CN108624778A - One Albatra metal handware - Google Patents
One Albatra metal handware Download PDFInfo
- Publication number
- CN108624778A CN108624778A CN201810650937.1A CN201810650937A CN108624778A CN 108624778 A CN108624778 A CN 108624778A CN 201810650937 A CN201810650937 A CN 201810650937A CN 108624778 A CN108624778 A CN 108624778A
- Authority
- CN
- China
- Prior art keywords
- manganese
- copper
- aluminium
- mass
- thermal conductivity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an Albatra metal handwares, it is characterised in that:For copper manganese aluminium series copper alloy plate, the copper alloy plate contains copper, manganese, aluminium and inevitable impurity, contain 1 mass % manganese below, contain 10 mass % aluminium below, surplus is copper and inevitable impurity, there is 150W/mK either lower thermal conductivity and to have 150W/mK or higher thermal conductivity at 200 DEG C of high temperature at room temperature.The beneficial effects of the invention are as follows:The Albatra metal handware has preferable thermal conductivity, while having stronger tensile strength, endurance and extensibility excellent, and increased manganese improves the abrasion resistant effect of handware.
Description
Technical field
The present invention relates to a kind of building panel more particularly to an Albatra metal handwares.
Background technology
There are many manufacturing method of automobile handware, but handware generally existing quality one prepared by current manufacturing method
As, easy-to-rust, adaptive capacity to environment is poor, and service life is short;Non- desulfurization process causes brittleness big, and easy fracture, there are security risks.
In addition, the handware generally existing piece surface wear-resisting property of current technique manufacture is poor, the short problem of service life.
Therefore, to solve the above problems, providing a kind of new technical solution.
Invention content
The present invention provides an Albatra metal handware.
The technical solution adopted by the present invention is:
One Albatra metal handware, be copper-manganese-aluminium series copper alloy plate, the copper alloy plate contain copper, manganese, aluminium and inevitably
Impurity, contain 1 mass % manganese below, contain 10 mass % aluminium below, surplus be copper and inevitable impurity, at room temperature
Either lower thermal conductivity and there is at 200 DEG C of high temperature 150W/mK or higher thermal conductivity with 150W/mK.
Further, the thermal conductivity of the copper alloy plate is gradually increased from room temperature to 200 DEG C of high temperature.
Further, the manganese containing 0.1-1 mass %.
Further, the aluminium containing 2-10 mass %.
Further, the aluminium containing 4-8 mass %.
The beneficial effects of the invention are as follows:The Albatra metal handware has preferable thermal conductivity, while having stronger anti-
Tensile strength, endurance and extensibility are excellent, and increased manganese improves the abrasion resistant effect of handware.
Specific implementation mode
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, the embodiment
It is only used for explaining the present invention, not restrict the protection scope of the present invention.
Embodiment 1
One Albatra metal handware, be copper-manganese-aluminium series copper alloy plate, the copper alloy plate contain copper, manganese, aluminium and inevitably
Impurity contains 0.1 mass % manganese below, the aluminium containing 2 mass %, and surplus is copper and inevitable impurity, is had at room temperature
There is 150W/mK either lower thermal conductivity and to there is 150W/mK or higher thermal conductivity at 200 DEG C of high temperature.
Embodiment 2
One Albatra metal handware, be copper-manganese-aluminium series copper alloy plate, the copper alloy plate contain copper, manganese, aluminium and inevitably
Impurity contains 0.5 mass % manganese below, the aluminium containing 5 mass %, and surplus is copper and inevitable impurity, is had at room temperature
There is 150W/mK either lower thermal conductivity and to there is 150W/mK or higher thermal conductivity at 200 DEG C of high temperature.
Embodiment 3
One Albatra metal handware, be copper-manganese-aluminium series copper alloy plate, the copper alloy plate contain copper, manganese, aluminium and inevitably
Impurity contains 1 mass % manganese below, the aluminium containing 10 mass %, and surplus is copper and inevitable impurity, is had at room temperature
150W/mK either lower thermal conductivity and has 150W/mK or higher thermal conductivity at 200 DEG C of high temperature.
The beneficial effects of the invention are as follows:The Albatra metal handware has preferable thermal conductivity, while having stronger anti-
Tensile strength, endurance and extensibility are excellent, and increased manganese improves the abrasion resistant effect of handware.
The above described is only a preferred embodiment of the present invention, being not the limit for making any other form to the present invention
System, and according to the technical essence of the invention made by any modification or equivalent variations, still fall within present invention model claimed
It encloses.
Claims (5)
1. an Albatra metal handware, it is characterised in that:For copper-manganese-aluminium series copper alloy plate, which contains copper, manganese, aluminium
With inevitable impurity, contain 1 mass % manganese below, contains 10 mass % aluminium below, surplus is for copper and inevitably
There is impurity 150W/mK either lower thermal conductivity and to have 150W/mK or higher at 200 DEG C of high temperature at room temperature
Thermal conductivity.
2. Albatra metal handware according to claim 1, it is characterised in that:The thermal conductivity of the copper alloy plate is from room
Temperature to 200 DEG C of high temperature gradually increases.
3. Albatra metal handware according to claim 1, it is characterised in that:Manganese containing 0.1-1 mass %.
4. Albatra metal handware according to claim 1, it is characterised in that:Aluminium containing 2-10 mass %.
5. Albatra metal handware according to claim 4, it is characterised in that:Aluminium containing 4-8 mass %.