CN108620725A - A kind of polishing method of laser glass - Google Patents
A kind of polishing method of laser glass Download PDFInfo
- Publication number
- CN108620725A CN108620725A CN201711371318.0A CN201711371318A CN108620725A CN 108620725 A CN108620725 A CN 108620725A CN 201711371318 A CN201711371318 A CN 201711371318A CN 108620725 A CN108620725 A CN 108620725A
- Authority
- CN
- China
- Prior art keywords
- laser
- glass
- laser glass
- corrosive agent
- laser cutting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of polishing methods of laser glass, are mainly processed by shot blasting to laser glass using corrosive agent corrosion and rotary laser cutting two ways;Corrosive agent corrosion is main to achieve the effect that etching glass peripheral granule using laser glass is rotated in corrosive agent;Laser cutting matrix is mainly set up in rotary laser cutting on laser cutting machine, and so that laser glass is fixed and done slow rotation laser glass using absorption and rotational structure;The present invention is combined using mild corrosion and vacuum rotating cutting, can greatly improve the finish of laser glass surface, while easy to operate, processing step is simple, of low cost.
Description
Technical field
The present invention relates to polishing method more particularly to a kind of polishing methods of laser glass.
Background technology
After laser glass manufactures, can all there be countless graininess on surface, these graininess ups and downs, to laser
Injection will produce prodigious influence, it is therefore desirable to handle surface, keep glass surface smooth, smooth, in favor of preferably
Cheng Guang, at present laser glass polishing mainly corrode glass surface using the method for corrosive agent, and shortcoming has at 2 points:Work
Skill is complicated, and of high cost, effect is general, it is therefore desirable to targetedly undergo technological transformation.
Invention content
For the above content, it is necessary to propose a kind of laser glass simple for process, of low cost, adaptable, effect is good
The polishing method of glass.
Particular technique of the present invention is as follows:A kind of polishing method of laser glass, mainly using corrosive agent corrosion and rotatably
Laser cutting two ways is processed by shot blasting laser glass;
The corrosive agent corrosion step is as follows:
(1)Corrosive agent is heated to certain temperature, after rotating mechanism being used to fix, laser glass is put into corrosive agent, and
Corrosive agent is set not have laser glass completely;
(2)Laser glass is made to the rotation of forward and reverse by rotating mechanism;
(3)Laser glass is taken out in corrosive agent, drying box heat is put into and dries a period of time;
(4)Laser glass is put into refrigerating box and refrigerates a period of time.
The rotary laser cutting step is as follows:
(1)Laser cutting matrix is set up on laser cutting machine, and laser glass is made into laser glass using absorption and rotational structure
Glass is fixed and does slow rotation;
(2)The laser glass slowly rotated is put into laser cutting matrix, size, the position of laser cutting matrix is adjusted, makes
Laser cutting matrix can just cut the front and back two sides of laser glass;
(3)Cutting glass by laser work is set alternately to rotate and reverse, and before so that laser cutting matrix is persistently cut laser glass
Latter two face.
The step of corrosive agent corrosion step(1)In, corrosive agent heating temperature is 5-20 DEG C.
The step of corrosive agent corrosion step(2)In, the rotating speed of rotating mechanism forward and reverse rotation is 50- per minute
It 60 turns, is divided into 1-3 seconds between inverting between rotating forward.
The step of corrosive agent corrosion step(3)In, drying box set temperature is 60-80 DEG C, and drying time is that 1-2 is small
When.
The step of corrosive agent corrosion step(4)In, the refrigerated storage temperature of refrigerating box is 0-5 DEG C, and cold preservation time is that 1-3 is small
When.
The present invention is combined using mild corrosion and vacuum rotating cutting, can greatly improve the bright and clean of laser glass surface
Degree, at the same it is easy to operate, and processing step is simple, of low cost.
Specific implementation mode
With reference to embodiment, the invention will be further described, but should not be limited the scope of the invention with this.
A kind of polishing method of laser glass, mainly using corrosive agent corrosion and rotary laser cutting two ways to swashing
Light glass is processed by shot blasting;
Corrosive agent corrosion step is told about first, it is specific as follows:
(1)Corrosive agent is heated to certain temperature, after rotating mechanism being used to fix, laser glass is put into corrosive agent, and
Corrosive agent is set not have laser glass completely;
(2)Laser glass is made to the rotation of forward and reverse by rotating mechanism;
(3)Laser glass is taken out in corrosive agent, drying box heat is put into and dries a period of time;
(4)Laser glass is put into refrigerating box and refrigerates a period of time.
Next it is as follows to tell about rotary laser cutting step:
(1)Laser cutting matrix is set up on laser cutting machine, and laser glass is made into laser glass using absorption and rotational structure
Glass is fixed and does slow rotation;
(2)The laser glass slowly rotated is put into laser cutting matrix, size, the position of laser cutting matrix is adjusted, makes
Laser cutting matrix can just cut the front and back two sides of laser glass;
(3)Cutting glass by laser work is set alternately to rotate and reverse, and before so that laser cutting matrix is persistently cut laser glass
Latter two face.
The corrosive agent corrosion step the step of(1)In, corrosive agent heating temperature is 5-20 DEG C.
The corrosive agent corrosion step the step of(2)In, the rotating speed of rotating mechanism forward and reverse rotation is 50-60 per minute
Turn, is divided into 1-3 seconds between inverting between rotating forward.
The corrosive agent corrosion step the step of(3)In, drying box set temperature is 60-80 DEG C, and drying time is that 1-2 is small
When.
The corrosive agent corrosion step the step of(4)In, the refrigerated storage temperature of refrigerating box is 0-5 DEG C, and cold preservation time is that 1-3 is small
When.
Generally speaking, the present invention is combined using mild corrosion and vacuum rotating cutting, can greatly improve laser glass
The finish on surface, at the same it is easy to operate, and processing step is simple, of low cost.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all originals in the present invention
Any modification made by within then, equivalent replacement and improvement etc. should all be included in the protection scope of the present invention.
Claims (5)
1. a kind of polishing method of laser glass mainly cuts two ways to laser using corrosive agent corrosion and rotary laser
Glass is processed by shot blasting, it is characterised in that:
The corrosive agent corrosion step is as follows:
Corrosive agent is heated to certain temperature, after rotating mechanism being used to fix, laser glass is put into corrosive agent, and make corruption
Erosion agent there was not laser glass completely;
Laser glass is made to the rotation of forward and reverse by rotating mechanism;
Laser glass is taken out in corrosive agent, drying box heat is put into and dries a period of time;
Laser glass is put into refrigerating box and refrigerates a period of time;
The rotary laser cutting step is as follows:
Laser cutting matrix is set up on laser cutting machine, and laser glass is made into laser glass using absorption and rotational structure
It fixes and does slow rotation;
The laser glass slowly rotated is put into laser cutting matrix, size, the position of laser cutting matrix is adjusted, makes laser
Cutting matrix can just cut the front and back two sides of laser glass;
So that cutting glass by laser work is alternately rotated and reverse, and laser cutting matrix is made persistently to cut front and back the two of laser glass
A face.
2. a kind of polishing method of laser glass as described in claim 1, which is characterized in that the corrosive agent corrosion step
Step(1)In, corrosive agent heating temperature is 5-20 DEG C.
3. a kind of polishing method of laser glass as described in claim 1, which is characterized in that the corrosive agent corrosion step
Step(2)In, the rotating speed of rotating mechanism forward and reverse rotation turns for 50-60 per minute, is divided between inverting between rotating forward
1-3 seconds.
4. a kind of polishing method of laser glass as described in claim 1, which is characterized in that the corrosive agent corrosion step
Step(3)In, drying box set temperature is 60-80 DEG C, and drying time is 1-2 hours.
5. a kind of polishing method of laser glass as described in claim 1, which is characterized in that the corrosive agent corrosion step
Step(4)In, the refrigerated storage temperature of refrigerating box is 0-5 DEG C, and cold preservation time is 1-3 hours.