CN108538515A - A kind of enameled wire machining technique - Google Patents
A kind of enameled wire machining technique Download PDFInfo
- Publication number
- CN108538515A CN108538515A CN201810444196.1A CN201810444196A CN108538515A CN 108538515 A CN108538515 A CN 108538515A CN 201810444196 A CN201810444196 A CN 201810444196A CN 108538515 A CN108538515 A CN 108538515A
- Authority
- CN
- China
- Prior art keywords
- wire
- metal wire
- enameled wire
- metal
- enameled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of enameled wire machining techniques, include the following steps：(1) metal wire is equably released from spool, raw material is provided and ensures the stability of japanning, in high speed board, carry out unwrapping wire by joint drawing machine；(2) metal wire to be processed after step (1) unwrapping wire is led in rinse bath, the greasy dirt and particle of metal line surface is removed with clear water；(3) metal wire to be processed carries out 46 drawings after cleaning step (2)；(4) 10 12 japannings are carried out to metal wire after drawing；(5) metal wire after japanning is handled by annealing furnace；(6) metal wire after annealing is put into baker and is dried to get to required enameled wire；(7) by enameled wire coiling, the packing after drying.The indexs such as tensile strength, elongation, the softening breakdown of the enameled wire of the present invention are obviously improved, and the quality of production of enameled wire is improved.
Description
Technical field
The present invention relates to enameled wire technical field, specifically a kind of enameled wire machining technique.
Background technology
Enameled wire is a kind of electrical material, it is to process a thin layer of high-strength polyester in a circular copper line surface
Insulating layer plays the role of that with external insulation, enameled wire the lousiness line also thinner than hair can be processed by specification, thick as thumb
Cotton-covered wire.The insulating layer on its surface is wiped off in use.Enameled wire evidence has good insulation effect and waterproof energy
Power is in terms of electric appliance using very such as motor, generator, water pump, electromagnet, electric welding machine, household electrical appliance, wireless telecommunications are raised extensively
Sound device, telegraph, transformer etc..Enameled wire is to apply one or more of coatings, shape after baked, cooling on the surface of conductor
At a kind of electric wire of tape insulation layer.
Invention content
The present invention provides a kind of enameled wire machining techniques, to solve the above technical problems.
A kind of enameled wire machining technique, includes the following steps：
(1) metal wire is equably released from spool, raw material is provided and ensures the stability of japanning, in high speed board, according to
Carry out unwrapping wire by joint drawing machine；
(2) metal wire to be processed after step (1) unwrapping wire is led in rinse bath, the oil of metal line surface is removed with clear water
Dirty and particle；
(3) metal wire to be processed carries out 4-6 drawing after cleaning step (2)；
(4) 10-12 road japannings are carried out to metal wire after drawing；
(5) metal wire after japanning is handled by annealing furnace；
(6) metal wire after annealing is put into baker and is dried to get to required enameled wire；
(7) by enameled wire coiling, the packing after drying.
Preferably, the temperature of annealing furnace is 450-490 DEG C in the step (5).
Preferably, the temperature of baker is controlled at 400-500 DEG C in the step (6).
Preferably, step (4) floating coating paints to metal wire using felt japanning method.
Beneficial effects of the present invention：
The beneficial effects of the invention are as follows：The production of enamel wire technique of the present invention is by carrying out every technique in each step
Adjustment makes the indexs such as tensile strength, elongation, the softening breakdown of enameled wire be obviously improved, ensure that enameled wire is being led
Other indexs can also satisfy the use demand while electrical performance indexes are met the requirements, and broaden the use scope of enameled wire, improve
The quality of production of enameled wire.
Specific implementation mode
The embodiment of the present invention is described in detail below, but what the present invention can be defined by the claims and cover
Multitude of different ways is implemented.
Below by way of specific embodiment, the present invention will be described in detail.
Embodiment 1
A kind of enameled wire machining technique, includes the following steps：
(1) metal wire is equably released from spool, raw material is provided and ensures the stability of japanning, in high speed board, according to
Carry out unwrapping wire by joint drawing machine；
(2) metal wire to be processed after step (1) unwrapping wire is led in rinse bath, the oil of metal line surface is removed with clear water
Dirty and particle；
(3) metal wire to be processed carries out 4-6 drawing after cleaning step (2)；
(4) 10-12 road japannings are carried out to metal wire after drawing；
(5) metal wire after japanning is handled by annealing furnace；
(6) metal wire after annealing is put into baker and is dried to get to required enameled wire；
(7) by enameled wire coiling, the packing after drying.
The temperature of annealing furnace is 450 DEG C in above-mentioned steps (5).
The temperature of baker is controlled at 400 DEG C in above-mentioned steps (6).
Above-mentioned steps (4) floating coating paints to metal wire using felt japanning method.
Embodiment 2
A kind of enameled wire machining technique, includes the following steps：
(1) metal wire is equably released from spool, raw material is provided and ensures the stability of japanning, in high speed board, according to
Carry out unwrapping wire by joint drawing machine；
(2) metal wire to be processed after step (1) unwrapping wire is led in rinse bath, the oil of metal line surface is removed with clear water
Dirty and particle；
(3) metal wire to be processed carries out 4-6 drawing after cleaning step (2)；
(4) 10-12 road japannings are carried out to metal wire after drawing；
(5) metal wire after japanning is handled by annealing furnace；
(6) metal wire after annealing is put into baker and is dried to get to required enameled wire；
(7) by enameled wire coiling, the packing after drying.
The temperature of annealing furnace is 470 DEG C in above-mentioned steps (5).
The temperature of baker is controlled at 450 DEG C in above-mentioned steps (6).
Above-mentioned steps (4) floating coating paints to metal wire using felt japanning method.
Embodiment 3
A kind of enameled wire machining technique, includes the following steps：
(1) metal wire is equably released from spool, raw material is provided and ensures the stability of japanning, in high speed board, according to
Carry out unwrapping wire by joint drawing machine；
(2) metal wire to be processed after step (1) unwrapping wire is led in rinse bath, the oil of metal line surface is removed with clear water
Dirty and particle；
(3) metal wire to be processed carries out 4-6 drawing after cleaning step (2)；
(4) 10-12 road japannings are carried out to metal wire after drawing；
(5) metal wire after japanning is handled by annealing furnace；
(6) metal wire after annealing is put into baker and is dried to get to required enameled wire；
(7) by enameled wire coiling, the packing after drying.
The temperature of annealing furnace is 490 DEG C in above-mentioned steps (5).
The temperature of baker is controlled at 500 DEG C in above-mentioned steps (6).
Above-mentioned steps (4) floating coating paints to metal wire using felt japanning method.
The embodiments of the present invention described above are not intended to limit the scope of the present invention, any in the present invention
Spirit and principle within made by modifications, equivalent substitutions and improvements etc., should be included in the claim protection model of the present invention
Within enclosing.
Claims (4)
1. a kind of enameled wire machining technique, which is characterized in that include the following steps：
(1) metal wire is equably released from spool, raw material is provided and ensures the stability of japanning, in high speed board, by connection
It closes drawing machine and carrys out unwrapping wire；
(2) metal wire to be processed after step (1) unwrapping wire is led in rinse bath, with clear water remove metal line surface greasy dirt and
Particle；
(3) metal wire to be processed carries out 4-6 drawing after cleaning step (2)；
(4) 10-12 road japannings are carried out to metal wire after drawing；
(5) metal wire after japanning is handled by annealing furnace；
(6) metal wire after annealing is put into baker and is dried to get to required enameled wire；
(7) by enameled wire coiling, the packing after drying.
2. enameled wire machining technique according to claim 1, which is characterized in that the temperature of annealing furnace in the step (5)
It is 450-490 DEG C.
3. enameled wire machining technique according to claim 1, which is characterized in that the temperature control of baker in the step (6)
System is at 400-500 DEG C.
4. enameled wire machining technique according to claim 1, which is characterized in that step (4) floating coating uses felt
Japanning method paints to metal wire.