CN108594468A - A kind of manufacturing method with anti-blue light color-changing lens - Google Patents
A kind of manufacturing method with anti-blue light color-changing lens Download PDFInfo
- Publication number
- CN108594468A CN108594468A CN201810353407.0A CN201810353407A CN108594468A CN 108594468 A CN108594468 A CN 108594468A CN 201810353407 A CN201810353407 A CN 201810353407A CN 108594468 A CN108594468 A CN 108594468A
- Authority
- CN
- China
- Prior art keywords
- blue light
- hours
- temperature
- eyeglass
- manufacturing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of manufacturing method with anti-blue light color-changing lens includes the following steps by quality ratio:1), dispensing;2), discoloration stiffened;3), solidification;4), plated film.The present invention, eyeglass only have 0.17% can penetrate the ultraviolet light of 470 nanometers of wave band, you can effectively to stop 99.83% UV470 ultraviolet lights; so as to our eyes of effective protection from the infringement of ultraviolet light; with technology uniqueness, feature simple for process, highly practical.
Description
Technical field
The present invention relates to the manufacture manufacture field of resin mirror, the systems of especially a kind of anti-blue light color-changing lens for high definition
Make method.
Background technology
Mobile phone has become for a kind of indispensable social tool of modern, from just getting up to having a meal, walks, to before sleep
Nearly all mobile phone is being stared at our eyes.But the high-energy for 410-500 nanometers of the wave band that the digital products such as mobile phone release
The eyes for injuring us of blue light silently.And wavelength 400-480nm blue light due to wavelength it is short, energy height is to people
Potential risk is very big caused by eyes, and blue light can be directed through crystal and reach on eye ground, cause ophthalmic uncomfortable, depending on
Feel fatigue, lead to the decline of retinal pigment epithelium, can be caused retina Huang by the irradiation of high intensity blue light for a long time
Spot portion lesion, generates blurred vision, and the consequence of visual impairment is damaged for caused by people's eyes by medicine in view of blue light
It confirms and confirms, so gradually causing medical field and the manufacturing great attention of glasses, various reductions are penetrated with blue light is prevented
Lens product come into being.
Invention content
It is to adopt in view of the above problems, the purpose of the present invention is to provide a kind of manufacturing method with anti-blue light color-changing lens
It is ontology with 1.56 monomers, has merged novel anti-blue light UV powder, stiffened photochromic layer is added outside ontology, is plated after stiffening layer solidification
Film so that eyeglass had both possessed the function of common plating diaphragm but also with anti-blue light and colour change function.
The technical scheme is that be accomplished by the following way:A kind of manufacturing method with anti-blue light color-changing lens,
By quality ratio, include the following steps:
1), dispensing:3-5 is pressed in 1.56 monomers:Ultraviolet-resistant absorbent UV powder is added at a temperature of 50 ~ 55 DEG C in 1000 ratios
It is stirred, is completely dissolved within 1 hour, toner, initiator insulated and stirred is then added and then vacuumizes 40 minutes;After half an hour
1-3 parts of initiators are added, enters cast after dispensing flow, is formed by curing substrate;
The heat curing temperature curve is as follows:34 DEG C keep the temperature 6 hours, and 65 DEG C are uniformly heating in 4 hours, continues heating 3
Hour to 95 degree simultaneously constant temperature 2 hours, 75 DEG C are cooled in 1 hour;Need complete solidification within 21 hours.
The initiator is one kind in isopropyl benzene hydroperoxide or tert-butyl hydroperoxide or di-t-butyl peroxide.
The toner is HISOL B75.
2), discoloration stiffened:Discoloration stiffened processing is carried out using substrate as ontology, stiffened promotes speed control in 1.5mm/s-
2.0mm/s;
3), solidification:Substrate stiffened is later with 120 DEG C of temperature-curables 1.5 hours, and subsequent Temperature fall is to 50 ~ 60 DEG C as eyeglass;
4), plated film:Eyeglass is put into vacuum coating equipment to vacuumize 5 ~ 10 minutes, after electron gun bombards eyeglass 120 seconds, using normal
It advises technique and silica, zirconium oxide is subjected to high temperature evaporation plated film, adjustment evaporation data make film layer be adsorbed onto on eyeglass and have
Radiation-proof effect.
The present invention can obstruct exhausted big portion with anti-blue light color-changing lens for the high energy blue light within 470 nanometers
Blue light, anti-blue light function is divided to improve 20% or more.
Specific implementation mode
A kind of manufacturing method of the discoloration anti-blue light eyeglass of high definition includes the following steps by quality ratio:
1,3-5 is pressed in 1.56 monomers:1000 ratios are added ultraviolet-resistant absorbent UV powder and are carried out at a temperature of 50 ~ 55 DEG C
Stirring, is completely dissolved for 1 hour, and toner, initiator insulated and stirred is then added and then vacuumizes 40 minutes;It is added after half an hour
1-3 parts of initiators enter cast after dispensing flow, are formed by curing substrate;The heat curing temperature curve is as follows:34℃
Heat preservation 6 hours, is uniformly heating to 65 DEG C in 4 hours, continues simultaneously constant temperature 2 hours of heating 3 hours to 95 degree, is dropped in 1 hour
Temperature is to 75 DEG C;Need complete solidification within 21 hours.The initiator is isopropyl benzene hydroperoxide or tert-butyl hydroperoxide or peroxide
Change one kind in di-t-butyl.Toner is HISOL B75, originates from KOC SOLUTION companies of South Korea.
2, change colour stiffened:Discoloration stiffened processing is carried out using substrate as ontology, stiffened promotes speed control in 1.5mm/s-
2.0mm/s;
3, cure:Substrate stiffened is later with 120 DEG C of temperature-curables 1.5 hours, and subsequent Temperature fall is to 50 ~ 60 DEG C as eyeglass;
4, plated film:Eyeglass is put into vacuum coating equipment to vacuumize 5 ~ 10 minutes, after electron gun bombards eyeglass 120 seconds, using normal
It advises technique and silica, zirconium oxide is subjected to high temperature evaporation plated film, adjustment evaporation data make film layer be adsorbed onto on eyeglass and have
Radiation-proof effect.
The present invention is obtained by following correction data:
One, the common uv blocking eyeglass in market
Two, eyeglass detection data of the present invention:
By above two groups of data it is not difficult to find that eyeglass of the present invention only has 0.17% can penetrate the ultraviolet light of 470 nanometers of wave band,
The UV470 ultraviolet lights that can effectively stop 99.83%, so as to our eyes of effective protection from the infringement of ultraviolet light.
Claims (4)
1. a kind of manufacturing method with anti-blue light color-changing lens includes the following steps by quality ratio:
1), dispensing:3-5 is pressed in 1.56 monomers:Ultraviolet-resistant absorbent UV powder is added at a temperature of 50 ~ 55 DEG C in 1000 ratios
It is stirred, is completely dissolved within 1 hour, toner, initiator insulated and stirred is then added and then vacuumizes 40 minutes;After half an hour
1-3 parts of initiators are added, enters cast after dispensing flow, is formed by curing substrate;
2), discoloration stiffened:Discoloration stiffened processing is carried out using substrate as ontology, stiffened promotes speed control in 1.5mm/s-
2.0mm/s;
3), solidification:Substrate stiffened is later with 120 DEG C of temperature-curables 1.5 hours, and subsequent Temperature fall is to 50 ~ 60 DEG C as eyeglass;
4), plated film:Eyeglass is put into vacuum coating equipment to vacuumize 5 ~ 10 minutes, after electron gun bombards eyeglass 120 seconds, using normal
It advises technique and silica, zirconium oxide is subjected to high temperature evaporation plated film, adjustment evaporation data make film layer be adsorbed onto on eyeglass and have
Radiation-proof effect.
2. a kind of manufacturing method with anti-blue light color-changing lens according to claim 1, it is characterised in that:The step
1)In heat curing temperature curve it is as follows:34 DEG C keep the temperature 6 hours, and 65 DEG C are uniformly heating in 4 hours, continue heating 3 hours
To 95 degree and constant temperature 2 hours, 75 DEG C are cooled in 1 hour;Need complete solidification within 21 hours.
3. a kind of manufacturing method with anti-blue light color-changing lens according to claim 1, it is characterised in that:The step
1)In initiator be one kind in isopropyl benzene hydroperoxide or tert-butyl hydroperoxide or di-t-butyl peroxide.
4. a kind of manufacturing method with anti-blue light color-changing lens according to claim 1, it is characterised in that:The step
1)Described in toner be HISOL B75.