CN108497621A - A kind of pregnant woman's Special shoe pad - Google Patents
A kind of pregnant woman's Special shoe pad Download PDFInfo
- Publication number
- CN108497621A CN108497621A CN201810410952.9A CN201810410952A CN108497621A CN 108497621 A CN108497621 A CN 108497621A CN 201810410952 A CN201810410952 A CN 201810410952A CN 108497621 A CN108497621 A CN 108497621A
- Authority
- CN
- China
- Prior art keywords
- insole
- layer
- half sole
- pregnant woman
- heel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of pregnant woman's Special shoe pads, including insole body, from the front end of insole body to rear end, include waist and insole heel in insole half sole, the insole pad heart, insole successively, 4~10 horizontal type grooves and 2~10 perpendicular type grooves are arranged on the upside of insole half sole, the downside of insole half sole is equipped with half sole beam, and half sole beam shape is spur blade profile；The upside that insole pads the heart is equipped with ovum type convex surface, and ovum type convex surface is equipped with pad heart damping spiral grooves；The both sides of waist up tilt respectively in insole, and the downside of waist corresponds to the flexible shield foot of position setting of human body arch portion in insole；Round convex surface is equipped on the upside of the middle part of insole heel, the outer of insole heel up tilts, and tilts tilting height of the height less than waist both sides in insole, back heel shock-absorbing pad is equipped on the downside of the middle part of insole heel.Damping of the present invention shield foot effect is strong, can alleviate that medicine, skid resistance are good, can prevent ankle injury, can health care massage.
Description
Technical field
The present invention relates to a kind of insole, more particularly to a kind of pregnant woman's Special shoe pad.
Background technology
Pregnant woman refers to just that woman is pregnant, son of giving birth to a child soon, prepares to work as mother, so being known as " pregnant woman ".Letter
For it, " pregnant woman " is videlicet by the woman of childbirth.
Pregnant woman, which should be noted that, to strike a proper balance between work and rest, and should not be engaged in heavy physical labour and the excessive work of the amount of labour；Also it is unfit to do and squats down
Or long-time stoop labour influences blood circulation because this posture can increase abdominal pressure, oppresses fetus, its unfavorable life
Long development, but it is motionless also to sit quietly.Pregnant woman should do as usual working, participate in light physical labor, and being for chore completely can be with
Competent.Appropriate activity can promote blood circulation and metabolism, enhances cardio-pulmonary function, and useful for sleeping can mitigate waist and leg ache
And prevent or mitigate edema of lower extremity, so that the muscular strength of whole body is increased, is conducive to give a birth.In the early, middle and late phase of pregnancy, in abdomen
The continuous growth of fetus, pregnant woman is in order to adapt to movable needs of each period, it is accordingly required in particular to which a comfort level is high and can meet respectively
The insole of the class environment of an activation.
Insole be apply very universal articles for daily use, by effect point, insole can be divided into health insoles, functional insole and often
Advise insole.Since pregnant woman's pregnancy leads to the stray arrow of internal calcium, bone calcium deficiency is serious, has fragility, therefore, pregnant woman is larger
During amplitude event, foot bones are easy injury, or even cracking.The structure of traditional pregnant woman's insole is that multilayer cloth sews
Either multilayer leather is suppressed, and with certain pliability and shock absorbing effect, substantially conforms to each period that is pregnant
The demand of usual stroll wear shoes.But when pregnant woman has movable by a relatively large margin, traditional sock is then not suitable for dangerous, has such as
Lower disadvantage：One, damping, shield foot effect it is poor, when movable, foot's half sole and followed by bottom impact force it is big, traditional sock is difficult to
Absorb the impact force generated to foot bones in walking, active procedure, it is difficult to protect vola bone, ankle-joint and knee joint；Its
Two, medicine can not be alleviated without effect to arch portion；Thirdly, skid resistance it is poor, be unfavorable for toe stretching, extension, grab ground；Four, pass
Insole each section thickness of uniting is almost the same, it is difficult to which the problem of preventing ankle injury is easy to cause sprain the ankle；Five, traditional sock is not
With health care massage effect, the mood of pregnant woman cannot be pacified well；It six：Substantially memory bubble is not used in existing insole
Silk floss, though have it is individual continuous using memory bubble but if without using promoting blood circulation, the functions such as resistance building.
Invention content
The technical problem to be solved by the present invention is in view of the above shortcomings of the prior art, provide a kind of damping shield foot effect
By force, can alleviate medicine, skid resistance are good, can prevent ankle injury, can health care massage pregnant woman's Special shoe pad.
In order to solve the above technical problems, the technical scheme is that：A kind of pregnant woman's Special shoe pad, including insole body,
From the front end of insole body to rear end, exist successively including waist in insole half sole, the insole pad heart, insole and insole heel, feature
In：It is arranged with 4~10 horizontal type grooves and 2~10 perpendicular type grooves on the upside of the insole half sole, the horizontal type groove and perpendicular
Type groove extends respectively to the both ends of insole half sole, and the downside of the insole half sole is equipped with half sole beam, the half sole damping
Pulvilliform shape is spur blade profile；The upside of the insole pad heart is equipped with ovum type convex surface, and ovum type convex surface is equipped with pad heart damping spiral goove
Slot；The both sides of waist up tilt respectively in the insole, and the downside of waist corresponds to the position setting of human body arch portion in insole
Flexible shield foot, the elasticity shield foot is around waist in entire insole；It is equipped on the upside of the middle part of the insole heel round convex
Face, the round convex surface are equipped with back heel shock-absorbing spiral grooves, and the outer of the insole heel up tilts, and it is low to tilt height
The middle part downside of the tilting height of waist both sides in insole, the insole heel is equipped with back heel shock-absorbing pad, the shape of back heel shock-absorbing pad
Shape is corresponding with the shape on round convex surface.
It is expanded on further as to the present invention：
Preferably, 5~9 horizontal type grooves and 2~8 perpendicular type grooves are arranged on the upside of the insole half sole；The heel subtracts
Convex grain of the shake pad equipped with multiple upper flats.
Preferably, the insole body includes nanometer bamboo carbon fiber layer, the first polyurethane slow rebound layer successively from top to bottom
And the second polyurethane slow rebound layer；The thickness of the nanometer bamboo carbon fiber layer is 0.3~0.8mm, and first polyurethane slow returns
The thickness of bullet layer is 3~6mm, and the thickness of the second polyurethane slow rebound layer is 3~6mm.
Preferably, it is respectively equipped with preceding accommodating cavity, middle accommodating cavity on the downside of the second polyurethane slow rebound layer and houses afterwards
Chamber, before the half sole beam is set in accommodating cavity, the elasticity shield foot is set in middle accommodating cavity, the back heel shock-absorbing pad edge
In in rear accommodating cavity.
Preferably, the first polyurethane slow rebound layer and the second polyurethane slow rebound layer are that polyether-type remembers foam sponge layer；
The thickness of the half sole beam is 2~10mm, and the thickness of the back heel shock-absorbing pad is 3~12mm.
Preferably, the first polyurethane slow rebound layer and the second polyurethane slow rebound layer are made of the following raw material reaction foaming
's：First 50 parts of polyether polyol, the second 45 parts of polyether polyol, 5~15 parts of methyl diphenylene diisocyanate, spiny jujuba seed powder
1~3 part, 0.8~2.5 part of cortex albiziae powder, 1~3 part of glossy ganoderma powder, 2~13 parts of water, 0.5~3 part of silicone oil, 0.2~1 part of catalyst,
0.5~1 part of foaming agent, 2~5 parts of crosslinking agent.
Preferably, the preparation method of the first polyurethane slow rebound layer and the second polyurethane slow rebound layer is：By corresponding weight
First polyether polyol of number, the second polyether polyol, methyl diphenylene diisocyanate, spiny jujuba seed powder, cortex albiziae powder and
Glossy ganoderma powder is added in mixer and stirs evenly, and is heated to 35~38 degrees Celsius, other raw materials of corresponding number are added to
In mixer, high-speed stirred is poured into after 6~8 seconds after mold foams and cure, and obtains remembering foam sponge layer accordingly；Described first
The hydroxyl value of polyether polyol is 70~90 mgKOH/g, and molecular weight is 8000~10000, the hydroxyl value of second polyether polyol
For 55~70 mgKOH/g, molecular weight is 4500~7000, and the silicone oil is BF-2370 and two kinds of mass ratioes of B-4900 are 3：1
Mixture；The catalyst is N, and N- dimethylaminoethyl-N- methyl amino ethanols and acetylacetone,2,4-pentanedione zirconium mass ratio are 0.5：1
Mixture；The foaming agent is carbon black；Crosslinking agent is that ethylenediamine and triethylene glycol press 1:1 mixture.
Preferably, the nanometer bamboo carbon fiber layer by nanometer bamboo carbon fiber, nano silver fibre, monocrystalline sapphire whisker and is glued
Glue fiber forms；Contain 0.8%-1% ceramic powders and coupling agent in viscose rayon, coupling agent is the 0.1%- of ceramic powders weight
0.3%；Ceramic powders are made of following weight percent composition：Manganese dioxide 10%-15%, tungstic acid 5%-8%, zirconium dioxide
30%-60%, silica 35%-40%, titanium dioxide 5%-15%；Coupling agent is titanate esters.
Preferably, the preparation method of the viscose rayon is：（1）, by manganese dioxide, tungstic acid, zirconium dioxide, dioxy
SiClx and titanium dioxide mixing, are crushed to the ceramic powders that average grain diameter is 1-2 μm after sintering；（2）, by coupling agent with it is described
Ceramic powders mix, and obtain modified ceramic powder；（3）, by the modified ceramic powder and viscose glue blending, squeeze out, slice, be made
Viscose glue is sliced；（4）, by the viscose glue be sliced heating melting, squeeze, spinneret molding, you can be made viscose rayon.
Preferably, the preparation method of nanometer bamboo carbon fiber layer is：
（1）, nanometer bamboo carbon fiber, nano silver fibre, monocrystalline sapphire whisker and viscose rayon be uniformly mixed, dispersion is added
Agent, binder, softening agent are stirred, and dry processing；
（2）, step will be passed through（1）The fiber of processing is handled through rove, spun yarn, automatic winding, yarn steaming, high speed doubling, double twisting
To spun yarn；
（3）, weaved using cassimere twill；
（4）, to fabric carry out washing process, water temperature control at 35-38 DEG C, wash 5-8min；
（5）, adjustment pH value to 5-7, be warming up to 80 DEG C, then impregnate 50 minutes, dry, cut obtained nanometer bamboo carbon fiber layer.
The beneficial effects of the invention are as follows：One, damping, shield foot, since the downside of insole half sole and insole heel is set respectively
There is beam, therefore, insole elasticity is good, and hardness is moderate, can effectively absorb in walking, active procedure and be rushed to foot bones generation
Hit power, protection vola bone, ankle-joint and knee joint；Secondly, alleviate medicine, the present invention according to principle of human engineering,
Insole pads center portion position setting ovum type convex surface, is bonded arch portion, sole center of gravity is redistributed, full sole stress equalization is made, alleviate
Activity, walking, generated stress fatigue of standing；Thirdly, stablize it is anti-skidding, it is low early and high after, it is outer thickness in it is thin, gravity leans forward so that
Toe has the activity space of bigger, conducive to toe stretching, extension, grabs ground, convex grain and spiral grooves design, significantly enhances frictional force, subtract
Rear cunning and the sideslip in active procedure are lacked, biped are made more to balance, support body more balances；Four, prevent ankle injury, this hair
Thin in bright low early and high after, outer thickness, the downside of waist corresponds to the flexible shield foot of position setting of human body arch portion, middle waist in insole
Portion both sides, which thicken, to be surrounded, and foot is wrapped up, joint displacements that can be during preventive activities, prevents to turn up, sprain the ankle situation, effectively
Reduce the risk that podarthrum is injured unexpectedly；Five, health care massage, the ovum type that insole pad center portion position is provided with spiral grooves are convex
Face can massage arch of the foot acupuncture point, effectively facilitate vola blood circulation；Six, memory bubble is continuous has outstanding memory function, after deformation
It can restore original form, and good permeability rapidly, the spiny jujuba seed powder used, cortex albiziae powder, glossy ganoderma powder, which have, promotes blood to follow
Ring relieves fatigue, and stablizes the function of Mood of Pregnancy and resistance building；Seven, the special preparation side of nanometer bamboo carbon fiber layer
Method makes insole with stronger self-cleaning function and odor-resistant result, and there is anti-inflammatory analgetic, relieve fatigue and prevent spur etc.
Effect.
Description of the drawings
Fig. 1 is the dispersed structure schematic diagram one of the present invention.
Fig. 2 is the dispersed structure schematic diagram two of the present invention.
In figure：1. insole half sole；2. insole pads the heart；3. waist in insole；4. insole heel；5. horizontal type groove；6. perpendicular type ditch
Slot；7. half sole beam；8. ovum type convex surface；9. elasticity shield foot；10. round convex surface；11. back heel shock-absorbing pad；12. convex grain；13.
Nanometer bamboo carbon fiber layer；14. the first polyurethane slow rebound layer；15. the second polyurethane slow rebound layer.
Specific implementation mode
Xia Mianjiehefutuduibenfamingjiegouyuanlihegongzuoyuanlizuojinyibuxiangxishuoming.
As shown in Figure 1 and Figure 2, the present invention is a kind of pregnant woman's Special shoe pad, including insole body, from the front end of insole body
Include waist 3 and insole heel 4 in insole half sole 1, the insole pad heart 2, insole successively to rear end, it is characterised in that：Before the insole
The upside of the palm 1 is arranged with 4~10 horizontal type grooves 5 and 2~10 perpendicular type grooves 6, and the horizontal type groove 5 and perpendicular type groove 6 divide
The both ends of insole half sole 1 are not extended to, and the downside of the insole half sole 1 is equipped with half sole beam 7,7 shape of half sole beam
Shape is spur blade profile；The upside of the insole pad heart 2 is equipped with ovum type convex surface 8, and ovum type convex surface 8 is equipped with pad heart damping spiral goove
Slot；The both sides of waist 3 up tilt respectively in the insole, and the downside of waist 3 is set corresponding to the position of human body arch portion in insole
It is equipped with elasticity shield foot 9, the elasticity shield foot 9 is around waist 3 in entire insole；It is equipped on the upside of the middle part of the insole heel 4
Round convex surface 10, the round convex surface 10 are equipped with back heel shock-absorbing spiral grooves, and the outer of the insole heel 4 up tilts,
It tilts tilting height of the height less than 3 both sides of waist in insole, and back heel shock-absorbing pad is equipped on the downside of the middle part of the insole heel 4
11, the shape of back heel shock-absorbing pad 11 is corresponding with the shape on round convex surface 10.
As shown in Figure 1 and Figure 2, the upside of the insole half sole 1 is arranged with 5~9 horizontal type grooves 5 and 2~8 perpendicular type ditches
Slot 6；The back heel shock-absorbing pad 11 is equipped with the convex grain 12 of multiple upper flats.
As shown in Figure 1 and Figure 2, the insole body includes nanometer bamboo carbon fiber layer 13, the first polyurethane successively from top to bottom
Low resilience layer 14 and the second polyurethane slow rebound layer 15；The thickness of the nanometer bamboo carbon fiber layer 13 is 0.3~0.8mm, described
The thickness of first polyurethane slow rebound layer 14 is 3~6mm, and the thickness of the second polyurethane slow rebound layer 15 is 3~6mm.It receives
Rice bamboo 13 has the characteristics that moisture absorption breathes freely, is bacteriostasis antibiosis, cool in summer and warm in winter, environmentally protective；First polyurethane slow rebound
Layer 14 and the second polyurethane slow rebound layer 15 have environmentally friendly degradable, ventilative, deodorization.
As shown in Figure 1 and Figure 2, the downside of the second polyurethane slow rebound layer 15 is respectively equipped with preceding accommodating cavity, middle accommodating cavity
And rear accommodating cavity, before the half sole beam 7 is set in accommodating cavity, the elasticity shield foot 9 is set in middle accommodating cavity, after described
It is set in rear accommodating cavity with beam 11.
As shown in Figure 1 and Figure 2, the first polyurethane slow rebound layer 14 and the second polyurethane slow rebound layer 15 are polyether-type
Remember foam sponge layer；The thickness of the half sole beam 7 is 2~10mm, and the thickness of the back heel shock-absorbing pad 11 is 3~12mm.
It is material prescription and process example below.
Embodiment 1
First polyurethane slow rebound layer 14 and the second polyurethane slow rebound layer 15 are made of the following raw material reaction foaming：First is poly-
50 parts of ethoxylated polyhydric alcohol, the second 45 parts of polyether polyol, 5 parts of methyl diphenylene diisocyanate, 1 part of spiny jujuba seed powder, cortex albiziae powder
0.8 part, 1 part of glossy ganoderma powder, 2 parts of water, 0.5 part of silicone oil, 0.2 part of catalyst, 0.5 part of foaming agent, 2~5 parts of crosslinking agent.
The preparation method of first polyurethane slow rebound layer 14 and the second polyurethane slow rebound layer 15 is：By corresponding parts by weight
The first polyether polyol, the second polyether polyol, methyl diphenylene diisocyanate, spiny jujuba seed powder, cortex albiziae powder and ganoderma lucidum
Powder is added in mixer and stirs evenly, and is heated to 35~38 degrees Celsius, other raw materials of corresponding number are added to mixing
In device, high-speed stirred is poured into after 6~8 seconds after mold foams and cure, and obtains remembering foam sponge layer accordingly；First polyethers
The hydroxyl value of polyalcohol is 72 mgKOH/g, and the hydroxyl value of molecular weight 8500, second polyether polyol is 58 mgKOH/g, point
Son amount is 4900, and the silicone oil is BF-2370 and two kinds of mass ratioes of B-4900 are 3：1 mixture；The catalyst is N, N-
Dimethylaminoethyl-N- methyl amino ethanols and acetylacetone,2,4-pentanedione zirconium mass ratio are 0.5：1 mixture；The foaming agent is charcoal
It is black；Crosslinking agent is that ethylenediamine and triethylene glycol press 1:1 mixture.
The nanometer bamboo carbon fiber layer 13 is fine by nanometer bamboo carbon fiber, nano silver fibre, monocrystalline sapphire whisker and viscose glue
Dimension composition；Contain 0.8% ceramic powders and coupling agent in viscose rayon, coupling agent is the 0.1% of ceramic powders weight；Ceramic powders
It is made of following weight percent composition：Manganese dioxide 10%, tungstic acid 5%, zirconium dioxide 30, silica 35, titanium dioxide
Titanium 5%；Coupling agent is titanate esters.
The preparation method of the viscose rayon is：（1）, by manganese dioxide, tungstic acid, zirconium dioxide, silica and
Titanium dioxide mixes, and is crushed to the ceramic powders that average grain diameter is 1-2 μm after sintering；（2）, by coupling agent and the ceramic powder
End mixing, obtains modified ceramic powder；（3）, by the modified ceramic powder and viscose glue blending, squeeze out, slice, obtained viscose glue is cut
Piece；（4）, by the viscose glue be sliced heating melting, squeeze, spinneret molding, you can be made viscose rayon.
The preparation method of nanometer bamboo carbon fiber layer 13 is：
（1）, nanometer bamboo carbon fiber, nano silver fibre, monocrystalline sapphire whisker and viscose rayon be uniformly mixed, dispersion is added
Agent, binder, softening agent are stirred, and dry processing；
（2）, step will be passed through（1）The fiber of processing is handled through rove, spun yarn, automatic winding, yarn steaming, high speed doubling, double twisting
To spun yarn；
（3）, weaved using cassimere twill；
（4）, to fabric carry out washing process, water temperature control at 35-38 DEG C, wash 5-8min；
（5）, adjustment pH value to 5-7, be warming up to 80 DEG C, then impregnate 50 minutes, dry, cut obtained nanometer bamboo carbon fiber layer
13。
Embodiment 2
First polyurethane slow rebound layer 14 and the second polyurethane slow rebound layer 15 are made of the following raw material reaction foaming：First is poly-
50 parts of ethoxylated polyhydric alcohol, the second 45 parts of polyether polyol, 15 parts of methyl diphenylene diisocyanate, 3 parts of spiny jujuba seed powder, cortex albiziae powder
2.5 parts, 3 parts of glossy ganoderma powder, 13 parts of water, 3 parts of silicone oil, 1 part of catalyst, 1 part of foaming agent, 5 parts of crosslinking agent.
The preparation method of first polyurethane slow rebound layer 14 and the second polyurethane slow rebound layer 15 is：By corresponding parts by weight
The first polyether polyol, the second polyether polyol, methyl diphenylene diisocyanate, spiny jujuba seed powder, cortex albiziae powder and ganoderma lucidum
Powder is added in mixer and stirs evenly, and is heated to 35~38 degrees Celsius, other raw materials of corresponding number are added to mixing
In device, high-speed stirred is poured into after 6~8 seconds after mold foams and cure, and obtains remembering foam sponge layer accordingly；First polyethers
The hydroxyl value of polyalcohol is 90 mgKOH/g, and the hydroxyl value of molecular weight 9500, second polyether polyol is 68 mgKOH/g, point
Son amount is 6500, and the silicone oil is BF-2370 and two kinds of mass ratioes of B-4900 are 3：1 mixture；The catalyst is N, N-
Dimethylaminoethyl-N- methyl amino ethanols and acetylacetone,2,4-pentanedione zirconium mass ratio are 0.5：1 mixture；The foaming agent is charcoal
It is black；Crosslinking agent is that ethylenediamine and triethylene glycol press 1:1 mixture.
The nanometer bamboo carbon fiber layer 13 is fine by nanometer bamboo carbon fiber, nano silver fibre, monocrystalline sapphire whisker and viscose glue
Dimension composition；Contain 1% ceramic powders and coupling agent in viscose rayon, coupling agent is the 0.3% of ceramic powders weight；Ceramic powders by
Following weight percent composition is made：Manganese dioxide 15%, tungstic acid 8%, zirconium dioxide 60%, silica 40%, titanium dioxide
Titanium 15%；Coupling agent is titanate esters.
The preparation method of the viscose rayon is：（1）, by manganese dioxide, tungstic acid, zirconium dioxide, silica and
Titanium dioxide mixes, and is crushed to the ceramic powders that average grain diameter is 1-2 μm after sintering；（2）, by coupling agent and the ceramic powder
End mixing, obtains modified ceramic powder；（3）, by the modified ceramic powder and viscose glue blending, squeeze out, slice, obtained viscose glue is cut
Piece；（4）, by the viscose glue be sliced heating melting, squeeze, spinneret molding, you can be made viscose rayon.
The preparation method of nanometer bamboo carbon fiber layer 13 is：
（1）, nanometer bamboo carbon fiber, nano silver fibre, monocrystalline sapphire whisker and viscose rayon be uniformly mixed, dispersion is added
Agent, binder, softening agent are stirred, and dry processing；
（2）, step will be passed through（1）The fiber of processing is handled through rove, spun yarn, automatic winding, yarn steaming, high speed doubling, double twisting
To spun yarn；
（3）, weaved using cassimere twill；
（4）, to fabric carry out washing process, water temperature control at 35-38 DEG C, wash 5-8min；
（5）, adjustment pH value to 5-7, be warming up to 80 DEG C, then impregnate 50 minutes, dry, cut obtained nanometer bamboo carbon fiber layer
13。
Embodiment 3
First polyurethane slow rebound layer 14 and the second polyurethane slow rebound layer 15 are made of the following raw material reaction foaming：First is poly-
50 parts of ethoxylated polyhydric alcohol, the second 45 parts of polyether polyol, 12 parts of methyl diphenylene diisocyanate, 2.8 parts of spiny jujuba seed powder, cortex albiziae
1.5 parts of powder, 1.9 parts of glossy ganoderma powder, 8 parts of water, 1.65 parts of silicone oil, 0.8 part of catalyst, 0.75 part of foaming agent, 3.6 parts of crosslinking agent.
The preparation method of first polyurethane slow rebound layer 14 and the second polyurethane slow rebound layer 15 is：By corresponding parts by weight
The first polyether polyol, the second polyether polyol, methyl diphenylene diisocyanate, spiny jujuba seed powder, cortex albiziae powder and ganoderma lucidum
Powder is added in mixer and stirs evenly, and is heated to 35~38 degrees Celsius, other raw materials of corresponding number are added to mixing
In device, high-speed stirred is poured into after 6~8 seconds after mold foams and cure, and obtains remembering foam sponge layer accordingly；First polyethers
The hydroxyl value of polyalcohol is 79 mgKOH/g, and the hydroxyl value of molecular weight 8000, second polyether polyol is 60 mgKOH/g, point
Son amount is 6600, and the silicone oil is BF-2370 and two kinds of mass ratioes of B-4900 are 3：1 mixture；The catalyst is N, N-
Dimethylaminoethyl-N- methyl amino ethanols and acetylacetone,2,4-pentanedione zirconium mass ratio are 0.5：1 mixture；The foaming agent is charcoal
It is black；Crosslinking agent is that ethylenediamine and triethylene glycol press 1:1 mixture.
The nanometer bamboo carbon fiber layer 13 is fine by nanometer bamboo carbon fiber, nano silver fibre, monocrystalline sapphire whisker and viscose glue
Dimension composition；Contain 0.86% ceramic powders and coupling agent in viscose rayon, coupling agent is the 0.22% of ceramic powders weight；Ceramic powder
End is made of following weight percent composition：Manganese dioxide 13%, tungstic acid 6.5%, zirconium dioxide 45%, silica 39%,
Titanium dioxide 6.5%；Coupling agent is titanate esters.
The preparation method of the viscose rayon is：（1）, by manganese dioxide, tungstic acid, zirconium dioxide, silica and
Titanium dioxide mixes, and is crushed to the ceramic powders that average grain diameter is 1-2 μm after sintering；（2）, by coupling agent and the ceramic powder
End mixing, obtains modified ceramic powder；（3）, by the modified ceramic powder and viscose glue blending, squeeze out, slice, obtained viscose glue is cut
Piece；（4）, by the viscose glue be sliced heating melting, squeeze, spinneret molding, you can be made viscose rayon.
The preparation method of nanometer bamboo carbon fiber layer 13 is：
（1）, nanometer bamboo carbon fiber, nano silver fibre, monocrystalline sapphire whisker and viscose rayon be uniformly mixed, dispersion is added
Agent, binder, softening agent are stirred, and dry processing；
（2）, step will be passed through（1）The fiber of processing is handled through rove, spun yarn, automatic winding, yarn steaming, high speed doubling, double twisting
To spun yarn；
（3）, weaved using cassimere twill；
（4）, to fabric carry out washing process, water temperature control at 35-38 DEG C, wash 5-8min；
（5）, adjustment pH value to 5-7, be warming up to 80 DEG C, then impregnate 50 minutes, dry, cut obtained nanometer bamboo carbon fiber layer
13。
Embodiment 4
First polyurethane slow rebound layer 14 and the second polyurethane slow rebound layer 15 are made of the following raw material reaction foaming：First is poly-
50 parts of ethoxylated polyhydric alcohol, the second 45 parts of polyether polyol, 6 parts of methyl diphenylene diisocyanate, 1.2 parts of spiny jujuba seed powder, cortex albiziae
1.7 parts of powder, 1.2 parts of glossy ganoderma powder, 12 parts of water, 2.7 parts of silicone oil, 0.6 part of catalyst, 0.65 part of foaming agent, 3.5 parts of crosslinking agent.
The preparation method of first polyurethane slow rebound layer 14 and the second polyurethane slow rebound layer 15 is：By corresponding parts by weight
The first polyether polyol, the second polyether polyol, methyl diphenylene diisocyanate, spiny jujuba seed powder, cortex albiziae powder and ganoderma lucidum
Powder is added in mixer and stirs evenly, and is heated to 35~38 degrees Celsius, other raw materials of corresponding number are added to mixing
In device, high-speed stirred is poured into after 6~8 seconds after mold foams and cure, and obtains remembering foam sponge layer accordingly；First polyethers
The hydroxyl value of polyalcohol is 88 mgKOH/g, and the hydroxyl value of molecular weight 8800, second polyether polyol is 61 mgKOH/g, point
Son amount is 5900, and the silicone oil is BF-2370 and two kinds of mass ratioes of B-4900 are 3：1 mixture；The catalyst is N, N-
Dimethylaminoethyl-N- methyl amino ethanols and acetylacetone,2,4-pentanedione zirconium mass ratio are 0.5：1 mixture；The foaming agent is charcoal
It is black；Crosslinking agent is that ethylenediamine and triethylene glycol press 1:1 mixture.
The nanometer bamboo carbon fiber layer 13 is fine by nanometer bamboo carbon fiber, nano silver fibre, monocrystalline sapphire whisker and viscose glue
Dimension composition；Contain 0.85% ceramic powders and coupling agent in viscose rayon, coupling agent is the 0.26% of ceramic powders weight；Ceramic powder
End is made of following weight percent composition：Manganese dioxide 11.5%, tungstic acid 6.3%, zirconium dioxide 45%, silica
36.5%, titanium dioxide 12.8%；Coupling agent is titanate esters.
The preparation method of the viscose rayon is：（1）, by manganese dioxide, tungstic acid, zirconium dioxide, silica and
Titanium dioxide mixes, and is crushed to the ceramic powders that average grain diameter is 1-2 μm after sintering；（2）, by coupling agent and the ceramic powder
End mixing, obtains modified ceramic powder；（3）, by the modified ceramic powder and viscose glue blending, squeeze out, slice, obtained viscose glue is cut
Piece；（4）, by the viscose glue be sliced heating melting, squeeze, spinneret molding, you can be made viscose rayon.
The preparation method of nanometer bamboo carbon fiber layer 13 is：
（1）, nanometer bamboo carbon fiber, nano silver fibre, monocrystalline sapphire whisker and viscose rayon be uniformly mixed, dispersion is added
Agent, binder, softening agent are stirred, and dry processing；
（2）, step will be passed through（1）The fiber of processing is handled through rove, spun yarn, automatic winding, yarn steaming, high speed doubling, double twisting
To spun yarn；
（3）, weaved using cassimere twill；
（4）, to fabric carry out washing process, water temperature control at 35-38 DEG C, wash 5-8min；
（5）, adjustment pH value to 5-7, be warming up to 80 DEG C, then impregnate 50 minutes, dry, cut obtained nanometer bamboo carbon fiber layer
13。
The the first polyurethane slow rebound layer 14 and the second polyurethane slow rebound layer 15 of embodiment 5 are same as Example 1, but make
With common nanometer bamboo carbon fiber layer.
The the first polyurethane slow rebound layer 14 and the second polyurethane slow rebound layer 15 of embodiment 6 are same as Example 2, but make
With common nanometer bamboo carbon fiber layer.
The nanometer bamboo carbon fiber layer of embodiment 7 is same as Example 1, but the first polyurethane slow rebound layer 14 and the second poly- ammonia
Ester low resilience layer 15 is that conventional polyurethanes bubble is continuous.
8 first polyurethane slow rebound layer 14 of embodiment and the second polyurethane slow rebound layer 15 and nanometer bamboo carbon fiber layer make
It is made with common existing material and method.
By the first polyurethane slow rebound layer 14 made from above example 1-8 and the second polyurethane slow rebound layer 15, nanometer
Bamboo and other structures are assembled into insole.
Common insole of the embodiment 1-7 comfortable foot feelings degree obviously higher than embodiment 8, embodiment 1-7 is found through experiments that
Experimental result it is as follows：
The compare good permeability of embodiment 5,6, comfort level of embodiment 1-4 and embodiment 7 is high, has and apparent promotes blood
It recycles, relieve fatigue, stablize wearer's mood and the function of resistance building.
Embodiment 1-4 and embodiment 5 compare embodiment 7 with 6, have stronger self-cleaning function and odor-resistant result, and
It with anti-inflammatory analgetic, relieves fatigue and prevents spur and other effects, placed 72 hours in 37 DEG C of incubators after wearing, detection bacterium
3 every square centimeter of content or less.
The above is only better embodiment of the present invention, and every technical solution according to the present invention is to above implementation
Any subtle modifications, equivalent variations and modifications, belong in the range of technical solution of the present invention made by mode.
Claims (10)
1. a kind of pregnant woman's Special shoe pad, including insole body, from the front end of insole body to rear end, include successively insole half sole,
Insole pads waist and insole heel in the heart, insole, it is characterised in that：4~10 horizontal type ditches are arranged on the upside of the insole half sole
Slot and 2~10 perpendicular type grooves, the horizontal type groove and perpendicular type groove extend respectively to the both ends of insole half sole, before the insole
The downside of the palm is equipped with half sole beam, and the half sole beam shape is spur blade profile；The upside of the insole pad heart is equipped with ovum
Type convex surface, ovum type convex surface are equipped with pad heart damping spiral grooves；The both sides of waist up tilt respectively in the insole, and in insole
Flexible shield foot is arranged in the position that the downside of waist corresponds to human body arch portion, and the elasticity shield foot is in entire insole
Waist；Round convex surface is equipped on the upside of the middle part of the insole heel, the round convex surface is equipped with back heel shock-absorbing spiral grooves, described
The outer of insole heel up tilts, and tilts tilting height of the height less than waist both sides in insole, in the insole heel
Subordinate side is equipped with back heel shock-absorbing pad, and the shape of back heel shock-absorbing pad is corresponding with the shape on round convex surface.
2. pregnant woman's Special shoe pad according to claim 1, it is characterised in that：It is arranged with 5~9 on the upside of the insole half sole
The horizontal type groove of item and 2~8 perpendicular type grooves；The back heel shock-absorbing pad is equipped with the convex grain of multiple upper flats.
3. pregnant woman's Special shoe pad according to claim 1, it is characterised in that：The insole body includes successively from top to bottom
Nanometer bamboo carbon fiber layer, the first polyurethane slow rebound layer and the second polyurethane slow rebound layer；The thickness of the nanometer bamboo carbon fiber layer
Degree is 0.3~0.8mm, and the thickness of the first polyurethane slow rebound layer is 3~6mm, the second polyurethane slow rebound layer
Thickness is 3~6mm.
4. pregnant woman's Special shoe pad according to claim 3, it is characterised in that：The downside of the second polyurethane slow rebound layer
It is respectively equipped with preceding accommodating cavity, middle accommodating cavity and rear accommodating cavity, before the half sole beam is set in accommodating cavity, the elasticity shield foot
Portion is set in middle accommodating cavity, and the back heel shock-absorbing pad is set in rear accommodating cavity.
5. pregnant woman's Special shoe pad according to any one of Claims 1 to 4, it is characterised in that：First polyurethane
Low resilience layer and the second polyurethane slow rebound layer are that polyether-type remembers foam sponge layer；The thickness of the half sole beam is 2~10mm,
The thickness of the back heel shock-absorbing pad is 3~12mm.
6. pregnant woman's Special shoe pad according to claim 1, it is characterised in that：First polyurethane slow rebound layer and the second poly- ammonia
Ester low resilience layer is made of the following raw material reaction foaming：First 50 parts of polyether polyol, the second 45 parts of polyether polyol, hexichol
5~15 parts of dicyclohexylmethane diisocyanate, 1~3 part of spiny jujuba seed powder, 0.8~2.5 part of cortex albiziae powder, 1~3 part of glossy ganoderma powder, water 2~
13 parts, 0.5~3 part of silicone oil, 0.2~1 part of catalyst, 0.5~1 part of foaming agent, 2~5 parts of crosslinking agent.
7. pregnant woman's Special shoe pad according to claim 6, it is characterised in that：First polyurethane slow rebound layer and the second poly- ammonia
The preparation method of ester low resilience layer is：By the first polyether polyol, the second polyether polyol, diphenylmethyl of corresponding parts by weight
Alkane diisocyanate, spiny jujuba seed powder, cortex albiziae powder and glossy ganoderma powder are added in mixer and stir evenly, and are heated to 35~38 and take the photograph
Other raw materials of corresponding number are added in mixer by family name's degree, and high-speed stirred pours into mold and foams and cure after 6~8 seconds
Afterwards, it obtains remembering foam sponge layer accordingly；The hydroxyl value of first polyether polyol is 70~90 mgKOH/g, molecular weight 8000
~10000, the hydroxyl value of second polyether polyol is 55~70 mgKOH/g, and molecular weight is 4500~7000, the silicone oil
It is 3 for two kinds of mass ratioes of BF-2370 and B-4900：1 mixture；The catalyst is N, N- dimethylaminoethyl-N- methyl
Ethylaminoethanol and acetylacetone,2,4-pentanedione zirconium mass ratio are 0.5：1 mixture；The foaming agent is carbon black；Crosslinking agent is ethylenediamine and three
Glycol presses 1:1 mixture.
8. pregnant woman's Special shoe pad according to claim 3, it is characterised in that：The nanometer bamboo carbon fiber layer is by bamboo charcoal nano
Fiber, nano silver fibre, monocrystalline sapphire whisker and viscose rayon composition；In viscose rayon containing 0.8%-1% ceramic powders and
Coupling agent, coupling agent are the 0.1%-0.3% of ceramic powders weight；Ceramic powders are made of following weight percent composition：Dioxy
Change manganese 10%-15%, tungstic acid 5%-8%, zirconium dioxide 30%-60%, silica 35%-40%, titanium dioxide 5%-15%；Coupling
Agent is titanate esters.
9. pregnant woman's Special shoe pad according to claim 8, it is characterised in that：The preparation method of the viscose rayon is：
（1）, by manganese dioxide, tungstic acid, zirconium dioxide, silica and titanium dioxide mix, be crushed to average grain after sintering
The ceramic powders that diameter is 1-2 μm；（2）, coupling agent mixed with the ceramic powders, obtain modified ceramic powder；（3）, by institute
Modified ceramic powder and viscose glue blending are stated, is squeezed out, slice, viscose glue slice is made；（4）, by the viscose glue be sliced heating melting, squeeze
Pressure, spinneret molding, you can viscose rayon is made.
10. pregnant woman's Special shoe pad according to claim 8, it is characterised in that：The preparation method of nanometer bamboo carbon fiber layer is
（1）, nanometer bamboo carbon fiber, nano silver fibre, monocrystalline sapphire whisker and viscose rayon be uniformly mixed, dispersion is added
Agent, binder, softening agent are stirred, and dry processing；
（2）, step will be passed through（1）The fiber of processing is handled through rove, spun yarn, automatic winding, yarn steaming, high speed doubling, double twisting
To spun yarn；
（3）, weaved using cassimere twill；
（4）, to fabric carry out washing process, water temperature control at 35-38 DEG C, wash 5-8min；
（5）, adjustment pH value to 5-7, be warming up to 80 DEG C, then impregnate 50 minutes, dry, cut obtained nanometer bamboo carbon fiber layer.