CN108588508A - A kind of durable use for diesel engine sealing element - Google Patents
A kind of durable use for diesel engine sealing element Download PDFInfo
- Publication number
- CN108588508A CN108588508A CN201810712224.3A CN201810712224A CN108588508A CN 108588508 A CN108588508 A CN 108588508A CN 201810712224 A CN201810712224 A CN 201810712224A CN 108588508 A CN108588508 A CN 108588508A
- Authority
- CN
- China
- Prior art keywords
- sealing element
- diesel engine
- aluminium
- silica
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention mainly relates to sealing material fields, disclose a kind of durable use for diesel engine sealing element, consist of the following components in percentage by weight:Copper 2 ~ 3%, manganese 2 ~ 3%, silica 1 ~ 2%, white carbon 1 ~ 1.5%, nickel 0.5 ~ 1.6%, vanadium 1 ~ 2.6%, boron 1.3 ~ 3.5%, remaining be aluminium and inevitable impurity;Various metals and nonmetallic raw material is added, hence it is evident that improve the corrosion resistance of sealing element, service life extends;After aluminium is melted completely, nonmetallic raw material heat preservation is added and dissolves, so that raw metal and nonmetallic raw material is sufficiently mixed, improves the antirust ability and wear-resisting property of sealing element;Fully cool down stage by stage after melting, reduces the crystal grain of crystallization, improve the intensity, hardness and toughness of sealing element, enhance the corrosion resistance of sealing element.
Description
Technical field
The invention mainly relates to sealing material field more particularly to a kind of durable use for diesel engine sealing elements.
Background technology
Diesel engine can use diesel oil, lubricating oil, generate higher temperature in the process of running, diesel engine sealing performance it is good
It is badly directly related to the operation of automobile, the sealing element corrosion resistance on diesel engines at present is weaker, easy tos produce abrasion and corrosion, makes
The spoilage of diesel engine is higher, and the maintenance cost of diesel engine is higher, hence it is evident that improves the use cost of diesel engine.
Invention content
In order to make up the defect of prior art, the object of the present invention is to provide a kind of durable use for diesel engine sealing elements.
A kind of durable use for diesel engine sealing element, consists of the following components in percentage by weight:Copper 2 ~ 3%, manganese 2 ~ 3%, two
Silica 1 ~ 2%, white carbon 1 ~ 1.5%, nickel 0.5 ~ 1.6%, vanadium 1 ~ 2.6%, boron 1.3 ~ 3.5%, remaining for aluminium and inevitably it is miscellaneous
Matter;The silica, grain size are 20 ~ 50nm.
Include the following steps:
(1)Aluminium is heated to 1800 DEG C, impurity is removed, obtains molten aluminum liquid.
(2)Silica, white carbon and boron are added in molten aluminum liquid, obtain mixture, then cooling cooling thing, then
To secondary mixture, after cooling, by mixture note in mold, 60 ~ 260 DEG C is naturally cooling to, stripping forming is carried out, must seal
Part blank.
(3)Sealing element blank is added in heating furnace, carbon dioxide gas is passed through, is warming up to 1.8 DEG C/min of speed
It 800 DEG C, is quenched in urea liquid after taking-up, obtains the corrosion-resistant sealing element for diesel engine;Sealing, packaging, must be used for
The corrosion-resistant sealing element finished product of diesel engine.
It is an advantage of the invention that:Provided by the present invention for the corrosion-resistant sealing element of diesel engine, various metals and non-are added
Raw metal, hence it is evident that the corrosion resistance for improving sealing element after melting aluminium completely, is added nonmetallic raw material heat preservation and dissolves, make gold
Belong to raw material and nonmetallic raw material is sufficiently mixed, improves the antirust ability and wear-resisting property of sealing element;Fully melting after stage by stage into
Row cooling, reduces the crystal grain of crystallization, improves the intensity, hardness and toughness of sealing element, enhance the corrosion resistance of sealing element;It is added surplus
Under raw material after be rapidly heated, make the abundant melting mixing of raw material, slowly rise again again after Temperature fall crystallization, it is accurate to improve raw material
Degree, enhances the corrosion resistance of sealing element;It is passed through carbon dioxide gas after sealing element stripping forming to be heated, carbon atom is made to penetrate into
Sealing element, heating, which is placed in urea liquid, to be quenched, and is formed protective film in seal surface, is improved the stability of sealing element
And corrosion resistance.
Specific implementation mode
Illustrate the present invention with specific embodiment below.
A kind of durable use for diesel engine sealing element, consists of the following components in percentage by weight:Copper 2 ~ 3%, manganese 2 ~ 3%, two
Silica 1 ~ 2%, white carbon 1 ~ 1.5%, nickel 0.5 ~ 1.6%, vanadium 1 ~ 2.6%, boron 1.3 ~ 3.5%, remaining for aluminium and inevitably it is miscellaneous
Matter;The silica, grain size are 20 ~ 50nm.
Include the following steps:
(1)Aluminium is heated to 1800 DEG C, impurity is removed, obtains molten aluminum liquid.
(2)Silica, white carbon and boron are added in molten aluminum liquid, obtain mixture, then cooling cooling thing, then
To secondary mixture, after cooling, by mixture note in mold, 60 ~ 260 DEG C is naturally cooling to, stripping forming is carried out, must seal
Part blank.
(3)Sealing element blank is added in heating furnace, carbon dioxide gas is passed through, is warming up to 1.8 DEG C/min of speed
It 800 DEG C, is quenched in urea liquid after taking-up, obtains the corrosion-resistant sealing element for diesel engine;Sealing, packaging, must be used for
The corrosion-resistant sealing element finished product of diesel engine.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (2)
1. a kind of durable use for diesel engine sealing element, which is characterized in that consist of the following components in percentage by weight:Copper 2 ~ 3%,
Manganese 2 ~ 3%, silica 1 ~ 2%, white carbon 1 ~ 1.5%, nickel 0.5 ~ 1.6%, vanadium 1 ~ 2.6%, boron 1.3 ~ 3.5%, remaining be aluminium and not
Evitable impurity;The silica, grain size are 20 ~ 50nm.
2. a kind of durable use for diesel engine sealing element a kind of according to claim 1, which is characterized in that include the following steps:
(1)Aluminium is heated to 1800 DEG C, impurity is removed, obtains molten aluminum liquid;
(2)Silica, white carbon and boron are added in molten aluminum liquid, obtain mixture, then cooling cooling thing, then obtains two
Secondary mixture after cooling, by mixture note in mold, is naturally cooling to 60 ~ 260 DEG C, carries out stripping forming, obtain sealing element base
Material;
(3)Sealing element blank is added in heating furnace, carbon dioxide gas is passed through, 800 is warming up to 1.8 DEG C/min of speed
DEG C, it is quenched in urea liquid after taking-up, obtains the corrosion-resistant sealing element for diesel engine;Sealing, packaging, obtains for diesel oil
The corrosion-resistant sealing element finished product of machine.