CN108608790A - 透气型除臭装饰贴膜 - Google Patents
透气型除臭装饰贴膜 Download PDFInfo
- Publication number
- CN108608790A CN108608790A CN201710052896.1A CN201710052896A CN108608790A CN 108608790 A CN108608790 A CN 108608790A CN 201710052896 A CN201710052896 A CN 201710052896A CN 108608790 A CN108608790 A CN 108608790A
- Authority
- CN
- China
- Prior art keywords
- layer
- coating
- functional coating
- coating layer
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种透气型除臭装饰贴膜，至上而下依次包含：一图案喷绘层；一功能涂布层；一基材层；一底涂层；一黏贴层；一离型层；其中，所述的功能涂布层内分布有孔穴。本发明的透气型除臭装饰贴膜能吸收室内H2S和甲硫醇等气体，发生反应后除臭，最后生成了Ca(SCH3)3，放出量几乎为零，属于化学吸附。消石灰微粉能促进甲醛缩糖反应，是无害的，吸附的甲醛不再排除，同样是化学吸附，无二次排放污染，极小的消石灰微粉颗粒吸附了纳米级大小的病毒、细菌，抑制繁殖，防止发霉。另外，本发明的透气型除臭装饰贴膜具有自然素材的独特丰韵与质感，兼具有消臭味性、抗菌性、抗病毒性、防霉变性、吸湿性、不燃性、吸收甲醛的作用。
Description
技术领域
本发明涉及一种装饰贴膜，更确切地说，是一种透气型除臭装饰贴膜。
背景技术
生活中我们常常会被各种臭味所环绕，恶臭污染对人心理的影响大于对人机体的影响，所以恶臭污染也是扰民污染，他关系着人们的生活工作环境的质量，社会的稳定及环境的安全。由恶臭物质的气味特性刺激人的嗅觉器官，使人产生不愉快和厌恶感，污染了生产和生活环境，这种污染称为恶臭污染，恶臭物质种类很多，包括脚臭、生物臭、汗臭、腐烂臭等。
另外，随着生活水平的提高，住房条件的改善，家具装饰造成的室内环境污染成为人们健康的大敌，甲醛是其中最常见的毒气之一，对人体的危害具有长期性、潜伏性、隐蔽性的特点。
发明内容
本发明主要是解决现有技术所存在的技术问题，从而提供一种透气型除臭装饰贴膜。
本发明的上述技术问题主要是通过下述技术方案得以解决的：
本发明公开了一种透气型除臭装饰贴膜，至上而下依次包含：
一图案喷绘层；
一功能涂布层；
一基材层；
一底涂层；
一黏贴层；
一离型层。
作为本发明较佳的实施例，所述的功能涂布层内分布有孔穴。
作为本发明较佳的实施例，
所述的功能涂布层为消石灰微粉、植物提取液、植物纤维、分散剂、增稠剂、成膜树脂和动物骨材的混合物通过高速分散机与水充分混合后所形成的均一粘稠状膏体涂布而成，厚度为20～100微米；
所述的基材层为丙纶不织布、涤纶无纺布、石头纸、长纤维纸、透气PET膜中的其中一种，厚度为50～200微米；
所述的底涂层为氯化聚丙烯、水性不饱和聚酯、硅烷偶联剂和乙烯-丙烯酸水性共聚物中的至少一种，干膜重量为0.1～1克/平方米；
所述的黏贴层为压敏胶层，是水性丙烯酸酯胶、热熔型苯乙烯-异戊二烯-苯乙烯、增粘树脂、三甲基氯硅烷和环氧聚醚中的至少一种，厚度为15～80微米；
所述的离型层为淋膜离型纸、格拉辛离型纸、涂硅油PET薄膜中的至少一种，克重为20～150克/平方米。
作为本发明较佳的实施例，
所述的消石灰微粉为80-800目，在烧制过程中加盐；
所述的植物提取液为红藻门植物或银杏叶烧煮后抽取物；
所述的分散剂为脂肪酸钠盐或有机硅或长碳链胺类化合物；
所述的增稠剂为甲基纤维素、羟乙基纤维素、聚氨酯增稠剂和聚丙烯酸钠中的至少一种；
所述的成膜树脂为丙烯酸酯和聚氨酯中的至少一种。
作为本发明较佳的实施例，
所述的功能涂布层包含一第一功能涂布层和一第二功能涂布层，其中，
所述的第一功能涂布层的配料为：消石灰微粉20-30质量份，植物提取液20-40质量份，植物纤维0.5-1质量份，分散剂0.5-1质量份，增稠剂0.5-1质量份，成膜树脂10-30质量份，动物骨材3-5质量份，水40-60质量份；
所述的第二功能涂布层的植物纤维含量为零。
本发明还公开了一种如前述的透气型除臭装饰贴膜的制备方法，包含步骤：
1)、将基材层放在等离子处理机的放卷端，以车速100-200m/min的速度对面料两面进行处理，使表面张力达到38达因以上；
2)、将植物提取液收集后蒸煮熬浆，过滤后备用；
3)、对功能涂布层进行配料，在1000-2000转/分钟的分散机上搅拌10-40分钟，放置除泡，形成均一相粘稠膏体；
4)、采用双辊狭缝涂布技术，将步骤3)得到的的膏体涂覆于基材层的上层，所形成的涂层具有一定的空隙，便于气体的流通，车速为10-20米/分钟，经烘干箱干燥后收卷，烘干箱温度设定为60-100摄氏度；
5)、另配一份功能涂料，然后相同工艺同步涂布在第一功能涂布层之上，使表面更光滑，更适合油墨附着，车速为15米/分钟，经烘干箱干燥后收卷，烘干箱温度设定为60-100摄氏度；
6)、把步骤5)得到的卷材放置在光棍涂布机的放卷区，将底涂层的水溶液涂布于基材层的另一面，经烘干后收卷，干膜重量为0.1-1克/平方米，速度为40-80米/分钟，干燥温度为60-100摄氏度，得到底涂层；
7)、将黏贴层的胶体倒在凹版涂布复合机的胶槽中，开启胶槽循环装置，以车速10-60米/分钟的速度把胶水涂布于步骤5)得到的底涂层上，经烘箱干燥后与离型层进行复合，收卷，胶层厚度为15-80微米，烘箱温度为60-100摄氏度；
8)将步骤6)得到的卷材放入模切机，分割为A4大小的片材，进行喷墨数码打印。
本发明的透气型除臭装饰贴膜能吸收室内H2S和甲硫醇等气体，发生反应后除臭，最后生成了Ca(SCH3)3，放出量几乎为零，属于化学吸附。另外，消石灰微粉能促进甲醛缩糖反应，是无害的，吸附的甲醛不再排除，同样是化学吸附，无二次排放污染。由于本发明的透气型除臭装饰贴膜的表面呈强碱性，极小的消石灰微粉颗粒吸附了纳米级大小的病毒、细菌，抑制繁殖，防止发霉。另外，本发明的透气型除臭装饰贴膜具有自然素材的独特丰韵与质感，兼具有消臭味性、抗菌性、抗病毒性、防霉变性、吸湿性、不燃性、吸收甲醛的作用。
附图说明
为了更清楚地说明本发明实施例或现有技术中的技术方案，下面将对实施例或现有技术描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他的附图。
图1为本发明的透气型除臭装饰贴膜的结构示意图；
图2为本发明的透气型除臭装饰贴膜的第二种实施方式中的功能涂布层的结构示意图；
其中，
11、图案喷绘层；12、功能涂布层；13、基材层；14、底涂层；15、黏贴层；16、离型层；12b、第一功能涂布层；12a、第二功能涂布层。
具体实施方式
下面结合附图对本发明的优选实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
如图1所示，该透气型除臭装饰贴膜，至上而下依次包含：一图案喷绘层11、一功能涂布层12、一基材层13、一底涂层14、一黏贴层15和一离型层16。
图2为本发明的透气型除臭装饰贴膜的第二种实施方式中的功能涂布层，此时，该功能涂布层12包含一第一功能涂布层12b和一第二功能涂布层12a，该第一功能涂布层12b中的植物纤维的含量高于该第二功能涂布层12a。一般，第二功能涂布层12a中的植物纤维的含量为零。
下面通过三个实施例对本发明进行进一步的说明。
实施例1：
将厚度为50微米，幅宽为1040mm，长3000m的丙纶不织布放在等离子处理机的放卷端，以车速120m/min的速度对面料两面进行处理，使表面张力达到38达因以上。将银杏草收集后蒸煮熬浆，过滤后备用。
将厚度为50微米，幅宽为1040mm，长3000m的丙纶不织布放在等离子处理机的放卷端，以车速120m/min的速度对面料两面进行处理，使表面张力达到38达因以上。将银杏草收集后蒸煮熬浆，过滤后备用。按照消石灰微粉30质量份，银杏草提取液40质量份，短纤亚麻0.5质量份，分散剂NUOSPERSE W-30 0.5质量份，增稠剂甲基纤维素0.5质量份，成膜树脂丙烯酸树脂10质量份，动物骨材3质量份，水40质量份配制第一功能层。把上述材料在1500转/分钟的分散机上搅拌20分钟，放置除泡，形成均一相粘稠膏体。采用双辊狭缝涂布技术，将制得的膏体涂覆于丙纶不织布的上层，所形成的涂层具有一定的空隙，便于气体的流通。车速为15米/分钟，经烘干箱干燥后收卷，烘干箱温度设定为80摄氏度。
另配一份功能涂料，成份如上，不同之处是不添加亚麻，然后相同工艺同步涂布在第一涂布层之上，使表面更光滑，更适合油墨附着。车速为15米/分钟，经烘干箱干燥后收卷，烘干箱温度设定为80摄氏度。总厚度为35微米。把上述卷材放置在光棍涂布机的放卷区，将氯化聚丙烯水溶液涂布于丙纶不织布的另一面，经烘干后收卷，干膜重量为0.1克/平方米，速度为60米/分钟，干燥温度为80摄氏度。将水性丙烯酸酯胶倒在凹版涂布复合机的胶槽中，开启胶槽循环装置，以车速30米/分钟的速度把胶水涂布于上述底涂层，经烘箱干燥后与20g的格拉辛离型纸进行复合，收卷。胶层厚度为30微米，烘箱温度为80摄氏度。将上述卷材放入模切机，分割为A4大小的片材，进行喷墨数码打印。图案选择为公司司徽LOGO，将打印好图案的装饰贴直接贴在车间工人换装处的鞋柜。
实施例2
将厚度为85微米，幅宽为1280mm，长3000m的涤纶无纺布放在电晕处理机的放卷端，以车速100m/min的速度对面料两面进行处理，使表面张力达到48达因以上。将红藻门植物收集后蒸煮熬浆，过滤后备用。按照消石灰微粉25质量份，红藻门提取液30质量份，短纤亚麻0.7质量份，分散剂NUOSPERSE W-300.6质量份，增稠剂甲基纤维素0.7质量份，成膜树脂丙烯酸树脂20质量份，动物骨材4质量份，水50质量份配制第一功能层；把上述材料在1000转/分钟的分散机上搅拌10分钟，放置除泡，形成均一相粘稠膏体。采用双辊狭缝涂布技术，将制得的膏体涂覆于涤纶无纺布的上层，所形成的涂层具有一定的空隙，便于气体的流通。车速为20米/分钟，经烘干箱干燥后收卷，烘干箱温度设定为70摄氏度。另配一份功能涂料，成份如上，不同之处是不添加亚麻，然后相同工艺同步涂布在第一涂布层之上，使表面更光滑，更适合油墨附着。车速为15米/分钟，经烘干箱干燥后收卷，烘干箱温度设定为100摄氏度。总厚度为20微米。把上述卷材放置在光棍涂布机的放卷区，将氯化聚丙烯水溶液涂布于涤纶无纺布的另一面，经烘干后收卷，干膜重量为0.1克/平方米，速度为40米/分钟，干燥温度为60摄氏度。将水性丙烯酸酯胶倒在凹版涂布复合机的胶槽中，开启胶槽循环装置，以车速10米/分钟的速度把胶水涂布于上述底涂层，经烘箱干燥后与120g的格拉辛离型纸进行复合，收卷。胶层厚度为40微米，烘箱温度为60摄氏度。将上述卷材分切为640mm宽卷材后，进行喷墨数码打印。图案选择山水风景画，将打印好图案的装饰膜贴于居家卧室的床头墙面。
实施例3
将厚度为75微米，幅宽为1100mm，长3000m的石头纸放在等离子处理机的放卷端，以车速200m/min的速度对面料两面进行处理，使表面张力达到42达因以上。将银杏草收集后蒸煮熬浆，过滤后备用。按照消石灰微粉20质量份，银杏草提取液40质量份，短纤苎麻1质量份，分散剂长碳链胺类，如十八胺1质量份，增稠剂甲基纤维素1质量份，成膜树脂聚氨酯30质量份，动物骨材5质量份，水60质量份配制第一功能层；把上述材料在1800转/分钟的分散机上搅拌40分钟，放置除泡，形成均一相粘稠膏体。采用双辊狭缝涂布技术，将制得的膏体涂覆于石头纸的上层，所形成的涂层具有一定的空隙，便于气体的流通。车速为10米/分钟，经烘干箱干燥后收卷，烘干箱温度设定为60摄氏度。
另配一份功能涂料，成份如上，不同之处是不添加苎麻，然后相同工艺同步涂布在第一涂布层之上，使表面更光滑，更适合油墨附着。车速为30米/分钟，经烘干箱干燥后收卷，烘干箱温度设定为70摄氏度。总厚度为100微米。把上述卷材放置在光棍涂布机的放卷区，将水性不饱和聚酯、硅烷偶联剂水溶液涂布于石头纸的另一面，经烘干后收卷，干膜重量为0.3克/平方米，速度为80米/分钟，干燥温度为100摄氏度。将水性丙烯酸酯胶倒在凹版涂布复合机的胶槽中，开启胶槽循环装置，以车速60米/分钟的速度把胶水涂布于上述底涂层，经烘箱干燥后与80g的格拉辛离型纸进行复合，收卷。胶层厚度为80微米，烘箱温度为100摄氏度。将上述卷材放入模切机，分割为10cm*10cm正方形大小的片材，进行喷墨数码打印，图案选择水果蔬菜。将完成的装饰膜直接贴于冰箱内侧使用。
实施例4
将厚度为200微米，幅宽为13400mm，长2000m的长纤维纸放在电晕处理机的放卷端，以车速120m/min的速度对面料两面进行处理，使表面张力达到44达因以上。将红藻门植物收集后蒸煮熬浆，过滤后备用。按照消石灰微粉28质量份，红藻门提取液40质量份，短纤亚麻1质量份，分散剂脂肪酸钠盐1质量份，增稠剂羟乙基纤维素和聚氨酯增稠剂各0.5质量份，成膜树脂丙烯酸树脂30质量份，动物骨材5质量份，水60质量份配制第一功能层；把上述材料在2000转/分钟的分散机上搅拌15分钟，放置除泡，形成均一相粘稠膏体。采用双辊狭缝涂布技术，将制得的膏体涂覆于长纤维纸的上层，所形成的涂层具有一定的空隙，便于气体的流通。车速为15米/分钟，经烘干箱干燥后收卷，烘干箱温度设定为100摄氏度。另配一份功能涂料，成份如上，不同之处是不添加亚麻，然后相同工艺同步涂布在第一涂布层之上，使表面更光滑，更适合油墨附着。车速为30米/分钟，经烘干箱干燥后收卷，烘干箱温度设定为60摄氏度。总厚度为35微米。把上述卷材放置在光棍涂布机的放卷区，将氯化聚丙烯水溶液涂布于长纤维纸的另一面，经烘干后收卷，干膜重量为1克/平方米，速度为60米/分钟，干燥温度为80摄氏度。
将热熔型苯乙烯-异戊二烯-苯乙烯(SIS)、增粘树脂倒入在挤出涂布复合机的料斗中，以车速50米/分钟的速度把热压敏胶流延到上述底涂层，与150g的淋膜离型纸进行复合，收卷，胶层厚度为15微米。将上述卷材分切为670mm宽卷材后，进行喷墨数码打印。图案选择商家主打衣服广告，将打印好图案的装饰膜贴于商场更衣间使用。
需要说明的是，制作植物提取液时，按照蒸煮前植物叶子占叶子和水的总重量的10—30％，蒸煮后去除固体即可。比如，制造银杏草提取液时，准备银杏草叶子10质量份和水90质量份，这样，银杏草叶子的质量：银杏草叶子的质量+水的质量＝10:100。其他植物的提取液依照类似的方法制作。
本发明的透气型除臭装饰贴膜能吸收室内H2S和甲硫醇等气体，发生反应后除臭，最后生成了Ca(SCH3)3，放出量几乎为零，属于化学吸附。另外，消石灰微粉能促进甲醛缩糖反应，是无害的，吸附的甲醛不再排除，同样是化学吸附，无二次排放污染。由于本发明的透气型除臭装饰贴膜的表面呈强碱性，极小的消石灰微粉颗粒吸附了纳米级大小的病毒、细菌，抑制繁殖，防止发霉。另外，本发明的透气型除臭装饰贴膜具有自然素材的独特丰韵与质感，兼具有消臭味性、抗菌性、抗病毒性、防霉变性、吸湿性、不燃性、吸收甲醛等作用。
不局限于此，任何不经过创造性劳动想到的变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求书所限定的保护范围为准。
Claims (6)
1.一种透气型除臭装饰贴膜，至上而下依次包含：
一图案喷绘层(11)；
一功能涂布层(12)；
一基材层(13)；
一底涂层(14)；
一黏贴层(15)；
一离型层(16)。
2.根据权利要求1所述的透气型除臭装饰贴膜，其特征在于，所述的功能涂布层(12)内分布有孔穴。
3.根据权利要求1所述的透气型除臭装饰贴膜，其特征在于，
所述的功能涂布层(12)为消石灰微粉、植物提取液、植物纤维、分散剂、增稠剂、成膜树脂和动物骨材的混合物通过高速分散机与水充分混合后所形成的均一粘稠状膏体涂布而成，厚度为20～100微米；
所述的基材层(13)为丙纶不织布、涤纶无纺布、石头纸、长纤维纸、透气PET膜中的其中一种，厚度为50～200微米；
所述的底涂层(14)为氯化聚丙烯、水性不饱和聚酯、硅烷偶联剂和乙烯-丙烯酸水性共聚物中的至少一种，干膜重量为0.1～1克/平方米；
所述的黏贴层(15)为压敏胶层，是水性丙烯酸酯胶、热熔型苯乙烯-异戊二烯-苯乙烯(SIS)、增粘树脂、三甲基氯硅烷和环氧聚醚中的至少一种，厚度为15～80微米；
所述的离型层(16)为淋膜离型纸、格拉辛离型纸、涂硅油PET薄膜中的至少一种，克重为20～150克/平方米。
4.根据权利要求3所述的透气型除臭装饰贴膜，其特征在于,
所述的消石灰微粉为80-800目，在烧制过程中加盐；
所述的植物提取液为红藻门植物或银杏叶烧煮后抽取物；
所述的分散剂为脂肪酸钠盐或有机硅或长碳链胺类化合物；
所述的增稠剂为甲基纤维素、羟乙基纤维素、聚氨酯增稠剂和聚丙烯酸钠中的至少一种；
所述的成膜树脂为丙烯酸酯和聚氨酯中的至少一种。
5.根据权利要求3或4所述的透气型除臭装饰贴膜，其特征在于，所述的功能涂布层(12)包含一第一功能涂布层(12b)和一第二功能涂布层(12a)，其中，
所述的第一功能涂布层(12b)的配料为：消石灰微粉20-30质量份，植物提取液20-40质量份，植物纤维0.5-1质量份，分散剂0.5-1质量份，增稠剂0.5-1质量份，成膜树脂10-30质量份，动物骨材3-5质量份，水40-60质量份；
所述的第二功能涂布层(12a)的植物纤维含量为零。
6.一种如权利要求3或4所述的透气型除臭装饰贴膜的制备方法，包含步骤：
1)、将基材层(13)放在等离子处理机的放卷端，以车速100-200m/min的速度对面料两面进行处理，使表面张力达到38达因以上；
2)、将植物提取液收集后蒸煮熬浆，过滤后备用；
3)、对功能涂布层(12)进行配料，在1000-2000转/分钟的分散机上搅拌10-40分钟，放置除泡，形成均一相粘稠膏体；
4)、采用双辊狭缝涂布技术，将步骤3)得到的的膏体涂覆于基材层(13)的上层，所形成的涂层具有一定的空隙，便于气体的流通，车速为10-20米/分钟，经烘干箱干燥后收卷，烘干箱温度设定为60-100摄氏度；
5)、另配一份功能涂料，然后相同工艺同步涂布在第一功能涂布层之上，使表面更光滑，更适合油墨附着，车速为15米/分钟，经烘干箱干燥后收卷，烘干箱温度设定为60-100摄氏度；
6)、把步骤5)得到的卷材放置在光棍涂布机的放卷区，将底涂层(14)的水溶液涂布于基材层(13)的另一面，经烘干后收卷，干膜重量为0.1-1克/平方米，速度为40-80米/分钟，干燥温度为60-100摄氏度，得到底涂层(14)；
7)、将黏贴层(15)的胶体倒在凹版涂布复合机的胶槽中，开启胶槽循环装置，以车速10-60米/分钟的速度把胶水涂布于步骤5)得到的底涂层(14)上，经烘箱干燥后与离型层(16)进行复合，收卷，胶层厚度为15-80微米，烘箱温度为60-100摄氏度；
8)将步骤6)得到的卷材放入模切机，分割为A4大小的片材，进行喷墨数码打印。