CN108661292A - 一种健身房抗菌防霉释放负离子装修施工方法 - Google Patents

一种健身房抗菌防霉释放负离子装修施工方法 Download PDF

Info

Publication number
CN108661292A
CN108661292A CN201810472284.2A CN201810472284A CN108661292A CN 108661292 A CN108661292 A CN 108661292A CN 201810472284 A CN201810472284 A CN 201810472284A CN 108661292 A CN108661292 A CN 108661292A
Authority
CN
China
Prior art keywords
parts
antibacterial
mouldproof
powder
decoration construction
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810472284.2A
Other languages
English (en)
Inventor
朱德官
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Lead Technology Co Ltd
Original Assignee
Shanghai Lead Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Lead Technology Co Ltd filed Critical Shanghai Lead Technology Co Ltd
Priority to CN201810472284.2A priority Critical patent/CN108661292A/zh
Publication of CN108661292A publication Critical patent/CN108661292A/zh
Withdrawn legal-status Critical Current

Abstract

本发明提供一种健身房抗菌防霉释放负离子装修施工方法，涉及建筑装修领域，其特征在于包括顶棚抗菌防霉释放负离子装修施工、墙面抗菌防霉释放负离子装修施工、地面抗菌防霉释放负离子装修施工，其有益效果是：装修工艺简单环保，原料价廉易得，有效起到抗菌防霉释放负离子的作用，改善空气质量，负离子能使人们在运动时呼吸顺畅有益于身体健康。

Description

一种健身房抗菌防霉释放负离子装修施工方法
技术领域
本发明涉及建筑装修领域。具体涉及一种健身房抗菌防霉释放负离子装修施工方法。
背景技术
当人们在健身房运动时由于每个人的呼吸量加大，造成空气中负离子含量降低，氧气含量降低，二氧化碳升高，并且空气弥漫着很多致病病毒，对人们的健康会造成很大的危害，针对现有技术的不足，因此发明一种健身房抗菌防霉释放负离子装修施工方法，其有益效果是：装修工艺简单环保，原料价廉易得，有效起到抗菌防霉释放负离子的作用，改善空气质量，负离子能使人们在运动时呼吸顺畅有益于身体健康。
发明内容
本发明就是为了解决现有技术中的问题，提供一种健身房抗菌防霉释放负离子装修施工方法。
本发明所要解决的技术问题。通过以下技术方案实现。
一种健身房抗菌防霉释放负离子装修施工方法，其特征在于包括顶棚抗菌防霉释放负离子装修施工、墙面抗菌防霉释放负离子装修施工、地面抗菌防霉释放负离子装修施工。
进一步的所述一种健身房抗菌防霉释放负离子装修施工方法，其特征在于所述顶棚抗菌防霉释放负离子装修施工包括以下步骤：（1）将水管、强电管线、弱电管线、智能、消防、新风管、排风管、进风口、出风口、排序、连接、安装；（2）顶棚立面造型；（3）处理接缝（4）涂刷抗菌防霉释放负离子界面剂（5）刮抗菌防霉释放负离子腻子找平打磨；（6）施工装饰面；（7）所述抗菌防霉释放负离子界面剂为包括：丙烯酸乳液30-45份、VAE乳液10-25份、碳酸钙6-10份、、二氧化钛3-10份、硅藻土3-10份、稀土精矿粉1-6份、电气石粉10-22份、羟乙基纤维素1-4份、胶粉1-4份、杀菌防霉剂0.3-2份、防冻剂0.5-1份、流平剂2-6份、分散剂0.5-1份、消泡剂0.3-1份，涂刷1-3遍；（8）所述抗菌防霉释放负离子腻子为包括硅藻土30-45份、灰钙粉15-30份、双飞粉15-30份、钛白粉2-8份、石英粉5-10份、稀土精矿粉1-6份、电气石粉10-22份、可再分散乳胶粉6-15份、黄原胶粉4-10份、白水泥3-6份、聚丙烯短纤维2-6份、季铵盐0.5-1.5份、碳酸氢钠0.3-1份、山梨酸0.2-1.2份、硫酸铜0.2-1.2份、氟化钠0.1-1份、OBPA 0.5-2份、二乙醇胺0.8-2.5份、分散剂0.05-0.7份、润滑剂0.03-0.5份、余量：水，厚度范围为0.3-1.5mm。
进一步的所述一种健身房抗菌防霉释放负离子装修施工方法，其特征在于所述墙面抗菌防霉释放负离子装修施工包括以下步骤：（1）将水管、强电管线、弱电管线、智能、开关、消防、插座、排序、连接、安装；（2）涂刷抗菌防霉释放负离子界面剂（3）刮抗菌防霉释放负离子腻子找平打磨；（4）涂装饰面；（5）所述抗菌防霉释放负离子界面剂为包括：丙烯酸乳液30-45份、VAE乳液10-25份、碳酸钙6-10份、二氧化钛3-10份、硅藻土3-10份、稀土精矿粉1-6份、电气石粉10-22份、羟乙基纤维素1-4份、胶粉1-4份、杀菌防霉剂1-4份、防冻剂0.5-1份、流平剂2-6份、分散剂0.5-1份、消泡剂0.3-1份，涂刷1-3遍；（6）所述抗菌防霉释放负离子腻子为包括硅藻土30-45份、灰钙粉15-30份、双飞粉15-30份、钛白粉2-8份、石英粉5-10份、稀土精矿粉1-6份、电气石粉10-22份、可再分散乳胶粉6-15份、黄原胶粉4-10份、白水泥3-6份、聚丙烯短纤维2-6份、季铵盐0.5-1.5份、碳酸氢钠0.3-1份、山梨酸0.2-1.2份、硫酸铜0.2-1.2份、氟化钠0.1-1份、OBPA 0.5-2份、二乙醇胺0.8-2.5份、分散剂0.05-0.7份、润滑剂0.03-0.5份、余量：水，厚度范围为0.5-1.5mm。
进一步的所述一种健身房抗菌防霉释放负离子装修施工方法，其特征在于所述地面抗菌防霉释放负离子装修施工包括以下步骤：（1）将水管、地暖、强电管线、弱电管线、智能、消防、开关、插座、排序、连接、安装；（2）浇筑抗菌防霉释放负离子自流平 ；（3）铺设地面装饰；（4）所述抗菌防霉释放负离子自流平为包括OBPA 1-6份、纳米银粉1-3份、稀土精矿粉1-6份、电气石粉15-25份、防潮剂1-5份、高铝水泥30-40份、硅酸盐水泥30-40份、石英砂5-10份、大白粉5-10份、无水石膏2-6份、可再分散乳胶粉3-8份、分散剂1-3份、流平剂1-5份、消泡剂1-3份、缓凝减水剂1-3份、助剂2-8份、余量：水，厚度范围为3-12mm，养护7-20天。
本发明其有益效果是：装修工艺简单环保，原料价廉易得，有效起到抗菌防霉释放负离子的作用，改善空气质量，负离子能使人们在运动时呼吸顺畅有益于身体健康。
具体实施方式
实施例1：一种健身房抗菌防霉释放负离子装修施工方法，其特征在于包括顶棚抗菌防霉释放负离子装修施工、墙面抗菌防霉释放负离子装修施工、地面抗菌防霉释放负离子装修施工。
本实施例所述一种健身房抗菌防霉释放负离子装修施工方法，其特征在于所述顶棚抗菌防霉释放负离子装修施工包括以下步骤：（1）将水管、强电管线、弱电管线、智能、消防、新风管、排风管、进风口、出风口、排序、连接、安装；（2）顶棚立面造型；（3）处理接缝（4）涂刷抗菌防霉释放负离子界面剂（5）刮抗菌防霉释放负离子腻子找平打磨；（6）施工装饰面；（7）所述抗菌防霉释放负离子界面剂为包括：丙烯酸乳液35份、VAE乳液20份、碳酸钙8份、、二氧化钛6份、硅藻土8份、稀土精矿粉3份、电气石粉16份、羟乙基纤维素3份、胶粉3份、杀菌防霉剂2份、防冻剂0.5份、流平剂2份、分散剂1份、消泡剂0.3份，涂刷3遍；（8）所述抗菌防霉释放负离子腻子为包括硅藻土38份、灰钙粉30份、双飞粉15份、钛白粉5份、石英粉5份、稀土精矿粉3份、电气石粉16份、可再分散乳胶粉9份、黄原胶粉4份、白水泥6份、聚丙烯短纤维3份、季铵盐1份、碳酸氢钠0.3份、山梨酸0.8份、硫酸铜1.2份、氟化钠1份、OBPA 2份、二乙醇胺2.5份、分散剂0.7份、润滑剂0.5份、余量：水，厚度范围为0.9mm。
本实施例所述一种健身房抗菌防霉释放负离子装修施工方法，其特征在于所述墙面抗菌防霉释放负离子装修施工包括以下步骤：（1）将水管、强电管线、弱电管线、智能、开关、消防、插座、排序、连接、安装；（2）涂刷抗菌防霉释放负离子界面剂（3）刮抗菌防霉释放负离子腻子找平打磨；（4）涂装饰面；（5）所述抗菌防霉释放负离子界面剂为包括：丙烯酸乳液35份、VAE乳液20份、碳酸钙10份、二氧化钛10份、硅藻土8份、稀土精矿粉3份、电气石粉18份、羟乙基纤维素4份、胶粉4份、杀菌防霉剂3份、防冻剂1份、流平剂3份、分散剂0.5份、消泡剂0.3份，涂刷3遍；（6）所述抗菌防霉释放负离子腻子为包括硅藻土35份、灰钙粉30份、双飞粉15份、钛白粉3份、石英粉5份、稀土精矿粉3份、电气石粉12份、可再分散乳胶粉7份、黄原胶粉5份、白水泥6份、聚丙烯短纤维6份、季铵盐1份、碳酸氢钠0.3份、山梨酸1.2份、硫酸铜1.2份、氟化钠1份、OBPA 0.5份、二乙醇胺2.5份、分散剂0.7份、润滑剂0.5份、余量：水，厚度范围为1.5mm。
本实施例所述一种健身房抗菌防霉释放负离子装修施工方法，其特征在于所述地面抗菌防霉释放负离子装修施工包括以下步骤：（1）将水管、地暖、强电管线、弱电管线、智能、消防、开关、插座、排序、连接、安装；（2）浇筑抗菌防霉释放负离子自流平 ；（3）铺设地面装饰；（4）所述抗菌防霉释放负离子自流平为包括OBPA 3份、纳米银粉1份、稀土精矿粉5份、电气石粉25份、防潮剂5份、高铝水泥40份、硅酸盐水泥30份、石英砂10份、大白粉5份、无水石膏4份、可再分散乳胶粉3份、分散剂1份、流平剂3份、消泡剂1份、缓凝减水剂3份、助剂4份、余量：水，厚度范围为12mm，养护10天。
实施例2：一种健身房抗菌防霉释放负离子装修施工方法，其特征在于包括顶棚抗菌防霉释放负离子装修施工、墙面抗菌防霉释放负离子装修施工、地面抗菌防霉释放负离子装修施工。
本实施例所述一种健身房抗菌防霉释放负离子装修施工方法，其特征在于所述顶棚抗菌防霉释放负离子装修施工包括以下步骤：（1）将水管、强电管线、弱电管线、智能、消防、新风管、排风管、进风口、出风口、排序、连接、安装；（2）顶棚立面造型；（3）处理接缝（4）涂刷抗菌防霉释放负离子界面剂（5）刮抗菌防霉释放负离子腻子找平打磨；（6）施工装饰面；（7）所述抗菌防霉释放负离子界面剂为包括：丙烯酸乳液40份、VAE乳液20份、碳酸钙10份、、二氧化钛6份、硅藻土8份、稀土精矿粉4份、电气石粉18份、羟乙基纤维素3份、胶粉3份、杀菌防霉剂2份、防冻剂0.5份、流平剂2份、分散剂1份、消泡剂0.3份，涂刷3遍；（8）所述抗菌防霉释放负离子腻子为包括硅藻土38份、灰钙粉30份、双飞粉15份、钛白粉5份、石英粉5份、稀土精矿粉4份、电气石粉18份、可再分散乳胶粉9份、黄原胶粉4份、白水泥6份、聚丙烯短纤维3份、季铵盐1份、碳酸氢钠0.3份、山梨酸0.8份、硫酸铜1.2份、氟化钠1份、OBPA 2份、二乙醇胺2.5份、分散剂0.7份、润滑剂0.5份、余量：水，厚度范围为0.9mm。
本实施例所述一种健身房抗菌防霉释放负离子装修施工方法，其特征在于所述墙面抗菌防霉释放负离子装修施工包括以下步骤：（1）将水管、强电管线、弱电管线、智能、开关、消防、插座、排序、连接、安装；（2）涂刷抗菌防霉释放负离子界面剂（3）刮抗菌防霉释放负离子腻子找平打磨；（4）涂装饰面；（5）所述抗菌防霉释放负离子界面剂为包括：丙烯酸乳液40份、VAE乳液20份、碳酸钙10份、二氧化钛10份、硅藻土10份、稀土精矿粉5份、电气石粉18份、羟乙基纤维素4份、胶粉4份、杀菌防霉剂3份、防冻剂1份、流平剂3份、分散剂0.5份、消泡剂0.3份，涂刷2遍；（6）所述抗菌防霉释放负离子腻子为包括硅藻土35份、灰钙粉30份、双飞粉15份、钛白粉6份、石英粉7份、稀土精矿粉3份、电气石粉15份、可再分散乳胶粉7份、黄原胶粉5份、白水泥5份、聚丙烯短纤维6份、季铵盐1份、碳酸氢钠0.3份、山梨酸1.2份、硫酸铜1.2份、氟化钠1份、OBPA 0.5份、二乙醇胺2.5份、分散剂0.7份、润滑剂0.5份、余量：水，厚度范围为1mm。
本实施例所述一种健身房抗菌防霉释放负离子装修施工方法，其特征在于所述地面抗菌防霉释放负离子装修施工包括以下步骤：（1）将水管、地暖、强电管线、弱电管线、智能、消防、开关、插座、排序、连接、安装；（2）浇筑抗菌防霉释放负离子自流平 ；（3）铺设地面装饰；（4）所述抗菌防霉释放负离子自流平为包括OBPA 3份、纳米银粉1份、稀土精矿粉6份、电气石粉25份、防潮剂5份、高铝水泥40份、硅酸盐水泥35份、石英砂10份、大白粉7份、无水石膏5份、可再分散乳胶粉5份、分散剂1份、流平剂3份、消泡剂1份、缓凝减水剂3份、助剂4份、余量：水，厚度范围为11mm，养护13天。
实施例3：一种健身房抗菌防霉释放负离子装修施工方法，其特征在于包括顶棚抗菌防霉释放负离子装修施工、墙面抗菌防霉释放负离子装修施工、地面抗菌防霉释放负离子装修施工。
本实施例所述一种健身房抗菌防霉释放负离子装修施工方法，其特征在于所述顶棚抗菌防霉释放负离子装修施工包括以下步骤：（1）将水管、强电管线、弱电管线、智能、消防、新风管、排风管、进风口、出风口、排序、连接、安装；（2）顶棚立面造型；（3）处理接缝（4）涂刷抗菌防霉释放负离子界面剂（5）刮抗菌防霉释放负离子腻子找平打磨；（6）施工装饰面；（7）所述抗菌防霉释放负离子界面剂为包括：丙烯酸乳液45份、VAE乳液25份、碳酸钙10份、、二氧化钛9份、硅藻土10份、稀土精矿粉6份、电气石粉22份、羟乙基纤维素4份、胶粉3份、杀菌防霉剂2份、防冻剂0.5份、流平剂2份、分散剂1份、消泡剂0.3份，涂刷3遍；（8）所述抗菌防霉释放负离子腻子为包括硅藻土45份、灰钙粉30份、双飞粉30份、钛白粉5份、石英粉5份、稀土精矿粉4份、电气石粉18份、可再分散乳胶粉9份、黄原胶粉4份、白水泥6份、聚丙烯短纤维6份、季铵盐1份、碳酸氢钠1份、山梨酸1份、硫酸铜1.2份、氟化钠1份、OBPA 2份、二乙醇胺2.5份、分散剂0.7份、润滑剂0.5份、余量：水，厚度范围为1mm。
本实施例所述一种健身房抗菌防霉释放负离子装修施工方法，其特征在于所述墙面抗菌防霉释放负离子装修施工包括以下步骤：（1）将水管、强电管线、弱电管线、智能、开关、消防、插座、排序、连接、安装；（2）涂刷抗菌防霉释放负离子界面剂（3）刮抗菌防霉释放负离子腻子找平打磨；（4）涂装饰面；（5）所述抗菌防霉释放负离子界面剂为包括：丙烯酸乳液45份、VAE乳液25份、碳酸钙10份、二氧化钛10份、硅藻土10份、稀土精矿粉5份、电气石粉22份、羟乙基纤维素4份、胶粉4份、杀菌防霉剂3份、防冻剂1份、流平剂3份、分散剂0.5份、消泡剂0.3份，涂刷2遍；（6）所述抗菌防霉释放负离子腻子为包括硅藻土45份、灰钙粉30份、双飞粉30份、钛白粉6份、石英粉9份、稀土精矿粉6份、电气石粉20份、可再分散乳胶粉7份、黄原胶粉5份、白水泥6份、聚丙烯短纤维6份、季铵盐1份、碳酸氢钠0.3份、山梨酸1.2份、硫酸铜1.2份、氟化钠1份、OBPA 0.5份、二乙醇胺2.5份、分散剂0.7份、润滑剂0.5份、余量：水，厚度范围为1mm。
本实施例所述一种健身房抗菌防霉释放负离子装修施工方法，其特征在于所述地面抗菌防霉释放负离子装修施工包括以下步骤：（1）将水管、地暖、强电管线、弱电管线、智能、消防、开关、插座、排序、连接、安装；（2）浇筑抗菌防霉释放负离子自流平 ；（3）铺设地面装饰；（4）所述抗菌防霉释放负离子自流平为包括OBPA 3份、纳米银粉1份、稀土精矿粉6份、电气石粉25份、防潮剂5份、高铝水泥40份、硅酸盐水泥40份、石英砂10份、大白粉10份、无水石膏6份、可再分散乳胶粉8份、分散剂3份、流平剂3份、消泡剂3份、缓凝减水剂3份、助剂8份、余量：水，厚度范围为12mm，养护14天。
上述实施例仅是对本发明的说明并非对本发明做出形式上的限制，在不脱离本发明的技术方案范围之内任何利用上述揭示的技术内容做出简单变化的等同等方案均属于本发明的保护范围。

Claims (4)

1.一种健身房抗菌防霉释放负离子装修施工方法，其特征在于包括顶棚抗菌防霉释放负离子装修施工、墙面抗菌防霉释放负离子装修施工、地面抗菌防霉释放负离子装修施工。
2.根据权利要求1所述一种健身房抗菌防霉释放负离子装修施工方法，其特征在于所述顶棚抗菌防霉释放负离子装修施工包括以下步骤：（1）将水管、强电管线、弱电管线、智能、消防、新风管、排风管、进风口、出风口、排序、连接、安装；（2）顶棚立面造型；（3）处理接缝（4）涂刷抗菌防霉释放负离子界面剂（5）刮抗菌防霉释放负离子腻子找平打磨；（6）施工装饰面；（7）所述抗菌防霉释放负离子界面剂为包括：丙烯酸乳液30-45份、VAE乳液10-25份、碳酸钙6-10份、、二氧化钛3-10份、硅藻土3-10份、稀土精矿粉1-6份、电气石粉10-22份、羟乙基纤维素1-4份、胶粉1-4份、杀菌防霉剂0.3-2份、防冻剂0.5-1份、流平剂2-6份、分散剂0.5-1份、消泡剂0.3-1份，涂刷1-3遍；（8）所述抗菌防霉释放负离子腻子为包括硅藻土30-45份、灰钙粉15-30份、双飞粉15-30份、钛白粉2-8份、石英粉5-10份、稀土精矿粉1-6份、电气石粉10-22份、可再分散乳胶粉6-15份、黄原胶粉4-10份、白水泥3-6份、聚丙烯短纤维2-6份、季铵盐0.5-1.5份、碳酸氢钠0.3-1份、山梨酸0.2-1.2份、硫酸铜0.2-1.2份、氟化钠0.1-1份、OBPA 0.5-2份、二乙醇胺0.8-2.5份、分散剂0.05-0.7份、润滑剂0.03-0.5份、余量：水，厚度范围为0.3-1.5mm。
3. 根据权利要求1所述一种健身房抗菌防霉释放负离子装修施工方法，其特征在于所述墙面抗菌防霉释放负离子装修施工包括以下步骤：（1）将水管、强电管线、弱电管线、智能、开关、消防、插座、排序、连接、安装；（2）涂刷抗菌防霉释放负离子界面剂（3）刮抗菌防霉释放负离子腻子找平打磨；（4）涂装饰面；（5）所述抗菌防霉释放负离子界面剂为包括：丙烯酸乳液30-45份、VAE乳液10-25份、碳酸钙6-10份、二氧化钛3-10份、硅藻土3-10份、稀土精矿粉1-6份、电气石粉10-22份、羟乙基纤维素1-4份、胶粉1-4份、杀菌防霉剂1-4份、防冻剂0.5-1份、流平剂2-6份、分散剂0.5-1份、消泡剂0.3-1份，涂刷1-3遍；（6）所述抗菌防霉释放负离子腻子为包括硅藻土30-45份、灰钙粉15-30份、双飞粉15-30份、钛白粉2-8份、石英粉5-10份、稀土精矿粉1-6份、电气石粉10-22份、可再分散乳胶粉6-15份、黄原胶粉4-10份、白水泥3-6份、聚丙烯短纤维2-6份、季铵盐0.5-1.5份、碳酸氢钠0.3-1份、山梨酸0.2-1.2份、硫酸铜0.2-1.2份、氟化钠0.1-1份、OBPA 0.5-2份、二乙醇胺0.8-2.5份、分散剂0.05-0.7份、润滑剂0.03-0.5份、余量：水，厚度范围为0.5-1.5mm。
4. 根据权利要求1所述一种健身房抗菌防霉释放负离子装修施工方法，其特征在于所述 地面抗菌防霉释放负离子装修施工包括以下步骤：（1）将水管、地暖、强电管线、弱电管线、智能、消防、开关、插座、排序、连接、安装；（2）浇筑抗菌防霉释放负离子自流平 ；（3）铺设地面装饰；（4）所述抗菌防霉释放负离子自流平为包括OBPA 1-6份、纳米银粉1-3份、稀土精矿粉1-6份、电气石粉15-25份、防潮剂1-5份、高铝水泥30-40份、硅酸盐水泥30-40份、石英砂5-10份、大白粉5-10份、无水石膏2-6份、可再分散乳胶粉3-8份、分散剂1-3份、流平剂1-5份、消泡剂1-3份、缓凝减水剂1-3份、助剂2-8份、余量：水，厚度范围为3-12mm，养护7-20天。
CN201810472284.2A 2018-05-17 2018-05-17 一种健身房抗菌防霉释放负离子装修施工方法 Withdrawn CN108661292A (zh)