CN108642863A - It is a kind of can room temperature dyeing nylon facing material preparation method - Google Patents
It is a kind of can room temperature dyeing nylon facing material preparation method Download PDFInfo
- Publication number
- CN108642863A CN108642863A CN201810475674.5A CN201810475674A CN108642863A CN 108642863 A CN108642863 A CN 108642863A CN 201810475674 A CN201810475674 A CN 201810475674A CN 108642863 A CN108642863 A CN 108642863A
- Authority
- CN
- China
- Prior art keywords
- fabric
- room temperature
- facing material
- material preparation
- nylon facing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses it is a kind of can room temperature dyeing nylon facing material preparation method, include the following steps:S1, pretreatment:Ready-made clothes is made into the cutting of undyed fabric, first puts dye vat into and is heated to 70~90 DEG C and do pre-treatment, remove the greasy dirt and impurity of cloth cover;S2, modification:MAC 3~5% and piece alkali 2~4% will be added in manufactured fabric in S1,20~30min is kept the temperature under conditions of 50~70 DEG C;S3, washing:In the fabric handled in S2 plus the special beautiful dyestuff 4~6% of the speed of selected color, 5~10min of cold water wash adjust acid 5g:4.7~5.3 times 70~90 DEG C of heatings of 0.8~1.2L or pH value, 20~30min of moisturizing.It is proposed by the present invention to be washed or the characteristic of nylon entirely by changing, the stiff looks of sportswear can be revolutionized with garment dyeing under normal temperature and pressure conditions and ready-made clothes washing technique, sportswear is allowed to keep up with the trend of fashionable dress development.
Description
Technical field
The present invention relates to garment material processing technique field more particularly to it is a kind of can room temperature dyeing nylon facing material preparation
Method.
Background technology
Dyeing catches color, also referred to as paints, and referring to chemistry or other methods influences substance itself and it is made
Color.Under conditions of technology allows, object can be made to show desirable a variety of colors by dyeing, use is colourful
To decorate life.The method of dyeing has it from ancient times, and continues to develop.
Conventional motion dress ornament is washed or nylon facing material due to the use of complete, in view of washing entirely or the characteristic of nylon facing material, it is necessary to high temperature
High pressure dyeing can not use for reference garment dyeing and ready-made clothes washing work under the normal temperature and pressure conditions largely used in cotton sportswear
Skill, can only pass through change fabric structure, color, print embroider etc. common process so that the fabric processed is stiff, fashion by
To limitation, therefore, we have proposed it is a kind of can room temperature dyeing nylon facing material preparation method for solving the above problems.
Invention content
The purpose of the present invention is to solve disadvantage existing in the prior art, and propose it is a kind of can room temperature dyeing Buddhist nun
The preparation method of imperial fabric.
It is a kind of can room temperature dyeing nylon facing material preparation method, include the following steps:
S1, pretreatment:Ready-made clothes is made into the cutting of undyed fabric, first puts dye vat into and is heated to 70~90 DEG C and do preceding place
Reason, removes the greasy dirt and impurity of cloth cover;
S2, modification:MAC 3~5% and piece alkali 2~4% will be added in manufactured fabric in S1, in 50~70 DEG C of condition
20~30min of lower heat preservation;
S3, washing:In the fabric handled in S2 plus the special beautiful dyestuff 4~6% of the speed of selected color, cold water wash 5~
10min adjusts acid 5g:4.7~5.3 times 70~90 DEG C, 20~30min of moisturizing of heatings of 0.8~1.2L or pH value, then with 40~60
DEG C clear water wash 10~15min, dehydration ring dries;
S4, reprocessing:Potassium permanganate and 80 will be wiped by hand on the fabric dried by dehydration ring in S3:Then 60 phosphoric acid add
It in sodium pyrosulfite and 15~25min, then washs 2 times, 5~10min, dehydration ring dry every time.
Preferably, in the S1, ready-made clothes is made into the cutting of undyed fabric, first puts dye vat into and is heated to 75~85 DEG C
Pre-treatment is done, the greasy dirt and impurity of cloth cover are removed.
Preferably, in the S2, the concentration ratio of modified MAC and piece alkali is 3~5:2~4.
Preferably, in the S2, MAC 3.5~4.5% and piece alkali 2.5~3.5% will be added in manufactured fabric in S1,
23~28min is kept the temperature under conditions of 55~65 DEG C.
Preferably, the special beautiful dyestuff 4.5~5.5% of the speed of selected color is added in the S3, in the fabric handled in S2, it is cold
Water cleans 6~9min, adjusts acid 5g:4.9~5.1 times 75~85 DEG C, 22~28min of moisturizing of heatings of 0.9~1.1L or pH value, then
11~14min is washed with 45~55 DEG C of clear water, dehydration ring dries.
Preferably, in the S4, potassium permanganate and 80 will be wiped by hand on the fabric dried by dehydration ring in S3:60 phosphoric acid,
Then it plus in sodium pyrosulfite and 18~23min, then washs 2 times, 6~9min, dehydration ring dry every time.
It is proposed by the present invention it is a kind of can room temperature dyeing nylon facing material preparation method it is easy to operate, by change entirely wash or
The characteristic of nylon can revolutionize the stiff face of sportswear with garment dyeing under normal temperature and pressure conditions and ready-made clothes washing technique
Looks allow sportswear to keep up with the trend of fashionable dress development, and preparation process is simple, and manufacturing cost is low, is worthy to be popularized.
Description of the drawings
Fig. 1 is the nylon facing material schematic diagram of prior art processing;
Fig. 2 be it is proposed by the present invention it is a kind of can room temperature dyeing nylon facing material preparation method nylon facing material schematic diagram.
Specific implementation mode
The present invention is made further to explain with reference to specific embodiment.
Embodiment one
With reference to Fig. 2, it is proposed by the present invention it is a kind of can room temperature dyeing nylon facing material preparation method, include the following steps:
S1, pretreatment:Ready-made clothes is made into the cutting of undyed fabric, first puts dye vat into and is heated to 70 DEG C and do pre-treatment,
Remove the greasy dirt and impurity of cloth cover;
S2, modification:MAC 3% and piece alkali 2% will be added in manufactured fabric in S1, is kept the temperature under conditions of 50 DEG C
20min;
S3, washing:In the fabric handled in S2 plus the special beautiful dyestuff 4% of the speed of selected color, cold water wash 5min adjust acid
5g:4.7 times 70 DEG C, moisturizing 20min of heatings of 0.8L or pH value, then wash 10min with 40 DEG C of clear water, and dehydration ring dries;
S4, reprocessing:Potassium permanganate and 80 will be wiped by hand on the fabric dried by dehydration ring in S3:Then 60 phosphoric acid add
It in sodium pyrosulfite and 15min, then washs 2 times, each 5min, dehydration ring dries.
Embodiment two
With reference to Fig. 2, it is proposed by the present invention it is a kind of can room temperature dyeing nylon facing material preparation method, include the following steps:
S1, pretreatment:Ready-made clothes is made into the cutting of undyed fabric, first puts dye vat into and is heated to 80 DEG C and do pre-treatment,
Remove the greasy dirt and impurity of cloth cover;
S2, modification:MAC 4% and piece alkali 3% will be added in manufactured fabric in S1, is kept the temperature under conditions of 60 DEG C
25min;
S3, washing:In the fabric handled in S2 plus the special beautiful dyestuff 5% of the speed of selected color, cold water wash 8min adjust acid
5g:5.0 times 80 DEG C, moisturizing 25min of heatings of 1.0L or pH value, then wash 13min with 50 DEG C of clear water, and dehydration ring dries;
S4, reprocessing:Potassium permanganate and 80 will be wiped by hand on the fabric dried by dehydration ring in S3:Then 60 phosphoric acid add
It in sodium pyrosulfite and 20min, then washs 2 times, each 8min, dehydration ring dries.
Embodiment three
With reference to Fig. 2, it is proposed by the present invention it is a kind of can room temperature dyeing nylon facing material preparation method, include the following steps:
S1, pretreatment:Ready-made clothes is made into the cutting of undyed fabric, first puts dye vat into and is heated to 90 DEG C and do pre-treatment,
Remove the greasy dirt and impurity of cloth cover;
S2, modification:MAC 5% and piece alkali 4% will be added in manufactured fabric in S1, is kept the temperature under conditions of 70 DEG C
30min;
S3, washing:In the fabric handled in S2 plus the special beautiful dyestuff 6% of the speed of selected color, cold water wash 10min are adjusted
Sour 5g:5.3 times 90 DEG C, moisturizing 30min of heatings of 1.2L or pH value, then wash 15min with 60 DEG C of clear water, and dehydration ring dries;
S4, reprocessing:Potassium permanganate and 80 will be wiped by hand on the fabric dried by dehydration ring in S3:Then 60 phosphoric acid add
It in sodium pyrosulfite and 25min, then washs 2 times, each 10min, dehydration ring dries.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (6)
1. it is a kind of can room temperature dyeing nylon facing material preparation method, which is characterized in that include the following steps:
S1, pretreatment:Ready-made clothes is made into the cutting of undyed fabric, first puts dye vat into and is heated to 70~90 DEG C and do pre-treatment,
Remove the greasy dirt and impurity of cloth cover;
S2, modification:MAC 3~5% and piece alkali 2~4% will be added in manufactured fabric in S1, is protected under conditions of 50~70 DEG C
20~30min of temperature;
S3, washing:In the fabric handled in S2 plus the special beautiful dyestuff 4~6% of the speed of selected color, 5~10min of cold water wash,
Adjust acid 5g:0.8~1.2L or pH value 4.7~5.3 times heat 70~90 DEG C, 20~30min of moisturizing, then clear with 40~60 DEG C
10~15min is washed, dehydration ring dries;
S4, reprocessing:Potassium permanganate and 80 will be wiped by hand on the fabric dried by dehydration ring in S3:60 phosphoric acid, then Jia Jiaoya
It in sodium sulphate and 15~25min, then washs 2 times, 5~10min, dehydration ring dry every time.
2. it is according to claim 1 it is a kind of can room temperature dyeing nylon facing material preparation method, which is characterized in that the S1
In, ready-made clothes is made into the cutting of undyed fabric, first puts dye vat into and is heated to 75~85 DEG C and do pre-treatment, remove the oil of cloth cover
Dirty and impurity.
3. it is according to claim 1 it is a kind of can room temperature dyeing nylon facing material preparation method, which is characterized in that the S2
In, the concentration ratio of modified MAC and piece alkali is 3~5:2~4.
4. it is according to claim 1 it is a kind of can room temperature dyeing nylon facing material preparation method, which is characterized in that the S2
In, MAC 3.5~4.5% and piece alkali 2.5~3.5% will be added in manufactured fabric in S1, is protected under conditions of 55~65 DEG C
23~28min of temperature.
5. it is according to claim 1 it is a kind of can room temperature dyeing nylon facing material preparation method, which is characterized in that the S3
In, in the fabric handled in S2 plus the special beautiful dyestuff 4.5~5.5% of the speed of selected color, 6~9min of cold water wash adjust acid 5g:
4.9~5.1 times 75~85 DEG C of heatings of 0.9~1.1L or pH value, then 22~28min of moisturizing washes 11 with 45~55 DEG C of clear water
~14min, dehydration ring dry.
6. it is according to claim 1 it is a kind of can room temperature dyeing nylon facing material preparation method, which is characterized in that the S4
In, potassium permanganate and 80 will be wiped by hand on the fabric dried by dehydration ring in S3:60 phosphoric acid, then plus sodium pyrosulfite in and 18
~23min, then wash 2 times, 6~9min, dehydration ring dry every time.