CN108676389A - 一种可降解甲醛的硅藻泥涂料及其制备方法 - Google Patents
一种可降解甲醛的硅藻泥涂料及其制备方法 Download PDFInfo
- Publication number
- CN108676389A CN108676389A CN201810414335.6A CN201810414335A CN108676389A CN 108676389 A CN108676389 A CN 108676389A CN 201810414335 A CN201810414335 A CN 201810414335A CN 108676389 A CN108676389 A CN 108676389A
- Authority
- CN
- China
- Prior art keywords
- parts
- diatom ooze
- ooze coating
- formaldehyde
- coating according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供了可降解甲醛的硅藻泥涂料及其制备方法，其主要成分为低品位硅藻土，通过造孔‑焙烧的步骤后，与其他原料一起混合得到了一种可降解甲醛的硅藻泥涂料，不仅可以吸收甲醛，还可以降解甲醛，同时具有强度高，耐久性强，释放负离子，成本低等优点。
Description
技术领域
本发明涉及涂料技术领域，尤其涉及硅藻泥涂料。
背景技术
硅藻泥是一种天然环保内墙装饰材料，用来替代墙纸和乳胶漆，起内墙装饰及室内空气净化作用。粉体包装，并非液态桶装。硅藻泥的适用范围很广泛。可以适用在以下地方：家庭(客厅、卧室、书房、婴儿房、天花等等墙面)、公寓、幼稚园、老人院、医院、疗养院、会所、主题俱乐部、高档饭店、度假酒店写字楼、风格餐厅等。
硅藻泥的主要原材料是历经亿万年形成的硅藻矿物——硅藻土，硅藻是一种生活在海洋、湖泊中的藻类。硅藻泥采取生活在数百万年前的水生浮游类生物——硅藻沉积而成的天然物质，主要成分为蛋白石，富含多种有益矿物质，质地轻软，电子显微镜显示其粒子表面具有无数微小的孔穴，孔隙率达90％以上，比表面积高达65m2/g。正是这种突出的分子筛结构，决定了其独特的功能——具有很强的物理吸附性能和离子交换性能，在墙面大面积喷水，能吸收大量水，说明吸附性很强，并缓慢持续释放负氧离子，能有效分解甲醛、苯、氡气等有害致癌物质。
但是，目前硅藻泥的主要原料硅藻土价格较高，使得硅藻泥的价格普遍高于其他涂料，从而使得硅藻泥的应用十分受限；其次，国内硅藻土矿主要以低品位硅藻土为主，而目前制备硅藻泥涂料的硅藻土为普通硅藻土或者硅藻精土；再次，硅藻土由于其具有发达的孔隙结构具有吸附甲醛的效果，但是其并不能降解甲醛，因此，其制备的硅藻泥涂料也不具有降解甲醛的性能，当吸收甲醛达到饱和时，其不但不能再吸收甲醛，也有可能放出甲醛，从而造成二次污染。最后，目前硅藻泥的强度较差，时间长了容易掉粉，从而影响硅藻泥涂料的美观。
发明内容
为解决上述问题，本发明提供的一种采用低品位硅藻土制备的硅藻泥，不仅可以吸收甲醛，还可以降解甲醛，同时具有强度高，耐久性强，释放负离子、成本低等优点。
一种可降解甲醛的硅藻泥涂料，其质量份配比为：
低品位硅藻土150-250份
工业废酸20-80份
碳酸氢钠2-5份
纳米二氧化钛2-5份
纤维素醚2-6份
所述低品位硅藻土的品位为15-30％的硅藻土，其伴生矿物主要是粘土矿物、石英、和铁矿。
所述工业废酸为工业浓酸。
作为本发明另一技术方案，硅藻泥涂料中还包括骨料20-40份、和/或填料20-100份。
所述骨料为石英砂或彩砂；也可以是玻璃微珠。
所述填料为滑石粉、石英粉、海鸥石粉，造纸白泥、重钙粉、膨润土中的至少一种。
所述填料为海鸥石粉，和/或造纸白泥。
作为本发明另一技术方案，硅藻泥涂料中还包括苯乙烯-甲基丙烯酸乳液12-24份。
一种可降解甲醛的硅藻泥涂料的制备方法：
(1)按照质量配比称取低品位硅藻土150-250份、工业废酸20-80份、以及碳酸氢钠2-5份，并进行搅拌混合；
(2)将步骤(1)得到的混合物料在100-120℃的温度下焙烧1-3h；
(3)将步骤(2)得到的焙烧物料打散后与其他剩余原料混合后充分搅拌，即得硅藻泥涂料。
与现有技术相比，本发明的有益效果主要体现在：
(1)制备方法简单、原料成本低。由于目前市场均采用普通硅藻土或硅藻精土，使得硅藻泥的涂料成本较高，部分工艺复杂也导致成本较高。而本发明的硅藻泥涂料采用低品位硅藻土，其原料来源广泛，成本低廉。
(2)本发明采用工业废酸和碳酸氢钠对低品位硅藻土进行了造孔，从而使得低品位硅藻土的孔隙、以及比表面积均接近于，甚至优于优质硅藻土，从而达到较好的吸收甲醛的效果，并且还利用了工业废酸，进行了废物再利用，达到了预料不到的技术效果。如果直接使用工业废酸对硅藻土进行造孔，搅拌后容易团聚，本发明创造性地加入了少量碳酸氢钠，使得混合过程中放出大量气体，降低了硅藻土的团聚，在硅藻土焙烧后，较为松散，从而为了将纳米二氧化钛较好地负载在硅藻土的孔隙中提供了良好的条件。
(3)本发明在造孔后的硅藻土中加入了少量纳米二氧化钛，不仅能够提高硅藻泥中各原料的分散均匀性，而且还能在可见光的状态下降解甲醛，由于纳米二氧化钛大量吸附于硅藻土的孔隙结构中，从而使得纳米二氧化钛降解甲醛的性能大大提升。
具体实施方式
下面结合具体实施例，对本发明的内容做进一步的详细说明：
为了达到本发明的目的，以下结合实施例1-4对本发明作进一步的描述。
实施例1
一种可降解甲醛的硅藻泥涂料的制备方法：
(1)按照质量配比称取低品位硅藻土200份、工业废酸40份、以及碳酸氢钠3份，并进行搅拌混合；
(2)将步骤(1)得到的混合物料在105℃的温度下焙烧1h；
(3)将步骤(2)得到的焙烧物料打散后，加入纳米二氧化钛4份，纤维素醚3份，混合后充分搅拌，即得硅藻泥涂料。
实施例2
一种可降解甲醛的硅藻泥涂料的制备方法：
(1)按照质量配比称取低品位硅藻土250份、工业废酸60份、以及碳酸氢钠5份，并进行搅拌混合；
(2)将步骤(1)得到的混合物料在105℃的温度下焙烧2h；
(3)将步骤(2)得到的焙烧物料打散后，加入纳米二氧化钛4份，纤维素醚6份，彩砂25份混合后充分搅拌，即得硅藻泥涂料。
实施例3
一种可降解甲醛的硅藻泥涂料的制备方法：
(1)按照质量配比称取低品位硅藻土180份、工业废酸30份、以及碳酸氢钠4份，并进行搅拌混合；
(2)将步骤(1)得到的混合物料在110℃的温度下焙烧3h；
(3)将步骤(2)得到的焙烧物料打散后，加入纳米二氧化钛2份，纤维素醚2份，玻璃微珠40份、海鸥石粉20份、造纸白泥50份混合后充分搅拌，即得硅藻泥涂料。
实施例4
一种可降解甲醛的硅藻泥涂料的制备方法：
(1)按照质量配比称取低品位硅藻土150份、工业废酸60份、以及碳酸氢钠5份，并进行搅拌混合；
(2)将步骤(1)得到的混合物料在120℃的温度下焙烧1h；
(3)将步骤(2)得到的焙烧物料打散后，加入纳米二氧化钛4份，纤维素醚2份，海鸥石粉50份、苯乙烯-甲基丙烯酸乳液18份混合后充分搅拌，即得硅藻泥涂料。
对实施例1-4进行性能测试，耐久性测试：分别在涂料完工6个月和12个月后，用高压水枪向涂有实施例1-4中硅藻泥涂料的墙壁连续喷射1000L水。空气净化性能测试：在环境温度(20±2)℃、相对湿度50％、密闭的空间内(20平方)，涂覆实施例1-4的硅藻泥涂料，涂覆面积为10平方，24h后测试甲醛净化率。其性能指标如表1所示：
表1实施例1-4进行性能测试结果
虽然，上文中己经用一般性说明及具体实施例对本发明作了详尽的描述，但在本发明基础上，可以对之作一些修改或改进，这对本领域技术人员而言是显而易见的。因此，在不偏离本发明精神的基础上所做的这些修改或改进，均属于本发明要求保护的范围。
Claims (9)
1.一种可降解甲醛的硅藻泥涂料，由以下质量份配比组成：
低品位硅藻土 150-250份
工业废酸 20-80份
碳酸氢钠 2-5份
纳米二氧化钛 2-5份
纤维素醚 2-6份。
2.根据权利要求1所述的硅藻泥涂料，所述低品位硅藻土的品位为15-30％。
3.根据权利要求1所述的硅藻泥涂料，所述工业废酸为工业浓酸。
4.根据权利要求1所述的硅藻泥涂料，还包括骨料20-40份、和/或填料20-100份。
5.根据权利要求1所述的硅藻泥涂料，所述骨料为石英砂或彩砂。
6.根据权利要求1所述的硅藻泥涂料，所述填料为滑石粉、石英粉、海鸥石粉，造纸白泥、重钙粉、膨润土中的至少一种。
7.根据权利要求1所述的硅藻泥涂料，所述填料为海鸥石粉，和/或造纸白泥。
8.根据权利要求1所述的硅藻泥涂料，硅藻泥涂料中还包括苯乙烯-甲基丙烯酸乳液12-24份。
9.一种可降解甲醛的硅藻泥涂料的制备方法：
(1)按照质量配比称取低品位硅藻土150-250份、工业废酸20-80份、以及碳酸氢钠2-5份，并进行搅拌混合；
(2)将步骤(1)得到的混合物料在100-120℃的温度下焙烧1-3h；
(3)将步骤(2)得到的焙烧物料打散后与其他剩余原料混合后充分搅拌，即得硅藻泥涂料。