior.
By using gradient prints technique fade effect is made in first rupture pressure disc by the embodiment of the present invention on one side
Face makes optical diaphragm to be prepared that can have color gradient effect and/or gloss fade effect so that the optical diaphragm prepared
Fashion, the appearance demand of trend of consumer's pursuit can more be met.
Optionally, as one embodiment, described first is prevented using gradient prints technique described in above-described embodiment
Fade effect face is made in quick-fried film on one side, specifically can be achieved be:
Using from around to center gradual change 4.5MM, the gradual change silk-screen file of gradual change 100MM, prepares galley from bottom to top;
First rupture pressure disc is placed on the platform of the printing machine equipped with the galley and is printed, to obtain
The first rupture pressure disc with fade effect face.
Illustratively, concrete operation step can be:It first, will be from around to center gradual change 4.5MM, from bottom to top gradual change
The gradual change silk-screen file of 100MM, is prepared into galley;Then, by galley on UV printing machines, the first rupture pressure disc is placed
On the platform of printing machine, booting printing, to obtain first rupture pressure disc with fade effect face.
Supplement is needed exist for, the fade effect face of the first rupture pressure disc is damaged in order to prevent, after being completed for printing,
Protective film is attached on the fade effect face of first rupture pressure disc, to ensure that fade effect face is injury-free.When continuing step after execution,
The protective film is torn again.
The embodiment of the present invention, by using from around to center gradual change 4.5MM, the gradual change silk of gradual change 100MM from bottom to top
Printed text part prepares galley, the first rupture pressure disc is placed on the platform of the printing machine equipped with galley and is printed, makes to wait for
The optical diaphragm entirety luster effect of preparation is strong by four circumferentially intermediate changes, becomes strong from bottom to top, can more meet consumer's pursuit
Fashion, the appearance demand of trend.
Optionally, as one embodiment, step 102 specifically can be achieved be:
Injection transfer glue in the mould, to form transfer glue-line;
First rupture pressure disc is placed in the mold with the transfer glue-line;
First rupture pressure disc and transfer glue lamination are closed by pressing process, by the preset optical structure pair
The texture answered is transferred on first rupture pressure disc;
Cure first rupture pressure disc and the transfer glue-line by curing process, it is explosion-proof to form second with texture face
Film.
In this step, which may be used existing pressing process.Illustratively, which can be to adopt
The first rupture pressure disc and transfer glue-line are suppressed with pressure roller, the first rupture pressure disc is made to be bonded completely with transfer glue-line.
In this step, which may be used existing curing process.Illustratively, which may be used
Ultraviolet light cures.
Supplement is needed exist for, the first rupture pressure disc is askew in order to prevent sets in mold, has the first positioning in the mold
First rupture pressure disc is placed on by structure correspondingly, the first rupture pressure disc is equipped with the second location structure corresponding with the location structure
After in mold, the first location structure is aligned with the second location structure, and to effectively prevent in mold, the first rupture pressure disc is askew to be set.Show
Example property, which can be positioning column, which can be location hole.
Supplement is needed exist for, the texture face of the second rupture pressure disc is damaged in order to prevent, after the completion of transfer, second
Protective film is attached on the texture face of rupture pressure disc, to ensure that texture face is injury-free.When continuing step after execution, then by the protective film
It tears.
Optionally, as one embodiment, step 103 specifically can be achieved be:
Second rupture pressure disc is placed in the optics plating stove of preset optical degree parameter, to the line of second rupture pressure disc
Reason face is coated with electroplated layer with 50mins-60mins durations, forms third rupture pressure disc.
The preset optical degree parameter can be the wavelength of RGB three coloured lights.It in practical applications, can be according to actual color
Demand sets preset optical degree parameter, and the embodiment of the present invention is not specifically limited.
Supplement is needed exist for, the electroplated layer of third rupture pressure disc is damaged in order to prevent, after the completion of being coated with, in third
Protective film is attached on the electroplated layer of rupture pressure disc, to ensure that electroplated layer is injury-free.When continuing step after execution, then by the protective film
It tears.
In the embodiment of the present invention, by the way that the second rupture pressure disc to be placed in the optics plating stove of preset optical degree parameter, to
The texture face of two rupture pressure discs is coated with electroplated layer with 50mins-60mins durations, to improve brightness and the color of rupture pressure disc so that light
Damp level it is abundant naturally, effect bright gleams of light are reflecting on waves in the river.
Optionally, as one embodiment, step 104 specifically can be achieved be:
The screen mesh printing plate that mesh number is 350 is covered on the electroplated layer of the third rupture pressure disc;
After the ink for printing pre-color on the screen mesh printing plate, preset time is toasted with preset temperature, forms the 4th
Rupture pressure disc;
Wherein, the ranging from 30-50 degree of the preset temperature, the ranging from 40-50mins of the preset time.It is preferred that
, preset temperature is 40 degree, preset time 45mins.
Wherein, the ink of preset color can arbitrarily be chosen according to actual demand, and the embodiment of the present invention is not specifically limited.
Illustratively, the present embodiment concrete operation step can be:First, third rupture pressure disc is adsorbed on screening printing platform
On, the screen mesh printing plate that mesh number is 350 is covered on the electroplated layer of the third rupture pressure disc;Second, it is printed on screen mesh printing plate
The ink of default pre-color, and the third rupture pressure disc for printing ink is placed on grill;Grill is put into oven by third
In, preset time is toasted with preset temperature, to achieve the purpose that thorough shading.In practical applications, the second step and second step
It can be in triplicate.
The embodiment of the present invention, by the way that mesh number to be covered in for 350 screen mesh printing plate on the electroplated layer of third rupture pressure disc, in silk
After the ink for printing pre-color on net halftone, preset time is toasted with preset temperature, to embody the color of rupture pressure disc so that light
Damp level it is more rich naturally, effect more bright gleams of light are reflecting on waves in the river.
In the specific implementation, face where the ink layer of the 4th rupture pressure disc is damaged above-described embodiment in order to prevent, is being printed
After the completion, protective film is attached on the whole in the ink layer of the 4th rupture pressure disc, to ensure that face where ink layer is injury-free.It is holding
When row subsequent step, which can be torn.
Optionally, as one embodiment, the mold described in above-described embodiment is the duplication replicated by original mould
Mold saves original mould, realizes the recycling to the preset optical structure in original mould, and practicability is higher.
Supplement is needed exist for, after executing step 105, to ginsengs such as appearance, the sizes of the optical diaphragm prepared
Number is tested according to predetermined quality standard, and qualified optical diaphragm will be examined to pack.
More than, the preparation method of the optical diaphragm of the embodiment of the present invention is described in detail in conjunction with Fig. 1, in the following, in conjunction with Fig. 2,
The back-cover for embodiment that the present invention will be described in detail.
Fig. 2 shows the effect diagrams of back-cover provided in an embodiment of the present invention, as shown in Fig. 2, the back-cover includes lid,
The material of the lid is glass or acrylic material.Wherein, the top surface is covered with optical diaphragm, the optical diaphragm
It is what the preparation method based on the optical diaphragm described in above-described embodiment generated.Specific preparation process, refers to above-described embodiment,
The embodiment of the present invention repeats no more.
In embodiments of the present invention, by using the mold of preset optical structure so that the optical diaphragm prepared is presented
Go out multi-level optical texture, there is stereovision;Again by the way that the first rupture pressure disc of predetermined size to be fitted in the mold, pass through
The corresponding texture of preset optical structure is transferred on the first rupture pressure disc by transfer printing process, anti-to form second with texture face
Quick-fried film is coated with electroplated layer on the texture face of the second rupture pressure disc, to form third rupture pressure disc, is passed through by optical coating technique
Face where the electroplated layer of third rupture pressure disc is printed to the ink layer of pre-color by silk-screen printing technique, explosion-proof to form the 4th
4th rupture pressure disc is placed in laser carving machine platform by film, carries out laser carving molding so that the optical diaphragm gloss level prepared is rich
Rich nature and have color gradient effect, meets fashion, the appearance demand of trend of consumer's pursuit.
It is above a kind of preparation method of optical diaphragm provided by the invention, the preparation method based on the optical diaphragm, this
The embodiment of invention also provides a kind of electronic equipment, including the back-cover described in foregoing invention embodiment.
It should be noted that herein, the terms "include", "comprise" or its any other variant are intended to non-row
His property includes, so that process, method, article or device including a series of elements include not only those elements, and
And further include other elements that are not explicitly listed, or further include for this process, method, article or device institute it is intrinsic
Element.In the absence of more restrictions, the element limited by sentence "including a ...", it is not excluded that including this
There is also other identical elements in the process of element, method, article or device.
The embodiment of the present invention is described with above attached drawing, but the invention is not limited in above-mentioned specific
Embodiment, the above mentioned embodiment is only schematical, rather than restrictive, those skilled in the art
Under the inspiration of the present invention, without breaking away from the scope protected by the purposes and claims of the present invention, it can also make very much
Form belongs within the protection of the present invention.
Claims (10)
1. a kind of preparation method of optical diaphragm, which is characterized in that including:
The mold of preset optical structure is obtained, the preset optical structure is multi-level optical figuring structure;
In the mould by the first rupture pressure disc fitting of predetermined size, the preset optical structure is corresponded to by transfer printing process
Texture be transferred on first rupture pressure disc, with formed with texture face the second rupture pressure disc;
By optical coating technique, it is coated with electroplated layer on the texture face of second rupture pressure disc, to form third rupture pressure disc;
By silk-screen printing technique, face where the electroplated layer of the third rupture pressure disc is printed to the ink layer of pre-color, with
Form the 4th rupture pressure disc;
4th rupture pressure disc is placed in laser carving machine platform, laser carving molding is carried out.
2. according to the method described in claim 1, it is characterized in that, the preset optical structure includes:
Bottom, the bottom are the crosslamination of default geometric figure;
Light beam lamina, the light beam lamina are laid on the bottom;
N layers of flash-point layer, the N layers of flash-point layer are laid on the light beam lamina;
Wherein, the first flash-point layer in the N layers of flash-point layer to M flash-point layers are positive visual angle flash-point layer, M+1 flash-points layer to the
P flash-point layers be left side perspective flash-point layer, P+1 flash-points layer to Q flash-point layers be right side perspective flash-point layer, N >=Q > P > M, and
N, Q, P and M are positive integer.
3. according to the method described in claim 1, it is characterized in that, first rupture pressure disc of predetermined size is fitted in institute described
Before stating in mold, further include:
First rupture pressure disc is made by fade effect face using gradient prints technique on one side;
First rupture pressure disc by predetermined size is bonded in the mould, including:
The fade effect face paste of first rupture pressure disc is closed in the mould.
4. according to the method described in claim 3, it is characterized in that, described use gradient prints technique by first rupture pressure disc
Be made fade effect face on one side, including:
Using from around to center gradual change 4.5MM, the gradual change silk-screen file of gradual change 100MM, prepares galley from bottom to top;
According to the galley, fade effect face is made in first rupture pressure disc on one side.
5. according to the method described in claim 1, it is characterized in that, it is described first rupture pressure disc of predetermined size is fitted in it is described
In mold, the corresponding texture of the preset optical structure is transferred on first rupture pressure disc by transfer printing process, to be formed
The second rupture pressure disc with texture face, including:
Injection transfer glue in the mould, to form transfer glue-line;
First rupture pressure disc is placed in the mold with the transfer glue-line;
First rupture pressure disc and transfer glue lamination are closed by pressing process, the preset optical structure is corresponding
Texture is transferred on first rupture pressure disc;
Cure first rupture pressure disc and the transfer glue-line by curing process, forms the second rupture pressure disc with texture face.
6. explosion-proof described second according to the method described in claim 1, it is characterized in that, described by optical coating technique
It is coated with electroplated layer on the texture face of film, to form third rupture pressure disc, including:
Second rupture pressure disc is placed in the optics plating stove of preset optical degree parameter, to the texture face of second rupture pressure disc
It is coated with electroplated layer with 50mins-60mins durations, forms third rupture pressure disc.
7. according to the method described in claim 1, it is characterized in that, described by silk-screen printing technique, the third is explosion-proof
Face where the electroplated layer of film is printed to the ink layer of pre-color, to form the 4th rupture pressure disc, including:
The screen mesh printing plate that mesh number is 350 is covered on the electroplated layer of the third rupture pressure disc;
After the ink for printing pre-color on the screen mesh printing plate, preset time is toasted with preset temperature, it is explosion-proof to form the 4th
Film;
Wherein, the ranging from 30-50 degree of the preset temperature, the ranging from 40-50mins of the preset time.
8. according to the method described in claim 1, it is characterized in that, described be placed on laser carving machine platform by the 4th rupture pressure disc
Before interior, further include:
By face covering protection film where the ink layer of the 4th rupture pressure disc.
9. a kind of back-cover, which is characterized in that including:
The material of lid, the lid is glass or acrylic material;The top surface is covered with optical diaphragm, the optics
Diaphragm is what the preparation method based on the optical diaphragm described in any one of the claims 1-8 generated.
10. a kind of electronic equipment, which is characterized in that including:Back-cover described in the claims 9.