CN108690431A - A kind of multifunction green environment protection type nano paint - Google Patents
A kind of multifunction green environment protection type nano paint Download PDFInfo
- Publication number
- CN108690431A CN108690431A CN201710102288.7A CN201710102288A CN108690431A CN 108690431 A CN108690431 A CN 108690431A CN 201710102288 A CN201710102288 A CN 201710102288A CN 108690431 A CN108690431 A CN 108690431A
- Authority
- CN
- China
- Prior art keywords
- nano
- calcium carbonate
- agent
- titanium dioxide
- environment protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of multifunction green environment protection type nano paint, main ingredient(Weight percent)For:Methacrylic acid, butyl acrylate, styrene and methyl methacrylate quadripolymer latex 20~65%;Nano-titanium dioxide 0.3~5%;Nano zine oxide 0.2~3%;Nano silicon dioxide 0.3~3%;Nano-calcium carbonate 0.5~5%;Deionized water 3~12%;Superfine talcum powder 1~3%;Calcium carbonate superfine powder 3~15%;Titanium dioxide 3~25%;The auxiliary agents such as dispersant, wetting agent, rheological agent, thickener, mill base, antifoaming agent 2~12%, this nano paint produced using this formula has the characteristics that nontoxic, pollution-free, washability, damage resistant, UV resistant, ageing-resistant, waterproof, mould proof, and also there is self-cleaning function, which is widely used in the surface anticorrosion processing of the decoration and metal material of various inner, external walls.
Description
Technical field
The present invention relates to a kind of multifunction green environment protection type nano paints.
Background technology
The kind that market is coated is more, but generally there is have a single function (to be only applicable to the dress of wall for these coating
Decorations) and coating not damage resistant the defects of.
Invention content
The object of the present invention is to provide a kind of waterproof, mould proof, washability, damage resistant, it is ageing-resistant, nontoxic, pollution-free and
A kind of multifunction green environment protection type nanometer painting for being not only suitable for wall body decoration and being suitable for anti-corrosion of metal again with self-cleaning function
Material.
In order to achieve the above object, a kind of multifunction green environment protection type nano paint of the invention is mainly by metering system
Acid, butyl acrylate, styrene and methyl methacrylate quadripolymer latex be equipped with nano-titanium dioxide, nano zine oxide,
Nano silicon dioxide and nano-calcium carbonate are formed.It specifically matches (weight percent):Methacrylic acid, acrylic acid fourth
Ester, styrene and methyl methacrylate quadripolymer latex 20~65%;Nano-titanium dioxide 0.3~5%;It is nano oxidized
Zinc 0.2~3%;Nano silicon dioxide 0.3~3%;Nano-calcium carbonate 0.5~5%;Deionized water 3~12%;Extra fine talc
Powder 1~3%;Calcium carbonate superfine powder 3~15%;Titanium dioxide 3~25%;Dispersant, rheological agent, thickener, mill base, disappears at wetting agent
The auxiliary agents such as infusion 2~12%.
The present invention specific method and facilities be:By deionized water, dispersant, moistening temperature agent, rheological agent, antifoaming agent (part)
Equal auxiliary agents are added in dispersion machine, are opened dispersion machine, are then successively delayed superfine talcum powder and calcium carbonate superfine powder and titanium dioxide
Slow to be added in dispersion machine, the material in dispersion machine was sent into grinder with pump and is ground after 30 minutes by high speed dispersion.From grinding
The material flowed out in machine enters intermediate storage tank, if necessary requirement is not achieved into the material size in intermediate storage tank, uses
Pump, which is sent in grinder, to be regrind, until reaching necessary requirement.
By methacrylic acid, butyl acrylate, styrene, methyl methacrylate quadripolymer latex and thickener, color
Slurry and part antifoaming agent are added in blend tank, open the stirring slurry of blend tank, under stiring, successively slowly into blend tank
Nano-titanium dioxide, nano zine oxide, nano silicon dioxide and nano-calcium carbonate is added, it, will be intermediate with pump after stirring 30 minutes
Material in storage tank is slowly added in blend tank, continues stirring 30 minutes, then sampling and testing, if qualification can spout bag
Dress.
The beneficial effects of the invention are as follows:Methacrylic acid, butyl acrylate, styrene and methyl methacrylate quaternary
Copolymer emulsion has excellent film-formation result, and the coating of its coating can be made to have the effect of waterproof, damage resistant, four kinds of nanometers
Material is used cooperatively, make its coating have excellent hydrophily, photocatalytic, water proofing property, stain resistance, resistance to ag(e)ing with
And mildew resistance and good workability.The coating can be used not only for the decoration of various walls and can be also used for metal
The surface anticorrosion of material is handled.
Embodiment 1, by deionized water 12%, dispersant 1.2%, wetting agent 0.4%, rheological agent 2.3%, antifoaming agent
0.05% is added in dispersion machine, dispersion machine is opened, then successively by superfine talcum powder 2%, calcium carbonate superfine powder 8%, titanium dioxide
14% is added in dispersion machine, and the material in dispersion machine was sent into grinder with pump and is ground after 30 minutes by high speed dispersion.From grinding
The material flowed out in grinding machine enters intermediate storage tank, if necessary requirement is not achieved into the material size in intermediate storage tank,
It is sent in grinder and is regrind with pump, until reaching necessary requirement.
By methacrylic acid, butyl acrylate, styrene, methyl methacrylate quadripolymer latex 50%, thickener
0.4%, mill base 1.6% and antifoaming agent 0.05% are added in blend tank, the stirring slurry of blend tank are opened, under stiring, to tune
Nano-titanium dioxide 2%, nano zine oxide 1.5%, nano silicon dioxide 2%, nano-calcium carbonate are slowly added in distribution tank successively
2.5%, after stirring 30 minutes, the material in intermediate storage tank is slowly added in blend tank with pump, after continuing stirring 30 minutes
Sampling and testing, if test passes, you can discharging packaging.
Claims (2)
1. a kind of multifunction green environment protection type nano paint is mainly made of lotion, water, filler and auxiliary agent etc., feature
It is:It is by methacrylic acid, butyl acrylate, styrene and methyl methacrylate quadripolymer latex, nanometer titanium dioxide
Titanium, nano zine oxide, nano silicon dioxide, nano-calcium carbonate, deionized water, superfine talcum powder, calcium carbonate superfine powder, titanium white
The auxiliary agents such as powder, dispersant, wetting agent, rheological agent, thickener, mill base, antifoaming agent are formed.
2. a kind of multifunction green environment protection type nano paint according to claim 1, characterized in that its proportioning (weight
Amount percentage) be:Methacrylic acid, butyl acrylate, styrene and methyl methacrylate quadripolymer latex 20~
65%;Nano-titanium dioxide 0.3~5%;Nano zine oxide 0.2~3%;Nano silicon dioxide 0.3~3%;Nano-calcium carbonate
Calcium 0.5~5%;Deionized water 3~12%;Superfine talcum powder 1~3%;Calcium carbonate superfine powder 3~15%;Titanium dioxide 3~25%;
The auxiliary agents such as dispersant, wetting agent, rheological agent, thickener, mill base, antifoaming agent 2~12%.