CN103302049A - Enameled bare wire cleaning process - Google Patents
Enameled bare wire cleaning process Download PDFInfo
- Publication number
- CN103302049A CN103302049A CN2013101916059A CN201310191605A CN103302049A CN 103302049 A CN103302049 A CN 103302049A CN 2013101916059 A CN2013101916059 A CN 2013101916059A CN 201310191605 A CN201310191605 A CN 201310191605A CN 103302049 A CN103302049 A CN 103302049A
- Authority
- CN
- China
- Prior art keywords
- cleaning
- copper flat
- flat wire
- bare copper
- wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an enameled bare wire cleaning process, which includes the following steps: arranging a cleaning tank before a bare copper flat wire is painted, wherein the cleaning tank is filled with pure water and pure alcohol blended in the proportion of 1:80-120; heating and softening the bare copper flat wire in a drying oven after the bare copper flat wire is cleaned in the cleaning tank for a first time; and cleaning the heated and softened bare copper flat wire in the cleaning tank for a second time, and then drying and painting the wire in the drying oven. According to the invention, the bare copper flat wire placed in the cleaning tank for the second time transmits heat to the water of the tank, so as to keep the temperature of the water inside the cleaning tank; the temperature of the bare copper flat wire can be adjusted through the water temperature inside the cleaning tank; and through the adoption of the cleaning process, the enameled bare wire is better cleaned, and the bare copper flat wire is prevented from oxidation.
Description
Technical field
The present invention relates to a kind of transformer, specifically a kind of enamel-cover bare wire cleaning.
Background technology
Enameled sheet wire all adopts bare copper flat wire japanning stoving process at present, and the bare copper flat wire surface cleanness degree has a strong impact on the electric property of enameled sheet wire finished product.The bare copper flat wire cleaning surfaces is generally in the source---and wire-drawing process begins control, because process environments restriction, bare copper flat wire unavoidably is stained with the pollutants such as wire drawing oil, copper scale, although adopt felt, calico to carry out wiping, still exist because of felt, calico and in time change, the bare copper flat wire cleaning surfaces is very poor situation still.
Summary of the invention
The problem that exists in order to overcome prior art the purpose of this invention is to provide a kind of enamel-cover bare wire cleaning, and by this cleaning, enamel-cover bare wire cleaning performance is better, and can avoid the bare copper flat wire oxidation.
The objective of the invention is to be achieved through the following technical solutions:
A kind of enamel-cover bare wire cleaning is characterized in that this cleaning may further comprise the steps:
1) the cleaning pond is set before the bare copper flat wire japanning, Chi Shui is pure water and absolute alcohol, and absolute alcohol and pure water are in the ratio allotment of 1:80-120;
2) bare copper flat wire cleans through the cleaning pond for the first time, after enter the drying oven thermoplastic;
3) bare copper flat wire after the thermoplastic enters the cleaning of cleaning pond for the second time, and then enters drying oven oven dry, japanning.
Among the present invention, absolute alcohol and pure water are in the ratio allotment of 1:100.Bare copper flat wire through the cleaning pond, is delivered to Chi Shuizhong with heat, pond water temperature in the pond that keeps clean for the second time.Can regulate the temperature of bare copper flat wire by pond water temperature in the cleaning pond.For preventing that heat runs off, can above the cleaning pond, be provided with insulation cover.
The cleaning pond is installed in the present invention additional before the bare copper flat wire japanning, Chi Shui is that absolute alcohol and pure water are allocated in proportion.Twice process cleaning of bare copper flat wire pond for the first time through entering the drying oven thermoplastic after the cleaning of cleaning pond, enters the cleaning pond again and cleans, and enters at last drying oven oven dry, japanning again.During for the second time through the cleaning pond, the heat of bare copper flat wire is delivered to Chi Shuizhong, and bare copper flat wire moves continuously, and cleaning pond water temperature rises, and forms warm water, and cleaning performance is better.
The invention has the beneficial effects as follows: 1. twice cleaning, cleaning effect is more thorough; 2. bare copper flat wire is brought heat into the cleaning pond through burner hearth, need not other heating; 3. clean pond warm water, cleaning performance is better; 4. clean Chi Shui and contain alcohol, can avoid the bare copper flat wire oxidation; 5. clean the pond and can control the temperature of bare copper flat wire, can reach bating effect, avoid again excess Temperature impact japanning performance.
The specific embodiment
A kind of enamel-cover bare wire cleaning, this cleaning may further comprise the steps:
1) the cleaning pond is set before the bare copper flat wire japanning, Chi Shui is pure water and absolute alcohol, and absolute alcohol and pure water are in the ratio allotment of 1:100;
2) bare copper flat wire cleans through the cleaning pond for the first time, and bare copper flat wire out enters the drying oven thermoplastic afterwards by the other end after entering, pass the cleaning pond by an end that cleans the pond;
3) bare copper flat wire after the thermoplastic enters the cleaning of cleaning pond for the second time, and then enters drying oven oven dry, japanning.Bare copper flat wire is for the second time through cleaning during the pond, and the heat of bare copper flat wire is delivered to Chi Shuizhong, and bare copper flat wire moves continuously, and cleaning pond water temperature rises, and forms warm water, and cleaning performance is better.Can regulate the temperature of bare copper flat wire by pond water temperature in the cleaning pond, can reach bating effect, avoid again excess Temperature impact japanning performance.For preventing that heat runs off, can above the cleaning pond, be provided with insulation cover.
Bare copper flat wire among the present invention is through twice cleaning, and cleaning effect is more thorough; Bare copper flat wire is brought heat into the cleaning pond through burner hearth, need not other heating; Cleaning pond warm water, cleaning performance is better; Because cleaning Chi Shui contains alcohol, can avoid the bare copper flat wire oxidation.
Claims (5)
1. enamel-cover bare wire cleaning is characterized in that this cleaning may further comprise the steps:
1) the cleaning pond is set before the bare copper flat wire japanning, Chi Shui is pure water and absolute alcohol, and absolute alcohol and pure water are in the ratio allotment of 1:80-120;
2) bare copper flat wire cleans through the cleaning pond for the first time, after enter the drying oven thermoplastic;
3) bare copper flat wire after the thermoplastic enters the cleaning of cleaning pond for the second time, and then enters drying oven oven dry, japanning.
2. enamel-cover bare wire cleaning according to claim 1 is characterized in that: in the step 1), absolute alcohol and pure water are in the ratio allotment of 1:100.
3. enamel-cover bare wire cleaning according to claim 1 is characterized in that: in the step 3), by pond water temperature in the cleaning pond temperature of bare copper flat wire is regulated.
4. enamel-cover bare wire cleaning according to claim 1 is characterized in that: in the step 3), bare copper flat wire through the cleaning pond, is delivered to Chi Shuizhong with heat, pond water temperature in the pond that keeps clean for the second time.
5. enamel-cover bare wire cleaning according to claim 1 is characterized in that: be provided with insulation cover above the cleaning pond.