CN108532053A - Compound ice sense fiber of colored polyester-nylon mica and preparation method thereof - Google Patents
Compound ice sense fiber of colored polyester-nylon mica and preparation method thereof Download PDFInfo
- Publication number
- CN108532053A CN108532053A CN201810174357.XA CN201810174357A CN108532053A CN 108532053 A CN108532053 A CN 108532053A CN 201810174357 A CN201810174357 A CN 201810174357A CN 108532053 A CN108532053 A CN 108532053A
- Authority
- CN
- China
- Prior art keywords
- parts
- fiber
- mica
- nylon
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of compound ice sense fibers of colored polyester-nylon mica, including twist mutually together wash bright and beautiful mica fiber and ice silk fiber, it is using polyester fiber as core wire to wash bright and beautiful mica fiber described in wherein, outer cladding nylon fibre forms, the nylon fibre includes 92 95 parts of polyamide fibres, 35 parts of Masterbatch, 25 parts of far infrared powder by weight, and the far infrared powder includes 40 50 parts of silica, 20 30 parts of zinc oxide, 5 10 parts of medical stones, 10 15 parts of molybdenum oxides, 23 parts of tin oxide, 15 parts of talcum powder, 0.1 0.8 parts of rare earths by weight.The present invention will be by that will wash bright and beautiful mica fiber and ice silk fiber mutually together with twisting, in addition it is using polyester fiber as core wire to wash bright and beautiful mica fiber described in, outer cladding nylon fibre forms, so that various fibers carry out complementation, protrusion advantage, improve disadvantage, final obtained composite fibre comfortable feel, intensity is high, has certain far infrared ability.
Description
Technical field
The present invention relates to the compound ice sense fibers of a kind of composite fibre, especially colored polyester-nylon mica.
Background technology
Polyester fabric is very more a kind of chemical fiber garment fabrics in daily life, its biggest advantage is that wrinkle resistance
It is fine with conformality, therefore, it is suitble to do the outdoor goods such as coat garment, all kinds of luggages and tent.The intensity of polyester fiber compares cotton
Nearly 1 times of height is spent, it is 3 times higher than wool, therefore dacron is durable.Polyester fiber can be used at 70~170 DEG C, be that synthesis is fine
Heat resistance and thermal stability are best in dimension.The elasticity of terylene is more than other fibers close to wool, crease resistance, and fabric does not wrinkle, and protects
Shape is good.The water suction regain of terylene is low, good insulation preformance, but since water imbibition is low, and the electrostatic for the generation that rubs is big, dyeability
It is poor.
Strength, the wearability of polyamide fibre are good, occupy first of all fibres.Its wearability is 10 times of cotton fiber, is that dry state is viscous
10 times of glue fiber are 140 times of hygrometric state fiber.Therefore, durability is splendid.The elasticity of nylon fabric and elastic recovery pole
It is good but yielding under small external force, therefore its fabric variable fold during wearing.Polyamide fibre has good moth resistance and corrosion resistance.
But as the improvement of people's living standards, the requirement to textile is also higher and higher, above-mentioned polyester fabric and brocade
Synthetic fibre fabric can no longer meet the requirement of people because of respective advantage and disadvantage.Start occurred washing bright and beautiful fiber on the market therewith,
Have the advantages that soft, dress is comfortable, intensity is high, but it is of low quality, easy dyeing, defect rate be not high, deficiency in economic performance.
Invention content
There is provided the purpose of the present invention is to solve above-mentioned the deficiencies in the prior art it is a kind of it is compound it is secured, soft,
Elasticity has well the compound ice sense fiber of colored polyester-nylon mica of certain far infrared ability and the preparation method of the composite fibre.
To achieve the goals above, the present invention is designed with color and washs the compound ice sense fiber of bright and beautiful mica, including twists mutually
Together wash bright and beautiful mica fiber and ice silk fiber, wherein described, to wash bright and beautiful mica fiber be the outer cladding using polyester fiber as core wire
Nylon fibre forms, and the polyester fiber is described by weight including 90-95 parts of terylene, 3-5 parts of carbon fibers, 2-5 parts of modifying agent
Modifying agent includes 20-40 parts of micas, 10-15 parts of zirconium oxides, 30-40 parts of polyacrylamides, 2-5 parts of antimony glycols by weight;
The nylon fibre is described remote red by weight including 92-95 parts of polyamide fibres, 3-5 parts of Masterbatch, 2-5 parts of far infrared powder
Outer powder includes 40-50 parts of silica, 20-30 parts of zinc oxide, 5-10 parts of medical stones, 10-15 parts of molybdenum oxides, 2-3 by weight
Part tin oxide, 1-5 parts of talcum powder, 0.1-0.8 parts of rare earths;
The ice silk fiber by weight include 60-75 parts of poly- viscose rayons, 20-25 parts of chitin fibers, 1-2 portions of elasticator (elasticizer)s,
The elasticator (elasticizer) includes 40-50 parts of chlorinated polyethylene elastomers, 20-28 parts of polyurea elastomer, 3-5 parts of glass fibers by weight
Dimension, 1-2 parts of bismuth carboxylates, 5-7 parts of N-methylmorpholines.
The invention also discloses a kind of preparation methods of the compound ice sense fiber of colored polyester-nylon mica, include the following steps:
The first step:Prepare polyester fiber, first by 20-40 parts of micas, 10-15 parts of zirconium oxides, 30-40 parts of polyacrylamides, 2-5 parts
Antimony glycol is pulverized after mixing up to modifying agent, then by 90-95 parts of terylene, 3-5 parts of carbon fibers, 2-5 parts of modifications
Agent is uniformly mixed to be added in screw extruder and carries out melt extruded and obtain modified dacron melt, and temperature is 240-250 DEG C;
Second step:Far infrared powder is prepared, first by 40-50 parts of silica, 20-30 parts of zinc oxide, 5-10 parts of medical stones, 10-15
After part molybdenum oxide, 2-3 parts of tin oxide, 1-5 parts of talcum powder, 0.1-0.8 parts of rare earths heat 24 hours in reacting furnace, then ball milling
At powder to get far infrared powder;
Third walks:Bright and beautiful mica fiber is washed in preparation, is first mixed 92-95 parts of polyamide fibres, 3-5 parts of Masterbatch, 2-5 parts of far infrared powder equal
It is even be added in screw extruder carry out melt extruded obtain denaturation polyamide fibre melt, temperature be 300-320 DEG C, then pass through conjugation
Denaturation polyamide fibre melt coating outside the core wire of modified dacron melt is carried out wire drawing formation and washs bright and beautiful mica fiber by filament spinning component;
4th step:The compound ice sense fiber of colored polyester-nylon mica is prepared, first gathers 40-50 parts of chlorinated polyethylene elastomers, 20-28 parts
Urea elastomers, 3-5 part glass fibre, 1-2 parts of bismuth carboxylates, 5-7 parts of N-methylmorpholines mix after 5min again in high-speed mixer
It is put into after heating 2 h in 450 DEG C of heating furnace and takes out, grind into powder is to get elasticator (elasticizer) after cooling, then by 60-75 parts
Poly- viscose rayon, 20-25 part chitin fiber, extruding spinning obtains ice to 1-2 portions of elasticator (elasticizer)s after frit reaction 2h in extruder
Silk fiber will finally wash bright and beautiful mica fiber and ice silk fiber and obtain the compound ice sense fibre of colored polyester-nylon mica together with twisting mutually
Dimension.
The polyester fiber is that carbon fiber is added in terylene to increase its intensity, adds modifying agent to improve toughness.Institute
It states the mica in modifying agent and can be improved its mechanical strength, enhancing toughness, adhesive force is anti-aging and corrosion resistant type etc..Except with high
Electrical insulating property, antiacid caustic corrosion, elasticity, outside toughness and the performances such as sliding, heat-resistant sound-insulation, coefficient of thermal expansion be small, also have
The features such as surface is smooth, radius-thickness ratio is big, form is regular, strong adhesive force.Zirconium oxide can improve polyester fiber as inorganic powder
Intensity, cooperateed between simultaneous oxidation zirconium and mica, polyester fiber can be acted on simultaneously.Polyacrylamide has
Good flocculation, plays the role of connection.Antimony glycol can improve the performance of above-mentioned active ingredient as catalyst.
It is added with far infrared powder in the nylon fibre, to improve the far infrared ability of polyamide fibre, improves heat storage capacity.
Silica and zinc oxide in the far infrared powder can form silicon-zinc system, improve far infrared ability, medical stone and talcum
Powder is as additive, and to auxiliary silicon-zinc system, molybdenum oxide and tin oxide then improve the intensity and toughness of polyamide fibre, rare earth conduct
Catalyst can improve the far infrared ability of silicon-zinc system.
The ice silk fiber is to add chitin fiber and elasticator (elasticizer), wherein chitosan molecule band just in poly- viscose rayon
Electrically, it is adsorbed on cell surface, a floor height molecular film can be formed, prevents nutriment to intracellular transport, plays antibacterial
Effect.Chlorinated polyethylene elastomer and polyurea elastomer in elasticator (elasticizer) play as main elastomer and strengthen poly- viscose rayon
Elasticity, glass fibre mentions intensity, and bismuth carboxylate is as catalyst, the elasticity for improving chlorinated polyethylene elastomer, N- first
Base morpholine can improve the elasticity of polyurea elastomer.
The compound ice sense fiber of colored polyester-nylon mica that the present invention obtains, technique effect will be by that will wash bright and beautiful mica fiber and ice
Together, in addition described to wash bright and beautiful mica fiber be the outer cladding nylon fibre group using polyester fiber as core wire to silk fiber for twisting mutually
At so that various fibers carry out complementary, protrusion advantage, improve disadvantage, final composite fibre comfortable feel obtained, intensity is high,
There is certain far infrared ability.
Specific implementation mode
With reference to embodiment, the present invention is further described.
Embodiment 1:
The compound ice sense fiber of colored polyester-nylon mica provided in this embodiment, including twist mutually together wash bright and beautiful mica fiber and
Ice silk fiber, wherein described, to wash bright and beautiful mica fiber be the outer cladding nylon fibre composition using polyester fiber as core wire, and the terylene is fine
Dimension includes 90 parts of terylene, 3 parts of carbon fibers, 2 parts of modifying agent by weight, and the modifying agent includes 20 parts of micas, 10 by weight
Part zirconium oxide, 30 parts of polyacrylamides, 2 parts of antimony glycols;
The nylon fibre includes 92 parts of polyamide fibres, 3 parts of Masterbatch, 2 parts of far infrared powder by weight, and the far infrared powder is pressed
Parts by weight include 40 parts of silica, 20 parts of zinc oxide, 5 parts of medical stones, 10 parts of molybdenum oxides, 2 parts of tin oxide, 1 part of talcum powder, 0.5
Part rare earth;
The ice silk fiber includes 60 parts of poly- viscose rayons, 20 parts of chitin fibers, 1 portion of elasticator (elasticizer), the elasticity by weight
Agent includes 40 parts of chlorinated polyethylene elastomers, 20 parts of polyurea elastomer, 3 parts of glass fibres, 1 part of bismuth carboxylate, 5 parts of N- by weight
Methyl morpholine.
The invention also discloses a kind of preparation methods of the compound ice sense fiber of colored polyester-nylon mica, include the following steps:
The first step:Polyester fiber is prepared, first mixes 20 parts of micas, 10 parts of zirconium oxides, 30 parts of polyacrylamides, 2 parts of antimony glycols
It is pulverized after closing uniformly up to modifying agent, then 90 parts of terylene, 3 parts of carbon fibers, 2 parts of modifying agent is uniformly mixed and is added to spiral shell
Melt extruded is carried out in bar extruder and obtains modified dacron melt, and temperature is 240-250 DEG C;
Second step:Prepare far infrared powder, first by 40 parts of silica, 20 parts of zinc oxide, 5 parts of medical stones, 10 parts of molybdenum oxides, 2 parts
After tin oxide, 1 part of talcum powder, 0.5 part of rare earth heat 24 hours in reacting furnace, then ball is clayed into power to get far-infrared powder
End;
Third walks:Bright and beautiful mica fiber is washed in preparation, and first 92 parts of polyamide fibres, 3 parts of Masterbatch, 2 parts of far infrared powder are uniformly mixed and are added
Denaturation polyamide fibre melt is obtained to melt extruded is carried out in screw extruder, temperature is 300-320 DEG C, then passes through conjugate spinning group
Denaturation polyamide fibre melt coating outside the core wire of modified dacron melt is carried out wire drawing formation and washs bright and beautiful mica fiber by part;
4th step:The compound ice sense fiber of colored polyester-nylon mica is prepared, first by 40 parts of chlorinated polyethylene elastomers, 20 parts of polyureas elasticity
Body, 3 parts of glass fibres, 1 part of bismuth carboxylate, 5 parts of N-methylmorpholines mixed in high-speed mixer place into after 5min 450 DEG C plus
It is taken out after heating 2 h in hot stove, grind into powder is to get elasticator (elasticizer) after cooling, then by 60 parts of poly- viscose rayons, 20 parts of shells
Glycan fiber, extruding spinning obtains ice silk fiber to 1 portion of elasticator (elasticizer) after frit reaction 2h in extruder, and it is fine will finally to wash bright and beautiful mica
Twisting obtains the compound ice sense fiber of colored polyester-nylon mica to peacekeeping ice silk fiber together mutually.
Far infrared detection is carried out to the compound ice sense fiber of colored polyester-nylon mica obtained by the present embodiment, measures it in room temperature wavelength
Infrared emittance reaches 90% or more within the scope of 2-16, has preferable heat storage capacity.
Embodiment 2:
The compound ice sense fiber of colored polyester-nylon mica that the present embodiment is provided, raw material and preparation method are substantially identical with embodiment 1,
It includes 95 parts of terylene, 5 parts of carbon fibers, 5 parts of modifying agent, the modifying agent that its main distinction, which is the polyester fiber by weight,
Include 40 parts of micas, 15 parts of zirconium oxides, 40 parts of polyacrylamides, 5 parts of antimony glycols by weight.
Far infrared detection is carried out to the compound ice sense fiber of colored polyester-nylon mica obtained by the present embodiment, measures it in room temperature wavelength
Infrared emittance reaches 90% or more within the scope of 2-16, has preferable heat storage capacity.
Embodiment 3:
The compound ice sense fiber of colored polyester-nylon mica that the present embodiment is provided, raw material and preparation method are substantially identical with embodiment 1,
Its main distinction is the nylon fibre by weight and includes 95 parts of polyamide fibres, 5 parts of Masterbatch, 5 parts of far infrared powder, described remote
Infrared powder by weight include 50 parts of silica, 30 parts of zinc oxide, 10 parts of medical stones, 15 parts of molybdenum oxides, 3 parts of tin oxide, 5 parts
Talcum powder, 0.8 part of rare earth.
Far infrared detection is carried out to the compound ice sense fiber of colored polyester-nylon mica obtained by the present embodiment, measures it in room temperature wavelength
Infrared emittance reaches 90% or more within the scope of 2-16, has preferable heat storage capacity.
Embodiment 4:
The compound ice sense fiber of colored polyester-nylon mica that the present embodiment is provided, raw material and preparation method substantially with 1 phase of embodiment
Together, it includes 75 parts of poly- viscose rayons, 25 parts of chitin fibers, 2 parts of bullets that the main distinction, which is the ice silk fiber by weight,
Property agent, the elasticator (elasticizer) by weight include 50 parts of chlorinated polyethylene elastomers, 28 parts of polyurea elastomer, 5 parts of glass fibres, 2
Part bismuth carboxylate, 7 parts of N-methylmorpholines.
Far infrared detection is carried out to the compound ice sense fiber of colored polyester-nylon mica obtained by the present embodiment, measures it in room temperature wavelength
Infrared emittance reaches 90% or more within the scope of 2-16, has preferable heat storage capacity.
Claims (2)
1. a kind of compound ice sense fiber of colored polyester-nylon mica, it is characterised in that:Including twist mutually together to wash bright and beautiful mica fine
Peacekeeping ice silk fiber, wherein described, to wash bright and beautiful mica fiber be the outer cladding nylon fibre composition using polyester fiber as core wire, described to wash
Synthetic fibre fiber includes 90-95 parts of terylene, 3-5 parts of carbon fibers, 2-5 parts of modifying agent by weight, and the modifying agent includes by weight
20-40 parts of micas, 10-15 parts of zirconium oxides, 30-40 parts of polyacrylamides, 2-5 parts of antimony glycols;
The nylon fibre is described remote red by weight including 92-95 parts of polyamide fibres, 3-5 parts of Masterbatch, 2-5 parts of far infrared powder
Outer powder includes 40-50 parts of silica, 20-30 parts of zinc oxide, 5-10 parts of medical stones, 10-15 parts of molybdenum oxides, 2-3 by weight
Part tin oxide, 1-5 parts of talcum powder, 0.1-0.8 parts of rare earths;
The ice silk fiber by weight include 60-75 parts of poly- viscose rayons, 20-25 parts of chitin fibers, 1-2 portions of elasticator (elasticizer)s,
The elasticator (elasticizer) includes 40-50 parts of chlorinated polyethylene elastomers, 20-28 parts of polyurea elastomer, 3-5 parts of glass fibers by weight
Dimension, 1-2 parts of bismuth carboxylates, 5-7 parts of N-methylmorpholines.
2. the preparation method of the compound ice sense fiber of colored polyester-nylon mica according to claim 1, which is characterized in that including with
Lower step:
The first step:Prepare polyester fiber, first by 20-40 parts of micas, 10-15 parts of zirconium oxides, 30-40 parts of polyacrylamides, 2-5 parts
Antimony glycol is pulverized after mixing up to modifying agent, then by 90-95 parts of terylene, 3-5 parts of carbon fibers, 2-5 parts of modifications
Agent is uniformly mixed to be added in screw extruder and carries out melt extruded and obtain modified dacron melt, and temperature is 240-250 DEG C;
Second step:Far infrared powder is prepared, first by 40-50 parts of silica, 20-30 parts of zinc oxide, 5-10 parts of medical stones, 10-15
After part molybdenum oxide, 2-3 parts of tin oxide, 1-5 parts of talcum powder, 0.1-0.8 parts of rare earths heat 24 hours in reacting furnace, then ball milling
At powder to get far infrared powder;
Third walks:Bright and beautiful mica fiber is washed in preparation, is first mixed 92-95 parts of polyamide fibres, 3-5 parts of Masterbatch, 2-5 parts of far infrared powder equal
It is even be added in screw extruder carry out melt extruded obtain denaturation polyamide fibre melt, temperature be 300-320 DEG C, then pass through conjugation
Denaturation polyamide fibre melt coating outside the core wire of modified dacron melt is carried out wire drawing formation and washs bright and beautiful mica fiber by filament spinning component;
4th step:The compound ice sense fiber of colored polyester-nylon mica is prepared, first gathers 40-50 parts of chlorinated polyethylene elastomers, 20-28 parts
Urea elastomers, 3-5 part glass fibre, 1-2 parts of bismuth carboxylates, 5-7 parts of N-methylmorpholines mix after 5min again in high-speed mixer
It is put into after heating 2 h in 450 DEG C of heating furnace and takes out, grind into powder is to get elasticator (elasticizer) after cooling;Then by 60-75 parts
Poly- viscose rayon, 20-25 part chitin fiber, extruding spinning obtains ice to 1-2 portions of elasticator (elasticizer)s after frit reaction 2h in extruder
Silk fiber will finally wash bright and beautiful mica fiber and ice silk fiber and obtain the compound ice sense fibre of colored polyester-nylon mica together with twisting mutually
Dimension.