CN102956386B - Key and manufacturing method thereof - Google Patents

Key and manufacturing method thereof Download PDF

Info

Publication number
CN102956386B
CN102956386B CN201110239802.4A CN201110239802A CN102956386B CN 102956386 B CN102956386 B CN 102956386B CN 201110239802 A CN201110239802 A CN 201110239802A CN 102956386 B CN102956386 B CN 102956386B
Authority
CN
China
Prior art keywords
layer
color
key
character
body
Prior art date
Application number
CN201110239802.4A
Other languages
Chinese (zh)
Other versions
CN102956386A (en
Inventor
蒋安邦
莫均瑜
杨宇
马建
Original Assignee
比亚迪股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 比亚迪股份有限公司 filed Critical 比亚迪股份有限公司
Priority to CN201110239802.4A priority Critical patent/CN102956386B/en
Publication of CN102956386A publication Critical patent/CN102956386A/en
Application granted granted Critical
Publication of CN102956386B publication Critical patent/CN102956386B/en

Abstract

本发明提供了一种按键,其包括:按键本体,以及附着在按键本体表面的透光率大于50%的字符颜色层,所述字符颜色层上覆盖有透光率小于15%的边框颜色层,所述边框颜色层上覆盖有透光率小于15%的遮蔽层,所述遮蔽层上覆盖有按键主体颜色层,所述按键主体颜色层上覆盖有透光率大于50%的保护层;所述遮蔽层、按键主体颜色层部分镂空形成边框部;所述边框部部分镂空在边框颜色层上形成边框,所述字符颜色层从镂空部露出形成字符;所述字符颜色层与所述按键主体颜色层的颜色相同;所述边框颜色层与所述字符颜色层及按键主体颜色层的颜色不相同。 The present invention provides a key comprising: a key body and a key attached to the body surface of the light transmittance of greater than 50% of the character color layer, the color layer is covered with a character color of the border layer of the light transmittance of less than 15% the upper frame is covered with a layer of color light transmittance of less than 15% of the shielding layer, the shielding layer is covered with a color layer on the main key, the key is covered with a protective layer on the body layer color light transmittance of greater than 50%; the shielding layer, a color layer key body portion is formed hollow frame portion; said hollow frame portion is formed on the frame border color layer, the color layer is exposed from the hollow character portion is formed characters; the color layer and the character key the same color of the body layer color; color of the border color layer and the color layer and the key character layer is not the same as the color of the body. 本发明还提供了一种制造该按键的方法,本发明提供的按键可以明显区分字符区域与非字符区域。 The present invention further provides a method of manufacturing the key, provided by the present invention can be clearly distinguished key character region and the non-character region.

Description

一种按键及其制造方法 One kind of the key and its manufacturing method

技术领域 FIELD

[0001] 本发明属于手持电子设备按键领域,尤其涉及一种按键及其制造方法。 [0001] The present invention belongs to the field of handheld electronic device keys, and more particularly to a method of manufacturing the key.

背景技术 Background technique

[0002] 随着社会的不断进步,高效快速的沟通已经成为当今社会的主题,人们不再只把手机作为简单的通话工具,而在不断追求眩彩、新颖的外观,方便快捷的输入操作媒介及方法。 [0002] As society progresses, the rapid and efficient communication has been the subject of today's society, people are no longer just the phone call as a simple tool, and in constant pursuit of Xuancai, novel appearance, convenient operation input media and methods. 按键作为电子设备的关键组件,承担着外部指令输入作用。 Key as a key component of the electronic apparatus, the external command to assume the role of the input. 目前按键产品往往字符和非字符表面需要存在较大的颜色差异,才可以明显地区分按键上的字符,常见的如,非字符表面设置为黑色,字符为白色;非字符表面设置为白色,字符为蓝色或者灰色。 At present there is often need for character and non-character product key surface large color differences, we can clearly distinguish the characters on the keys, such as the common, non-surface character set to black, white characters; the surface is set to a non-character white, character blue or gray. 但是对于非字符表面颜色和字符颜色相同的按键产品,如需要非字符表面设置为白色,字符也为白色,则用户很难明显分辨字符的存在,影响用户的使用。 But for the same non-character color and surface character color key product, if necessary, a non-character is set to a white surface, also as a white character, the user is difficult to distinguish clearly the presence of the character, affect the user.

发明内容 SUMMARY

[0003] 本发明的目的是为了克服现有按键非字符区域与字符区域颜色相同,造成无法清晰分辨字符的技术问题,提供一种在非字符区域与字符区域颜色相同也能清晰分辨字符的按键及其制造方法。 [0003] The object of the present invention is to overcome the prior same key character region and the non-character region color, resulting character can not clearly distinguish the technical problem is provided a non-character region in the same region and the character colors can clearly distinguish the character keys and its manufacturing method.

[0004] 本发明提供了一种按键,包括按键本体,以及附着在按键本体表面的透光率大于50%的字符颜色层,所述字符颜色层上覆盖有透光率小于15%的边框颜色层,所述边框颜色层上覆盖有透光率小于15%的遮蔽层,所述遮蔽层上覆盖有按键主体颜色层,所述按键主体颜色层上覆盖有透光率大于50%的保护层;所述遮蔽层、按键主体颜色层部分镂空形成边框部;所述边框部部分镂空在边框颜色层上形成边框,所述字符颜色层从镂空部露出形成字符;所述字符颜色层与所述按键主体颜色层的颜色相同;所述边框颜色层与所述字符颜色层及按键主体颜色层的颜色不相同。 [0004] The present invention provides a key comprising a key body and a key attached to the surface of the body of the light transmittance of greater than 50% of the character color layer, the color of the character frame is covered with a color layer on the light transmittance of less than 15% layer, the upper layer covering the border color shielding layer light transmittance of less than 15%, the color layer is covered with a layer masking the key body, said key body is covered with a protective layer color layer is of a light transmittance greater than 50% ; the masking layer, the color layer key body portion is formed hollow frame portion; said hollow frame portion is formed on the frame border color layer, the color layer is exposed from the hollow character portion is formed characters; the character color layer and the a key body of the same color of the color layer; border color of the color layer and the color layer and the key character layer is not the same as the color of the body.

[0005] 另外,本发明还提供了一种按键制造方法,该方法包括如下步骤: [0005] Further, the present invention also provides a method for manufacturing a key, the method comprising the steps of:

[0006] A、注塑按键本体:采用透明塑胶原料注塑得到按键本体;对按键本体进行超声波清洗,并烘烤去除应力,烘烤温度为60~110°C,烘烤时间为60~120分钟; [0006] A, the injection button body: a transparent key body obtained by injection molding of plastic materials; the body of the button subjected to ultrasonic cleaning, and baking the stress is removed, baking temperature is 60 ~ 110 ° C, baking time of 60 to 120 minutes;

[0007] B、设置字符颜色层:在按键本体层上印刷、或喷涂透光率大于50%的字符颜色层; [0007] B, a character color layer is provided: on the key body layer printing, or spraying a light transmittance greater than 50% of the character color layer;

[0008] C、设置边框颜色层:在字符颜色层上印刷、或喷涂透光率小于15%的边框颜色层,所述边框颜色层的颜色与所述字符颜色层的颜色不相同; [0008] C, border color layer is provided: the character color layer is printed on, or spraying light transmittance of less than 15% of the border color layer, the color of the border color of the color layer and the color layer is not the same character;

[0009] D、设置遮蔽层:在边框颜色层上印刷、或喷涂透光率小于15%的遮蔽层; [0009] D, the shielding layer is provided: on the border color layer is printed, sprayed, or less than 15% of the light transmittance of the shielding layer;

[0010] E、设置按键主体颜色层:在遮蔽层上喷涂按键主体颜色层,所述按键主体颜色层的颜色与所述字符颜色层的颜色相同; [0010] E, the body color layer is disposed key: the key body shielding coating layer color layer, the color of the button body color of the color layer and the color layer is the same character;

[0011] F、镭雕边框部:按边框形状镭雕穿过按键主体颜色层、遮蔽层,露出边框颜色层,完成边框部的儀雕; [0011] F, laser engraving unit frame: frame shape by laser carving through the key body color layer, the masking layer to expose the layer border color, border portion to complete the carving instrument;

[0012] G、镭雕字符:按字符形状镭雕穿过边框颜色层上的边框部,露出字符颜色层,完成子符的儀雕; [0012] G, laser engraving characters: the character shape by laser carving through the frame border color layer portion, a character color layer is exposed, the complete sub-character carved instrument;

[0013] H、喷涂保护层:在按键主体颜色层上喷涂透明保护层; [0013] H, a protective layer coating: Spray a transparent protective layer on the color layer, the key body;

[0014] 1、冲型、组装:通过冲压模具及冲压设备将整框按键冲压为单个的按键;单个按键经过贴合组装为完整的按键。 [0014] 1, punching, assembling: stamping dies and stamping equipment by the entire frame as a single key press of a key; a single key after bonded assembly of the complete key.

[0015] 本发明通过设置边框颜色层,并在字符的周围形成与字符颜色不同的边框,使字符及与字符颜色相同的按键主体颜色层上的非字符区域能区分,使用户能清晰分辨字符,且使按键更加美观。 [0015] The present invention by providing a border color layer, and is formed with a character color different border around the character of the non-character region in the character and the character color same key body color layers can be distinguished, so that the user can clearly distinguish the characters , and so the button is more beautiful.

附图说明 BRIEF DESCRIPTION

[0016] 图1是本发明实施例提供的按键剖面示意图。 [0016] FIG. 1 is a schematic cross-sectional view button provided in the embodiment of the present invention.

[0017] 图2是本发明实施例提供的按键结构示意图。 [0017] FIG. 2 is a schematic structural diagram of a key embodiment of the present invention.

[0018] 图3是本发明实施例提供的按键制造方法流程图。 [0018] FIG. 3 is a method for manufacturing a key according to an embodiment of the present invention a flowchart.

具体实施方式 Detailed ways

[0019] 为了使本发明所解决的技术问题、技术方案及有益效果更加清楚明白,以下结合附图及实施例,对本发明进行进一步详细说明。 [0019] In order to solve the technical problem of the present invention, technical solutions and beneficial effects clearer, the accompanying drawings and the following embodiments, the present invention will be further described in detail. 应当理解,此处所描述的具体实施例仅仅用以解释本发明,并不用于限定本发明。 It should be understood that the specific embodiments described herein are only intended to illustrate the present invention and are not intended to limit the present invention.

[0020] 本发明实施例提供了一种按键,其按键剖面结构如图1所示,结合图2所示,所述按键I包括:按键本体11,以及附着在按键本体11表面的透光率大于50%的字符颜色层12,所述字符颜色层12上覆盖有透光率小于15%的边框颜色层13,所述边框颜色层13上覆盖有透光率小于15%的遮蔽层14,所述遮蔽层14上覆盖有按键主体颜色层15,所述按键主体颜色层15上覆盖有透光率大于50%的保护层16 ;所述遮蔽层14、按键主体颜色层15部分镂空形成边框部;所述边框部部分镂空,在所述边框颜色层13上形成边框131,所述字符颜色层12从镂空部露出形成字符121 ;所述字符颜色层12与所述按键主体颜色层15的颜色相同;所述边框颜色层13与所述字符颜色层12及按键主体颜色层15的颜色不相同。 [0020] The present invention provides a button, which button sectional structure shown in Figure 1, in conjunction with FIG. 2, the key I comprises: 11, and the light transmittance of the keys attached to the surface of the body 11 of the button body character color layer 12 is greater than 50%, of the character 12 is covered with a light transmittance of less than 15% of the color layer border color layer 13, the shielding layer 14 has a light transmittance of less than 15% coverage of the border color layer 13, the shielding layer 14 is covered with the button body color layer 15, the light transmittance of the keys is covered with a protective layer of more than 50% of the color layer 16 on the body 15; the masking layer 14, the color of the button body layer 15 is formed partially hollow frame part; portion of the hollow frame, the bezel 131 is formed on the border color layer 13, a character color layer 12 is exposed from the hollow portion 121 is formed of characters; the character color layer 12 and the key body 15 of the color layer the same color; the border color of the character layer 13 and the color layer 12 and the key body color of the color layers 15 are different. 151是按键主体颜色层15上的非字符区域。 151 non-character region is the main key 15 on the color layer.

[0021] 字符121的尺寸是由边框131尺寸往内缩小一定比例形成。 Size [0021] to the character 121 is reduced from a certain percentage of the size of the bezel 131 is formed. 所述字符121的尺寸为所述边框131尺寸的50~80%。 The character size 121 is 50 to 80% of the size of the frame 131.

[0022] 为了按键耐用且容易制造,对按键本体及每个涂层的构成材料都有相应的限制。 [0022] In order button durable and easy to manufacture, has a corresponding restriction on the material constituting the button body and each of the coating. 上述按键本体11由聚碳酸酯或聚甲基丙烯酸甲酯注塑而成;所述字符颜色层12、边框颜色层13均为带颜色的透光油墨印刷或透光油漆喷涂而成;所述遮蔽层14、按键主体颜色层15均为带颜色的不透光油墨印刷或透光油漆喷涂而成;所述保护层16为透明紫外线固化油漆喷涂而成。 Said key button main body 11 molded from polycarbonate or polymethyl methacrylate formed; the character color layer 12, light-transmissive ink border color print layer 13 are translucent colored paint from the spray; said shield layer 14, a key body color layer is opaque or translucent printing ink colored paint coating 15 are formed; the transparent protective layer 16 is formed by coating an ultraviolet curing paint.

[0023] 所述字符颜色层12提供字符所需的颜色。 [0023] The character layer 12 provide a desired color character color. 因按键在使用时一般具有背光,所以,字符颜色层12的透光率大于50%,以便光线更好通过。 When general keys by using a backlight, the light transmittance of a character color layer 12 is greater than 50%, better to light through. 字符颜色层12的透光率更优选为大于90%ο Light transmittance of character color layer 12 is more preferably greater than 90% ο

[0024] 边框颜色层13提供边框所需的颜色。 [0024] Border Color layer 13 to provide the desired border color. 边框颜色层13的颜色与字符颜色层12的颜色不一样,以便区分和清晰分辨字符121与非字符区域151。 Color Border Color color character color layer 12, layer 13 is not the same, in order to distinguish and clearly identifiable character 121 and the non-character region 151. 边框颜色层13透光率小于15%,更优选透光率小于5%。 Border color light transmittance layer 13 is less than 15%, more preferably less than 5% transmittance.

[0025] 所述遮蔽层14用来防止非字符区域151透光或者字符121周围的边框131渗色,以达到按键I的非字符区域151遮光,且避免字符121周围的边框131渗色的问题出现。 [0025] The shielding layer 14 for preventing the non-character region border 131 151 121 transmissive or bleeding around the character, in order to achieve non-character region 151 of the light shielding key I, and to avoid the problem of the border 131 around 121 characters bleeding appear. 遮蔽层14透光率小于15%,更优选透光率小于5%。 The light transmittance of the shielding layer 14 is less than 15%, more preferably less than 5% transmittance.

[0026] 按键主体颜色层15提供按键的外观颜色,其与字符颜色层12的颜色相同。 [0026] The button body color layer to provide color appearance button 15, which is the same color character color layer 12.

[0027] 保护层16为透明紫外线固化油漆喷涂而成,其为按键I提供保护作用,且使按键I耐磨。 [0027] The protective layer 16 is made of a transparent ultraviolet curable paint spraying, which provides protection for the key I, and so the button I wear. 保护层16也可选用其他透明的油漆喷涂,但是紫外线固化油漆固化时间短,可提高生产效率。 The protective layer 16 may also use other transparent paint spraying, paint curing the ultraviolet curable but short time, productivity can be improved. 保护层16透光率大于50%,以便光线更好通过。 The protective layer 16 is greater than 50% transmittance to light through better. 保护层16的透光率更优选为大于90%ο The light transmittance of the protective layer 16 is more preferably greater than 90% ο

[0028] 为了避免涂层太厚造成按键字符透光效果差、或涂层太薄需保留的颜色层会被雕穿,或发生渗色的现象,对各涂层厚度都有相应的限制。 [0028] In order to avoid thick coating causing poor light transmitting key characters, or the coating color layer too thin to be retained will be carved through, or the bleeding phenomenon occurs, the corresponding limitation on the coatings have a thickness.

[0029] 所述字符颜色层12的厚度取值范围为2~6Mm ;使字符颜色层12具有良好的透光性能。 [0029] The thickness of the layer 12 in the range of character color 2 ~ 6Mm; make a character color layer 12 has good light transmissive properties.

[0030] 所述边框颜色层13的厚度取值范围为8~12Mm ;防止在镭雕时容易雕穿。 A thickness in the range [0030] The border color layer 13 is 8 ~ 12Mm; easily carved prevent wear during laser engraving.

[0031] 所述遮蔽层14的厚度取值范围为8~12Mm ;以防止渗色,且提供遮蔽效果。 A thickness in the range [0031] The shielding layer 14 is 8 ~ 12Mm; to prevent bleeding and provides a shielding effect.

[0032] 所述按键主体颜色层15的厚度取值范围为10~14Mm ;防止在镭雕时容易雕穿。 The [0032] thickness in the range button body color layer 15 is 10 ~ 14Mm; easily carved prevent wear during laser engraving.

[0033] 所述保护层16的厚度取值范围为10~14Mm,以获得按键I的各项表面性能较好。 [0033] The protective layer thickness ranges from 16 to 10 ~ 14Mm, to obtain a better performance of the key I of the surface. 如耐磨、抗划痕等性能。 The abrasion resistant, scratch resistant properties.

[0034] 本发明通过设置边框颜色层,并在字符的周围形成与字符颜色不同的边框,使字符及与字符颜色相同的按键主体颜色层上的非字符区域能区分,使用户能清晰分辨字符,且使按键更加美观。 [0034] The present invention by providing a border color layer, and is formed with a character color different border around the character of the non-character region in the character and the character color same key body color layers can be distinguished, so that the user can clearly distinguish the characters , and so the button is more beautiful.

[0035] 另外,本发明还提供了一种按键制造方法,如图3所示,该按键制造方法包括如下步骤:A、注塑按键本体:采用透明塑胶原料注塑得到按键本体;对按键本体进行超声波清洗,并烘烤去除应力,烘烤温度为60~110°C,烘烤时间为60~120分钟; [0035] Further, the present invention also provides a method for manufacturing a key, shown in Figure 3, the method comprising the steps of buttons: A, injection button body: a transparent key body obtained by injection molding of plastic materials; ultrasonically of key bodies washed and baked stress is removed, baking temperature is 60 ~ 110 ° C, baking time of 60 to 120 minutes;

[0036] B、设置字符颜色层:在按键本体层上印刷、或喷涂透光率大于50%的字符颜色层; [0036] B, a character color layer is provided: on the key body layer printing, or spraying a light transmittance greater than 50% of the character color layer;

[0037] C、设置边框颜色层:在字符颜色层上印刷、或喷涂透光率小于15%的边框颜色层,所述边框颜色层的颜色与所述字符颜色层的颜色不相同; [0037] C, border color layer is provided: the character color layer is printed on, or spraying light transmittance of less than 15% of the border color layer, the color of the border color of the color layer and the color layer is not the same character;

[0038] D、设置遮蔽层:在边框颜色层上印刷、或喷涂透光率小于15%的遮蔽层; [0038] D, the shielding layer is provided: on the border color layer is printed, sprayed, or less than 15% of the light transmittance of the shielding layer;

[0039] E、设置按键主体颜色层:在遮蔽层上喷涂按键主体颜色层,所述按键主体颜色层的颜色与所述字符颜色层的颜色相同; [0039] E, the body color layer is disposed key: the key body shielding coating layer color layer, the color of the button body color of the color layer and the color layer is the same character;

[0040] F、镭雕边框部:按边框形状镭雕穿过按键主体颜色层、遮蔽层,露出边框颜色层,完成边框部的儀雕; [0040] F, laser engraving unit frame: frame shape by laser carving through the key body color layer, the masking layer to expose the layer border color, border portion to complete the carving instrument;

[0041] G、镭雕字符:按字符形状镭雕穿过边框颜色层上的边框部,露出字符颜色层,完成子符的儀雕; [0041] G, laser engraving characters: the character shape by laser carving through the frame border color layer portion, a character color layer is exposed, the complete sub-character carved instrument;

[0042] H、喷涂保护层:在按键主体颜色层上喷涂透明保护层; [0042] H, a protective layer coating: Spray a transparent protective layer on the color layer, the key body;

[0043] 1、冲型、组装:通过冲压模具及冲压设备将整框按键冲压为单个的按键;单个按键经过贴合组装为完整的按键。 [0043] 1, punching, assembling: stamping dies and stamping equipment by the entire frame as a single key press of a key; a single key after bonded assembly of the complete key.

[0044] 所述字符颜色层材质为彩色透光油墨、或彩色透光油漆,字符颜色层的厚度取值范围为2~6Mm,所述步骤B还包括如下步骤:B1、将喷涂、或印刷有字符颜色层的按键本体进行烘烤,烘烤温度为85°C,烘烤时间为30分钟。 [0044] The character color ink layer is made of a light-transmitting color, translucent color or a thickness in the range of paint, a character color layer is 2 ~ 6Mm, said step B further comprises the step of: B1, spraying, or printing with a character color layer key bodies baking, baking temperature is 85 ° C, the baking time is 30 minutes. 烘烤使字符颜色层较快干燥,避免与下面工序的涂层发生咬底或混色、渗色的现象。 Fast baking that the character color layer was dried, avoid biting bottom or mixing the coating step following the occurrence of bleeding phenomenon. 所述字符颜色层选用透光性较好的彩色透光油墨、或彩色透光油漆,使按键在背光情况下亮度足够。 The character selection translucent color layer is preferably translucent color inks, paints or colored light transmissive, so that a sufficient luminance in the backlight key case. 对按键本体进行烘烤去应力时,烘烤时设定的温度及烘烤的时间根据按键本体层的材质而定。 When the button body to stress baking, the baking temperature and baking time setting depends on the material of the key body layer. 例如:按键本体层的材质为聚碳酸酯时,烘烤温度设为110°C,烘烤时间设为120分钟;按键本体层的材质为聚甲基丙烯酸甲酯时,烘烤温度设为60°C,烘烤时间设为60分钟。 For example: Key bulk layer material is polycarbonate, the baking temperature is set at 110 ° C, baking time was 120 min; when the key body layer material is polymethyl methacrylate, the baking temperature is set to 60 ° C, the baking time was 60 minutes.

[0045] 所述边框颜色层与字符颜色层的颜色不相同,所述边框颜色层厚度取值范围为所述步骤C还包括如下步骤:Cl、将喷涂、或印刷有边框颜色层的按键本体进行烘烤,烘烤温度为85°C,烘烤时间为60分钟。 [0045] The border color color layer and the color of the character layer is not the same, the border color layer thickness in the range of said step C further comprises the step of: Cl, sprayed, or printed color layer border key bodies baking, baking temperature is 85 ° C, the baking time was 60 minutes. 烘烤使字符颜色层较快干燥,避免与下面工序的涂层发生咬底或混色、渗色的现象。 Fast baking that the character color layer was dried, avoid biting bottom or mixing the coating step following the occurrence of bleeding phenomenon. 所述边框颜色层选用耐镭雕性能优异的油漆或油墨,使其在镭雕过程中不会出现边缘锯齿状或其他镭雕缺陷。 The choice of border color layer excellent in resistance to laser engraving properties of the paint or ink, so that jagged edges or other defects do not appear in the laser engraving laser engraving process.

[0046] 所述遮蔽层的厚度取值范围为8~12Mm ;遮蔽层避免非字符区域漏光,厚度取值范围为8~12Mm即可以满足非字符区域部漏光,且节约遮蔽层的油漆或油墨的用量。 [0046] The thickness of the masking layer is in the range of 8 to 12mm; non-character region shielding layer prevents light leakage, a thickness in the range of 8 to the shielding layer is a paint or ink that is non-character region to meet the light leakage section, and save 12mm amount. 所述步骤D还包括如下步骤:D1、将喷涂、或印刷有边框颜色层的按键本体进行烘烤,烘烤温度为85°C,烘烤时间为60分钟。 Said step D further comprises the step of: D1, sprayed, or printed color layer border key bodies baking, baking temperature is 85 ° C, the baking time was 60 minutes. 烘烤使遮蔽层较快干燥,避免与下面工序的涂层发生咬底或混色、渗色的现象。 Baking the shielding layer is dried rapidly, following the coating step to avoid the occurrence of biting bottom or mixing, the phenomenon of bleeding.

[0047] 所述按键主体颜色层厚度取值范围为;按键主体颜色层的油漆或油墨要求具有良好的流平性及容易镭雕性。 The [0047] button body a layer thickness in the range of color; button body color paint or ink layer is required to have excellent leveling properties and easy laser engraving. 所述步骤E还包括如下步骤:El、将喷涂有按键主体颜色层的按键本体进行烘烤,烘烤温度为85°C,烘烤时间为90分钟。 Said step E further comprises the step of: El, the main body push button keys sprayed with a color layer is baked, the baking temperature of 85 ° C, baking time 90 minutes. 烘烤使按键主体颜色层较快干燥,避免与下面工序的涂层发生咬底或混色、渗色的现象。 Baking so the button body color layer is dried faster, avoid biting bottom or mixing the coating step following the occurrence of bleeding phenomenon.

[0048] 所述保护层的厚度取值范围为10~14Mm;所述步骤H还包括如下步骤:H1、将喷涂有透明保护层的按键本体进行烘烤,烘烤温度范围为60~70°C,时间范围为3~5分钟;然后对其用800-1000mj/cm2的紫外光照射,照射时间取值范围为60~80秒。 [0048] The thickness of the protective layer is in the range of 10 ~ 14Mm; H step further comprises the step of: H1, the key body having a baking spray transparent protective layer, the baking temperature range of 60 ~ 70 ° C, the time ranges from 3 to 5 minutes; then subjected to irradiation with ultraviolet 800-1000mj / cm2, the irradiation time ranging from 60 to 80 seconds. 保护层一般采用紫外光固化油漆,紫外线固化油漆固化时间短,可提高生产效率。 The protective layer is generally used UV-curable paint, an ultraviolet curing paint curing time is short, productivity can be improved.

[0049] 为了达到按键上边框和字符的颜色不同,字符与非字符区域颜色相同或相近,需要字符颜色层和边框颜色层的颜色不相同,按键主体颜色层和字符颜色层的颜色相同。 [0049] In order to achieve different color and border on the key characters, the same or similar non-character region and the character color, character color the color layer and the need to border color layers are not identical, the color layer and the color layer, the color of the character key body. 在具体实施例中用户可以自行选择不同的颜色,只要满足字符能清晰分辨即可,在下面的本实施例1中,字符颜色层为白色,边框颜色层为黑色,按键主体颜色层为与字符颜色层相同的白色。 In a particular embodiment, the user can select different color itself, as long as characters can be clearly distinguished, in the following the present embodiment 1, the character is white color layer, the color layer is a black border, the key character with the body color layer the same white color layer. 在下面的本实施例2中,字符颜色层为橙色,边框颜色层为白色,按键主体颜色层为与字符颜色层相同的橙色。 In the following embodiments of the present embodiment 2, the character layer as an orange color, border color layer is white, the color of the button body and the character color layer is a layer of the same orange.

[0050] 为了更加详细了解本发明按键制造方法。 [0050] For a more detailed understanding of the present invention is a method of manufacturing the key. 下面通过具体实施例对其进行描述。 It is described below by way of specific embodiments.

[0051] 实施例1 [0051] Example 1

[0052] A、注塑按键本体:采用透明聚碳酸酯注塑按键本体,对按键本体进行超声波清洗,并烘烤去除应力,烘烤温度为110 °C,烘烤时间为120分钟; [0052] A, the injection button body: transparent polycarbonate injection button body of the button body subjected to ultrasonic cleaning, the stress is removed and baked, the baking temperature of 110 ° C, baking time is 120 minutes;

[0053] B、设置字符颜色层:在塑胶注塑件喷涂白色透光油漆,白色透光油漆型号为中国江西省赣州市赐彩涂料实业有限公司提供的CY01-102A,油漆粘度为8秒,控制喷涂的时间使其膜厚为2~6Mm,然后在85°C环境下烘烤30分钟,确保油漆充分烤干,形成字符颜色层。 [0053] B, a character color layer provided: translucent white paint spraying plastic injection-molded part, translucent white paint China Ganzhou model given color of paint Co., Limited CY01-102A, paint viscosity was 8 seconds, the control spraying time so that a thickness of 2 ~ 6Mm, then baked for 30 minutes at 85 ° C environment to ensure sufficient paint to dry to form a character color layer.

[0054] C、设置边框颜色层:在字符颜色层上喷涂与白色的字符颜色层的颜色形成对比的黑色油漆,黑色油漆的型号为中国江西省赣州市赐彩涂料实业有限公司提供的CY01-510-699,油漆粘度为9_10秒,控制喷涂的时间使其的膜厚为8~12μπι,然后在85°C环境下烘烤60分钟,确保油漆充分烤干,形成边框颜色层。 [0054] C, set the border color layers: on the character color layer and the color coating layer of the white character color contrast of black paint, black paint model for China Jiangxi Ganzhou give color Paint Industry Co., Ltd. provides CY01- 510-699, paint viscosity 9_10 seconds spraying time so that the control of the film thickness of 8 ~ 12μπι, and then baked for 60 minutes at 85 ° C environment to ensure sufficient paint to dry, border color forming layer.

[0055] D、设置遮蔽层:在边框颜色层上喷涂透光率小于15%的银色油漆;银色油漆型号为中国江西省赣州市赐彩涂料实业有限公司提供的CY01-510-698,油漆粘度为9_10秒,控制喷涂的时间使其膜厚为8~12Mm,然后在85°C环境下烘烤60分钟,确保油漆充分烤干,形成字符遮蔽层。 [0055] D, the shielding layer: Coating on the border color light transmittance of less than 15% silver paint; CY01-510-698, silver paint viscosity for the paint type Chinese Ganzhou given color of paint Co., Limited 9_10 seconds to control the spraying time so that a thickness of 8 ~ 12Mm, then baked at 85 ° C environment for 60 minutes to ensure adequate paint to dry, the shielding layer is formed characters. 银色遮蔽层避免下面的黑色的边框颜色层渗色影响外观。 Silver shielding layer below the black border to avoid color bleed layer affect the appearance.

[0056] E、设置按键主体颜色层:在遮蔽层上喷涂透光率小于15%的白色油漆,白色油漆型号为中国江西省赣州市赐彩涂料实业有限公司提供的CY01-510-697,油漆粘度为9_10秒,控制喷涂的时间使其膜厚为10~14Mm,然后在85°C环境下烘烤90分钟,确保油漆充分烤干,形成按键主体颜色层的白色油漆与字符颜色层的白色油漆颜色相同。 [0056] E, the key body color layer is disposed: in the upper shielding layer light transmittance of less than 15% coating of white paint, white paint China Ganzhou model given color of paint Co., Limited CY01-510-697, paint 9_10 viscosity of seconds, the control spraying time so that the film thickness of 10 ~ 14Mm, and then baked for 90 minutes at 85 ° C environment to ensure sufficient paint to dry, forming a key body layer color and the character color white white paint layer the same paint color.

[0057] F、镭雕边框部:镭雕设备为深圳市大族激光科技股份有限公司提供的EP-12镭雕设备。 [0057] F, laser engraving bezel part: EP-12 Laser engraving equipment Laser engraving equipment Shenzhen Han's Laser Technology Co., Ltd. provides. 先根据经验粗略调节镭雕,试镭雕,再精确调整镭雕设备参数,按边框形状镭雕穿过白色的按键主体颜色层、银色的遮蔽层,露出黑色的边框颜色层,完成边框部的镭雕;镭雕后无残留油漆,边框部边缘平滑无锯齿。 First roughly adjusted empirically laser engraving, laser engraving trial, and then precisely adjust laser carving equipment parameters, press the frame through the shape of laser engraving white key main color layer, the masking layer of silver, a black border color layer is exposed, the complete frame portion laser engraving; no paint residue after laser engraving, a smooth non-serrated edge frame portion.

[0058] 镭雕边框部的字稿设置为比字符大的大字稿,以便在后续镭雕字符后得到字符黑色边框。 [0058] Word draft frame portion disposed laser engraving larger characters than the character is issued in order to obtain a black character in the subsequent laser engraving border characters.

[0059] G、镭雕字符:按字符形状镭雕穿过黑色边框颜色层上的边框部,露出白色字符颜色层,完成子符的儀雕;儀雕子符的子稿在儀雕边框部的大子稿基础上内缩,内缩后子符的尺寸为所述边框尺寸的50~80%,经过镭雕字符,得到白色字符,边框黑色的半成品按键。 [0059] G, laser engraving characters: the character shape by laser engraving frame portion through the border color on a black layer, a white character color layer is exposed, the complete instrument sub character carved; carving instrument is issued in the sub-sub-icon carving instrument frame portion issued on the basis of a large sub retracted, the retracted dimension of the sub-character 50 to 80% of the size of the frame, after laser engraving characters, the characters to give a white, semi-finished buttons black border.

[0060] H、喷涂保护层:在按键主体颜色层上喷涂透明保护层; [0060] H, a protective layer coating: Spray a transparent protective layer on the color layer, the key body;

[0061] 将镭雕字符后的半成品按键使用酒精擦拭,静电除尘,然后喷涂无色透明紫外光固化保护油漆,无色透明紫外光固化保护油漆型号为中国江西省赣州市赐彩涂料实业有限公司提供的UV-058,油漆粘度为8-9秒,控制喷涂的时间使其膜厚为10~14Mm,然后在60~70°C环境下烘烤3~5分钟,然后对其用800-1000mj/cm2的紫外光照射,照射时间取值范围为60~80秒,形成保护层。 [0061] The semi-key after laser engraving characters using alcohol wipes, electrostatic dust, then spray colorless, transparent UV-curable protective paint, UV-curable protective paint colorless and transparent model for China Jiangxi Ganzhou gave Cai Paint Co., Ltd. UV-058 supplied paint viscosity of 8-9 seconds, the control spraying time so that film thickness of 10 ~ 14mm, then baked at 60 ~ 70 ° C environment for 3-5 minutes, then subjected to a 800-1000mj UV radiation / cm2, the irradiation time ranging from 60 to 80 seconds to form a protective layer. 保护层还提供按键的光泽。 The protective layer also provides keys shine.

[0062] 1、冲型、组装:通过冲压模具及冲压设备将整框按键冲压为单个的按键;单个按键经过贴合组装为完整的按键。 [0062] 1, punching, assembling: stamping dies and stamping equipment by the entire frame as a single key press of a key; a single key after bonded assembly of the complete key.

[0063] 实施例2 [0063] Example 2

[0064] A、注塑按键本体:采用透明聚甲基丙烯酸甲酯注塑按键本体,对按键本体进行超声波清洗,并烘烤去除应力,烘烤温度为60°C,烘烤时间为60分钟; [0064] A, the injection button body: transparent polymethylmethacrylate injection button body of the button body subjected to ultrasonic cleaning, the stress is removed and baked, the baking temperature of 60 ° C, baking time 60 min;

[0065] B、设置字符颜色层:在塑胶注塑件喷涂橙色透光油漆,橙色透光油漆型号为中国江西省赣州市赐彩涂料实业有限公司提供的CY01-390-672,油漆粘度为8秒,控制喷涂的时间使其膜厚为2~6Mm,然后在85°C环境下烘烤30分钟,确保油漆充分烤干,形成字符颜色层。 [0065] B, provided a character color layer: Spray paint orange translucent plastic injection molded parts, as orange translucent paint type Chinese Ganzhou given color of paint Co., Limited CY01-390-672, paint viscosity was 8 seconds , so as to control the time spraying a thickness of 2 ~ 6Mm, then baked for 30 minutes at 85 ° C environment to ensure sufficient paint to dry to form a character color layer.

[0066] C、设置边框颜色层:在字符颜色层上喷涂与橙色的字符颜色层的颜色形成对比的白色油漆,白色油漆的型号为中国江西省赣州市赐彩涂料实业有限公司提供的CY01-510-697,油漆粘度为9_10秒,控制喷涂的时间使其的膜厚为8~12μπι,然后在85°C环境下烘烤60分钟,确保油漆充分烤干,形成边框颜色层。 [0066] C, set the border color layers: on the character color layer sprayed with orange color character color contrast layer of white paint, white paint models for China Jiangxi Ganzhou give color Paint Industry Co., Ltd. provides CY01- 510-697, paint viscosity 9_10 seconds spraying time so that the control of the film thickness of 8 ~ 12μπι, and then baked for 60 minutes at 85 ° C environment to ensure sufficient paint to dry, border color forming layer.

[0067] D、设置遮蔽层:在边框颜色层上喷涂透光率小于15%的银色油漆;银色油漆型号为中国江西省赣州市赐彩涂料实业有限公司提供的CY01-510-698,油漆粘度为9_10秒,控制喷涂的时间使其膜厚为8~12Mm,然后在85°C环境下烘烤60分钟,确保油漆充分烤干,形成字符遮蔽层。 [0067] D, the shielding layer: Coating on the border color light transmittance of less than 15% silver paint; CY01-510-698, silver paint viscosity for the paint type Chinese Ganzhou given color of paint Co., Limited 9_10 seconds to control the spraying time so that a thickness of 8 ~ 12Mm, then baked at 85 ° C environment for 60 minutes to ensure adequate paint to dry, the shielding layer is formed characters. 银色遮蔽层避免下面的白色的边框颜色层渗色影响外观。 Under shielding layer prevents the silver white color layer border bleeding affect the appearance.

[0068] E、设置按键主体颜色层:在遮蔽层上喷涂透光率大于50%的橙色油漆,橙色油漆型号为中国江西省赣州市赐彩涂料实业有限公司提供的CY01-390-672,油漆粘度为9_10秒,控制喷涂的时间使其膜厚为10~14Mm,然后在85°C环境下烘烤90分钟,确保油漆充分烤干,形成按键主体颜色层的橙色油漆与字符颜色层的橙色油漆颜色相同。 [0068] E, the key body color layer is disposed: in the upper shielding layer light transmittance of greater than 50% of the spray of paint orange, orange paint China Ganzhou model given color of paint Co., Limited CY01-390-672, paint 9_10 viscosity of seconds, the control spraying time so that the film thickness of 10 ~ 14Mm, and then baked for 90 minutes at 85 ° C environment to ensure sufficient paint to dry, forming a key body layer color and the character color orange orange paint layer the same paint color.

[0069] F、镭雕边框部:镭雕设备为深圳市大族激光科技股份有限公司提供的EP-12镭雕设备。 [0069] F, laser engraving bezel part: EP-12 Laser engraving equipment Laser engraving equipment Shenzhen Han's Laser Technology Co., Ltd. provides. 先根据经验粗略调节镭雕,试镭雕,再精确调整镭雕设备参数,按边框形状镭雕穿过橙色的按键主体颜色层、银色的遮蔽层,露出白色的边框颜色层,完成边框部的镭雕;镭雕后无残留油漆,边框部边缘平滑无锯齿。 First roughly adjusted empirically laser engraving, laser engraving trial, and then precisely adjust laser carving equipment parameters, press the frame through the shape of laser engraving orange body color layer key, silver shielding layer, a color layer is exposed white border, the border portion to complete laser engraving; no paint residue after laser engraving, a smooth non-serrated edge frame portion. 镭雕边框部的字稿设置为比字符大的大字稿,以便在后续儀雕子符后得到子符白色边框。 Laser engraving the word frame portion draft set to be larger than character draft characters, so as to obtain a white sub-frame character carved in the subsequent sub-device identifier.

[0070] G、镭雕字符:按字符形状镭雕穿过黑色边框颜色层上的边框部,露出白色字符颜色层,完成子符的儀雕;儀雕子符的子稿在儀雕边框部的大子稿基础上内缩,内缩后子符的尺寸为所述边框尺寸的50~80%,经过镭雕字符,得到白色字符,边框黑色的半成品按键。 [0070] G, laser engraving characters: the character shape by laser engraving frame portion through the border color on a black layer, a white character color layer is exposed, the complete instrument sub character carved; carving instrument is issued in the sub-sub-icon carving instrument frame portion issued on the basis of a large sub retracted, the retracted dimension of the sub-character 50 to 80% of the size of the frame, after laser engraving characters, the characters to give a white, semi-finished buttons black border.

[0071] H、喷涂保护层:在按键主体颜色层上喷涂透明保护层; [0071] H, a protective layer coating: Spray a transparent protective layer on the color layer, the key body;

[0072] 将镭雕字符后的半成品按键使用酒精擦拭,静电除尘,然后喷涂无色透明紫外光固化保护油漆,无色透明紫外光固化保护油漆型号为中国江西省赣州市赐彩涂料实业有限公司提供的UV-058,油漆粘度为8-9秒,控制喷涂的时间使其膜厚为10~14Mm,然后在60~70°C环境下烘烤3~5分钟,然后对其用800-1000mj/cm2的紫外光照射,照射时间取值范围为60~80秒,形成保护层。 [0072] The semi-key after laser engraving characters using alcohol wipes, electrostatic dust, then spray colorless, transparent UV-curable protective paint, UV-curable protective paint colorless and transparent model for China Jiangxi Ganzhou gave Cai Paint Co., Ltd. UV-058 supplied paint viscosity of 8-9 seconds, the control spraying time so that film thickness of 10 ~ 14mm, then baked at 60 ~ 70 ° C environment for 3-5 minutes, then subjected to a 800-1000mj UV radiation / cm2, the irradiation time ranging from 60 to 80 seconds to form a protective layer. 保护层还提供按键的光泽。 The protective layer also provides keys shine.

[0073] 1、冲型、组装:通过冲压模具及冲压设备将整框按键冲压为单个的按键;单个按键经过贴合组装为完整的按键。 [0073] 1, punching, assembling: stamping dies and stamping equipment by the entire frame as a single key press of a key; a single key after bonded assembly of the complete key.

[0074] 以上方案中字符颜色层、边框颜色层、设置遮蔽层及按键主体颜色层除具体实施例中所用的喷涂的方式来实现外,也可通过印刷来实现,在喷涂时通过调节喷涂时间等参数来控制涂层厚度,在印刷时通过印刷的次数等参数来控制涂层厚度。 [0074] The color layer border color layer above embodiment the characters, the shielding layer and the key body color layer is achieved, but also may be realized by printing, the spattering of the examples used in the specific embodiment when spraying by adjusting the spraying time other other parameters to control the thickness of the coating, when the coating thickness is controlled by the print number of printing parameters.

[0075] 以上所述仅为本发明的较佳实施例而已,并不用以限制本发明,凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等,均应包含在本发明的保护范围之内。 [0075] The foregoing is only preferred embodiments of the present invention but are not intended to limit the present invention, any modifications within the spirit and principle of the present invention, equivalent substitutions and improvements should be included in the present within the scope of the invention.

Claims (10)

1.一种按键,其特征在于,所述按键包括:按键本体,以及附着在按键本体表面的透光率大于50%的字符颜色层,所述字符颜色层上覆盖有透光率小于15%的边框颜色层,所述边框颜色层上覆盖有透光率小于15%的遮蔽层,所述遮蔽层上覆盖有按键主体颜色层,所述按键主体颜色层上覆盖有透光率大于50%的保护层;所述遮蔽层、按键主体颜色层部分镂空形成边框部;所述边框部部分镂空在边框颜色层上形成边框,所述字符颜色层从镂空部露出形成字符;所述字符颜色层与所述按键主体颜色层的颜色相同;所述边框颜色层与所述字符颜色层及按键主体颜色层的颜色不相同。 A key, wherein said key comprising: a key body in the key body and attached to the surface of the light transmittance of greater than 50% of the character color layer, the color layer is covered with a character light transmittance of less than 15% border color layer, the color layer is covered on the frame shielding layer light transmittance of less than 15%, the layer is covered with the shielding layer of a color key body, said key body is covered with a layer of color light transmittance of greater than 50% a protective layer; the shielding layer, a color layer key body portion is formed hollow frame portion; said hollow frame portion is formed on the frame border color layer, the color layer is exposed from the hollow character portion is formed characters; the character color layer the same as the color of the body color of the layer key; border color of the color layer and the color layer and the key character layer is not the same as the color of the body.
2.如权利要求1所述的按键,其特征在于,所述字符颜色层厚度取值范围为2~6Mm ;所述边框颜色层厚度取值范围为8~12Mm ;所述遮蔽层厚度取值范围为8~12Mm ;所述按键主体颜色层厚度取值范围为10~14μπι;所述保护层厚度取值范围为10~14Mm。 2. The key according to claim 1, wherein said character color layer thickness in the range of 2 ~ 6Mm; the border color layer thickness in the range of 8 ~ 12Mm; value of the shielding layer thickness in the range of 8 ~ 12Mm; the key body color layer thickness in the range of 10 ~ 14μπι; of the protective layer thickness in the range of 10 ~ 14Mm.
3.如权利要求1所述的按键,其特征在于,所述字符的尺寸为所述边框尺寸的50~80%。 The key as claimed in claim 1, wherein said character size is 50 to 80% of the frame size.
4.一种按键制造方法,其特征在于,包括如下步骤: A、注塑按键本体:采用透明塑胶原料注塑得到按键本体;对按键本体进行超声波清洗,并烘烤去除应力,烘烤温度为60~110°C,烘烤时间为60~120分钟; B、设置字符颜色层:在按键本体层上印刷、或喷涂透光率大于50%的字符颜色层; C、设置边框颜色层:在字符颜色层上印刷、或喷涂透光率小于15%的边框颜色层,所述边框颜色层的颜色与所述字符颜色层的颜色不相同; D、设置遮蔽层:在边框颜色层上印刷、或喷涂透光率小于15%的遮蔽层; E、设置按键主体颜色层:在遮蔽层上喷涂按键主体颜色层,所述按键主体颜色层的颜色与所述字符颜色层的颜色相同; F、镭雕边框部:按边框形状镭雕穿过按键主体颜色层、遮蔽层,露出边框颜色层,完成边框部的镭雕; G、镭雕字符:按字符形状镭雕穿过边框颜色层上的边 A key manufacturing method, comprising the steps of: A, injection button body: a transparent key body obtained by injection molding of plastic materials; the body of the button subjected to ultrasonic cleaning, the stress is removed and baked, the baking temperature of 60 to 110 ° C, baking time of 60 to 120 minutes; B, character color layer is provided: on the key body layer printing, or spraying a light transmittance greater than 50% of a character color layer; C, border color layer is provided: the character color printed layer, or spraying light transmittance of less than 15% of the border color layer, the color of the color layer and the color of the border of the character layer is not the same color; D, the shielding layer is provided: a color layer printed on the frame, or spraying less than 15% of the light transmittance of the shielding layer; color layer E, pushbutton bodies provided: key main color coating layer, the same color as the key of the character color of the body layer color layer on the masking layer; F, laser carving border unit: press the key frame shape through the body color laser engraving layer, the shielding layer, a color layer is exposed border, the border portion of the complete laser engraving; G, laser engraving characters: the character shape by laser engraving on the side border color through the layer 部,露出字符颜色层,完成字符的儀雕; H、喷涂保护层:在按键主体颜色层上喷涂透明保护层; 1、冲型、组装:通过冲压模具及冲压设备将整框按键冲压为单个的按键;单个按键经过贴合组装为完整的按键。 Portion exposed character color layer complete instrument carved character; H, paint protection layer is: In the button body Color Coating a transparent protective layer; 1, red type, assembled: by stamping die and the stamping equipment the entire block key press as a single key; a single key after bonded assembly of the complete key.
5.如权利要求4所述的按键制造方法,其特征在于:所述字符颜色层材质为彩色透光油墨、或彩色透光油漆,字符颜色层的厚度取值范围为2~6Mm。 5. The method of manufacturing a key according to claim 4, wherein: the character color ink layer is made of a light-transmitting color, translucent color or a thickness in the range of paint, a character color layer is 2 ~ 6Mm.
6.如权利要求4所述的按键制造方法,其特征在于:所述步骤B还包括如下步骤:B1、将喷涂、或印刷有字符颜色层的按键本体进行烘烤,烘烤温度为85°C,烘烤时间为30分钟。 6. The method of manufacturing a key according to claim 4, wherein: said step B further comprises the step of: Bl, spraying, or the character color printed layer key bodies baking, baking temperature is 85 ° C, baking time is 30 minutes.
7.如权利要求4所述的按键制造方法,其特征在于:所述边框颜色层与字符颜色层的颜色不相同,所述边框颜色层厚度取值范围为8~12Mm ; 所述步骤C还包括如下步骤: Cl、将喷涂、或印刷有边框颜色层的按键本体进行烘烤,烘烤温度为85°C,烘烤时间为60分钟。 7. The method of manufacturing a key according to claim 4, wherein: the character color and the border color layer layer are not the same color, the border color of a layer thickness in the range of 8 ~ 12Mm; C the further step of comprising the steps of: Cl, sprayed, or printed color layer border key bodies baking, baking temperature is 85 ° C, the baking time was 60 minutes.
8.如权利要求4所述的按键制造方法,其特征在于:所述遮蔽层的厚度取值范围为8~12Mm ;所述步骤D还包括如下步骤: D1、将喷涂、或印刷有遮蔽层的按键本体进行烘烤,烘烤温度为85°C,烘烤时间为60分钟。 8. The method of manufacturing a key according to claim 4, wherein: a thickness of the shielding layer is in the range of 8 ~ 12Mm; said step D further comprises the steps of: Dl, spraying, or printing the masking layer baking the key bodies, baking temperature is 85 ° C, the baking time was 60 minutes.
9.如权利要求4所述的按键制造方法,其特征在于:所述按键主体颜色层厚度取值范围为10~14Mm ;所述步骤E还包括如下步骤: E1、将喷涂有按键主体颜色层的按键本体进行烘烤,烘烤温度为85°C,烘烤时间为90分钟。 9. The method of manufacturing a key according to claim 4, wherein: said key body color layer thickness in the range of 10 ~ 14Mm; said step E further comprises the step of: E1, the color layer is sprayed with a key body baking the key bodies, baking temperature is 85 ° C, baking time 90 minutes.
10.如权利要求4所述的按键制造方法,其特征在于:所述保护层的厚度取值范围为10~14Mm ;所述步骤H还包括如下步骤: Hl、将喷涂有透明保护层的按键本体进行烘烤,烘烤温度范围为60~70°C,时间范围为3-5分钟;然后对其用800-1000mj/cm2的紫外光照射,照射时间取值范围为60~80秒。 10. The method of manufacturing a key according to claim 4, wherein: the thickness of the protective layer is in the range of 10 ~ 14Mm; H step further comprises the step of: on Hl, spraying with keys transparent protective layer body baking, the baking temperature range of 60 ~ 70 ° C, the time range of 3-5 minutes; then subjected to irradiation with ultraviolet 800-1000mj / cm2, the irradiation time ranging from 60 to 80 seconds.
CN201110239802.4A 2011-08-21 2011-08-21 Key and manufacturing method thereof CN102956386B (en)