CN108610756A - A kind of hyalomitome response type Self-adhesive waterproof material - Google Patents
A kind of hyalomitome response type Self-adhesive waterproof material Download PDFInfo
- Publication number
- CN108610756A CN108610756A CN201710031985.8A CN201710031985A CN108610756A CN 108610756 A CN108610756 A CN 108610756A CN 201710031985 A CN201710031985 A CN 201710031985A CN 108610756 A CN108610756 A CN 108610756A
- Authority
- CN
- China
- Prior art keywords
- hyalomitome
- response type
- type self
- waterproof material
- adhesive waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of hyalomitome response type Self-adhesive waterproof material, raw material includes by weight percentage：The extremely strong liquid resin of White softening oil, hot melt adhesive grade elastomer, styrene styrene block copolymer, tackified rubber, rubber latex, ultraviolet screener, penetrating power, tackifying resin, interfacial agents.In the present invention by rationally controlling White softening oil, hot melt adhesive grade elastomer, styrene styrene block copolymer, tackified rubber content can significantly increase the mechanical strength of product；Additionally by the extremely strong liquid resin of addition rubber latex, ultraviolet screener, penetrating power, tackifying resin and its content is controlled, the high mechanical strength of coating, excellent anti-corrosion performance can be increased.
Description
Technical field
The present invention relates to technical field of coatings more particularly to a kind of hyalomitome response type Self-adhesive waterproof materials.
Background technology
Water-proof acrylic acid paint be using pure acrylic acid polymer emulsion as base-material, prepared by other additives are added single group
Part water-emulsifying type waterproof coatings.The waterproofing membrane formed after water-repellent paint is cured has certain extensibility, elastoplasticity, cracking resistance
Property, impermeability and weatherability, waterproof can be played, anti-blend protective effect.Water-repellent paint has good thermal adaptability, operation letter
Just, for ease of maintenaince with maintenance.
Waterproof material has been applied in many fields of our lives, and composition proportion is respectively formed in water-repellent paint now
Unevenness causes coating that cannot use for a long time, for this purpose, it is proposed that a kind of hyalomitome response type Self-adhesive waterproof material.
Invention content
Technical problems based on background technology, the present invention propose a kind of hyalomitome response type Self-adhesive waterproof material.
The present invention proposes a kind of hyalomitome response type Self-adhesive waterproof material, and raw material includes by weight percentage：White
Softening oil 15-20%, hot melt adhesive grade elastomer 4-6%, styrene-styrene block copolymer (SBS) 3-9%, tackified rubber 20-
30%, the extremely strong liquid resin 5-6% of rubber latex 4-6%, ultraviolet screener 0.1-0.5%, penetrating power, tackifying resin 15-
25%, remaining group is divided into interfacial agents.
Preferably, White softening oil includes any one or a few the mixing in butyl oil, white oil and wax oil.
Preferably, the hot melt adhesive grade elastomer includes ethane-acetic acid ethyenyl（Sour person of outstanding talent's ethylene）Ester copolymer（EVA）, third
Any one or a few mixing in olefin(e) acid, butyl rubber
Preferably, the tackified rubber includes butadiene-styrene rubber, styrene-isoprene-styrene block copolymer（SBB）In
Any one or a few mixing.
Preferably, rubber latex includes any one or a few the mixing in benzene lotion, styrene-butadiene emulsion and silicon benzene lotion.
Preferably, the UV resistance agent include in UV531, UV327, UV328, UV320, UV1164 any one or
Several mixing.
Preferably, the extremely strong liquid resin of the penetrating power includes arbitrary in low molecular polyisobutylene, epoxy resin
One or more of mixing.
Preferably, the tackifying resin includes appointing in light C5 Petropols, light terpene resin plus hydrogen terpene resin
The mixing for one or more of anticipating.
Preferably, the interfacial agents are mainly used for improving the penetration with base material.
The present invention also proposes a kind of preparation method of hyalomitome response type Self-adhesive waterproof material, includes the following steps：
S1, first by White softening oil be added reaction kettle in, 130 DEG C be dehydrated 20 minutes；
S2,170-190 DEG C is then heated to, part tackifying resin is added by formula, temperature control stirs thickening between 180-190 DEG C
Resin is completely dissolved；
S3, hot melt adhesive grade elastomer, Styrene-Butadiene-Styrene Block Copolymer is added by formula（SBB）With thickening elasticity
Body, temperature control are stirred at 180-190 DEG C to melten gel grade elasticity, styrene block copolymer（SBB）It is completely dissolved with tackified elastomers；
S4, remaining tackifying resin is added, stirring is as a child slowly rear to be added rubber latex；
S5, it waits for that rubber latex is completely dissolved and moisture content all plays, the strong liquid of ultraviolet screener, anti-aging agent, penetrating power is added
Body rubber and basal plane agent；
S6, temperature control are molded at 160 DEG C on coating base.
The present invention by adding said components, and rationally controls the content of each component, and Mechanical Properties of Products is good, rub resistance,
Excellent anti-corrosion performance.By rationally control White softening oil, hot melt adhesive grade elastomer, styrene-styrene block copolymer,
Tackified rubber content can significantly increase the mechanical strength of product；Additionally by addition rubber latex, ultraviolet screener, penetrating power
Extremely strong liquid resin, tackifying resin simultaneously control its content, can increase the high mechanical strength of coating, excellent anti-corrosion performance.
Specific implementation mode
With reference to specific embodiment, the present invention will be further described.
Embodiment 1
A kind of hyalomitome response type Self-adhesive waterproof material, raw material include by weight percentage：White softening oil 15%, hot melt adhesive
Grade elastomer 4%, tackified rubber 20%, rubber latex 4%, ultraviolet screener 0.1%, oozes styrene-styrene block copolymer 4%
Very competent liquid resin 5%, tackifying resin 15%, interfacial agents 32.9% thoroughly.
Embodiment 2
A kind of hyalomitome response type Self-adhesive waterproof material, raw material include by weight percentage：White softening oil 17%, hot melt adhesive
Grade elastomer 5%, styrene-styrene block copolymer 5%, tackified rubber 24%, rubber latex 4.5%, ultraviolet screener 0.2%,
The extremely strong liquid resin 5.2% of penetrating power, tackifying resin 17%, interfacial agents 22.1%.
Embodiment 3
A kind of hyalomitome response type Self-adhesive waterproof material, raw material include by weight percentage：White softening oil 17%, hot melt adhesive
Grade elastomer 5%, styrene-styrene block copolymer 6%, tackified rubber 27%, rubber latex 5.3%, ultraviolet screener 0.4%,
The extremely strong liquid resin 5.6% of penetrating power, tackifying resin 22%, interfacial agents 11.7%.
Embodiment 4
A kind of hyalomitome response type Self-adhesive waterproof material, raw material include by weight percentage：White softening oil 18%, hot melt adhesive
Grade elastomer 6%, tackified rubber 20%, rubber latex 6%, ultraviolet screener 0.5%, oozes styrene-styrene block copolymer 9%
Very competent liquid resin 6%, tackifying resin 24%, interfacial agents 10.5% thoroughly.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (10)
1. a kind of hyalomitome response type Self-adhesive waterproof material, which is characterized in that its raw material includes by weight percentage：White softening
Oily 15-20%, hot melt adhesive grade elastomer 4-6%, styrene-styrene block copolymer 3-9%, tackified rubber 20-30%, latex rubber
The extremely strong liquid resin 5-6% of liquid 4-6%, ultraviolet screener 0.1-0.5%, penetrating power, tackifying resin 15-25%, remaining component
For interfacial agents.
2. hyalomitome response type Self-adhesive waterproof material according to claim 1, which is characterized in that White softening oil includes fourth
Any one or a few mixing in base oil, white oil and wax oil.
3. hyalomitome response type Self-adhesive waterproof material according to claim 1, which is characterized in that the hot melt adhesive grade elasticity
Body includes any one or a few the mixing in vinyl-vinyl acetate copolymer, acrylic acid, butyl rubber.
4. hyalomitome response type Self-adhesive waterproof material according to claim 1, which is characterized in that the tackified rubber includes
Any one or a few mixing in butadiene-styrene rubber, styrene-isoprene-styrene block copolymer.
5. hyalomitome response type Self-adhesive waterproof material according to claim 1, which is characterized in that rubber latex includes benzene breast
Any one or a few mixing in liquid, styrene-butadiene emulsion and silicon benzene lotion.
6. hyalomitome response type Self-adhesive waterproof material according to claim 1, which is characterized in that the UV resistance agent packet
Include the mixing of any one or a few in UV531, UV327, UV328, UV320, UV1164.
7. hyalomitome response type Self-adhesive waterproof material according to claim 1, which is characterized in that the penetrating power is extremely strong
Liquid resin include any one or a few mixing in low molecular polyisobutylene, epoxy resin.
8. hyalomitome response type Self-adhesive waterproof material according to claim 1, which is characterized in that the tackifying resin includes
Any one or a few mixing in light C5 Petropols, light terpene resin plus hydrogen terpene resin.
9. hyalomitome response type Self-adhesive waterproof material according to claim 1, which is characterized in that the interfacial agents are mainly used
Way is the penetration improved with base material.
10. a kind of preparation method according to claim 1-9 any one of them hyalomitome response type Self-adhesive waterproof materials, special
Sign is, includes the following steps：
S1, first by White softening oil be added reaction kettle in, 130 DEG C be dehydrated 20 minutes；
S2,170-190 DEG C is then heated to, part tackifying resin is added by formula, temperature control stirs thickening between 180-190 DEG C
Resin is completely dissolved；
S3, hot melt adhesive grade elastomer, Styrene-Butadiene-Styrene Block Copolymer and tackified elastomers, control are added by formula
Temperature is stirred to melten gel grade elasticity, styrene block copolymer and tackified elastomers at 180-190 DEG C and is completely dissolved；
S4, remaining tackifying resin is added, stirring is as a child slowly rear to be added rubber latex；
S5, it waits for that rubber latex is completely dissolved and moisture content all plays, the strong liquid of ultraviolet screener, anti-aging agent, penetrating power is added
Body rubber and basal plane agent；
S6, temperature control are molded at 160 DEG C on coating base.