CN108688334A - The production method and glass photo of glass photo - Google Patents
The production method and glass photo of glass photo Download PDFInfo
- Publication number
- CN108688334A CN108688334A CN201710218181.9A CN201710218181A CN108688334A CN 108688334 A CN108688334 A CN 108688334A CN 201710218181 A CN201710218181 A CN 201710218181A CN 108688334 A CN108688334 A CN 108688334A
- Authority
- CN
- China
- Prior art keywords
- printing
- layer
- spray
- photo
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of production method of glass photo, including:A transparent printing plate is provided, the transparent printing plate includes in face of the outer surface of viewer and the printing surface opposite with outer surface, to the printing surface cleaning treatment;UV spray drawing machines are provided, the UV spray drawing machines adhering agent layer colourless in printing surface spraying layer of transparent is utilized;The color graphics of spray printing will be needed to input the UV spray drawing machines, the UV spray drawing machines are according to the color graphics in the adhering agent layer surface spraying colored ink, the UV spray drawing machines include ultraviolet light source, cure the colored ink using the ultraviolet light source using the UV spray drawing machines while spray printing, to make to form photochrome in transparent printing plate surface.The invention further relates to a kind of the glass photo to be formed is made using the glass photo production method.
Description
Technical field
The present invention relates to a kind of photo manufacturing technology fields more particularly to the production method and glass of a kind of glass photo to shine
Piece.
Background technology
In the prior art, in order to make photo preserve for a long time, people often apply last layer adhesive-layer on the surface of glass, use
Glass and photo are bonded by adhesive-layer, and photo and glass can be integrally fixed, but since glue-line is easy oxygen in air
Change and turn yellow, can also reduce the ornamental quality of glass photo.
Invention content
In view of this, it is necessary to provide a kind of production methods and glass of the glass photo that can solve above-mentioned technical problem
Photo.
A kind of production method of glass photo, including:
There is provided a transparent printing plate, the transparent printing plate includes in face of the outer surface of viewer and opposite with outer surface
Printing surface, to the printing surface cleaning treatment;
UV spray drawing machines are provided, the UV spray drawing machines adhering agent layer colourless in printing surface spraying layer of transparent is utilized;
The color graphics of spray printing will be needed to input the UV spray drawing machines, the UV spray drawing machines are according to the color graphics in institute
Adhering agent layer surface spraying colored ink is stated, the UV spray drawing machines include ultraviolet light source, using described while spray printing
UV spray drawing machines cure the colored ink using the ultraviolet light source, to make to form colored photograph in transparent printing plate surface
Piece.
In a preferred embodiment, the material of the transparent printing plate provided is acrylic or chemical strengthening glass
Glass.
In a preferred embodiment, it further includes utilizing the UV spray drawing machines in the coloured silk to form the photochrome later
The surface spray printing white ink layer of color photo, to form one layer of white substrate layer on the photochrome surface.
In a preferred embodiment, the photo table is also coated with white substrate layer.
In a preferred embodiment, acrylate, 20% weight of the ingredient of the white ink by about 75% parts by weight
The titanium dioxide of amount and the additive of 5% weight are mixed to form at normal temperatures.
In a preferred embodiment, the ingredient of the white substrate layer by 65~75% parts by weight acrylic acid
Ester, the titanium dioxide less than 20% weight and the additive less than 15% weight are mixed to form at normal temperatures.
In a preferred embodiment, the adhering agent layer is acryl resin glue.
In a preferred embodiment, the thickness of the adhering agent layer is 5~40um.
In a preferred embodiment, to the printing surface carry out cleaning treatment before further include to the printing surface into
Row cure process.
A kind of glass photo comprising:Transparent printing plate, the transparent printing plate include in face of viewer outer surface with
And the printing surface opposite with outer surface, the printing surface are formed with one layer of adhering agent layer, are formed on the adhering agent layer surface
Photochrome, the photochrome are formed by spray printing colored ink and after curing to colored ink.
In a preferred embodiment, the surface of the photochrome is also formed with one layer of white substrate layer.
In a preferred embodiment, one layer of hardening coat is formed on the printing surface.
Compared with prior art, the present invention provides glass photo since photo is that direct spray printing is formed in transparent printing plate
Printing surface, it is permanent retain will not yellowing, it is easy to clean, can be washed with water;Without additional photo frame.
Description of the drawings
Fig. 1 is the making step figure for the glass photo that first embodiment of the invention provides.
Fig. 2 is that the present invention makes the glass photo formed.
Fig. 3 is glass photo exploded view provided by the invention.
Fig. 4 is the sectional view of glass photo provided by the invention.
Main element symbol description
| Glass photo | 100 |
| Transparent printing plate | 10 |
| Outer surface | 11 |
| Printing surface | 12 |
| Adhering agent layer | 14 |
| Photochrome | 16 |
| White substrate layer | 18 |
Following specific implementation mode will be further illustrated the present invention in conjunction with above-mentioned attached drawing.
Specific implementation mode
With reference to accompanying drawings and embodiments will be combined, glass photo production method provided by the invention and glass photo are made
It is further to be described in detail.
It please refers to Fig.1 to Fig.4, is a kind of production method for glass photo that first embodiment of the invention provides, including such as
Lower step:
The first step 21:A transparent printing plate 10 is provided, the transparent printing plate 10 includes in face of the outer surface 11 of viewer
And the printing surface 12 opposite with outer surface 11, to 12 cleaning treatment of the printing surface.The material of the transparent printing plate 10 is
Acrylic or strengthened glass.The transparent printing plate 10 is preferably acrylic material.Acrylic material have it is light, will not break
The broken, high grade of transparency, the advantages that being easy to be machined.
In other embodiments, further include being carried out firmly to the printing surface 14 before doing cleaning treatment to printing surface
Change is handled, and one layer of hardening coat (not shown) is formed on the printing surface 14.Hardness can after cure process for acrylic material
Up to 5-6H or more, the acrylic material after hardening can promote wear-resisting scratch-resisting ability and have stronger translucency, and finish
It is good.
Second step 22 provides UV (ultraviolet, ultraviolet) spray drawing machine, using the UV spray drawing machines in the printing surface
The colourless adhering agent layer 16 of 14 spraying layer of transparent.The adhering agent layer 16 increases color oil for colored ink of subsequently adhering
The black adhesion between transparent printing plate 10 is avoided in ink-jet on transparent printing plate 10, and colored ink falls off over time
And the phenomenon that influencing photograph quality.
The UV spray drawing machines include four nozzles, and one of nozzle forms adhering agent layer for spraying, remaining 3
A nozzle is respectively used to contain white ink, black ink and colored ink.Namely the UV air brushing function is realized in the print
Brush finish sprays and to form adhering agent layer, forms photochrome in the adhering agent layer surface spraying colored ink, in the colored photograph
Piece surface spraying white ink forms white substrate layer.And the UV spray drawing machines are provided with ultraviolet light source, while spraying
For curing the ink, to realize the whole flow process for the glass photo that completes on a machine, without as previously
Technology also needs to be additionally provided wire mesh machine and curing apparatus.
Third step 23, it would be desirable to which the electronic pictures of spray printing input the UV spray drawing machines, and the UV spray drawing machines are according to the electricity
Sub-pictures are in the adhering agent layer surface spraying colored ink, using the UV spray drawing machines using described ultraviolet while spray printing
Lamp source cures the colored ink, to make to form photochrome in transparent printing plate surface.
Specifically, the UV spray drawing machines can be made to be connect with computer, USB or electronic equipment, the colour editted is shone
The electronics shelves of piece input the UV spray drawing machines.The UV spray drawing machines will be formed with sticker according to the electronic pictures described
Colored ink is sprayed on the transparent printing plate of layer, while spraying the colored ink, the ultraviolet light source is opened, makes institute
It states ultraviolet light source and cures the ink, the cured time is 3~5 seconds.
4th step 24, in the surface spray printing white ink layer of the photochrome 16, in the photochrome 16
Surface forms one layer of white substrate layer 18, and the photochrome 16 is completely covered in the white substrate layer 18.The white substrate
Layer 18 is to prevent photochrome 16 from being scratched to protect the photochrome 16.The white substrate layer 18 by acrylate,
Titanium dioxide and additive are mixed to form at normal temperatures, in a preferred embodiment, the ingredient of the white substrate layer 18 by
The acrylate of 65~75% parts by weight, the titanium dioxide less than 20% weight and the additive less than 15% weight are at normal temperatures
It is mixed to form.And when watching the glass photo 16 by outer surface, it can make the photochrome 16 that atomizing effect be presented.Certainly
It is appreciated that the white substrate layer 18 nor is it necessary that.
In the present embodiment, the ingredient of the colored ink is UV cured printing inks.UV cured printing inks have without volatility
Machine compound (VOC), therefore compared to solvent-based inks, UV cured printing inks have no irritating odor, and can save ink drying time,
It not can cause environmental pollution.
Fig. 2~Fig. 4 is please referred to, a kind of glass photo 100 provided for second embodiment of the invention.Specifically, Fig. 3 is this
The glass photo exploded view provided is invented, Fig. 4 is the sectional view of glass photo provided by the invention.Glass photo 100 includes:Thoroughly
Bright printing plate 10, the transparent printing plate 10 include in face of the outer surface 11 of viewer and the printing surface opposite with outer surface 11
12, the printing surface 12 is formed with the colourless adhering agent layer 14 of layer of transparent, and chromatic colour is formed on 14 surface of the adhering agent layer
Photo 16, the photochrome 16 are formed by spray printing colored ink and after curing to colored ink.The colored photograph
16 surface of piece forms one layer of white substrate layer 18, and the photochrome is completely covered in the white substrate layer 18.The white lining
Bottom 18 is to prevent from being scratched to protect the photochrome.In fact, Fig. 3 and Fig. 4 are each layers to glass photo
Structure is exaggerated thickening, to understand each layer for illustrating the present invention.In fact, the adhering agent layer 14 of glass photo,
The thickness of photochrome 16 and white substrate layer 18 is range in the micron-scale.
Glass photo made of the present invention (is 340nm using wavelength, irradiation level 0.55W/m by burn-in test2UV
Light continues exposure 96 hours) afterwards color do not change significantly, photo direct print is also formed in the print of transparent printing plate
Brush finish can preserve photo for a long time.
In conclusion glass photo 100 provided by the invention, paper photo is made without the mode of exposure imaging,
Namely the use of developing solution is eliminated, it is more environmentally friendly, and dissolvent residual is not present;Since to be that direct printing is formed in transparent for photo
The printing surface of printing plate, it is permanent retain will not yellowing, it is easy to clean, can be washed with water without additional photo frame;It is aobvious due to being not necessarily to exposure
Shadow, and the entire production process of photo is the inkjet printing directly on a printer, and one can be completed within a few minutes
The making of glass photo simplifies the production process of glass photo, is greatly improved to the producing efficiency of photo.
It is understood that above example is only used for illustrating the present invention, it is not used as limitation of the invention.For this
For the those of ordinary skill in field, the various other corresponding changes and deformation that technique according to the invention design is made, all
It falls within the protection domain of the claims in the present invention.
Claims (10)
1. a kind of production method of glass photo, including step:
A transparent printing plate is provided, the transparent printing plate includes in face of the outer surface of viewer and the print opposite with outer surface
Brush finish, to the printing surface cleaning treatment;
UV spray drawing machines are provided, spray to form the colourless adhering agent layer of layer of transparent in the printing surface using the UV spray drawing machines;
The color graphics of spray printing will be needed to input the UV spray drawing machines, the UV spray drawing machines are according to the color graphics described viscous
Oxidant layer surface spraying colored ink, the UV spray drawing machines include ultraviolet light source, are sprayed using the UV while spray printing
The ultraviolet light source for painting machine cures the colored ink, to make to form photochrome in transparent printing plate surface.
2. the production method of glass photo as described in claim 1, which is characterized in that the material of the transparent printing plate of offer
Matter is acrylic or chemically reinforced glass.
3. the production method of glass photo as claimed in claim 2, which is characterized in that form the photochrome and also wrap later
It includes using the UV spray drawing machines in the surface spray printing white ink layer of the photochrome, the white ink is cured
To the step of the photochrome surface forms one layer of white substrate layer.
4. the production method of glass photo as claimed in claim 3, which is characterized in that the ingredient of the white substrate layer is by 65
The acrylate of~75% parts by weight, the titanium dioxide less than 20% weight and the additive less than 15% weight mix at normal temperatures
It closes and is formed.
5. the production method of glass photo as claimed in claim 4, which is characterized in that the adhering agent layer is acryl resin
Glue.
6. the production method of glass photo as claimed in claim 3, which is characterized in that the ingredient of the colored ink is solid for UV
Carburetion ink.
7. the production method of glass photo as claimed in claim 4, which is characterized in that carried out at cleaning to the printing surface
Further include the steps that cure process is carried out to the printing surface before reason.
8. a kind of glass photo comprising:Transparent printing plate, the transparent printing plate include in face of viewer outer surface and
The printing surface opposite with outer surface, the printing surface are formed with one layer of adhering agent layer, and coloured silk is formed on the adhering agent layer surface
Color photo, the photochrome are formed by spray printing colored ink and after curing to colored ink.
9. glass photo as claimed in claim 8, which is characterized in that the surface of the photochrome is also formed with one layer of white
Substrate layer.
10. glass photo as claimed in claim 8, which is characterized in that be formed with one layer of hardening coat, institute on the printing surface
Hardening coat is stated between the printing surface and the adhering agent layer.