CN108530983A - A kind of ionomer ink - Google Patents
A kind of ionomer ink Download PDFInfo
- Publication number
- CN108530983A CN108530983A CN201710122110.9A CN201710122110A CN108530983A CN 108530983 A CN108530983 A CN 108530983A CN 201710122110 A CN201710122110 A CN 201710122110A CN 108530983 A CN108530983 A CN 108530983A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- ink
- emulsion
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of ionomer ink, component includes by weight:Acrylic resin liquid, not filming emulsion, filming emulsion, waterborne wax emulsion, pigment, water, antifoaming agent, wetting agent, levelling agent, dispersant, titanate coupling agent, PH conditioning agents, zinc amine complex ion.The present invention rationally controls the content of each component, and proportioning is simple, and easy to use, one-component is easy to use, increases considerably the water resistance and other performances of ink, and water resistance improves 1000%, and resistance to ethyl alcohol improves 100%, and cost reduction 50%, rate of drying improves 30%.
Description
Technical field
The present invention relates to printing technical field of ink more particularly to a kind of ionomer inks.
Background technology
With the development of economy, printing packaging industry development is swift and violent, as the indispensable material of printing packaging pattern printing, oil
The demand of ink constantly increases, and the output of ink also constantly improves, and ink industry has huge development space, still
Because the contained toxic solvent of ink itself and heavy metal have very bad shadow to the pollution of environment and to health
It rings.So needing the developing direction that a kind of ink substitute harmless to environment and people's health is following.And ink is had
Environment protection health the characteristics of by be ink substitute.
For ink due to being free of volatile organic solvent, the solvent used is water rather than organic solvent.It is nonflammable,
Ink is stablized, bright in luster, does not corrode plate, easy to operate, cheap, adhesive force is good after print, greatly reduces organic wave
The discharge of hair object VOC improves the environment of press operator, is conducive to worker health to alleviate atmosphere pollution.It can
To completely eliminate certain poisonous and harmful substances in solvent-based ink, the harm to human body and the pollution to being packaged commodity are eliminated,
Improve overall environmental quality, is required strictly especially suitable for sanitary conditions such as cigarette, wine, food, beverage, drug, toys for children
Packaging Printing Product.It, can be in addition, it can not only reduce fire hazard and hidden danger caused by electrostatic and flammable solvent
The toxicity of printing remained on surface is reduced, and is convenient for cleaning of graphic arts equipment.It is universally acknowledged environment-friendly type printing material, and at present
The ink uniquely approved through international food drug association in all printing ink.
The current patented technology in relation to ink is more, and Related product is also more in the market, but we have tried out in the market
A large amount of sample finds mainly there is Railway Project at present:At present all there is high, the good valence of use environment requirement in water-based ink
Lattice are very expensive to be popularized, the drawbacks such as a bit cheaper not alkali resistant, not anti-second alcohol and water, dry slow, low in glossiness.These problems
Principal element is that main material lotion and water-base resin cause in ink, and so that ink is dissolved in water just must hydrophilic carboxyl base
Group, but this causes a series of defects and problem of ink again, solves the problems, such as that this main method uses certainly currently on the market
The method of crosslinked emulsions and additional curing agent, self-crossing emulsion price height are higher to printing environment temperature requirement, and only temperature is high
Self-crosslinking can just occur when certain value.Additional curing agent belongs to two-component materials at using very trouble inconvenient, and we
What is done is exactly to solve the problems, such as this, manufactures that a kind of performance is good cheap to require low one-component to be crosslinked ink use environment
Technology.
All there is use environment for ink currently on the market and require height, good price is very expensive to be popularized, cheaper
Not alkali resistant, not anti-second alcohol and water, the drawbacks such as dry slow, low in glossiness.We are theoretically largely studied first, really
A kind of fixed cheap, high performance formula for improving ink performance, then by a large amount of arduous again and again experiment, finally at
Work(develops " ionomer ink " formula, efficiently solves the problems, such as that ink exists.
Invention content
The purpose of the present invention is to solve disadvantages existing in the prior art, and a kind of ionomer ink proposed.
A kind of ionomer ink proposed by the present invention, component include by weight:
25-35 parts of acrylic resin liquid, not filming emulsion 8-12 parts, 17-23 parts of filming emulsion, 1-3 parts of waterborne wax emulsion,
12-18 parts of pigment, 14-18 parts of water, 0.3-0.8 parts of antifoaming agent, 0.1-0.5 parts of wetting agent, 0.1-0.4 parts of levelling agent, dispersant
0.5-1.5 parts, 0.5-1.5 parts of titanate coupling agent, 0.5-1.5 parts of PH conditioning agents, 1-5 parts of zinc amine complex ion.
Preferably, acrylic resin liquid, not filming emulsion, filming emulsion, waterborne wax emulsion weight ratio be 27-32:9-
11:19-21:1.5-2.5.
Preferably, pigment, water weight ratio be 14-16: 15-17.
Preferably, antifoaming agent, wetting agent, levelling agent, dispersant weight ratio be 0.4-0.6:0.2-0.4:0.2-0.3:
0.8-1.2。
Preferably, titanate coupling agent, PH conditioning agents, zinc amine complex ion weight ratio be 0.8-1.2:0.8-1.2:2-4.
Preferably, component includes by weight:
27-32 parts of acrylic resin liquid, not filming emulsion 9-11 parts, 19-21 parts of filming emulsion, waterborne wax emulsion 1.5-
2.5 parts, 14-16 parts of pigment, 15-17 parts of water, 0.4-0.6 parts of antifoaming agent, 0.2-0.4 parts of wetting agent, 0.2-0.3 parts of levelling agent,
0.8-1.2 parts of dispersant, 0.8-1.2 parts of titanate coupling agent, 0.8-1.2 parts of PH conditioning agents, 2-4 parts of zinc amine complex ion.
The present invention by adding said components, and rationally controls the content of each component, and proportioning is simple, easy to use, single group
Part is easy to use, increases considerably the water resistance and other performances of ink, and water resistance improves 1000%, and resistance to ethyl alcohol improves 100%,
Cost reduction 50%, rate of drying improve 30%.
Specific implementation mode
With reference to specific embodiment, the present invention will be further described.
Embodiment 1
A kind of ionomer ink, component include by weight:
25 parts of acrylic resin liquid, not 8 parts of filming emulsion, 17 parts of filming emulsion, 1 part of waterborne wax emulsion, 12 parts of pigment, water
14 parts, 0.3 part of antifoaming agent, 0.1 part of wetting agent, 0.1 part of levelling agent, 0.5 part of dispersant, 0.5 part of titanate coupling agent, PH adjust
0.5 part of agent, 1 part of zinc amine complex ion.
Embodiment 2
A kind of ionomer ink, component include by weight:
28 parts of acrylic resin liquid, not 9 parts of filming emulsion, 18 parts of filming emulsion, 1.5 parts of waterborne wax emulsion, 13 parts of pigment,
15 parts of water, 0.4 part of antifoaming agent, 0.2 part of wetting agent, 0.15 part of levelling agent, 0.8 part of dispersant, 0.8 part of titanate coupling agent, PH
0.8 part of conditioning agent, 2 parts of zinc amine complex ion.
Embodiment 3
A kind of ionomer ink, component include by weight:
30 parts of acrylic resin liquid, not 10 parts of filming emulsion, 20 parts of filming emulsion, 15 parts of pigment, 16 parts of water, water-borne wax breast
2 parts of liquid, 0.5 part of antifoaming agent, 0.3 part of wetting agent, 0.2 part of levelling agent, 1 part of dispersant, 1 part of titanate coupling agent, PH conditioning agents 1
Part, 3 parts of zinc amine complex ion.
Embodiment 4
A kind of ionomer ink, component include by weight:
32 parts of acrylic resin liquid, not 11 parts of filming emulsion, 21 parts of filming emulsion, 2.5 parts of waterborne wax emulsion, pigment 15
Part, 17 parts of water, 0.6 part of antifoaming agent, 0.4 part of wetting agent, 0.3 part of levelling agent, 1.2 parts of dispersant, 1.2 parts of titanate coupling agent,
1.2 parts of PH conditioning agents, 4 parts of zinc amine complex ion.
Embodiment 5
A kind of ionomer ink, component include by weight:
35 parts of acrylic resin liquid, not 12 parts of filming emulsion, 23 parts of filming emulsion, 3 parts of waterborne wax emulsion, 18 parts of pigment,
18 parts of water, 0.8 part of antifoaming agent, 0.5 part of wetting agent, 0.4 part of levelling agent, 1.5 parts of dispersant, 1.5 parts of titanate coupling agent, PH tune
Save 1.5 parts of agent, 5 parts of zinc amine complex ion.
In conclusion optimal component is:
30 parts of acrylic resin liquid, not 10 parts of filming emulsion, 20 parts of filming emulsion, 15 parts of pigment, 16 parts of water, water-borne wax breast
2 parts of liquid, 0.5 part of antifoaming agent, 0.3 part of wetting agent, 0.2 part of levelling agent, 1 part of dispersant, 1 part of titanate coupling agent, PH conditioning agents 1
Part, 3 parts of zinc amine complex ion.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (6)
1. a kind of ionomer ink, which is characterized in that its component includes by weight:
25-35 parts of acrylic resin liquid, not filming emulsion 8-12 parts, 17-23 parts of filming emulsion, 1-3 parts of waterborne wax emulsion, pigment
12-18 parts, 14-18 parts of water, 0.3-0.8 parts of antifoaming agent, 0.1-0.5 parts of wetting agent, 0.1-0.4 parts of levelling agent, dispersant 0.5-
1.5 parts, 0.5-1.5 parts of titanate coupling agent, 0.5-1.5 parts of PH conditioning agents, 1-5 parts of zinc amine complex ion.
2. ionomer ink according to claim 1, which is characterized in that acrylic resin liquid, not filming emulsion, film forming
Lotion, the weight ratio of waterborne wax emulsion are 27-32:9-11:19-21:1.5-2.5.
3. ionomer ink according to claim 1, which is characterized in that pigment, water weight ratio be 14-16:15-
17。
4. ionomer ink according to claim 1, which is characterized in that antifoaming agent, wetting agent, levelling agent, dispersant
Weight ratio be 0.4-0.6:0.2-0.4:0.2-0.3:0.8-1.2.
5. ionomer ink according to claim 1, which is characterized in that titanate coupling agent, PH conditioning agents, zinc amine network
The weight ratio of ion is 0.8-1.2: 0.8-1.2: 2-4.
6. according to claim 1-5 any one of them ionomer inks, which is characterized in that its component includes by weight:
27-32 parts of acrylic resin liquid, not filming emulsion 9-11 parts, 19-21 parts of filming emulsion, 1.5-2.5 parts of waterborne wax emulsion,
14-16 parts of pigment, 15-17 parts of water, 0.4-0.6 parts of antifoaming agent, 0.2-0.4 parts of wetting agent, 0.2-0.3 parts of levelling agent, dispersant
0.8-1.2 parts, 0.8-1.2 parts of titanate coupling agent, 0.8-1.2 parts of PH conditioning agents, 2-4 parts of zinc amine complex ion.