CN108691062A - A kind of outdoor wear production fabric - Google Patents
A kind of outdoor wear production fabric Download PDFInfo
- Publication number
- CN108691062A CN108691062A CN201810526666.9A CN201810526666A CN108691062A CN 108691062 A CN108691062 A CN 108691062A CN 201810526666 A CN201810526666 A CN 201810526666A CN 108691062 A CN108691062 A CN 108691062A
- Authority
- CN
- China
- Prior art keywords
- parts
- fabric
- outdoor wear
- phosphatidyl
- diatomite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of outdoor wear production fabric is made of following parts by weight raw material:20-40 parts of cotton fiber, 10-16 parts of polyacrylonitrile fibre, 20-30 parts of polylactic acid, 10-18 parts of polyurethanes, 18-22 parts of neopelex, 10-15 parts of phosphatidyl-ethanolamine, 5-9 parts of potassium metabisulfite, 10-15 parts of cetyl trimethylammonium bromide, 2-6 parts of nano silicon dioxide, 2-4 parts of linoleic acid, 2-4 parts of adhesive, 20-30 parts of acrylic resin, 1-3 parts of sodium sulphate, 2-6 parts of polyvinyl chloride, 10-14 parts of diatomite, 3-8 parts of ethyl chrysanthemate, 60-70 parts of deionized water.Beneficial effects of the present invention are:(1)This fabric has good wear-resisting and scratch resistance performance, can extend the service life of outdoor wear outdoors, while the fabric also has the performances such as good waterproof and antistatic;(2)The fabric prepared composition is simple, and low manufacture cost can be promoted the use of.
Description
Technical field
The invention belongs to outdoor wear production fields, and in particular to a kind of outdoor wear production fabric.
Background technology
Clothes refer to the general name of clothes shoes packet toy ornament etc., refer to clothes more.Clothes are early stage human social development
Just occur, a variety of materials that can be found at one's side are made coarse and crude " by men of old;Yi Fu "To flak jacket.The initial clothes of the mankind
It is to wrap up the " of body made of animal skin;Zhi Wu "With bast-fibre and grass system etc. at.
It is to sew to the definition of clothes in national standard, is through at human body and plays protection and decorative effect product, also known as clothing
Clothes.
For society now, clothes have been that everyone decorates oneself, protect oneself, can must use to oneself and household
Product, not just for wear or an identity, a kind of life attitudes, one displaying charisma performance.
Clothes are made with fabric, and fabric is exactly the material for making clothes.As one of clothes three elements, fabric
The style and characteristic of clothes can not only be annotated, and directly control the color of clothes, moulding expression effect.Presentation is come from
The noble quality of body is perfect, soft.
Clothes are made of style, color and fabric three elements.Wherein material is most basic element.Dress materials are
Refer to all materials for constituting clothes, it can be divided into garment material and garment accessories.Here, mainly garment material is introduced to everybody
Some knowledge.
Garment material concept:It refer to the material for embodying clothing body feature.
Fabric number is explained:
Number is a kind of mode that yarn indicates, usually Yi "Determine surely "(this computational methods is divided into as metric count and branch made in Great Britain
Several two kinds) in English count (S) indicate, i.e.,:Under the conditions of official regain (8.5%), in the spun yarn that weight is one pound, have
How many often twist the reeled yarn that length is 840 yards, as how many number.Number is related with weight with the length of yarn.
Garment material density is explained:
Density refers to the radical of the middle warp thread and weft yarn arranged per square inch, referred to as thread count.General L_N[PS "Warp thread number * latitudes
Yarn Shuo "It indicates.Common several density such as 110*90,128*68,65*78,133*73, illustrates that warp thread is respectively per square inch
110,128,65,133;Weft yarn is respectively 90,68,78,73.Generally high branch is highly dense premise.
Common garment material
One) cotton fabric:It refer to the fabric being made into cotton chemical mixed yarn line with cotton or cotton.Its good permeability, moisture absorption
Property is good, comfortable and easy to wear, is highly practical popular fabric.Can be divided into pure cotton product, cotton blended two major classes.
Two) linen look fabric:The pure linen be formed by weaving by flaxen fiber and fiber crops and other fiber blends or the fabric of intertexture
It is referred to as linen look fabric.The common feature of linen look fabric is quality hard tough, rough stiffening, cool and comfortable, good hygroscopicity, is reason
The summer clothes fabric thought, linen look fabric can be divided into pure spinning and blended two class.
Three) wire type fabric:It is the high-grade variety in textile.It refers mainly to by mulberry silk, tussah silk, artificial silk, synthesize fibre
Tie up the fabric that long filament is primary raw material.It has the advantages that thin light, soft, smooth, graceful, magnificent, comfortable.
Four) wool fabrics:Be using wool, the rabbit hair, camel hair, wool type chemical fiber as fabric made of primary raw material, generally with
Based on wool, it is high-grade fabric throughout the year, with elasticity is good, crease-resistant, well-pressed, strong to stand up to hard wear, warmth retention property is strong, easypro
It is the advantages that suitable beauty, pure color, welcomed by consumers.
Five) pure chemical fiber fabric:Chemical fiber plus material is big with its fastness, good, well-pressed, wear-resisting washable, the easy keeping collection of elasticity and by
To liking for people.Pure chemical fiber fabric is the fabric made of pure chemistry fibrous woven.Its characteristic is by its chemical fibre itself
Characteristic determines.Chemical fibre can according to different needs, be processed into certain length, and by different technique be made into imitative silk,
Imitative cotton, imitative fiber crops, elastic force imitate hair, middle length imitates the fabrics such as hair.
Six) other garment materials
1, knitted dress fabric:It is to be bent lopping continuously along broadwise or warp-wise by one or several one threads, and mutually go here and there
Made of set.
2, suede:English pelliccia, the leather with hairiness are generally used for winter winter protection boot, the shoe lining of shoes or welt dress
Decorations.
3, leather:The various Animal Skins processed by tanning.The purpose of tanning is that skin is rotten in order to prevent, some small domestic animals
Poultry, reptile, fish and birds skin be referred to as (Skin) in English and often used in Italy or some other countries;
Pelle"And its word is agreed to indicate this kind of leather.
4, novel fabric and extraordinary fabric:Space wadding etc..
The requirement of outdoor wear is relatively more, higher for the wear-resisting scratch resistance performance of clothes if moving outdoors for a long time, together
When should also have more good water resistance and antistatic property.
Invention content
Purpose of the invention is to overcome the shortcomings in the prior art, provides a kind of outdoor wear production fabric.
In order to solve the above technical problems, the technical scheme is that:
A kind of outdoor wear production fabric is made of following parts by weight raw material:20-40 parts of cotton fiber, polyacrylonitrile fibre
10-16 parts, 20-30 parts of polylactic acid, 10-18 parts of polyurethanes, 18-22 parts of neopelex, phosphatidyl ethanol
10-15 parts of amine, 5-9 parts of potassium metabisulfite, 10-15 parts of cetyl trimethylammonium bromide, 2-6 parts of nano silicon dioxide, Asia
2-4 parts of oleic acid, 2-4 parts of adhesive, 20-30 parts of acrylic resin, 1-3 parts of sodium sulphate, 2-6 parts of polyvinyl chloride, diatomite 10-14
Part, 3-8 parts of ethyl chrysanthemate, 60-70 parts of deionized water.
Further, it is made of following parts by weight raw material:Including 20 parts of cotton fiber, 10 parts of polyacrylonitrile fibre, poly- breast
20 parts of acid, 10 parts of polyurethanes, 18 parts of neopelex, 10 parts of phosphatidyl-ethanolamine, potassium metabisulfite 5
Part, 10 parts of cetyl trimethylammonium bromide, 2 parts of nano silicon dioxide, 2 parts of linoleic acid, 2 parts of adhesive, acrylic resin 20
Part, 1 part of sodium sulphate, 2 parts of polyvinyl chloride, 10 parts of diatomite, 3 parts of ethyl chrysanthemate, 60 parts of deionized water.
Further, it is made of following parts by weight raw material:Including 40 parts of cotton fiber, 16 parts of polyacrylonitrile fibre, poly- breast
30 parts of acid, 18 parts of polyurethanes, 22 parts of neopelex, 15 parts of phosphatidyl-ethanolamine, potassium metabisulfite 9
Part, 15 parts of cetyl trimethylammonium bromide, 6 parts of nano silicon dioxide, 4 parts of linoleic acid, 4 parts of adhesive, acrylic resin 30
Part, 3 parts of sodium sulphate, 6 parts of polyvinyl chloride, 14 parts of diatomite, 8 parts of ethyl chrysanthemate, 70 parts of deionized water.
Further, it is made of following parts by weight raw material:Including 30 parts of cotton fiber, 13 parts of polyacrylonitrile fibre, poly- breast
25 parts of acid, 14 parts of polyurethanes, 20 parts of neopelex, 13 parts of phosphatidyl-ethanolamine, potassium metabisulfite 7
Part, 13 parts of cetyl trimethylammonium bromide, 4 parts of nano silicon dioxide, 3 parts of linoleic acid, 3 parts of adhesive, acrylic resin 25
Part, 2 parts of sodium sulphate, 4 parts of polyvinyl chloride, 12 parts of diatomite, 5 parts of ethyl chrysanthemate, 65 parts of deionized water.
Beneficial effects of the present invention are:(1)This fabric has good wear-resisting and scratch resistance performance, can extend outdoor wear
Service life outdoors, while the fabric also has the performances such as good waterproof and antistatic;(2)The fabric prepared composition letter
Single, low manufacture cost can be promoted the use of.
Specific implementation mode
The effect of to make to structure feature of the invention and being reached, has a better understanding and awareness, to preferable
Embodiment cooperation detailed description, is described as follows:
Embodiment 1
A kind of outdoor wear production fabric is made of following parts by weight raw material:Including 20 parts of cotton fiber, polyacrylonitrile fibre
10 parts, 20 parts of polylactic acid, 10 parts of polyurethanes, 18 parts of neopelex, 10 parts of phosphatidyl-ethanolamine, lay particular stress on it is sub-
5 parts of potassium sulfate, 10 parts of cetyl trimethylammonium bromide, 2 parts of nano silicon dioxide, 2 parts of linoleic acid, 2 parts of adhesive, acrylic acid
20 parts of resin, 1 part of sodium sulphate, 2 parts of polyvinyl chloride, 10 parts of diatomite, 3 parts of ethyl chrysanthemate, 60 parts of deionized water.
Embodiment 2
A kind of outdoor wear production fabric is made of following parts by weight raw material:Including 40 parts of cotton fiber, polyacrylonitrile fibre
16 parts, 30 parts of polylactic acid, 18 parts of polyurethanes, 22 parts of neopelex, 15 parts of phosphatidyl-ethanolamine, lay particular stress on it is sub-
9 parts of potassium sulfate, 15 parts of cetyl trimethylammonium bromide, 6 parts of nano silicon dioxide, 4 parts of linoleic acid, 4 parts of adhesive, acrylic acid
30 parts of resin, 3 parts of sodium sulphate, 6 parts of polyvinyl chloride, 14 parts of diatomite, 8 parts of ethyl chrysanthemate, 70 parts of deionized water.
Embodiment 3
A kind of outdoor wear production fabric is made of following parts by weight raw material:Including 30 parts of cotton fiber, polyacrylonitrile fibre
13 parts, 25 parts of polylactic acid, 14 parts of polyurethanes, 20 parts of neopelex, 13 parts of phosphatidyl-ethanolamine, lay particular stress on it is sub-
7 parts of potassium sulfate, 13 parts of cetyl trimethylammonium bromide, 4 parts of nano silicon dioxide, 3 parts of linoleic acid, 3 parts of adhesive, acrylic acid
25 parts of resin, 2 parts of sodium sulphate, 4 parts of polyvinyl chloride, 12 parts of diatomite, 5 parts of ethyl chrysanthemate, 65 parts of deionized water.
Beneficial effects of the present invention are:(1)This fabric has good wear-resisting and scratch resistance performance, can extend outdoor wear
Service life outdoors, while the fabric also has the performances such as good waterproof and antistatic;(2)The fabric prepared composition letter
Single, low manufacture cost can be promoted the use of.
The basic principles, main features and advantages of the present invention have been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and what is described in the above embodiment and the description is only the present invention
Principle, various changes and improvements may be made to the invention without departing from the spirit and scope of the present invention, these variation and
Improvement is both fallen in the range of claimed invention.The present invention claims protection domain by appended claims and its
Equivalent defines.
Claims (4)
1. a kind of outdoor wear production fabric, it is characterised in that:It is made of following parts by weight raw material:20-40 parts of cotton fiber,
10-16 parts of polyacrylonitrile fibre, 20-30 parts of polylactic acid, 10-18 parts of polyurethanes, neopelex 18-22
Part, 10-15 parts of phosphatidyl-ethanolamine, 5-9 parts of potassium metabisulfite, 10-15 parts of cetyl trimethylammonium bromide, nano-silica
2-6 parts of SiClx, 2-4 parts of linoleic acid, 2-4 parts of adhesive, 20-30 parts of acrylic resin, 1-3 parts of sodium sulphate, polyvinyl chloride 2-6
Part, 10-14 parts of diatomite, 3-8 parts of ethyl chrysanthemate, 60-70 parts of deionized water.
2. a kind of outdoor wear production fabric according to claim 1, it is characterised in that:By following parts by weight raw material
Composition:Including 20 parts of cotton fiber, 10 parts of polyacrylonitrile fibre, 20 parts of polylactic acid, 10 parts of polyurethanes, detergent alkylate sulphur
18 parts of sour sodium, 10 parts of phosphatidyl-ethanolamine, 5 parts of potassium metabisulfite, 10 parts of cetyl trimethylammonium bromide, nanometer titanium dioxide
2 parts of silicon, 2 parts of linoleic acid, 2 parts of adhesive, 20 parts of acrylic resin, 1 part of sodium sulphate, 2 parts of polyvinyl chloride, 10 parts of diatomite, chrysanthemum
3 parts of acetoacetic ester, 60 parts of deionized water.
3. a kind of outdoor wear production fabric according to claim 1, it is characterised in that:By following parts by weight raw material
Composition:Including 40 parts of cotton fiber, 16 parts of polyacrylonitrile fibre, 30 parts of polylactic acid, 18 parts of polyurethanes, detergent alkylate sulphur
22 parts of sour sodium, 15 parts of phosphatidyl-ethanolamine, 9 parts of potassium metabisulfite, 15 parts of cetyl trimethylammonium bromide, nanometer titanium dioxide
6 parts of silicon, 4 parts of linoleic acid, 4 parts of adhesive, 30 parts of acrylic resin, 3 parts of sodium sulphate, 6 parts of polyvinyl chloride, 14 parts of diatomite, chrysanthemum
8 parts of acetoacetic ester, 70 parts of deionized water.
4. a kind of outdoor wear production fabric according to claim 1, it is characterised in that:By following parts by weight raw material
Composition:Including 30 parts of cotton fiber, 13 parts of polyacrylonitrile fibre, 25 parts of polylactic acid, 14 parts of polyurethanes, detergent alkylate sulphur
20 parts of sour sodium, 13 parts of phosphatidyl-ethanolamine, 7 parts of potassium metabisulfite, 13 parts of cetyl trimethylammonium bromide, nanometer titanium dioxide
4 parts of silicon, 3 parts of linoleic acid, 3 parts of adhesive, 25 parts of acrylic resin, 2 parts of sodium sulphate, 4 parts of polyvinyl chloride, 12 parts of diatomite, chrysanthemum
5 parts of acetoacetic ester, 65 parts of deionized water.