CN108505344A - A kind of waterproof and breathable composite material - Google Patents

A kind of waterproof and breathable composite material Download PDF

Info

Publication number
CN108505344A
CN108505344A CN201810297262.7A CN201810297262A CN108505344A CN 108505344 A CN108505344 A CN 108505344A CN 201810297262 A CN201810297262 A CN 201810297262A CN 108505344 A CN108505344 A CN 108505344A
Authority
CN
China
Prior art keywords
parts
fiber
composite material
waterproof
layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810297262.7A
Other languages
Chinese (zh)
Inventor
王益贵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Foshan Gui Li Garment Material Co Ltd
Original Assignee
Foshan Gui Li Garment Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Foshan Gui Li Garment Material Co Ltd filed Critical Foshan Gui Li Garment Material Co Ltd
Priority to CN201810297262.7A priority Critical patent/CN108505344A/en
Publication of CN108505344A publication Critical patent/CN108505344A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of waterproof and breathable composite material, composite material is made of waterproof layer, filter layer and ventilative internal layer, wherein：The waterproof layer is made of following composition by weight：24 28 parts of aqueous polyurethane, 8 12 parts of polyethylene, 6 10 parts of polylactic acid, 26 parts of antioxidant, 0.5 0.8 parts of surfactant, 15 25 parts of organic solvent；The filter layer is made of following composition by weight：25 35 parts of carbon nano-fiber, 12 17 parts of nano-far-infrared polyester staple fiber, 49 parts of nanometer polyester fiber；The ventilative internal layer is made of following composition by weight：25 35 parts of cotton, 14 22 parts of polyester fiber, 10 16 parts of bamboo charcoal fiber.A kind of waterproof and breathable composite material of the present invention, this composite material not only characteristic with waterproof, can prevent water penetration garment interior, cause uncomfortable but also ventilative, can comfortably be felt to people with deodorization.

Description

A kind of waterproof and breathable composite material
Technical field
The present invention relates to cloth textile field more particularly to a kind of waterproof and breathable composite materials.
Background technology
Clothes ancient times as Cold-resisting article, but with the development of society, people give more meanings to it, such as： Have the function of hushing up a scandal, the function of logo image, embody and reflect certain technology development level, reflection certain culture intension Function.
Clothes is final or to return the effect of its essence, and resisting cold is warming, pursues the function of practical function.
Existing many clothes fabric has its specific characteristic, such as：Antibacterial, anti-sweat, is breathed freely at waterproof.
But existing fabric characteristics are relatively simple, and by taking waterproof as an example, work(of the existing cloth textile tool if there is waterproof Can, then its fabric is airtight, and rainwater is kept out outside, does not have ventilative and deodorization function thus；Existing clothing If take fabric have the function of it is ventilative, must hole, could breathe freely, result in water that can also penetrate in this way, be not achieved The function of waterproof.Thus present cloth textile cannot reach the advantages of waterproof and breathable simultaneously, and function is relatively simple.
Invention content
In view of this, the present invention provides a kind of waterproof and breathable composite materials.
A kind of waterproof and breathable composite material, the composite material are made of waterproof layer, filter layer and ventilative internal layer, In：
The waterproof layer is made of following composition by weight：
The filter layer is made of following composition by weight：
12-17 parts of nano-far-infrared polyester staple fiber of 25-35 parts of carbon nano-fiber
4-9 parts of polyester fiber of nanometer；
The ventilative internal layer is made of following composition by weight：
14-22 parts of polyester fiber of 25-35 parts of cotton
10-16 parts of bamboo charcoal fiber.
Preferably, the waterproof layer is made of following composition by weight：
Preferably, the antioxidant is one kind in diphenylamines, p-phenylenediamine and dihydroquinoline.
Preferably, the surfactant is one in stearic acid, neopelex and fatty glyceride Kind.
Preferably, the organic solvent is ethyl alcohol or isopropanol.
Preferably, the filter layer is made of following composition by weight：
14-16 parts of nano-far-infrared polyester staple fiber of 27-32 parts of carbon nano-fiber
5-8 parts of polyester fiber of nanometer.
Preferably, the ventilative internal layer is made of following composition by weight：
16-21 parts of polyester fiber of 28-31 parts of cotton
12-15 parts of bamboo charcoal fiber.
A kind of waterproof and breathable composite material of the present invention, this composite material not only have the characteristic of waterproof, can prevent water It on the inside of impervious garment, causes uncomfortable but also ventilative, can comfortably be felt to people with deodorization.
Specific implementation mode
Below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described, Obviously, described embodiments are some of the embodiments of the present invention, instead of all the embodiments.Based on the implementation in the present invention Example, every other embodiment obtained by those of ordinary skill in the art without making creative efforts belong to The scope of protection of the invention.
It should be appreciated that ought use in this specification and in the appended claims, term " comprising " and "comprising" instruction Described feature, entirety, step, operation, the presence of element and/or component, but one or more of the other feature, whole is not precluded Body, step, operation, element, component and/or its presence or addition gathered.
It will be further appreciated that the term "and/or" used in description of the invention and the appended claims is Refer to any combinations and all possible combinations of one or more of associated item listed, and includes these combinations.
Embodiment 1
Waterproof and breathable composite material, composite material are made of waterproof layer, filter layer and ventilative internal layer, wherein：
Waterproof layer is made of following composition by weight：
Filter layer is made of following composition by weight：
25 parts of carbon nano-fiber, 17 parts of nano-far-infrared polyester staple fiber
9 parts of polyester fiber of nanometer；
Ventilative internal layer is made of following composition by weight：
35 parts of cotton, 14 parts of polyester fiber
10 parts of bamboo charcoal fiber.
Preparation method is：
The preparation of waterproof layer：
Weigh aqueous polyurethane, polyethylene, polylactic acid, diphenylamines, stearic acid, the ethyl alcohol of group component；
Ethyl alcohol is added into reaction kettle, is heated, heating rate is 5 DEG C/min, is heated to 60 DEG C；
Aqueous polyurethane, polyethylene and polylactic acid are added into reaction kettle, turn on agitator, mixing speed is 400r/min stirs 15min；
Diphenylamines and stearic acid are added into reaction kettle, 30min is reacted, obtains waterproof layer material.
The preparation of filter layer：
Carbon nano-fiber, nano-far-infrared polyester staple fiber and nanometer polyester fiber three are added to twin-screw extrusion It in machine, is mixed, then carries out spinning, woven, obtain filter layer.
The preparation of ventilative internal layer：
Cotton, polyester fiber and bamboo charcoal fiber are subjected to shuffling, obtain ventilative internal layer.
Filter layer and ventilative internal layer are subjected to die casting, are combined, waterproof layer material is coated in filter layer side, is smeared Uniformly, composite material is obtained.
Embodiment 2
Waterproof and breathable composite material, composite material are made of waterproof layer, filter layer and ventilative internal layer, wherein：
Waterproof layer is made of following composition by weight：
Filter layer is made of following composition by weight：
32 parts of carbon nano-fiber, 14 parts of nano-far-infrared polyester staple fiber
8 parts of polyester fiber of nanometer；
Ventilative internal layer is made of following composition by weight：
28 parts of cotton, 21 parts of polyester fiber
15 parts of bamboo charcoal fiber；
Preparation method is：
The preparation of waterproof layer：
Weigh the aqueous polyurethane of group component, polyethylene, polylactic acid, p-phenylenediamine, neopelex, isopropyl Alcohol；
Isopropanol is added into reaction kettle, is heated, heating rate is 3 DEG C/min, is heated to 64 DEG C；
Aqueous polyurethane, polyethylene and polylactic acid are added into reaction kettle, turn on agitator, mixing speed is 380r/min stirs 12min；
P-phenylenediamine and neopelex are added into reaction kettle, 27min is reacted, obtains waterproof layer material Material.
The preparation of filter layer：
Carbon nano-fiber, nano-far-infrared polyester staple fiber and nanometer polyester fiber three are added to twin-screw extrusion It in machine, is mixed, then carries out spinning, woven, obtain filter layer.
The preparation of ventilative internal layer：
Cotton, polyester fiber and bamboo charcoal fiber are subjected to shuffling, obtain ventilative internal layer.
Filter layer and ventilative internal layer are subjected to die casting, are combined, waterproof layer material is coated in filter layer side, is smeared Uniformly, composite material is obtained.
Embodiment 3
Waterproof and breathable composite material, composite material are made of waterproof layer, filter layer and ventilative internal layer, wherein：
Waterproof layer is made of following composition by weight：
Filter layer is made of following composition by weight：
35 parts of carbon nano-fiber, 12 parts of nano-far-infrared polyester staple fiber
4 parts of polyester fiber of nanometer；
Ventilative internal layer is made of following composition by weight：
25 parts of cotton, 22 parts of polyester fiber
16 parts of bamboo charcoal fiber.
Preparation method is：
The preparation of waterproof layer：
Weigh aqueous polyurethane, polyethylene, polylactic acid, dihydroquinoline, fatty glyceride, the ethyl alcohol of group component；
Ethyl alcohol is added into reaction kettle, is heated, heating rate is 2 DEG C/min, is heated to 75 DEG C；
Aqueous polyurethane, polyethylene and polylactic acid are added into reaction kettle, turn on agitator, mixing speed is 300r/min stirs 5min；
Dihydroquinoline and fatty glyceride are added into reaction kettle, 20min is reacted, obtains waterproof layer material.
The preparation of filter layer：
Carbon nano-fiber, nano-far-infrared polyester staple fiber and nanometer polyester fiber three are added to twin-screw extrusion It in machine, is mixed, then carries out spinning, woven, obtain filter layer.
The preparation of ventilative internal layer：
Cotton, polyester fiber and bamboo charcoal fiber are subjected to shuffling, obtain ventilative internal layer.
Filter layer and ventilative internal layer are subjected to die casting, are combined, waterproof layer material is coated in filter layer side, is smeared Uniformly, composite material is obtained.
Embodiment 4
Waterproof and breathable composite material, composite material are made of waterproof layer, filter layer and ventilative internal layer, wherein：
Waterproof layer is made of following composition by weight：
Filter layer is made of following composition by weight：
27 parts of carbon nano-fiber, 16 parts of nano-far-infrared polyester staple fiber
5 parts of polyester fiber of nanometer；
Ventilative internal layer is made of following composition by weight：
31 parts of cotton, 16 parts of polyester fiber
12 parts of bamboo charcoal fiber；
Preparation method is：
The preparation of waterproof layer：
Weigh the aqueous polyurethane of group component, polyethylene, polylactic acid, p-phenylenediamine, neopelex, isopropyl Alcohol；
Isopropanol is added into reaction kettle, is heated, heating rate is 4 DEG C/min, is heated to 71 DEG C；
Aqueous polyurethane, polyethylene and polylactic acid are added into reaction kettle, turn on agitator, mixing speed is 330r/min stirs 7min；
P-phenylenediamine and neopelex are added into reaction kettle, 23min is reacted, obtains waterproof layer material Material.
The preparation of filter layer：
Carbon nano-fiber, nano-far-infrared polyester staple fiber and nanometer polyester fiber three are added to twin-screw extrusion It in machine, is mixed, then carries out spinning, woven, obtain filter layer.
The preparation of ventilative internal layer：
Cotton, polyester fiber and bamboo charcoal fiber are subjected to shuffling, obtain ventilative internal layer.
Filter layer and ventilative internal layer are subjected to die casting, are combined, waterproof layer material is coated in filter layer side, is smeared Uniformly, composite material is obtained.
Embodiment 5
Waterproof and breathable composite material, composite material are made of waterproof layer, filter layer and ventilative internal layer, wherein：
Waterproof layer is made of following composition by weight：
Filter layer is made of following composition by weight：
29 parts of carbon nano-fiber, 15 parts of nano-far-infrared polyester staple fiber
7 parts of polyester fiber of nanometer；
Ventilative internal layer is made of following composition by weight：
29 parts of cotton, 19 parts of polyester fiber
14 parts of bamboo charcoal fiber；
Preparation method is：
The preparation of waterproof layer：
Weigh aqueous polyurethane, polyethylene, polylactic acid, diphenylamines, fatty glyceride, the ethyl alcohol of group component；
Ethyl alcohol is added into reaction kettle, is heated, heating rate is 4 DEG C/min, is heated to 68 DEG C；
Aqueous polyurethane, polyethylene and polylactic acid are added into reaction kettle, turn on agitator, mixing speed is 370r/min stirs 9min；
Diphenylamines and fatty glyceride are added into reaction kettle, 25min is reacted, obtains waterproof layer material.
The preparation of filter layer：
Carbon nano-fiber, nano-far-infrared polyester staple fiber and nanometer polyester fiber three are added to twin-screw extrusion It in machine, is mixed, then carries out spinning, woven, obtain filter layer.
The preparation of ventilative internal layer：
Cotton, polyester fiber and bamboo charcoal fiber are subjected to shuffling, obtain ventilative internal layer.
Filter layer and ventilative internal layer are subjected to die casting, are combined, waterproof layer material is coated in filter layer side, is smeared Uniformly, composite material is obtained.
The composite material of embodiment 1 to 5, tests its performance, and results of property is as follows：
By counting table above, it can be seen that this composite material permeability rate is especially low, can guard against 99.5% or more water, and Good air permeability, intensity is high, and tearing toughness is high, durable.
The steps in the embodiment of the present invention can be sequentially adjusted, merged and deleted according to actual needs.
It is described in detail herein, applies specific case and the principle of the present invention and embodiment are explained It states, above example is merely used to help understand the method and its core concept of the present invention；Meanwhile for the general skill of this field Art personnel, according to the thought of the present invention, there will be changes in the specific implementation manner and application range, in conclusion this Description should not be construed as limiting the invention.

Claims (7)

1. a kind of waterproof and breathable composite material, which is characterized in that the composite material is by waterproof layer, filter layer and ventilative internal layer Composition, wherein：
The waterproof layer is made of following composition by weight：
The filter layer is made of following composition by weight：
12-17 parts of nano-far-infrared polyester staple fiber of 25-35 parts of carbon nano-fiber
4-9 parts of polyester fiber of nanometer；
The ventilative internal layer is made of following composition by weight：
14-22 parts of polyester fiber of 25-35 parts of cotton
10-16 parts of bamboo charcoal fiber.
2. composite material according to claim 1, it is characterised in that：The waterproof layer is by weight by following composition group At：
3. composite material according to claim 2, it is characterised in that：The antioxidant be diphenylamines, p-phenylenediamine and One kind in dihydroquinoline.
4. composite material according to claim 2, it is characterised in that：The surfactant is stearic acid, dodecyl One kind in benzene sulfonic acid sodium salt and fatty glyceride.
5. composite material according to claim 2, it is characterised in that：The organic solvent is ethyl alcohol or isopropanol.
6. composite material according to claim 1, it is characterised in that：The filter layer is by weight by following composition group At：
14-16 parts of nano-far-infrared polyester staple fiber of 27-32 parts of carbon nano-fiber
5-8 parts of polyester fiber of nanometer.
7. composite material according to claim 1, it is characterised in that：The ventilative internal layer is by weight by following composition Composition：
16-21 parts of polyester fiber of 28-31 parts of cotton
12-15 parts of bamboo charcoal fiber.
CN201810297262.7A 2018-04-04 2018-04-04 A kind of waterproof and breathable composite material Withdrawn CN108505344A (en)