CN108641591A - A kind of corrosion-resistant hardware coating - Google Patents
A kind of corrosion-resistant hardware coating Download PDFInfo
- Publication number
- CN108641591A CN108641591A CN201810474653.1A CN201810474653A CN108641591A CN 108641591 A CN108641591 A CN 108641591A CN 201810474653 A CN201810474653 A CN 201810474653A CN 108641591 A CN108641591 A CN 108641591A
- Authority
- CN
- China
- Prior art keywords
- parts
- corrosion
- coating
- resistant hardware
- carbon fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of corrosion-resistant hardware coating, and raw material is calculated as by weight:24 ~ 36 parts of acryl-modified silicone resin resin, 15 ~ 20 parts of micaceous iron oxide, 32 ~ 40 parts of carbon fiber, 9 ~ 12 parts of talcum powder, 5 ~ 7 parts of titanium dioxide, 5 ~ 6 parts of carbon fiber, 2 ~ 3 parts of inorganic pigment, 1 ~ 2 part of diluent, 0.5 ~ 1 part of levelling agent.The present invention has excellent sea water resistance, durability, adhesive force, chemical resistance, and the film forming speed of coating is fast, can be applied on the equipment component outside long-term exposure chamber.
Description
Technical field
The present invention relates to hardware coating material technical fields, and in particular to a kind of corrosion-resistant hardware coating.
Technical background
Hardware tool refers to the metals such as iron, steel, aluminium be fabricated by Physical Processings such as forging, calendering, cuttings it is various
The general name of metal device.Hardware device is varied, and long-term exposure is easy to be damaged by corrosion, and is got over the call of sustainable development
Paid attention to by everybody to get over, in terms of coating, needs to invent a kind of formula of novel corrosion resistant coating.
Invention content
The present invention provides following technical schemes:
A kind of corrosion-resistant hardware coating, raw material are calculated as by weight:24 ~ 36 parts of acryl-modified silicone resin resin, mica oxygen
Change 15 ~ 20 parts of iron, 32 ~ 40 parts of carbon fiber, 9 ~ 12 parts of talcum powder, 5 ~ 7 parts of titanium dioxide, 5 ~ 6 parts of carbon fiber, inorganic pigment 2 ~ 3
Part, 1 ~ 2 part of diluent, 0.5 ~ 1 part of levelling agent.
Preferably, the levelling agent is polyacrylate.
Preferably, being added with adjuvant in the raw material, the adjuvant is in brightener, delustering agent, growth agent
It is one or more.
Preferably, the epoxy resin is modified epoxy.
Preferably, further including pigment and/or filler.
Compared with prior art, the present invention program is by one layer of corrosion resistant protective layer of hardware device surface smear, subtracting
The burn into of the compounds such as few soda acid destroys, and the hardness of the coating is high, uniform color, sea water resistance, durability, adhesive force, resistance toization
Corrosivity is excellent, and the film forming speed of coating is fast, can be applied on the equipment component outside long-term exposure chamber.
Specific implementation mode
The present invention is described in further detail below by specific embodiment.
Embodiment 1
A kind of corrosion-resistant hardware coating, raw material are calculated as by weight:24 parts of acryl-modified silicone resin resin, micaceous iron oxide
15 parts, 32 parts of carbon fiber, 12 parts of talcum powder, 5 parts of titanium dioxide, 5 parts of carbon fiber, 3 parts of inorganic pigment, 1 part of diluent, levelling agent
0.5 part.
Embodiment 2
A kind of corrosion-resistant hardware coating, raw material are calculated as by weight:36 parts of acryl-modified silicone resin resin, micaceous iron oxide
20 parts, 40 parts of carbon fiber, 9 parts of talcum powder, 7 parts of titanium dioxide, 6 parts of carbon fiber, 2 parts of inorganic pigment, 2 parts of diluent, levelling agent 1
Part.
Embodiment 3
A kind of corrosion-resistant hardware coating, raw material are calculated as by weight:27 parts of acryl-modified silicone resin resin, micaceous iron oxide
18 parts, 35 parts of carbon fiber, 11 parts of talcum powder, 6 parts of titanium dioxide, 5 parts of carbon fiber, 2 parts of inorganic pigment, 1 part of diluent, levelling agent
0.8 part.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, for the skill of this field
For art personnel, the invention may be variously modified and varied.All within the spirits and principles of the present invention, any made by repair
Change, equivalent replacement, improvement etc., should all be included in the protection scope of the present invention.
Claims (5)
1. a kind of corrosion-resistant hardware coating, which is characterized in that its raw material is calculated as by weight:Acryl-modified silicone resin resin 24
~ 36 parts, 15 ~ 20 parts of micaceous iron oxide, 32 ~ 40 parts of carbon fiber, 9 ~ 12 parts of talcum powder, 5 ~ 7 parts of titanium dioxide, 5 ~ 6 parts of carbon fiber,
2 ~ 3 parts of inorganic pigment, 1 ~ 2 part of diluent, 0.5 ~ 1 part of levelling agent.
2. corrosion-resistant hardware coating as described in claim 1, which is characterized in that the levelling agent is polyacrylate.
3. corrosion-resistant hardware coating as described in claim 1, which is characterized in that adjuvant is added in the raw material, it is described
Adjuvant is one or more in brightener, delustering agent, growth agent.
4. corrosion-resistant hardware coating as described in claim 1, which is characterized in that the epoxy resin is modified epoxy.
5. corrosion-resistant hardware coating as described in claim 1, which is characterized in that further include pigment and/or filler.