CN108547179A - Food package film and preparation method thereof - Google Patents
Food package film and preparation method thereof Download PDFInfo
- Publication number
- CN108547179A CN108547179A CN201810541870.8A CN201810541870A CN108547179A CN 108547179 A CN108547179 A CN 108547179A CN 201810541870 A CN201810541870 A CN 201810541870A CN 108547179 A CN108547179 A CN 108547179A
- Authority
- CN
- China
- Prior art keywords
- dosage
- weight
- parts
- preparation
- food package
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of food package film and preparation method thereof, which includes:Glass fibre and ceramic fibre are mixed, 12 is impregnated in sodium hydroxide solution later for 24 hours, is cleaned after taking-up, be thermally treated resulting in modified fibre twice respectively later;Pulp suspension M is formed after wood pulp, sodium benzoate, carboxymethyl cellulose, modified fibre, polyvinyl alcohol, polylactic resin and retention agent are stirred;The pulp suspension M is manufactured paper with pulp molding, food package film is obtained after processing;It is relatively low to solve common food package film its intensity, while heat-resisting ability is weaker, is easy to soften when containing hotter prepared food so that the problem of its mechanical strength is greatly reduced.
Description
Technical field
The present invention relates to packaging bag preparation fields, and in particular, to food package film and preparation method thereof.
Background technology
Food package film refers to directly being contacted with food, the membrane container for containing and protecting food.Common food
Its intensity of packaging film is relatively low, while heat-resisting ability is weaker, is easy to soften when containing hotter prepared food so that its mechanical strength
It is greatly reduced.
Therefore it provides a kind of heat-resisting ability is stronger, the food package film and preparation method thereof that heat will not soften is this
The problem of invention urgent need to resolve.
Invention content
The object of the present invention is to provide a kind of food package film and preparation method thereof, solve common food package film its
Intensity is relatively low, while heat-resisting ability is weaker, is easy to soften when containing hotter prepared food so that its mechanical strength is greatly reduced
The problem of.
To achieve the goals above, the present invention provides a kind of preparation methods of food package film, wherein the preparation side
Method includes:
(1) glass fibre and ceramic fibre are mixed, impregnates 12-24h in sodium hydroxide solution later, is carried out after taking-up
Cleaning, is thermally treated resulting in modified fibre twice respectively later;The condition of heat treatment includes for the first time:Temperature is 60-90 DEG C,
Time is 1-3min, and the condition of second of heat treatment includes:Temperature is 40-50 DEG C, time 10-20min;
(2) by wood pulp, sodium benzoate, carboxymethyl cellulose, modified fibre, polyvinyl alcohol, polylactic resin and retention agent
Pulp suspension M is formed after being stirred;
(3) the pulp suspension M is manufactured paper with pulp molding, food package film is obtained after processing;Wherein, relative to 100 weight
The dosage of the wood pulp of part, the sodium benzoate is 30-50 parts by weight, and the dosage of the carboxymethyl cellulose is 1-7 parts by weight, institute
The dosage for stating modified fibre is 3-10 parts by weight, and the dosage of the polyvinyl alcohol is 10-20 parts by weight, the polylactic resin
Dosage is 5-15 parts by weight, and the dosage of the retention agent is 1-5 parts by weight.
The present invention also provides a kind of food package films, wherein the food package film is made by above-mentioned preparation method.
Through the above technical solutions, the present invention provides a kind of food package films and preparation method thereof, wherein the preparation
Method includes:Glass fibre and ceramic fibre are mixed, impregnate 12-24h in sodium hydroxide solution later, is carried out after taking-up clear
It washes, is thermally treated resulting in modified fibre twice respectively later;The condition of heat treatment includes for the first time:Temperature is 60-90 DEG C, when
Between be 1-3min, the condition of second heat treatment includes:Temperature is 40-50 DEG C, time 10-20min;By wood pulp, benzoic acid
Sodium, carboxymethyl cellulose, modified fibre, polyvinyl alcohol, polylactic resin and retention agent form pulp suspension after being stirred
M;The pulp suspension M is manufactured paper with pulp molding, food package film is obtained after processing, by the synergistic effect between each raw material, makes
Packaging bag obtained has excellent mechanical strength and heat-resisting ability, while the method for being used to prepare the packaging bag it is simple,
Raw material is easy to get.
Other features and advantages of the present invention will be described in detail in subsequent specific embodiment part.
Specific implementation mode
The specific implementation mode of the present invention is described in detail below.It should be understood that described herein specific
Embodiment is merely to illustrate and explain the present invention, and is not intended to restrict the invention.
The present invention provides a kind of preparation method of food package film, the preparation method includes:By glass fibre and pottery
Porcelain fiber mixes, and impregnates 12-24h in sodium hydroxide solution later, is cleaned after taking-up, carries out respectively later at heat twice
Reason obtains modified fibre;The condition of heat treatment includes for the first time:Temperature is 60-90 DEG C, time 1-3min, second of heat treatment
Condition include:Temperature is 40-50 DEG C, time 10-20min;By wood pulp, sodium benzoate, carboxymethyl cellulose, modified fibre
Dimension, polyvinyl alcohol, polylactic resin and retention agent form pulp suspension M after being stirred;The pulp suspension M is manufactured paper with pulp
Molding, food package film is obtained after processing;Wherein, the dosage of the wood pulp relative to 100 parts by weight, the sodium benzoate is 30-
The dosage of 50 parts by weight, the carboxymethyl cellulose is 1-7 parts by weight, and the dosage of the modified fibre is 3-10 parts by weight, institute
The dosage for stating polyvinyl alcohol is 10-20 parts by weight, and the dosage of the polylactic resin is 5-15 parts by weight, the use of the retention agent
Amount is 1-5 parts by weight.
In order to enable packaging bag obtained has more excellent mechanical strength and heat-resisting ability, in one kind of the present invention
In preferred embodiment, relative to the wood pulp of 100 parts by weight, the dosage of the sodium benzoate is 35-45 parts by weight, the carboxylic
The dosage of methylcellulose is 2-4 parts by weight, and the dosage of the modified fibre is 5-7 parts by weight, the dosage of the polyvinyl alcohol
Dosage for 14-16 parts by weight, the polylactic resin is 8-12 parts by weight, and the dosage of the retention agent is 2-4 parts by weight.
In order to improve retention of the auxiliary material in wood pulp and sodium benzoate, in a kind of preferred embodiment of the present invention
In, the retention agent is made of polyethyleneimine and polyvinyl alcohol, and the quality of the polyethyleneimine and the polyvinyl alcohol
Than being 1:1-4.
The modified fibre can be the conventional use of type of those skilled in the art, for example, in order to improve packaging bag obtained
Mechanical strength, the length of the modified fibre is 1-3mm.
In order to enable preferably being mixed between raw material, in a kind of preferred embodiment of the present invention, the stirring is mixed
The speed of conjunction is 100-120r/min.
In order to enable packaging bag obtained has more excellent mechanical strength and heat-resisting ability, in one kind of the present invention
In preferred embodiment, in step (1), glass fibre and ceramic fibre are 1 according to mass ratio:1-2 is mixed.
The present invention also provides a kind of food package films, wherein the food package film is made by above-mentioned preparation method.
The present invention will be described in detail by way of examples below.In following embodiment, modified fibre is Beijing state person of outstanding talent
The commercially available product that chemical machinery Co., Ltd provides.
Embodiment 1
Glass fibre and ceramic fibre are mixed, 12h is impregnated in sodium hydroxide solution later, is cleaned after taking-up,
It is thermally treated resulting in modified fibre twice respectively later;The condition of heat treatment includes for the first time:Temperature is 60 DEG C, and the time is
1min, the condition being heat-treated for the second time include:Temperature is 40 DEG C, time 10min;By 100g wood pulps, 35g sodium benzoates, 2g
Carboxymethyl cellulose, 5g modified fibres, 14g polyvinyl alcohol, 8g polylactic resin and 2g retention agents are (by polyethyleneimine and poly- second
Enol forms, and the mass ratio of the polyethyleneimine and the polyvinyl alcohol is 1:1) it is stirred (mixing speed 100r/
Min pulp suspension M) is formed afterwards;The pulp suspension M is manufactured paper with pulp molding, food package film A1 is obtained after processing.
Embodiment 2
Glass fibre and ceramic fibre are mixed, impregnates in sodium hydroxide solution for 24 hours, is cleaned after taking-up later,
It is thermally treated resulting in modified fibre twice respectively later;The condition of heat treatment includes for the first time:Temperature is 90 DEG C, and the time is
3min, the condition being heat-treated for the second time include:Temperature is 50 DEG C, time 20min;By 100g wood pulps, 45g sodium benzoates, 4g
Carboxymethyl cellulose, 7g modified fibres, 16g polyvinyl alcohol, 12g polylactic resin and 4g retention agents (by polyethyleneimine and gather
Vinyl alcohol forms, and the mass ratio of the polyethyleneimine and the polyvinyl alcohol is 1:4) it is stirred (mixing speed 120r/
Min pulp suspension M) is formed afterwards;The pulp suspension M is manufactured paper with pulp molding, food package film A2 is obtained after processing.
Embodiment 3
Glass fibre and ceramic fibre are mixed, 18h is impregnated in sodium hydroxide solution later, is cleaned after taking-up,
It is thermally treated resulting in modified fibre twice respectively later;The condition of heat treatment includes for the first time:Temperature is 75 DEG C, and the time is
2min, the condition being heat-treated for the second time include:Temperature is 45 DEG C, time 15min;By 100g wood pulps, 40g sodium benzoates, 3g
Carboxymethyl cellulose, 6g modified fibres, 15g polyvinyl alcohol, 10g polylactic resin and 3g retention agents (by polyethyleneimine and gather
Vinyl alcohol forms, and the mass ratio of the polyethyleneimine and the polyvinyl alcohol is 1:2) it is stirred (mixing speed 110r/
Min pulp suspension M) is formed afterwards;The pulp suspension M is manufactured paper with pulp molding, food package film A3 is obtained after processing.
Embodiment 4
It is prepared according to the method for embodiment 1, unlike, the dosage of wood pulp is 100g, the use of the sodium benzoate
Amount is 30g, and the dosage of the carboxymethyl cellulose is 1g, and the dosage of the modified fibre is 3g, the dosage of the polyvinyl alcohol
Dosage for 10g, the polylactic resin is 5g, and the dosage of the retention agent is 1g, obtains food package film A4.
Embodiment 5
It is prepared according to the method for embodiment 1, unlike, the dosage of wood pulp is 100g, the use of the sodium benzoate
Amount is 50g, and the dosage of the carboxymethyl cellulose is 7g, and the dosage of the modified fibre is 10g, the dosage of the polyvinyl alcohol
Dosage for 20g, the polylactic resin is 15g, and the dosage of the retention agent is 5g, obtains food package film A5.
Comparative example 1
It is prepared according to the method for embodiment 1, unlike, the dosage of wood pulp is 100g, the use of the sodium benzoate
Amount is 20g, and the dosage of the carboxymethyl cellulose is 0.5g, and the dosage of the modified fibre is 2g, the use of the polyvinyl alcohol
Amount is 7g, and the dosage of the polylactic resin is 2g, and the dosage of the retention agent is 0.5g, obtains food package film D1.
Comparative example 2
It is prepared according to the method for embodiment 1, unlike, the dosage of wood pulp is 100g, the use of the sodium benzoate
Amount is 60g, and the dosage of the carboxymethyl cellulose is 10g, and the dosage of the modified fibre is 12g, the use of the polyvinyl alcohol
Amount is 22g, and the dosage of the polylactic resin is 18g, and the dosage of the retention agent is 8g, obtains food package film D2.
Test case 1
Food package film A1-A5, D1 and D2 obtained are placed in 30min under 70 DEG C of environment, observe its deformation.
Table 1
Embodiment is numbered | Tensile strength (MPa) | Surface deformation situation |
A1 | 35 | Without apparent deformation |
A2 | 32 | Without apparent deformation |
A3 | 31 | Without apparent deformation |
A4 | 23 | Without apparent deformation |
25 | 23 | Slight deformation |
D1 | 15 | Gross distortion |
D2 | 17 | Gross distortion |
Packaging bag A1-A5 produced within the scope of the present invention is can be seen that by above table data, tensile strength is wanted
Higher than packaging bag D1 and D2 produced outside the scope of the present invention, and packaging bag A1-A5 is unlikely to deform under high temperature environment, and D1 and
Gross distortion can occur for D2, while packaging bag obtained has more excellent performance in currently preferred range, thus
It can obtain that mechanical strength is higher, the strong packaging bag of heat-resisting ability.
The preferred embodiment of the present invention has been described above in detail, still, during present invention is not limited to the embodiments described above
Detail can carry out a variety of simple variants to technical scheme of the present invention within the scope of the technical concept of the present invention, this
A little simple variants all belong to the scope of protection of the present invention.
It is further to note that specific technical features described in the above specific embodiments, in not lance
In the case of shield, can be combined by any suitable means, in order to avoid unnecessary repetition, the present invention to it is various can
The combination of energy no longer separately illustrates.
In addition, various embodiments of the present invention can be combined randomly, as long as it is without prejudice to originally
The thought of invention, it should also be regarded as the disclosure of the present invention.
Claims (7)
1. a kind of preparation method of food package film, which is characterized in that the preparation method includes:
(1) glass fibre and ceramic fibre are mixed, impregnates 12-24h in sodium hydroxide solution later, carried out after taking-up clear
It washes, is thermally treated resulting in modified fibre twice respectively later;The condition of heat treatment includes for the first time:Temperature is 60-90 DEG C, when
Between be 1-3min, the condition of second heat treatment includes:Temperature is 40-50 DEG C, time 10-20min;
(2) wood pulp, sodium benzoate, carboxymethyl cellulose, modified fibre, polyvinyl alcohol, polylactic resin and retention agent are stirred
Pulp suspension M is formed after mixing;
(3) the pulp suspension M is manufactured paper with pulp molding, food package film is obtained after processing;Wherein, relative to 100 parts by weight
The dosage of wood pulp, the sodium benzoate is 30-50 parts by weight, and the dosage of the carboxymethyl cellulose is 1-7 parts by weight, described to change
Property fiber dosage be 3-10 parts by weight, the dosage of the polyvinyl alcohol is 10-20 parts by weight, the dosage of the polylactic resin
Dosage for 5-15 parts by weight, the retention agent is 1-5 parts by weight.
2. preparation method according to claim 1, wherein relative to the wood pulp of 100 parts by weight, the use of the sodium benzoate
Amount is 35-45 parts by weight, and the dosage of the carboxymethyl cellulose is 2-4 parts by weight, and the dosage of the modified fibre is 5-7 weight
Part, the dosage of the polyvinyl alcohol is 14-16 parts by weight, and the dosage of the polylactic resin is 8-12 parts by weight, the retention
The dosage of agent is 2-4 parts by weight.
3. preparation method according to claim 1, wherein the retention agent is made of polyethyleneimine and polyvinyl alcohol,
And the mass ratio of the polyethyleneimine and the polyvinyl alcohol is 1:1-4.
4. preparation method according to claim 1, wherein the length of the modified fibre is 1-3mm.
5. preparation method according to claim 1, wherein the speed being stirred is 100-120r/min.
6. preparation method according to claim 1, wherein in step (1), glass fibre and ceramic fibre are according to quality
Than being 1:1-2 is mixed.
7. a kind of food package film, which is characterized in that the food package film is by the system described in any one of claim 1-6
Preparation Method is made.